Evaluation of Mechanical Properties and Marginal Fit of Crowns Fabricated Using Commercially Pure Titanium and FUS-Invest.

This study investigated the mechanical properties and single crown accuracy of the tailor-made Fourth University Stomatology investment (FUS-invest) for casting titanium. Background. Current investment for casting titanium is not optimal for obtaining high-quality castings, and the commercially available titanium investment is costly. Methods. Titanium specimens were cast using the tailor-made FUS-invest. The mechanical properties were tested using a universal testing machine. Fractured castings were characterized by energy-dispersive spectroscopy. 19 titanium crowns were produced using FUS-invest and another 19 by Symbion. The accuracy of crowns was evaluated. Results. The mechanical properties of the titanium cast by FUS-invest were elastic modulus 125.6 ± 8.8 GPa, yield strength 567.5 ± 11.1 MPa, tensile strength 671.2 ± 15.6 MPa, and elongation 4.6 ± 0.2%. For marginal fit, no significant difference (P > 0.05) was found at four marker points of each group. For internal fit, no significant difference (P > 0.05) was found between two groups, whereas significant difference (P < 0.01) was found at different mark point of each group. Conclusions. The mechanical properties of titanium casted using FUS-invest fulfilled the ISO 9693 criteria. The marginal and internal fit of the titanium crowns using either the FUS-invest or Symbion were similar.

[Research on physical and mechanical properties, crown accuracy by using self- made FUS-invest dental investment].

PURPOSE: To evaluate the physical and mechanical properties of pure titanium castings cast by self- made FUS-invest dental investment, and evaluate casting accuracy. METHODS: Seven pure titanium castings were cast by self-made FUS-invest zirconium investment and analyzed using servo hydraulic dynamic experiment system (JJG139-83 standard), scanning electron microscope and energy spectrum analysis. Thirty-eight crowns of pure titanium were cast by two different methods. One cast by FUS-invest zirconium embedding material was used for experiment and the other cast by phosphate embedding material was used as control. Casting accuracy was assessed through measuring the difference value d at the marginal marker points and distance between casting pieces of wall and working modes of casting were examined under microscope. Scanning electron microscope with energy-dispersive spectrum (EDS) was used to analyze the status of composition of the casting surface. SPSS 17.0 software package was used to investigate the difference of two groups. RESULTS: ①Qualitative analysis of servo hydraulic dynamic experiment system showed various mechanical properties: elastic modulus (123.5±14.2) GPa, yield strength (569.3±16.5) MPa, tensile strength (668.4±16.1) MPa, elongation (4.5±0.2)%. EDS analysis of the fracture was observed at different depth (13, 25, 50, 350 µm) under the surface of pollution layer, a little Si and Fe with different atomic percentage was found but no Zr. ②No significant difference (P>0.05) was found between each group of four markers on the marginal fit, and internal fit, whereas significant difference (P<0.01) was found at different marker point. CONCLUSIONS: The mechanical properties of commercially pure titanium casting by self-made FUS-invest zirconium-based investment can meet the qualification of dental metal materials, although elongation was a little lower. Both the marginal adaptation and internal fit between the two groups had no significant difference. The mean marginal difference was 46 µm, the mean internal difference at axial angle was 56 µm and approximately 0 at axial wall.

Natural teeth-retained splint based on a patient-specific 3D-printed mandible used for implant surgery and vestibuloplasty: A case report.

RATIONALE: With respect to improving the quality of oral rehabilitation, the management of keratinized mucosa is as important as bone condition for implant success. To enhance this management, a natural teeth-retained splint based on a patient-specific 3-dimensional (3D) printed mandible was used in vestibuloplasty to provide sufficient keratinized mucosa around dental implants to support long-term implant maintenance. PATIENT CONCERNS: A 28-year-old male patient had a fracture of the anterior andible 1 year ago, and the fracture was treated with titanium. DIAGNOSES: The patient had lost mandibular incisors on both the sides and had a shallow vestibule and little keratinized mucosa. INTERVENTIONS: In the first-stage implant surgery, 2 implants were inserted and the titanium fracture fixation plates and screws were removed at the same time. During second-stage implant surgery, vestibuloplasty was performed, and the natural teeth-retained splint was applied. The splint was made based upon a patient-specific 3D-printed mandible. At 30-day follow-up, the splint was modified and reset. The modified splint was removed after an additional 60 days, and the patient received prosthetic treatment. OUTCOMES: After prosthetic treatment, successful oral rehabilitation was achieved. Within 1 year and 3 years after implant prosthesis finished, the patient exhibited a good quantity of keratinized gingiva. LESSONS SUBSECTIONS: The proposed splint is a simple and time-effective technique for correcting soft tissue defects in implant dentistry that ensures a good quantity of keratinized mucosa.