RESUMEN
Introduction: This study used different irrigation techniques to compare the levels of apical bacterial extrusion during the preparation of root canals with a reciprocating instrument widely used in endodontics, the Reciproc files 25/0.08 and 40/0.06. Materials and Methods: The irrigation techniques employed were conventional syringe irrigation and passive ultrasonic irrigation (PUI); the latter, with one or two activation cycles. Seventy extracted mandibular human premolars were contaminated with Enterococcus faecalis for 5 days and were distributed into 6 experimental groups (n=10), and the remaining specimens were used as positive and negative control groups (n=5). Group 1: instrumentation performed with Reciproc 25/0.08 and conventional syringe irrigation; Group 2: instrumentation performed with Reciproc 25/0.08 along with PUI for one minute after instrumentation (PUI-1); and Group 3: instrumentation performed with Reciproc 25/0.08 along with PUI for one minute before and after instrumentation (PUI-2). Groups 4, 5 and 6 were instrumented with Reciproc 40/0.06, and irrigation was performed similar to the previous groups, in the aforementioned order. Each root canal was irrigated with saline solution. Extruded debris was collected in microtubes. The contents of the microtubes were homogenized, diluted, and spread on Brain Heart Infusion agar. After 48 hours, the number of colony-forming units was determined for each sample. For statistical analysis, the Kruskal-Wallis test followed by the Dunn's tests were used (α=0.05). Results: The CFU/mL count indicated that the instrumentation with Reciproc 25/0.08 was associated with the highest bacterial extrusion, mainly when PUI was performed (P<0.05). Conclusion: All the instrumentation techniques caused bacterial extrusion through the apical foramen; however, the largest file size of the Reciproc 40/0.06 groups was associated with less apical bacterial extrusion.
RESUMEN
Objectives: This study evaluated the impact of different methods of irrigant agitation on smear layer removal in the apical third of curved mesial canals of 3 dimensionally (D) printed mandibular molars. Materials and Methods: Sixty 3D-printed mandibular second molars were used, presenting a 70° curvature and a Vertucci type II configuration in the mesial root. A round cavity was cut 2 mm from the apex using a trephine of 2 mm in diameter, 60 bovine dentin disks were made, and a smear layer was formed. The dentin disks had the adaptation checked in the apical third of the teeth with wax. The dentin disks were evaluated in environmental scanning electron microscope before and after the following irrigant agitation methods: G1(PIK Ultrasonic Tip), G2 (Passive Ultrasonic Irrigation with Irrisonic- PUI), G3 (Easy Clean), G4 (HBW Ultrasonic Tip), G5 (Ultramint X Ultrasonic tip), and G6 (conventional irrigation-CI) (n = 10). All groups were irrigated with 2.5% sodium hypochlorite and 17% ethylenediaminetetraacetic acid. Results: All dentin disks were 100% covered by the smear layer before treatment, and all groups significantly reduced the percentage of the smear layer after treatment. After the irrigation protocols, the Ultra-X group showed the lowest coverage percentage, statistically differing from the conventional, PIK, and HBW groups (p < 0.05). There was no significant difference among Ultramint X, PUI-Irrisonic, and Easy Clean (p > 0.05). None of the agitation methods could remove the smear layer altogether. Conclusions: Ultramint X resulted in the most significant number of completely clean specimens.
RESUMEN
INTRODUCTION: The purpose of this study was to evaluate whether the mixing method of AH Plus Jet sealer affects its physicochemical and mechanical properties. METHODS: The properties of AH Plus Jet sealer were analyzed when mixed using either the Auto Mix Tip or manual mixing. The evaluated properties included radiopacity (n = 5), initial and final setting times (n = 5), flow (n = 5), and solubility (n = 3), following specifications outlined in ISO 6876/2012 and ADA Nº 57/2000. pH levels were measured at intervals of 3, 24, 72, and 168 hours (n = 10). The push-out bond strength test was conducted using a universal testing machine and using bovine teeth (n = 30). Failure modes were analyzed with stereomicroscopy. Porosity was evaluated under micro-CT (n = 5), and scanning electron microscopy was also performed (n = 5). One-way analysis of variance and Tukey, unpaired t-tests, or Mann-Whitney tests were used with a significance level of 5%. RESULTS: The Auto Mix exhibited a radiopacity value of 12.11 mmAl, whereas manual mixing resulted in 12.55 mmAl (P > .05). For initial and final setting times, Auto Mix showed 901 minutes and 1779 minutes, respectively, while manual mixing recorded values of 631 minutes and 1504 minutes (P < .05). In terms of flow, Auto Mix demonstrated higher values (25.26 mm) than manual mixing (21.71 mm) (P < .05). No statistical differences were observed between the two methods for solubility and pH (P > .05). Manual mixing presented a higher bond strength value (14.52 MPa) than Auto Mix (9.81 MPa) (P < .05). The mixed failure mode was the most frequent outcome for both methods. The highest porosity was observed for Auto Mix (P < .05). Scanning electron microscopy analysis revealed that manual mixing resulted in a smoother surface with fewer pores and smaller, more evenly distributed agglomerates compared to automatic mixing. CONCLUSION: The mixing method employed for AH Plus Jet sealer influences some physicochemical and mechanical properties of the material.
