The subjects of this study were mortars with varying amounts of recycled ceramic aggregate (RCA). As part of the fine aggregate, the RCA volume share is 10%, 20%, 30%, 50% and 100%. First, fresh mixture parameters were evaluated, such as consistency and air content measurement by pressure method. Next, specimens were molded for compressive strength and flexural strength tests after 7, 28 and 56 days of curing. The thermo-humidity parameters of the composites, i.e., coefficient of capillary action and thermal conductivity coefficient were also investigated using nonstationary method. Sorption kinetics of the mortars at different moisture conditions at 20 °C were also evaluated. Sorption tests were carried out using two methods: TM and DVS. The sorption isotherms were plotted on the basis of equilibrium moisture content for the materials tested. The isotherms obtained by the two methods were evaluated. The results allowed us to draw conclusions on the physical and mechanical parameters of the composites with different amounts of RCA and to evaluate the ability to absorb moisture from the environment by these types of materials. A clear decrease in the compressive strength after 28 days of curing compared to the reference mortar was recorded after using 30% to 100% of RCA (approx. 26% to approx. 39%). Changes in flexural strength were significantly smaller, reaching no more than approx. 7.5%. It was shown that the amount of RCA translates into the ability to sorb moisture, which may affect the application of this type of composites. The amount of RCA translates also into the thermal conductivity coefficient, which decreased with increasing amount of RCA.
In line with the trend of using waste raw materials in the technology of building materials, experimental studies of cement mortars containing various amounts of fine-grained waste aggregate were carried out. The waste aggregate was based on an incinerated municipal sewage sludge which was mechanically crushed to an appropriate grading. Chemical and physical properties of the waste aggregate are presented. Mortars with varying amounts of waste aggregate as a replacement for natural sand were prepared. Study determines compressive strength and flexural strength up to 56 days. Properties such as capillary action, air content and thermal conductivity were determined. The results of the tests has shown that the incinerated waste sludge can be used as a partial or total replacement for natural aggregate. In mortars with waste aggregate, a favorable relation between flexural and compressive strengths was observed, which translates into increased strength of the interfacial transition zone. A significant increase in water absorption was observed for mortars containing high amounts of waste aggregate, which is directly related to its porous structure. Conducted studied prove that the aggregate obtained from incineration of the municipal sewage sludge can a feasible alternative for natural aggregates in production of masonry and rendering mortars for construction purposes.
This study presents the results of an experimental investigation of the effects of nanosilica (NS) on the strength development, transport properties, thermal conductivity, air-void, and pore characteristics of lightweight aggregate concrete (LWAC), with an oven-dry density <1000 kg/m3. Four types of concrete mixtures, containing 0 wt.%, 1 wt.%, 2 wt.%, and 4 wt.% of NS were prepared. The development of flexural and compressive strengths was determined for up to 90 days of curing. In addition, transport properties and microstructural properties were determined, with the use of RapidAir, mercury intrusion porosimetry (MIP), and scanning electron microscopy (SEM) techniques. The experimental results showed that NS has remarkable effects on the mechanical and transport properties of LWACs, even in small dosages. A significant improvement in strength and a reduction of transport properties, in specimens with an increased NS content, was observed. However, the positive effects of NS were more pronounced when a higher amount was incorporated into the mixtures (>1 wt.%). NS contributed to compaction of the LWAC matrix and a modification of the air-void system, by increasing the amount of solid content and refining the fine pore structure, which translated to a noticeable improvement in mechanical and transport properties. On the other hand, NS decreased the consistency, while increasing the viscosity of the fresh mixture. An increment of superplasticizer (SP), along with a decrement of stabilizer (ST) dosages, are thus required.
Recently, the recycling of waste glass has become a worldwide issue in the reduction of waste and energy consumption. Waste glass can be utilized in construction materials, and understanding its effects on material properties is crucial in developing advanced materials. In this study, recycled crushed and expanded glasses are used as lightweight aggregates for concrete, and their relation to the material characteristics and properties is investigated using several approaches. Lightweight concrete specimens containing only crushed and expanded waste glass as fine aggregates are produced, and their pore and structural characteristics are examined using image-based methods, such as scanning electron microscopy (SEM), X-ray computed tomography (CT), and automated image analysis (RapidAir). The thermal properties of the materials are measured using both Hot Disk and ISOMET devices to enhance measurement accuracy. Mechanical properties are also evaluated, and the correlation between material characteristics and properties is evaluated. As a control group, a concrete specimen with natural fine sand is prepared, and its characteristics are compared with those of the specimens containing crushed and expanded waste glass aggregates. The obtained results support the usability of crushed and expanded waste glass aggregates as alternative lightweight aggregates.
The recycling of waste glass is a major problem for municipalities worldwide. The problem concerns especially colored waste glass which, due to its low recycling rate as result of high level of impurity, has mostly been dumped into landfills. In recent years, a new use was found for it: instead of creating waste, it can be recycled as an additive in building materials. The aim of the study was to evaluate the possibility of manufacturing sustainable and self-cleaning cement mortars with use of commercially available nanomaterials and brown soda-lime waste glass. Mechanical and bactericidal properties of cement mortars containing brown soda-lime waste glass and commercially available nanomaterials (amorphous nanosilica and cement containing nanocrystalline titanium dioxide) were analyzed in terms of waste glass content and the effectiveness of nanomaterials. Quartz sand is replaced with brown waste glass at ratios of 25%, 50%, 75% and 100% by weight. Study has shown that waste glass can act as a successful replacement for sand (up to 100%) to produce cement mortars while nanosilica is incorporated. Additionally, a positive effect of waste glass aggregate for bactericidal properties of cement mortars was observed.