Room-temperature operation of npn- AlGaInAs/InP multiple quantum well transistor laser emitting at 1.3-µm wavelength.

Room-temperature pulsed operation of a 1.3-µm wavelength transistor laser (TL), consisting of a buried heterostructure (BH) with an npn configuration and an AlGaInAs/InP multiple-quantum-well (MQW) active region, was successfully attained. A threshold base current of 18 mA (threshold emitter current of 150 mA) was obtained with a stripe width of 1.3 µm and a cavity length of 500 µm. The transistor activity as well as the lasing operation were achieved at the same time, which is essential for the high-speed operation of TLs.

Lateral current injection GaInAsP/InP laser on semi-insulating substrate for membrane-based photonic circuits.

A room-temperature pulsed operation was demonstrated using lateral current injection-type lasers composed of a 400-nm-thick GaInAsP core layer with compressively strained 5 quantum wells. A threshold current of 105 mA and corresponding density of 1.3 kA/cm(2) (260 A/cm(2) per well) were obtained with the stripe width of 5.4 microm and the cavity length of 1.47 mm. A fundamental transverse mode operation was obtained with the narrower stripe device of 2.0 microm and the cavity length of 805 microm, while the threshold current and corresponding density were 49 mA and 3.0 kA/cm(2), respectively.