In this paper, an indium antimonide (InSb) saturable absorber (SA) was successfully fabricated. The saturable absorption properties of the InSb SA were studied, and they show a modulation depth and a saturable intensity of 5.17% and 9.23M W/c m 2, respectively. By employing the InSb SA and building the ring cavity laser structure, the bright-dark soliton operations were successfully obtained by increasing the pump power to 100.4 mW and adjusting the polarization controller. As the pump power increased from 100.4 to 180.3 mW, the average output power increased from 4.69 to 9.42 mW, the corresponding fundamental repetition rate was 2.85 MHz, and the signal-to-noise ratio was 68 dB. The experimental results show that InSb with excellent saturable absorption characteristics can be used as a SA to obtain pulse lasers. Therefore, InSb has important potential in fiber laser generation, further applications in optoelectronics, laser distance ranging, and optical fiber communication, and it can be widely developed.
In this work, a saturable absorber (SA) based on Cr2Si2Te6 (CST), with a modulation depth of 14.90% and saturation intensity of 4.81MW/cm2, was prepared by a liquid phase stripping method. Its nonlinear optical properties and application in obtaining mode-locked pulse output of bright-dark solitons are studied. When the pump power was 1250 mW, the maximum output power was 26.60 mW; the energy of the single pulse was 15.02 nJ, and the repetition rate was 1.77 MHz. Our results provided evidence that CST can be used as an excellent SA for a mode-locked laser and demonstrated that ferromagnetic insulators can be used for the study of bright-dark soliton pairs.
In our work, a new-type, to the best of our knowledge, ferromagnetic insulator and its nonlinear optical absorption characteristics and related ultrafast modulation applications were investigated. Cr2Si2Te6 saturable absorbers (SAs) with a modulation depth and a saturable intensity of 9.7% and 3.5MW/cm2 were fabricated. By adjusting the pump power to 120 mW and optimizing the polarization state, traditional soliton operations were obtained successfully; the corresponding duration of pulse and the fundamental repetition rate were â¼1.33ps and 6.70 MHz, and the signal-to-noise ratio was 50 dB. The experimental results reveal that Cr2Si2Te6 with excellent saturable absorption characteristics can be used as a SA to obtain ultrafast pulse lasers.