RESUMEN
OBJECTIVES: This study aimed to evaluate the dentin bond performance of various resin luting cement (RLC) systems combined with universal adhesives in different luting strategies. MATERIALS AND METHODS: Three self-adhesive resin luting cements (SRLCs) were used with universal adhesives as primers. Twelve specimens per group were prepared to measure shear bond strength (SBS) under distinct luting strategies in etch-&-rinse and self-etch modes. Regarding luting strategies, the bonded specimens were categorized into four groups based on tooth primer application and the curing mode of the SRLC paste: (i) with light irradiation of the tooth primer (wL) + dual-cure mode (DC) of the SRLC paste, (ii) wL + self-cure mode (SC) of the SRLC paste, (iii) without light irradiation of the tooth primer (woL) + DC mode of the SRLC paste, and (iv) woL + SC mode of the SRLC paste. Specimens were also subjected to different storage conditions: 24 h in water (baseline condition) and 10,000 cycles of thermal cycling. RESULTS: Luting strategy, storage condition, and SRLC system type significantly influenced dentin SBS values in both etching modes. Notably, certain SRLCs exhibited significantly higher dentin SBS when the primer was light-irradiated compared with no primer irradiation. CONCLUSION: Most SRLCs demonstrated higher dentin bond strength with light-irradiated primers, suggesting potential enhancement of dentin bond performance via primer light irradiation.
Asunto(s)
Recubrimiento Dental Adhesivo , Análisis del Estrés Dental , Ensayo de Materiales , Cementos de Resina , Resistencia al Corte , Cementos de Resina/química , Recubrimiento Dental Adhesivo/métodos , Recubrimientos Dentinarios/química , Propiedades de Superficie , Técnicas In Vitro , Cementos Dentales/química , Dentina , HumanosRESUMEN
OBJECTIVE: The color matching of single-shade resin composites after in-office whitening was investigated. MATERIALS AND METHODS: Four single-shade resin composites were used. A total of 35% hydrogen peroxide was used as the whitening agent. The resin composite was placed in a cavity of an artificially discolored bovine tooth. The color differences between the restoration and surrounding enamel before and after whitening were determined based on ΔE*ab, ΔE00, and ΔWID. The color stability, surface roughness (Sa), and surface gloss (GU) of the resin composite alone were also evaluated. Statistical analyses were performed using repeated-measures analysis of variance with the Tukey-Kramer test. RESULTS: Based on the 50:50% of perceptibility and acceptability thresholds of ΔE*ab and ΔE00, none of the resin composite restorations were clinically acceptable before or after whitening. Regarding ΔWID, although all resin composites showed "acceptable match" in the baseline, they showed "mismatch" after the third session of whitening. Most of the resin composites alone were stable in color against whitening. CONCLUSIONS: Although the single-shade resin composites failed to achieve the expected color matching on discolored teeth either before or after the whitening, the impact of the whitening on the color of the resin composite alone may be negligible.
RESUMEN
This study aimed to evaluate the bonding performance of self-adhesive flowable resin composites (SARs) to bovine teeth. Three SARs, one experimental, and two commercially available products, were used. The study parameters were shear bond strength (SBS), microleakage, and scanning electron microscopy (SEM) evaluation of bonding interfaces. The SBS of the materials was 14.1-15.1 MPa to enamel, 22.2-23.2 MPa to etched enamel, and 7.4-10.7 MPa to dentin. Specimens with pre-etching showed lower microleakage scores than those without pre-etching. SEM images of the interfaces of the materials showed excellent adaptation regardless of the substrate or etching mode. The study results indicate that enamel pre-etching can improve the bonding performance of SARs.