RESUMEN
BACKGROUND: Symptomatic irreversible pulpitis often results in heightened reactions to thermal stimuli such as pain evoked by a cold stimulus, and spontaneous odontogenic pain (unprovoked pain). OBJECTIVE: This study primarily compared the clinical manifestations of odontogenic spontaneous pain and pain provoked by cold stimulus specifically focusing on their sensory discriminative characteristics (intensity, duration and quality) between symptomatic irreversible pulpitis patients with and without referred pain. METHODS: Twenty-three patients with symptomatic irreversible pulpitis with referred pain and 12 patients without referred pain were included in this cross-sectional study. The following outcomes were assessed: odontogenic spontaneous pain and its descriptors; pain evoked by cold stimulus and qualitative sensory testing before and after local anaesthesia; referred pain location; use of analgesic medication; complementary anaesthesia efficacy. T-test, chi-squared and McNemar tests were applied to the data (p < .50). RESULTS: Patients with referred pain presented a greater odontogenic pain intensity (p < .05) when considered the average of the last 24 h. These patients also showed higher pain rating and pain descriptors (p < .05). Intensity and duration of the pain evoked by cold stimulus in the non-affected contralateral tooth at baseline were higher for patients with referred pain (p < .05). CONCLUSION: Symptomatic irreversible pulpitis patients with referred pain present greater odontogenic spontaneous pain and a heightened pain sensitivity. Therefore, patients with referred pain seem more complex from a pain severity perspective, supporting the clinical utility of discriminating symptomatic irreversible pulpitis with and without referred pain.
Asunto(s)
Dimensión del Dolor , Umbral del Dolor , Dolor Referido , Pulpitis , Odontalgia , Humanos , Pulpitis/fisiopatología , Pulpitis/complicaciones , Femenino , Masculino , Estudios Transversales , Adulto , Dolor Referido/fisiopatología , Umbral del Dolor/fisiología , Odontalgia/fisiopatología , Persona de Mediana Edad , Frío , Adulto JovenRESUMEN
PURPOSE: The strength of temporary restorations plays a vital role in full-mouth reconstruction, and it can be impacted by the aging process. The aim of this in vitro study was to evaluate the biaxial flexural strength and fractographic features of different resin-based materials submitted to thermal aging. MATERIAL AND METHODS: One hundred and ninety-two resin disc-shaped specimens (6.5 mm in diameter and 0.5 mm in thickness) were fabricated and divided into six experimental groups according to the resin-based materials (Filtek Bulk-Fill flowable resin; J-Temp temporary resin; and Fuji Lining glass ionomer cement) and aging process (before and after thermal cycling). Biaxial flexural strength test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min before and after thermal cycling (5 °C and 55 °C, 5760 cycles, 30 s). The mechanical properties were assessed using Weibull parameters (characteristic strength and Weibull modulus) (n = 30). Fractured specimens were examined under a polarized light stereomicroscope to identify crack origin and propagation direction. The surface microstructure of the resin-based materials was assessed by scanning electron microscopy (n = 2). The Weibull modulus (m), characteristic strength, and reliability properties were calculated, and a contour plot was used to detect differences among groups (95% confidence interval). RESULTS: The Weibull modulus (m), characteristic strength, and reliability of the resin-based compounds were influenced by material type and thermal aging (p < 0.05). Weibull modulus (m) revealed no differences when comparing the materials and aging process (p > 0.05), except for the preceding aging period where Filtek Bulk-Fill exhibited higher values compared to J-Temp (p < 0.05). Filtek Bulk-Fill demonstrated superior characteristic strength and reliability compared to J-Temp and Fuji Lining before and after thermal cycling (p < 0.05). Fractography of the resin-based materials showed fractures originating from surface defects exposed to tensile side and their propagation toward the compressive side. Generally, no differences in surface microstructure were observed on micrographs before and after thermal aging for Filtek Bulk-Fill and Fuji Lining. However, the aging process developed flaws in J-Temp. CONCLUSION: Resin-based material composition resulted in different flexural strength performance, impacting the Weibull modulus (m), characteristic strength, and reliability of the resin-based restorations.
