RESUMEN
Fe-~30 at.%Pd is a ferromagnetic shape memory alloy (SMA) with a reversible thermoelastic fcc-fct phase transformation. The advantage of adding a small amount of Indium to Fe-Pd SMAs is, among other things, the upward shift of the transformation temperatures, which allows us to maintain the material in the martensitic state (fct structure) at room temperature. In this work, we study the microstructure and the magnetic properties of nominally Fe67.6-Pd32-In0.4 (at.%) melt-spun ribbons. Energy-dispersive spectroscopy analysis showed a certain level of non-uniformity of Indium distribution in the as-spun ribbon. However, the attempt to homogenize the ribbon by annealing at 1273 K for 120 h resulted in an unfavoured structural change to bct martensite. Magneto strains induced by a 9 kOe magnetic field reached over 400 ppm for certain field orientations, which is around four times more than the magneto strains of near-binary Fe-Pd shape memory alloys.
RESUMEN
Nafion possesses many interesting properties such as a high ion-conductivity, hydrophilicity, and thermal and chemical stability that make this material highly suitable for many applications including fuel cells and various (bio-)chemical and physical sensors. However, the mechanical properties of a Nafion membrane that are known to be affected by the viscoplastic characteristics of the material itself have a strong impact on the performance of Nafion-based sensors. In this study, the mechanical properties of Nafion under the cyclic loading have been investigated in detail. After cyclic tensile loading (i.e., maximum elongation about 25% at a room temperature and relative humidity about 40%) a time-dependent recovery comes into play. This recovery process is also shown being strain-rate dependent. Our results reveal that the recovery behavior weakens after performing several stress-strain cycles. Present findings can be of a great importance in future design of various chemical and biological microsensors and nanosensors such as hydrogen or glucose ones.
RESUMEN
Both poly(methyl methacrylate) (PMMA) and NiTi possess shape memory and biocompatibility behavior. The macroscale properties of PMMA-NiTi composites depend immensely on the quality of the interaction between two components. NiTi shape memory alloy (SMA) and superelastic (SE) sheets were spin coated on one side with PMMA. The composite was prepared by the spin coating method with an alloy-to-polymer-thickness ratio of 1:3. The bending stiffness and radius of curvature were calculated by using numerical and experimental methods during thermal cycles. The experimental radius curvatures in actuation have good agreement with the model. The change in shape results from the difference in coefficients of thermal expansion between PMMA and NiTi. Actuation temperatures were between 0 and 100 °C for the SMA-PMMA composite with a change in curvature from 10 to 120 mm with fixed Young's modulus of PMMA at 3 GPa, and a change in Young's modulus of NiTi from 30 to 70 GPa. PMMA-NiTi composites are useful as actuators and sensor elements.
RESUMEN
In the present study, in situ microbending experiments on magnesium single crystalline microcantilevers are presented. Microcantilevers with pentagonal cross-section were fabricated by focus ion beam. Two basic crystallographic orientations of the microcantilevers were investigated: {0001} and {10-10}, i.e., the c-axis perpendicular to and parallel with the cantilever top surface, respectively. After bending, the longitudinal sections of the microcantilevers were analyzed using electron backscatter diffraction to investigate the crystal lattice rotations and accumulated deformations. The stress levels in the loaded cantilevers are strongly dependent on the crystal orientation. Extension twins were found in the {10-10} cantilevers.