Asunto(s)
Grabado Ácido Dental , Resinas Compuestas , Recubrimiento Dental Adhesivo , Esmalte Dental , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Resistencia al Corte , Propiedades de Superficie , Animales , Bovinos , Resinas Compuestas/química , Recubrimiento Dental Adhesivo/métodos , Dentina , Técnicas In Vitro , Filtración Dental , Análisis del Estrés DentalRESUMEN
This study investigated the potential of BioUnion filler containing glass ionomer cement (GIC) to enhance the properties of enamel surrounding restorations, with a specific focus on the effect on hardness. The hardness of the bovine enamel immersed in the cement was measured using Vickers hardness numbers. Following sliding and impact wear simulations, the enamel facets were examined using confocal-laser-scanning microscopy and scanning-electron microscopy. Surface properties were further analyzed using energy-dispersive X-ray spectroscopy and X-ray diffraction (XRD). A significant increase in Vickers hardness numbers was observed in the BioUnion filler GIC after 2 days. Furthermore, the mean depth of enamel facets treated with BioUnion filler GIC was significantly less than that of untreated facets. Characteristic XRD peaks indicating the presence of hydroxyapatite were also observed. Our findings imply that GIC with BioUnion fillers enhances the mechanical properties of the tooth surface adjacent to the cement.
Asunto(s)
Esmalte Dental , Cementos de Ionómero Vítreo , Animales , Bovinos , Cementos de Ionómero Vítreo/química , Dureza , Propiedades de Superficie , Espectrometría por Rayos X , Ensayo de MaterialesRESUMEN
This study aimed to observe and compare the resin luting cement (RLC)/dentin interfaces of different types of RLC systems with scanning electron microscopy (SEM). This study evaluated six self-adhesive resin luting cement systems (SARLCs), four systems combining a SARLC with a tooth primer (SARLCPs), and six conventional resin luting cement systems (CVRLCs). Cured resin composite rods were bonded to bovine dentin using RLCs in different etching modes. The morphological features at the interfaces were observed using SEM. Although all RLCs in etch-&-rinse (ER) mode showed a clear hybrid layer, most SARLCs had a thinner and more porous hybrid layer than the SARLCPs and CVRLCs. All SARLCPs with primer and CVRLCs showed a thin high-density layer below the primer layer in both etching modes. CVRLCs and SARLCPs with primer treatment systems may be more versatile and reliable when compared to simplified RLC systems.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Animales , Bovinos , Microscopía Electrónica de Rastreo , Cementos de Resina/química , Cementos Dentales , Recubrimientos Dentinarios/química , Resinas Compuestas/química , Dentina , Ensayo de Materiales , Propiedades de SuperficieRESUMEN
OBJECTIVES: This study aimed to investigate the immediate dentin bond performance and bond durability of self-adhesive resin luting cements (RLCs) in combination with universal adhesives in different curing modes. METHODS: Two self-adhesive RLCs were used with universal adhesives as primers. They were also used alone as self-adhesive RLCs. Two multiple-step RLC systems were used as comparison materials. To measure the shear bond strength (SBS) in different curing modes, 12 specimens were prepared for each group. Stainless-steel rods were bonded to bovine dentin, and the bonded specimens were assigned to the baseline group (stored for 24 h) and artificially aged group (thermal cycling [TC], 10,000 cycles). After each storage period, the SBS of the bonded specimens was measured. The Knoop hardness number (KHN) of the cured RLCs was measured with or without primer application in different curing modes at 24 h and after 10,000 TC. The representative RLC/dentin interfaces were observed using scanning electron microscopy (SEM). RESULTS: Dentin SBS was significantly influenced by the RLC system but not by the curing mode. Self-adhesive RLCs alone showed significantly lower SBS values than self-adhesive RLCs with primer regardless of the curing mode or storage period. The storage period, curing mode, and RLC system significantly influenced the KHN. SIGNIFICANCE: The use of universal adhesives as a primer may help enhance the immediate dentin bond performance and bond durability of self-adhesive RLCs.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Animales , Bovinos , Cementos de Resina/química , Cementos Dentales , Recubrimientos Dentinarios/química , Ensayo de Materiales , Resistencia al Corte , Dentina , AdhesivosRESUMEN
This study aimed to evaluate the influence of surface pretreatment on the shear bond strength of resin luting cement to saliva-contaminated resin core foundation. The surface free energy (γS) of the adherent surfaces was examined. The two-way analysis of variance revealed that the surface pretreatment and storage conditions had a significant effect on the strength of the bond to resin core foundation. The γS values of the saliva-contaminated group were significantly lower than those of the other groups, and they tended to improve after surface pretreatment. The tendency of improvement in γS values differed depending on the type of pretreatment agents. Surface treatment with solutions containing functional monomers is effective in removing saliva contaminants from the resin core foundation surfaces and in creating an effective bonding surface for the resin luting cement.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Cementos Dentales/química , Saliva , Cementos de Resina/química , Ensayo de Materiales , Propiedades de Superficie , Resistencia al Corte , Análisis del Estrés DentalRESUMEN
This study aimed to determine the influence of surface roughness of the color adjustment potential restoration of universal resin composites. A structural colored resin composite (Omnichroma, OC) and a pigment-employed universal shade resin composite (Beautifil Unishade, BU) were used. Each resin composite was placed in a cavity to determine its ability to match the color of artificial teeth. The surface of the resin composites was polished with #800- or #2000-grit SiC paper before performing color measurements. One-way analysis of variance and Tukey post hoc tests were performed (α=0.05). The color difference (ΔE*ab) ranged from 2.5-3.9 for OC and 1.8-8.7 for BU. OC has a more stable color adjustment than BU. The color adjustment potential of universal resin composites was affected by the surface roughness of the restorations.