Asunto(s)
Resinas Compuestas , Resistencia Flexional , Ensayo de Materiales , Resinas Compuestas/química , Resinas Sintéticas/química , Temperatura , Factores de Tiempo , Agua/química , Estrés MecánicoRESUMEN
OBJECTIVE: The Journal of Esthetic and Restorative Dentistry (JERD) stands out as one of the most prominent international journals publishing research in esthetic dentistry. This study analyzed articles published by JERD since the year 2000 through bibliometric analysis. METHODOLOGY: The search was conducted in January 2024 using Scopus. The following data were extracted from the articles: citation count, year, language, access type, funding agency, study design, theme (general and specific), country, institution, authors, and keywords. The VOSviewer software was used to generate collaborative network maps among the data. Dimensions were consulted to measure altmetric data. Google Trends was used to investigate the global popularity of JERD research. RESULTS: A total of 1394 articles were included in this analysis. Citation count ranged from 0 to 625 (average: 16.9). Articles were published between 2000 and 2023. Laboratory studies were more prevalent (n = 850), with the most investigated general theme being restorative procedures (n = 882), and the highlighted specific theme being the use of composite resin (n = 327). The United States had the highest number of articles (n = 640), with the diverse distribution among other countries. The most common keyword was "cad/cam" (n = 63). VOSviewer demonstrated high collaboration among countries. Intense mentions were identified primarily on Facebook. According to Google Trends, Egypt was the country that searched for JERD the most. CONCLUSIONS: JERD exhibited significant growth in the number of published articles and their diversity by topics, types, origin (country), number of citations, and impact factor. CLINICAL SIGNIFICANCE: The JERD is a journal that publishes studies influencing clinical practice. Identifying the key characteristics of this journal is essential for charting future paths.
Asunto(s)
Bibliometría , Estética Dental , Publicaciones Periódicas como Asunto , Humanos , Edición/tendencias , Edición/estadística & datos numéricos , Restauración Dental PermanenteRESUMEN
OBJECTIVES: To perform a systematic review of animal studies that compared the histopathological characteristics between teeth with apical periodontitis after endodontic treatment in one or two visits. MATERIALS AND METHODS: This systematic review was registered on the International Prospective Register of Systematic Reviews (PROSPERO) - CRD42022340849. Studies were collected from PubMed/MEDLINE, LILACS, EMBASE, Livivo, SciELO, Web of Science, Scopus, and Cochrane Library and manual and gray literature searches. Animal studies that evaluated histological characteristics after endodontic treatment of teeth with apical periodontitis in one or two visits were included. Risk of bias analysis of the included studies was performed using the Systematic Review Centre for Laboratory Animal Experimentation (SYRCLE) tool. Data synthesis of the included studies with quantitative data was performed, and meta-analysis was conducted with the Comprehensive Meta-Analysis software, using the random effects model and odds ratio (OR). RESULTS: Eighteen studies met the inclusion criteria (Kappa = 0.891). Meta-analyses indicated values in inflammatory infiltrate intensity with effect size of 5.5% (95% CI: 0.020-0.148; p < 0.001), periodontal ligament thickness: 25.6% (95% CI: 0.134-0.487; p < 0.001), dentin resorption: 13% (95% CI: 0.015-1.141; p = 0.066), cementum resorption: 7.1% (95% CI: 0.015-0.325; p = 0.001), bone resorption: 1.4% (95% CI: 0.002-0.130; p < 0.001), mineralized tissue resorption: 42.8% (95% CI: 0.110-1.671; p = 0.222), biological apical sealing: 13.1% (95% CI: 0.055-0.314; p < 0.001), and presence of microorganisms: 10.3% (95% CI: 0.014-0.747; p = 0.025). CONCLUSIONS: When considering animal studies, the two-visit endodontic treatment, using calcium hydroxide-based intracanal medication, resulted in better biological repair characteristics. CLINICAL RELEVANCE: A two-visit endodontic treatment with calcium hydroxide-based intracanal medication yields superior histopathological outcomes.
