The donor-acceptor type π-conjugated polymers having heterole units were prepared by the reaction of a regioregular organometallic polymer having both reactive titanacyclopentadiene and electron-donor thiophene-2,5-diyl units in the main chain with electrophiles such as diphenyltin dichloride, dichlorophenylphosphine, and diiodophenylarsine. For example, a polymer having electron-accepting phosphole unit was obtained in 54% yield whose number-average molecular weight (Mn) and molecular weight distribution (Mw/Mn) were estimated as 3,000 and 1.9, respectively. The obtained polymer exhibits a high highest occupied molecular orbital (HOMO) and low lowest unoccupied molecular orbital (LUMO) energy levels (-5.13 eV and -3.25 eV, respectively) due to the electron-donating thiophene and electron-accepting phosphole units. Reflecting upon the alternating structure of thiophene and phosphole, the polymer exhibits a band gap energy level (Eg) of 1.78 eV which is narrower than that of a derivative of poly(thiophene) (Eg = 2.25 eV).
RESUMEN
The synthesis of a polymer containing alternating titanafluorene and arylene ethynylene moieties is described. The polymerization of a 2,7-dibromo-9-titanafluorene derivative with 1,4-dioctyloxy-2,5-diethynylbenzene is carried out at 70 °C for 48 h in tetrahydrofuran (THF) in the presence of palladium dichloride/4,5-bis(diphenylphosphino)-9,9-dimethylxanthene as a catalyst and diisopropylamine as a base to produce a dark red polymer. The polymer thus obtained is soluble in organic solvents and stable towards both air and moisture. In the UV-vis absorption spectrum of the polymer, the absorption maxima (λmax) are observed at 321 nm and 395 nm, which are bathochromically shifted compared to those of a model compound of the repeating unit, a 2,7-bis(phenylethynyl)titanafluorene derivative (λmax = 309 nm and 364 nm). The optical band gap (Eg) of the polymer is estimated to be 2.8 eV on the basis of the absorption onset, which is narrower than that of the model compound (3.1 eV).