RESUMEN
The recently developed biphasic calcium phosphate cement (BCPC) consists of α-tricalcium phosphate-tetracalcium phosphate as the solid phase and calcium phosphate solution as the liquid phase. BCPC powder is composed of a single solid solution with a monomodal size distribution. Here, we used a bacterial leakage model to examine the utility of BCPC as a seal for root-end filling. We prepared large (median particle size=9.96 µm; BCPC-L) and small (median particle size=4.84 µm; BCPC-S) BCPC powders. In total, 45 single-rooted teeth were instrumented, resected at the root-end, and retrofilled with experimental materials. Mineral trioxide aggregate (MTA) was used as the control. After visual confirmation of BCPC powder size and retrofilling quality by microscopy, bacterial leakage tests were conducted using Enterococcus faecalis. The bacterial leakage tests did not reveal any significant differences between BCPC-S and MTA. Our findings suggest that BCPC-S is useful for root-end filling.
Asunto(s)
Filtración Dental , Materiales de Obturación del Conducto Radicular , Humanos , Compuestos de Calcio , Polvos , Óxidos , Cementos Dentales , Cementos de Ionómero Vítreo , Combinación de Medicamentos , Compuestos de Aluminio , Silicatos , Filtración Dental/microbiologíaRESUMEN
OBJECTIVE: This controlled randomized clinical trial determined the whitening efficacy and the intensity and absolute risk of tooth sensitivity in dual whitening when prefilled at-home whitening trays were used between in-office whitening intervals. MATERIALS AND METHODS: An in-office whitening agent containing 35% hydrogen peroxide was used. A prefilled tray with a whitening agent containing 6% hydrogen peroxide was used for at-home whitening. Sixty-six subjects were randomly assigned to three groups. Group I: at-home whitening was performed 10 times between the in-office whitening treatments. Group II: at-home whitening was performed five times between the in-office whitening treatments. Group III: only in-office whitening was performed. The tooth color changes were evaluated using a spectrophotometer. A visual analog scale was used to express the pain intensity. RESULTS: All the groups showed increased ΔE*ab, ΔE00 , and ΔWID with increased whitening sessions. Group I at the 3rd whitening session showed significantly higher ΔE*ab, ΔE00 , and ΔWID than group III. Tooth sensitivity showed higher values up to 24 h after whitening. CONCLUSIONS: Although dual whitening with the prefilled tray and in-office whitening had higher whitening ability than in-office whitening alone, the intensity and absolute risk of tooth sensitivity was similar. CLINICAL RELEVANCE: The dual whitening might produce faster and stronger whitening effects than in-office whitening alone.