Asunto(s)
Periodontitis Periapical , Tratamiento del Conducto Radicular , Animales , Tratamiento del Conducto Radicular/métodos , Periodontitis Periapical/terapiaRESUMEN
Introduction: The aim of this study was to assess the effectiveness of filling removal material from the apical third of curved mesial root canals of mandibular molars. Reciprocating instrumentation followed by additional rotary instrumentation with instruments made of alloys with different heat treatments was evaluated. Materials and Methods: Thirty-six mesial roots of mandibular molars were divided into two groups: Group Class IV consisted of 16 roots with two independent canals, and Group Class II consisted of 20 roots with two canals that merged into one at their apical level. Each of these two groups were further divided into two subgroups, according to the additional rotary instrument used after the reciprocating instrumentation: Group RH and Group RM for Hyflex and Mtwo, respectively. After each procedural step, the roots were scanned by micro-tomography. After each step of filling removal, the Wilcoxon matched pair test and the Mann-Whitney test were used for the evaluation between groups. The significance level adopted was 5%. Results: Significant differences were observed between groups with different Class II and Class IV anatomies, regarding filling removal after Reciproc (P<0.05). After the use of an additional rotary instrumentation, no differences were observed between the two groups (P>0.05). Conclusions: In the apical third of mesial roots of mandibular molars with Class II anatomy, an additional rotary instrumentation was shown to be necessary for improving the removal of filling material after using the single-file reciprocating instrumentation technique.
RESUMEN
INTRODUCTION: This review aimed to analyze the trend and main characteristics of articles related to guided endodontics (GE). METHODS: The search was conducted in May 2023 on Web of Science. GE-related articles were included, and conferences were excluded. Three researchers selected the articles and extracted: the number of citations; year and journal; design and study theme; authorship and institutions; country and continent. Collaborative networks were generated in the Visualization of Similarities Viewer software. The relationship between data was determined by Spearman's correlation. Google Trends was used to investigate the global popularity of GE research. RESULTS: The search resulted in 135 articles, of which 85 were included. The most cited article totaled 116 citations. The studies were published between 2016 and 2023, most frequently in 2022 (n = 22). The most prevalent journal was the Journal of Endodontics (n = 28). Case report (n = 38) was the most frequent study design. The most studied theme was the use of static GE for calcified canals (n = 27). Connert T was the author with the highest number of articles (n = 13). The University of Basel (n = 9) stood out. The most prevalent country was Brazil (n = 13). Europe was the most frequent continent (n = 38). Visualization of Similarities Viewer demonstrated an interaction between authors. There was a moderate positive correlation between citations and the impact factor (rho = .483). According to Google Trends, the United States was the country that most researched GE. CONCLUSIONS: Based on this review, a more significant research interest in GE was observed in Europe, addressing the application of GE in locating severely calcified root canals.
Asunto(s)
Endodoncia , Humanos , Estados Unidos , Bibliometría , Atención Odontológica , Proyectos de Investigación , BrasilRESUMEN
OBJECTIVES: The study aimed to evaluate the potential for the dissolution of organic tissue in areas of simulated complexity and cleaning of root canal walls of the new iVac® endodontic irrigation system. MATERIAL AND METHODS: Thirty mandibular premolars were evaluated by scanning electron microscopy before and after biomechanical preparation. Then, they were distributed according to the final irrigation protocol into groups with conventional irrigation, ultrasonic agitation with metallic insert (UA), and iVac® system, and new photomicrographs were obtained. For tissue dissolution analysis, glass capillaries filled with catgut were attached to the cervical and apical thirds of twenty-one prototyped upper incisors. They were weighed before and after the previously mentioned irrigation protocols. The data were statistically compared with a significance level of 5%. RESULTS: The final irrigation provided greater cleaning of the root canal walls in the cervical, middle, and apical thirds of the root canals (P < 0.05), with no statistically significant difference between UA and iVac®, regardless of the analyzed thirds. Both ultrasonic irrigation protocols dissolved a significantly greater volume than the conventional irrigation protocol (P < 0.05), with no difference between the two protocols (P < 0.05). CONCLUSIONS: The iVac® system showed root canal wall cleaning and tissue dissolution similar to UA with a metallic insert, and both were superior to conventional irrigation. CLINICAL RELEVANCE: The new irrigation system iVac is more effective than conventional irrigation and has similar root canal wall cleaning and tissue dissolution to UA.
