RESUMEN
In this work we prove that ordered single-layer MoS2 can be grown epitaxially on Ag(110), despite the different crystalline geometry of adsorbate and substrate. A comprehensive investigation of electronic and structural features of this interface is carried out by combining several techniques. Photoelectron diffraction experiments show that only two mirror crystalline domains coexist in equal amount in the grown layer. Angle-resolved valence band photoelectron spectroscopy shows that MoS2 undergoes a semiconductor-to-metal transition. Low-energy electron diffraction and scanning-tunneling microscopy experiments reveal the formation of a commensurate moiré superlattice at the interface, which implies an anisotropic uniaxial strain of the MoS2 crystalline lattice of ca. 3% in the [11Ì0] direction of the Ag(110) surface. These outcomes suggest that the epitaxial growth on anisotropic substrates might be an effective and scalable method to generate a controlled and homogeneous strain in MoS2 and possibly other transition-metal dichalcogenides.
RESUMEN
The adsorption of Si atoms on a metal surface might proceed through complex surface processes, whose rate is determined differently by factors such as temperature, Si coverage, and metal cohesive energy. Among other transition metals, iridium is a special case since the Ir(111) surface was reported first, in addition to Ag(111), as being suitable for the epitaxy of silicene monolayers. In this study we followed the adsorption of Si on the Ir(111) surface via high resolution core level photoelectron spectroscopy, starting from the clean metal surface up to a coverage exceeding one monolayer, in a temperature range between 300 and 670 K. Density functional theory calculations were carried out in order to evaluate the stability of the different Si adsorption configurations as a function of the coverage. Results indicate that, at low coverage, the Si adatoms tend to occupy the hollow Ir sites, although a small fraction of them penetrates the first Ir layer. Si penetration of the Ir surface can take place if the energy gained upon Si adsorption is used to displace the Ir surface atoms, rather then being dissipated differently. At a Si coverage of â¼1 monolayer, the Ir 4f spectrum indicates that not only the metal surface but also the layers underneath are perturbed. Our results point out that the Si/Ir(111) interface is unstable towards Si-Ir intermixing, in agreement with the silicide phase formation reported in the literature for the reverted interface.