Asunto(s)
Blanqueadores , Sensibilidad de la Dentina , Blanqueadores Dentales , Blanqueamiento de Dientes , Humanos , Peróxido de Hidrógeno , Ensayos Clínicos Controlados Aleatorios como Asunto , Resultado del TratamientoRESUMEN
This study investigated the enamel and dentin bond durability of a two-step adhesive system, using a universal adhesive-derived primer (G2-Bond Universal [GU]), and compared it with the two conventional, two-step, self-etch adhesive systems (Clearfil SE Bond 2 [CS] and OptiBond XTR [OX]) under thermal cycling (TC) and long-term water storage (WS). The shear bond strengths to bovine enamel and dentin were determined using the etch-and-rinse and self-etch modes. Twelve specimens per test group were prepared and further divided into the following subgroups: 1) subjected to TC, 2) long-term WS, and 3) WS for 24 h (baseline). The enamel and dentin bond durability of GU was superior to those of CS and OX in different etching modes and under different degradation conditions. The latest two-step adhesive system, which utilizes universal adhesives' benefits in its primer, might offer durable clinical bonding performances and can be widely used in a clinical setting.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Animales , Bovinos , Recubrimientos Dentinarios/química , Ensayo de Materiales , Dentina , Cementos de Resina/química , Agua , Resistencia al CorteRESUMEN
PURPOSE: To investigate the changes in the enamel bond performance of a two-step adhesive containing a primer derived from a universal adhesive in the early phase before 24 h and compare them to those of other adhesives. The Knoop hardness number (KHN) of the cured adhesive layers and resin composite was measured. MATERIALS AND METHODS: A new two-step adhesive using universal adhesive technology, G2-Bond Universal, was tested. Two conventional two-step adhesives, Clearfil SE Bond 2 and OptiBond eXTRa, and an established universal adhesive, Scotchbond Universal Plus Adhesive, were used as comparison materials. Twelve specimens per group were used to measure the shear bond strength (SBS) to bovine enamel in different etching modes. The bonded specimens were stored in distilled water at 37°C for 5 min or 1, 6, 12, or 24 h before SBS testing. The KHN of the adhesive layer and resin composite was determined after the same storage periods as for SBS testing. RESULTS: All adhesives exhibited increased SBS with prolonged storage periods, irrespective of the etching mode. The KHN of the adhesive layer and resin composite increased over time. CONCLUSIONS: There were strong positive correlations between the SBS and KHN of the adhesive layer and resin composite. Phosphoric acid pre-etching of enamel effectively increases enamel bond performance. The two-step adhesive G2-Bond Universal demonstrated significantly higher bond strength in the early phase than the other adhesives in self-etch mode.
Asunto(s)
Grabado Ácido Dental , Recubrimiento Dental Adhesivo , Bovinos , Animales , Recubrimientos Dentinarios/química , Cementos Dentales/química , Ensayo de Materiales , Cementos de Resina/química , Esmalte Dental/química , Resistencia al Corte , Resinas CompuestasRESUMEN
Numerous laboratory evaluations have been conducted since Dr. Rafael Bowen introduced a method for determining the bond strengths of adhesive systems to dental substrates in 1965. Most of the past studies have been conducted using static bond strength tests, such as shear and tensile bond strength testing with either macro or micro sized specimens. These static bond strength tests are conducted using a monotonically increasing load in which stress is applied continuously until failure occurs. Although the type of stress that develops in static bond strength tests is not typically encountered in clinical situations, over the years clinicians have based their choice of adhesive systems for use in daily practice on the results of such tests. However, some well-known researchers have reported that the results obtained from static bond strength testing may have limited clinical relevance and should not be used only by themselves to make recommendations for clinical use. In clinical situations, restorations undergo cyclic stress during mastication at stress levels well below the breaking stress used in static bond strength tests. Thus, dynamic bond strength tests, using cyclic loading, should be more clinically relevant than static bond strength tests. Over 15 years, a testing method designed to assess fatigue bond strengths of dental adhesive systems has been developed through inter-collegial and international collaborative efforts. This review discusses the development of fatigue bond strength testing methodology, provides both a historical perspective and current information regarding available testing data for all categories of adhesive systems to enamel and dentin and perspectives on the future development of both adhesive systems and testing methods.