Asunto(s)
Capa de Barro Dentinario , Humanos , Vidrio , Incisivo , Microscopía Electrónica de Rastreo , CuelloRESUMEN
This case report aimed to describe the importance of endodontic treatment in reducing infectious foci in patients with Eisenmenger syndrome (ES) and describe the characteristics of ES, so that the endodontist can safely treat these patients. A 57-year-old male with ES sought dental care complaining of dental pain. Irreversible pulpitis was diagnosed in tooth 37 and pulp necrosis in teeth 36, 34 and 31. Tests of prothrombin time (PT), activated partial thromboblastin time (APTT) and international normalized ratio (INR) were prescribed to evaluate the profile of coagulation using Marevan and antibiotic prophylaxis with amoxicillin. The endodontic treatments were performed. At the end, the patient reported no pain or discomfort in the teeth and improved masticatory function. The removal of oral infectious foci in patients with ES is important to reduce the risk of IE, which could seriously compromise the health and overall prognosis of the patient.
Este reporte de caso tuvo como objetivo describir la importancia del tratamiento endodóntico en la reducción de focos infecciosos en pacientes con síndrome de Eisenmenger (SE) y describir las características del SE, para que el endodoncista pueda tratar con seguridad a estos pacientes. Un hombre de 57 años con ES buscó atención dental quejándose de dolor dental. Se diagnosticó pulpitis irreversible en el diente 37 y necrosis pulpar en los dientes 36, 34 y 31. Se solicitaron pruebas de tiempo de protrombina (PT), tiempo de tromboblastina parcial activada (TTPA) y índice internacional normalizado (INR) para evaluar el perfil de coagulación utilizando Marevan y profilaxis antibiótica con amoxicilina. Se realizaron los tratamientos de endodoncia. Al final, el paciente no refirió dolor ni molestias en los dientes y mejoró la función masticatoria. La eliminación de focos infecciosos orales en pacientes con ES es importante para reducir el riesgo de EI, que podría comprometer gravemente la salud y el pronóstico general del paciente.
RESUMEN
Aims: The aim was to evaluate the cyclic and torsional fatigue resistance among thermally treated NiTi rotary instruments with different design features.Materials and methods: Sixty instruments of three systems were used (n=20): TruNatomy 26.04 (TN 26.04), BassiLogic 25.05 (BL 25.05), and Flat File 25.04 (FF 25.04). The cyclic fatigue test (n=10) was performed to evaluate the time to fracture (s) and the number of cycles until failure (NCF). The torsion test was performed to evaluate the torque (N.cm) and maximum angular deflection until fracture (n=10). The fracture surface of each fragment was examined under a scanning electron microscope. The data were analyzed by Tukey's test (p<0.05).Results: BL 25.05 and FF 25.04 instruments had a higher number of cycles and time to fracture compared with TN 26.04 (p<0.05). TN 26.04 instruments showed lower torque to fracture.Conclusions: Based on the proposed objectives and the methodology used, TruNatomy 26.04 instruments present lower resistance to cyclic fatigue and torsional fatigue when compared to BassiLogic 25.05 and Flat File 25.04 instruments.
RESUMEN
Abstract This study aimed to evaluate the influence of temperature on torsional strength and angular deflection of two experimental NiTi rotary instruments manufactured from Blue and Gold thermal treatments and with identical cross-sections. A total of 40 experimental NiTi instruments 25.06 and with a triangular cross-section and manufactured from Blue and Gold thermal treatments were used (n=20). The torsional test was performed in the 3 mm from the tip of the instrument according to ISO 3630-1. The torsional test evaluated the torsional strength and angular deflection to failure at room temperature (21°C ± 1° C) and body temperature (36°C ±1°C). The fractured surface of each fragment was observed by using scanning electron microscopy (SEM). Data were analyzed using an unpaired t test for inter and intra-group comparison and the level of significance was set at 5%. The results showed that the body temperature did not affect the torsional strength and angular deflection of the instruments when compared with room temperature (P>0.05). However, at body temperature, the Blue NiTi instruments presented significantly lower angular deflection in comparison with Gold NiTi instruments (P<0.05). There was no significant difference regarding the torsional strength of the instruments at body temperature (P>0.05). The temperature did not affect the torsional strength of the instruments manufactured from Blue and Gold technology. However, the Blue NiTi instruments presented significantly lower angular deflection than Gold instruments at 36°C temperature.
