Disordered topological insulator (TI) films have gained intense interest by benefiting from both the TI's exotic transport properties and the advantage of mass production by sputtering. Here, we report on the clear evidence of spin-charge conversion (SCC) in amorphous Gd-alloyed BixSe1-x (BSG)/CoFeB bilayers fabricated by sputtering, which could be related to the amorphous TI surface states. Two methods have been employed to study SCC in BSG (tBSG = 6-16 nm)/CoFeB(5 nm) bilayers with different BSG thicknesses. First, spin pumping is used to generate a spin current in CoFeB and detect SCC by the inverse Edelstein effect (IEE). The maximum SCC efficiency (SCE) is measured to be as large as 0.035 nm (IEE length λIEE) in a 6 nm thick BSG sample, which shows a strong decay when tBSG increases due to the increase of BSG surface roughness. The second method is THz time-domain spectroscopy, which reveals a small tBSG dependence of SCE, validating the occurrence of a pure interface state-related SCC. Furthermore, our angle-resolved photoemission spectroscopy data show dispersive two-dimensional surface states that cross the bulk gap until the Fermi level, strengthening the possibility of SCC due to the amorphous TI states. Our studies provide a new experimental direction toward the search for topological systems in amorphous solids.
RESUMEN
Perpendicular magnetic tunnel junctions (p-MTJs) switched utilizing bipolar electric fields have extensive applications in energy-efficient memory and logic devices. Voltage-controlled magnetic anisotropy linearly lowers the energy barrier of the ferromagnetic layer via the electric field effect and efficiently switches p-MTJs only with a unipolar behavior. Here, we demonstrate a bipolar electric field effect switching of 100 nm p-MTJs with a synthetic antiferromagnetic free layer through voltage-controlled exchange coupling (VCEC). The switching current density, â¼1.1 × 105 A/cm2, is 1 order of magnitude lower than that of the best-reported spin-transfer torque devices. Theoretical results suggest that the electric field induces a ferromagnetic-antiferromagnetic exchange coupling transition of the synthetic antiferromagnetic free layer and generates a fieldlike interlayer exchange coupling torque, which causes the bidirectional magnetization switching of p-MTJs. These results could eliminate the major obstacle in the development of spin memory devices beyond their embedded applications.