RESUMEN
To examine the effect of mold enclosure and chisel design on macro shear fatigue bond strengths of dental adhesive systems. The fatigue bond strength testing was conducted with two commercially available dental adhesive systems, (1) OptiBond eXTRa and (2) Scotchbond Universal, for bonding a resin composite (Filtek Supreme Ultra) to both enamel and dentin using a mold enclosure and a non-mold enclosure with a knife-edge and two sized notched-edge chisel assemblies for loading. As a loading reference for the fatigue testing, macro shear bond strengths of the adhesive systems to enamel and dentin were conducted using a mold enclosure and a knife-edge chisel assembly. The shear bond strengths with the mold enclosure using knife-edge chisel assembly did not exhibit a significant difference between the adhesive systems for either enamel or dentin. The fatigue bond strengths of bonded specimens demonstrated significant differences when comparing the mold enclosure and non-mold enclosure, but not between knife-edge and notched-edge chisel assemblies. The fatigue bond strengths of dental adhesive systems demonstrated significantly higher values when using mold-enclosed bonded specimens than a non-mold enclosure, regardless of type of chisel assembly.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Resinas Compuestas/química , Cementos Dentales , Dentina/química , Recubrimientos Dentinarios/química , Ensayo de Materiales , Cementos de Resina/química , Resistencia al CorteRESUMEN
This study investigated the effect of the bonding agent application method on the dentin bond durability of a two-step adhesive utilizing a universal-adhesive-derived primer. The bonding durability of a universal adhesive was compared with those of two conventional two-step adhesives by shear bond strength testing after thermal cycling. The primer was applied (with or without phosphoric acid pre-etching), and the specimens were divided into three groups based on the bonding agent application method used as follows: (i) strong air-flow application, (ii) gentle air-flow application, and (iii) gentle air-flow + second bonding application. The shear bond strength was determined after thermal cycling. All the factors (bonding agent application method, adhesive system, and storage condition) significantly influenced the dentin shear bond strength both with and without phosphoric acid pre-etching. The specimens exposed to gentle air-flow showed a higher shear bond strength than did those exposed to strong air-flow and gentle air-flow + second bonding. The bond durability of the tested adhesive systems was influenced by the bonding agent application method, and this trend was material dependent. The G2-Bond Universal exhibited the same or greater dentin bond durability to the other two-step adhesive systems.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Grabado Ácido Dental , Cementos Dentales , Dentina , Recubrimientos Dentinarios/química , Ensayo de Materiales , Cementos de Resina , Resistencia al CorteRESUMEN
The purpose of this study was to investigate the protective effect of a glass ionomer cement (GIC) consisting of fluoro-zinc-silicate glass on the demineralization of bovine dentin using the ultrasonic pulse-echo method. The findings were compared with those obtained using a conventional GIC. Slabs of dentin from bovine teeth were sliced, shaped into a rectangular form, and immersed in 0.5 M ethylenediaminetetraacetic acid solution at 25ºC for 6 days, followed by storage in distilled water for 3 days. After demineralization, they were immersed in artificial saliva with and without the GIC specimens. The propagation times of the longitudinal ultrasonic waves in the samples were measured. The ultrasonic velocities of the fluoro-zinc-silicate glass-containing GICs were significantly increased 2-3 days after the start of the experiment and showed an upward trend thereafter. These findings indicate that the GICs containing fluoro-zinc-silicate glass might exhibit the potential to promote remineralization in the dentin.
Asunto(s)
Cementos de Ionómero Vítreo , Desmineralización Dental , Animales , Bovinos , Dentina , Cementos de Ionómero Vítreo/farmacología , Ensayo de Materiales , Silicatos/farmacología , Ultrasonido , Zinc/farmacologíaRESUMEN
The purpose of this study was to evaluate the immediate shear bond strength of resin composite luting systems to tooth with or without saliva contamination in different curing modes. The Knoop hardness number of the resin composite luting agents was measured. Four combinations of resin composite luting systems were used. The shear bond strength to bovine teeth was measured with and without saliva contamination in different curing modes at different storage periods. The Knoop hardness number of the resin composite luting agents was also evaluated. Significantly lower enamel and dentin shear bond strengths and Knoop hardness number values were observed in all resin composite luting systems at 5 min versus 24 h, regardless of the curing mode or saliva contamination. The influence of the curing mode of the resin composite luting systems on shear bond strengths and Knoop hardness number was dependent on material. For the saliva contamination conditions, only G-CEM ONE EM did not show any significant difference in shear bond strength among the groups with and without saliva contamination, regardless of curing mode, storage period, or tooth substrate. All the resin composite luting systems showed lower shear bond strengths and Knoop hardness number values immediately after setting.