Resumo O objetivo deste estudo foi avaliar a influência da temperatura nas propriedades de torção (resistência à torção e deflexão angular) de dois instrumentos rotatórios experimentais de NiTi fabricados com secção triangu.ar e tratamentos térmicos Blue e Gold. Quarenta instrumentos experimentais de NiTi 25.06 com tratamento térmico Blue e Gold foram usados (n= 20). Foi avaliada a resistência torcional e a deflexão angular até a fratura na temperatura ambiente (21°C ± 1°C) e corporal (36°C ± 1°C). O teste torcional foi realizado nos 3 mm da ponta dos instrumentos de acordo com a ISO 3630-1. A superfície fraturada de cada instrumento foi observada pelo microscópio eletrônico de varredura (MEV). Os dados foram analisados por meio do teste t não pareado para a comparação inter e intragrupos e o nível de significância à 5%. Os resultados demonstraram que a temperatura corporal não afetou a resistência a torção e deflexão angular quando comparada com a temperatura ambiente (P>0.05). No entanto, na temperatura de 36°C o instrumento com tratamento térmico Blue apresentou menor deflexão angular quando comparado com o Gold (P<0.05). Não houve diferença significante entre os dois instrumentos em relação a resistência à torção. A temperatura corporal não modificou a resistência torcional dos instrumentos fabricados com tecnologia Blue e Gold. No entanto, os instrumentos com NiTi Blue apresentaram menor deflexão angular do que o Gold a 36°C.
RESUMEN
Abstract This study aimed to assess the self-reported levels of confidence and knowledge related to non-odontogenic pain among a group of Brazilian endodontists. Methodology A total of one hundred and forty-six endodontists affiliated with the Brazilian Society of Endodontics participated in the survey. The questionnaire, distributed via email or WhatsApp, contained inquiries designed to gauge self-perceived confidence and knowledge concerning non-odontogenic pain. The practitioners were categorized into four groups based on their self-reported familiarity with various orofacial pain types, classified as either sufficient or insufficient, and on their engagement in ongoing educational programs related to orofacial pain. Data were analyzed by Chi-Square Test and Fischer's exact test (p<0.05). Results Overall, self-reported confidence about non-odontogenic pain was high, especially for endodontists who considered their knowledge about orofacial pain sufficient, regardless of whether they had (71.1% - 97.8%) or not (35.7% - 96.4%) been continuously involved in education courses on orofacial pain. In general, self-reported knowledge about non-odontogenic pain was insufficient (0% - 42%), except in the question about how they would act in cases of pain that persists beyond the normal healing time after an endodontic procedure (70.6% - 81.9%). In general, endodontists are confident in their diagnosis and treatment of non-odontogenic pain. Nonetheless, this confidence did not correlate with a commensurate knowledge depth of. Thus, specialization courses in endodontics should highly consider training and qualifying these professionals in the diagnosis of non-odontogenic pain.
RESUMEN
Background: The aim of this study was to evaluate the cyclic fatigue and torsional fatigue resistance of three thermally treated rotary instruments, such as: Logic 2 25.05 (LOG 25.05), Edge Taper Platinum 25.06 (EDT 25.06) and ProTaper Gold 25.08 (PTG 25.08).Methods: A total of 60 rotary instruments of LOG 25.05, EDT 25.06 and PTG 25.08 were used (n=20). Cyclic fatigue tests were performed at 36°C using an artificial stainless steel canal with a 60ºangle and a 5-mm radius of curvature. The time (in seconds) and number of cycles to fracture (NCF) was recorded. The torsional test evaluated the torque and angle of rotation to failure at 3 mm from the tip according to ISO 3630-1. The fractured surface of each fragment was observed by using scanning electron microscopy (SEM). Data were analyzed using one-way ANOVA and Holm-Sidak's tests for multiple comparison, the level of significance was set at 5%.Results: EDT 25.06 had highest cyclic fatigue resistance (time and NFC), followed by LOG 25.05 and PTG 25.08 (P<0.05). There were no significantly difference between LOG 25.05 and ETP 25.06 regarding the NCF (P>0.05). In relation the torsional test, the LOG 25.05 and ETP 25.06 presented similar torque (P>0.05). The PTG presented greater torque than the other groups (P<0.05). The PTG 25.08 presented the lowest angular rotation to fracture than the other groups (P<0.05). The SEM images demonstrated typical features of cyclic and torsional fracture.Conclusion: In conclusion, the LOG 25.05 and ETP 25.06 presented similar cyclic and torsional properties. The PTG 25.08 showed greater torsional strength.
