Gas sensing materials roadmap.

Gas sensor technology is widely utilized in various areas ranging from home security, environment and air pollution, to industrial production. It also hold great promise in non-invasive exhaled breath detection and an essential device in future internet of things. The past decade has witnessed giant advance in both fundamental research and industrial development of gas sensors, yet current efforts are being explored to achieve better selectivity, higher sensitivity and lower power consumption. The sensing layer in gas sensors have attracted dominant attention in the past research. In addition to the conventional metal oxide semiconductors, emerging nanocomposites and graphene-like two-dimensional materials also have drawn considerable research interest. This inspires us to organize this comprehensive 2020 gas sensing materials roadmap to discuss the current status, state-of-the-art progress, and present and future challenges in various materials that is potentially useful for gas sensors.

Ultra-sensitive and selective NH3 room temperature gas sensing induced by manganese-doped titanium dioxide nanoparticles.

The study of the fabrication of ultra-high sensitive and selective room temperature ammonia (NH3) and nitrogen dioxide (NO2) gas sensors remains an important scientific challenge in the gas sensing field. This is motivated by their harmful impact on the human health and environment. Therefore, herein, we report for the first time on the gas sensing properties of TiO2 nanoparticles doped with various concentrations of manganese (Mn) (1.0, 1.5, 2.0, 2.5 and 3.0mol.% presented as S1, S2, S3, S4 and S5, respectively), synthesized using hydrothermal method. Structural analyses showed that both undoped and Mn-doped TiO2 crystallized in tetragonal phases. Optical studies revealed that the Mn doped TiO2 nanoparticles have enhanced UV→Vis emission with a broad shoulder at 540nm, signifying induced defects by substituting Ti4+ ions with Mn2+. The X-ray photoelectron spectroscopy and the electron paramagnetic resonance studies revealed the presence of Ti3+ and singly ionized oxygen vacancies in both pure and Mn doped TiO2 nanoparticles. Additionally, a hyperfine split due to Mn2+ ferromagnetic ordering was observed, confirming incorporation of Mn ions into the lattice sites. The sensitivity, selectivity, operating temperature, and response-recovery times were thoroughly evaluated according to the alteration in the materials electrical resistance in the presence of the target gases. Gas sensing studies showed that Mn2+ doped on the TiO2 surface improved the NH3 sensing performance in terms of response, sensitivity and selectivity. The S1 sensing material revealed higher sensitivity of 127.39 at 20 ppm NH3 gas. The sensing mechanism towards NH3 gas is also proposed.