Asunto(s)
Recubrimiento Dental Adhesivo , Animales , Bovinos , Resinas Compuestas/química , Esmalte Dental , Análisis del Estrés Dental , Dentina , Recubrimientos Dentinarios/química , Ensayo de Materiales , Cementos de Resina/química , Saliva , Resistencia al CorteRESUMEN
This study investigated the bonding performance of two different types of resin cements to computer-aided design/computer-aided manufacturing (CAD/CAM) composite blocks based on the shear bond strength (SBS) test. A silane-containing self-adhesive resin cement (Panavia SA Cement Universal) and resin luting cement (Block HC Cem) with a primer, were used. Specimens were fabricated from three different types of CAD/CAM composite blocks, and their surfaces were blasted with alumina. Resin cements were bonded to the specimens, and their SBSs were measured after 15 min, 24 h, and after being subjected to thermal cycling for 10,000 and 30,000 cycles. Three-way ANOVA for bond strength revealed that CAD/CAM composite block, resin cement and storage time significantly influenced the SBS values, and the three-way interactions between the evaluated factors, and all the interactions were significant. It was concluded that the bonding performance of resin cements to CAD/CAM composite blocks were material and storage period dependent.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Resinas Compuestas , Diseño Asistido por Computadora , Cementos Dentales , Ensayo de Materiales , Resistencia al Corte , Propiedades de SuperficieRESUMEN
Little information is available about enamel wear caused by zirconia brackets, an inadvertent side effect of orthodontic treatment. The purpose of this study was to examine potential enamel damage induced by contact with zirconia brackets. Sliding and impact wear simulations were performed using bovine enamel specimens positioned at a 25° slant to a zirconium ball to determine wear behaviour. Different chewing patterns, tapping and grinding, were simulated. Specimens were profiled using confocal laser scanning microscopy, and the mean maximum depth and surface roughness were measured. Scanning electron microscopy was also performed. The mean maximum depth of wear values differed according to the number of mastication cycles, with a higher number of cycles producing higher depths of wear. The facet wear depth was significantly greater with the tapping pattern than with the grinding pattern. Scanning electron microscopic observation of the wear facets revealed that surface textures at the edges were rougher than those at the centre of all facets. The results of this study indicated that enamel wear was induced by contact with zirconia brackets during the early period of mastication, and that the patterns and number of cycles of mastication affected the wear progression of enamel.
Asunto(s)
Porcelana Dental , Circonio , Animales , Bovinos , Esmalte Dental , Masticación , Ensayo de Materiales , Propiedades de Superficie , Circonio/efectos adversosRESUMEN
PURPOSE: To examine the effects of an ion-releasing filler-containing gel on the remineralization of dentin using optical coherence tomography (OCT). METHODS: Dentin slabs of bovine teeth were sliced and shaped into a rectangular form. Specimens were treated with undersaturated 0.1 M lactic acid buffer solution (pH 4.75) for 10 minutes and then placed in artificial saliva (pH 7.0). This procedure was repeated three times a day for 28 days. The dentin remineralization effects of a fluoride/S-PRG filler-containing gel (PRG) and a 38% SDF solution (SDF) on dentin slabs of bovine teeth were compared. After treatment, the dentin slabs were immersed in a 0.1 M lactic acid buffer solution and then placed in artificial saliva. This procedure was repeated three times a day for 28 days. OCT imaging was conducted on the selected location of the dentin surface. The peak intensity and width at 1/e² were recorded in each of the six areas on the sample and averaged. Each group had a sample size of 10. Knoop hardness number (KHN) measurements and scanning electron microscopy (SEM) observations were also conducted. The data for each group were subjected to a one-way repeated-measures ANOVA and Tukey tests (α= 0.05). The samples were also observed using SEM. RESULTS: The peak signal intensities of SDF and PRG decreased on day 7 and then slightly increased during the experimental period for the one-off application groups and then decreased for frequent-time application groups. Although the width at 1/e² in the untreated specimens decreased over the test period, SDF and PRG for the one-off application groups exhibited an increase in widths on day 7 followed by a slight decrease, whereas it increased for the frequent-time application groups. The average KHN of the dentin samples exhibited the same tendency as the width at 1/e². Closure of the dentin tubules and crystal precipitation were detected on the surface of both SDF and PRG groups. CLINICAL SIGNIFICANCE: S-PRG filler-containing gel might have the ability to prevent dentin demineralization and could be useful for the prevention of hard-to-access lesions. This material achieved remineralization of the demineralized root dentin and had the same remineralization ability as SDF in vitro.