Asunto(s)
Humanos , EndodonciaRESUMEN
Abstract Filling materials should be restricted to the root canal space. However, sometimes it is impossible to control the apical extrusion, in this case, the fate of the filling material and the result of the treatment will depend on its physicochemical properties and biocompatibility. Objective To evaluate the tissue response and bone repair capacity of endodontic sealers that were implanted in the calvaria of Wistar rats, forming the groups (n=16): AH Plus and Sealer Plus, compared to the clot group. Methodology On days 30 and 60, the animals were euthanized, the calvaria was removed and processed for hematoxylin-eosin, immunohistochemistry for collagen type I, Picrosirus red and microtomographic analysis. Data were subjected to ANOVA and Tuckey tests (p<0.05). Results At 30 days, all groups showed an intense inflammatory reaction (p>0.05). At 60 days, the AH Plus and Sealer Plus maintained an intense inflammatory infiltrate compared to the clot group (p<0.05). We observed immunopositive areas for type I collagen in all groups at 30 days and 60 days (p>0.05). We observed more red collagen fibers for the Sealer Plus compared to the clot group at 30 days (p<0.05). Considering the total fibers, the clot group at 30 days compared to 60 days after surgery showed an increase in the amount of matrix (p<0.05). There were no statistical differences between groups for green and yellow fibers (p>0.05). Regarding morphometric parameters, at 30 days, the newly formed bone volume and number of bone trabeculae were higher in the groups with sealers compared to the clot group (p<0.05). At 60 days, AH Plus and Sealer Plus showed greater bone neoformation compared to the clot group (p<0.05). Conclusions Despite AH Plus and Sealer Plus induced an intense inflammatory reaction, they can be considered biocompatible materials, since they allowed bone repair.
RESUMEN
Abstract This study aimed to evaluate the root canal real length (RL) changes due to the mechanical instrumentation use with different flaring magnitudes. After access cavity, 60 mesial root canals of mandibular molars were randomly separated in three groups: Hyflex EDM (HF; #25/.12, #10/.05 e #25/~), Reciproc Blue (RB; R25), and MTwo (M2; #10/.04, #15/.05, #20/.06 e #25/.06). The RL was defined as the apical limit, and 2.5% sodium hypochlorite irrigating solution was chosen. After the access cavity (RL 1), cervical flaring (RL 2), and complete chemical-mechanical preparation (RL 3), the RL was evaluated. The RL was evaluated by a blind examiner with the aid of a microscope (16x) placing the endodontic file stop at the coronary reference. When comparing length measurements, the RL was shorter before instrumentation than that after instrumentation. A reduction of 0.65 mm (HF), 0.61 mm (RB), and 0.48 mm (M2) was observed. However, among groups, no statistical differences were found (p > 0.05). Under the conditions tested, it can be inferred that all mechanical systems provoked RL variations, which emphasizes the need for constant verification of the odontometry, mainly before root canal obturation.
RESUMEN
Abstract The aim of this study was to evaluate the quality of curved root canal preparation, torsional fatigue, and cyclic fatigue of rotary systems manufactured with different NiTi alloys. Ninety single-rooted canals with curvatures of 15° to 30o were scanned and divided into three groups according to the rotary system used: BT-Race (BTR) - 10.06, 35.00, 35.04; SequenceRotaryFile (SRF) - 15.04, 25.06, 35.04; and ProDesignLogic (PDL) - 25.01, 25.06, 35.05. Each system was used on three specimens. The teeth were prepared, scanned, and analyzed to assess increase in volume, transportation, and centering ability of the root canal. Torsional fatigue of glide path instruments (BTR 10.06, SRF 15.04 and PDL 25.01) and cyclic fatigue of the finishing instrument (BTR 35.04, SRF 35.04 and PDL 35.05) were obtained by analyzing completely new instruments (n = 10) and instruments after they had been used three times (n = 10). After the torsional and cyclic fatigue tests, the fractured surface of the new and used instruments were examined by scanning electron microscopy. Increase in volume, canal transportation, and centering ability showed no significant differences among the groups (p > 0.05). The torsional test showed that SRF 15.04 produced the highest torque values for both new and used instruments, followed by PDL 25.01 and BTR 10.06 (p < 0.05). PDL 25.01, both new and used, exhibited higher values of angular deflection followed by SRF 15.04 and BTR 10.06 (p < 0.05). As regards cyclic fatigue, use of PDL 35.05, both new and used, required a longer time and larger number of cycles than did SRF 35.04 and BTR 35.04 (p < 0.05). Clinical use affected the torsional fatigue of BTR; however, cyclic fatigue was not significantly affected (p < 0.05). All rotary systems were able to prepare the curved canals satisfactorily and were used safely on the three specimens. Relative to torsional fatigue, SRF 15.04 exhibited a higher torque, and PDL 25.01, higher angular deflection. BTR 10.06 was the most affected by clinical use. PDL 35.05 showed greater resistance to cyclic fatigue.
RESUMEN
Abstract This study aimed to evaluate physicochemical properties of three ready-to-use calcium silicate-based endodontic sealers: Endosequence BC Sealer, Bio C Sealer, and Sealer Plus BC. Radiopacity was evaluated using specimens of 10 mm in diameter and 1 mm in height, along with an aluminum step wedge. For the flow test, 0.5 mL of each sealer was deposited between glass plates and the mean of the measurement of two diameters was considered the cement flow value. For pH and calcium release, root canals of 30 prototypes of upper incisor acrylic resin teeth were filled with sealer and gutta percha point and then immersed in containers with 13 mL of ultrapure water. Both pH and release of calcium ions (atomic absorption spectrophotometer) were measured at 3, 24, 72, and 168 h. Acrylic resin teeth were scanned by Micro-CT 1174 at the time of pH and calcium ion readings for volumetric change analysis. The data were analyzed by ANOVA, Tukey's, Kruskal-Wallis, and Dunn's tests. Endosequence BC Sealer presented the lowest, and Bio C Sealer the highest volumetric change after 72 h and 168 h (p < 0.05). Endosequence BC Sealer presented higher radiopacity (p < 0.05). All materials showed alkalinization capacity. All of them presented calcium ion release, with a higher value for Sealer Plus BC. All materials presented alkalinization, calcium release capacity, radiopacity, and flow above the minimum values required by the ISO standard. The highest volumetric loss was experienced by Bio C Sealer and the lowest one by Endosequence BC Sealer.
RESUMEN
Aim: This study aimed to evaluate the pH, Ca2+ release, solubility, and antimicrobial activity of calcium hydroxide (Ca(OH)2) pastes in association with different substances. Methods: Sixty acrylic teeth (n=10) were filled with pastes that associated Ca(OH)2 with the following substances: benzalkonium chloride 5% (G1) and 50% (G2) both in propylene glycol, arnica glycolic extract (G3), green tea glycolic extract (G4), Calen/PMCC™ (G5), and Calen™ (G6). In the group G1 to G4 were used 1g of Ca(OH)2 powder with 0,8g of vehicle. pH and Ca2+ release was measured after 7, 15, and 30 days. For solubility, micro-CT was used immediately and at the periods of 7, 15, and 30 days. For the antimicrobial analysis, a biofilm of E. faecalis was induced in vitro on bovine dentin discs. Live/dead viability dye and confocal scanning microscopy were used. Results: The highest pH values occurred on the first 7 days, and the G6, G1, G3, and G5 presented the highest pH values at this period (P <0.05). Ca2+ release was higher in all groups at 7 days, with the highest values observed in G1, G5, and G6. The volume of all pastes showed no significant difference in the intragroup analysis at 7 and 15 days (P <0.05). G1 and G2 showed the highest antimicrobial action (P <0.05). For the biovolume, there was difference between the G6 and the other groups (P >0.05) with G1 presenting the lowest values. Conclusion: Benzalkonium chloride 5% increases the antimicrobial action of the Ca(OH2), without impairs physicochemical properties