Influence of Etchants on Etched Surfaces of High-Strength and High-Conductivity Cu Alloy of Different Processing States.

With the continuous integration of semiconductor devices, the requirements of the size accuracy and surface quality of etched lead frames are stricter. The etchant is a key factor in the etching process and etched surface quality, while the effects of the difference in etchants on the etched surface morphology of Cu alloy have not been directly studied. In this study, aqua regia, acidic FeCl3 and two CuCl2 solutions were used as etchants, and different CuCrSn specimens were etched and characterized. The results show that the etching rate in aqua regia is high, and the grain orientation, grain boundary (GB) and dislocations have significant influences on the local etching rate. The preferential etching of some atomic planes forms steps between the grains with different orientations, and preferential etching around the GB and dislocation group forms grooves, resulting in high surface roughness. For the surfaces etched by the FeCl3 and CuCl2 etchants, the steps and grooves are blurred; thus, they are less rough. The CuCrSn alloy surface etched by the aqua regia is clean, with little Cr-rich particles, while high-density Cr-rich particles remain on the surfaces etched by the FeCl3 and CuCl2 etchants. For the same kind of etchant, the ion concentration can affect the etching mechanism, rate and the etched surface morphology.

Effect of Extrusion on Mechanical Property, Corrosion Behavior, and In Vitro Biocompatibility of the As-Cast Mg-Zn-Y-Sr Alloy.

The effect of extrusion on the microstructure, mechanical property, corrosion behavior, and in vitro biocompatibility of as-cast Mg-1.5Zn-1.2Y-0.1Sr (wt.%) alloy was investigated via tensile tests, electrochemical methods, immersion tests, methylthiazolyl diphenyltetrazolium bromide (MTT), and analytical techniques. Results showed that the as-cast and as-extruded Mg-1.5Zn-1.2Y-0.1Sr alloys comprised an α-Mg matrix and Mg3Y2Zn3 phase (W-phase). In the as-cast alloy, the W-phase was mainly distributed at the grain boundaries, with a small amount of W-phase in the grains. After hot extrusion, the W-phase was broken down into small particles that were dispersed in the alloy, and the grains were refined considerably. The as-extruded alloy exhibited appropriate mechanical properties that were attributed to refinement strengthening, dispersion strengthening, dislocation strengthening, and precipitation strengthening. The as-cast and as-extruded alloys exhibited galvanic corrosion between the W-phase and α-Mg matrix as the main corrosion mechanism. The coarse W-phase directly caused the poor corrosion resistance of the as-cast alloy. The as-extruded alloy obtained via hydrogen evolution and mass loss had corrosion rates of less than 0.5 mm/year. MTT, high-content screening (HCS) analysis, and cell adhesion tests revealed that the as-extruded alloy can improve L929 cell viability and has great potential in the field of biomedical biodegradable implant materials.

Genome-based classification of the family Haloferacaceae and description of five novel species of Halobaculum.

The taxonomic status of some species of Halobellus, Haloferax, Halogranum, and Haloplanus within the family Haloferacaceae was elucidated by phylogenetic, phylogenomic, and comparative genomic analyses. The relative species of each genus should constitute a single species based on the overall genome-related indexes proposed for species demarcation. The cutoff values of AAI (72.1%), ANI (82.2%), and rpoB' gene similarity (90.7%) were proposed to differentiate genera within the family Haloferacaceae. According to these standards, a novel genus related to the genus Halobaculum was proposed to accommodate Halobaculum halophilum Gai3-2 T and Halobaculum salinum NJ-3-1 T. Five halophilic archaeal strains, DT31T, DT55T, DT92T, SYNS20T, and YSMS11T, isolated from a tidal flat and a marine solar saltern in China, were subjected to polyphasic classification. The phenotypic, phylogenetic, phylogenomic, and comparative genomic analyses revealed that strains DT31T (= CGMCC 1.18923 T = JCM 35417 T), DT55T (= CGMCC 1.19048 T = JCM 36147 T), DT92T (= CGMCC 1.19057 T = JCM 36148 T), SYNS20T (= CGMCC 1.62628 T = JCM 36154 T), and YSMS11T (= CGMCC 1.18927 T = JCM 34912 T) represent five novel species of the genus Halobaculum, for which the names, Halobaculum lipolyticum sp. nov., Halobaculum marinum sp. nov., Halobaculum litoreum sp. nov., Halobaculum halobium sp. nov., and Halobaculum limi sp. nov., are proposed.

Influences of Cold Rolling and Aging on Microstructure and Property of CuCrSn Alloy.

The CuCrSn alloy is promising as a high-strength and high-conductivity Cu alloy due to its relatively low smelting requirement. However, thus far investigations into the CuCrSn alloy are still quite lacking. In this study, the microstructure and properties of Cu-0.20Cr-0.25Sn (wt%) alloy specimens prepared under different rolling and aging combinations were comprehensively characterized, in order to reveal the effects of cold rolling and aging on properties of the CuCrSn. The results show that increasing the aging temperature from 400 °C to 450 °C can noticeably accelerate precipitation, and cold rolling before aging significantly increases its microhardness and promotes precipitation However, the deformation hardening is eliminated during the aging process, making the microhardness decrease monotonically when the aging temperature and the cold rolling ratio before aging are high. Performing cold rolling after aging can maximize precipitation strengthening and deformation strengthening, and the adverse impact on its conductivity is not serious. A tensile strength of 506.5 MPa and a conductivity of 70.33% IACS were obtained by such a treatment, whereas only the elongation decreases a little. Different strength-conductivity combinations of the CuCrSn alloy can be achieved through appropriate design of the aging and post-aging cold rolling conditions.

Strengthening Mechanism of Rotary-Forged Deformable Biodegradable Zn-0.45Li Alloys.

The use of zinc (Zn) alloys as a biodegradable metal for medical purposes has been a popular research topic. This study investigated the strengthening mechanism of Zn alloys to enhance their mechanical properties. Three Zn-0.45Li (wt.%) alloys with different deformation amounts were prepared by rotary forging deformation. Their mechanical properties and microstructures were tested. A simultaneous increase in strength and ductility was observed in the Zn-0.45Li alloys. Grain refinement occurred when the rotary forging deformation reached 75.7%. The surface average grain size reached 1.19 ± 0.31 µm, and the grain size was uniformly distributed. Meanwhile, the maximum elongation of the deformed Zn-0.45Li was 139.2 ± 18.6%, and the ultimate tensile strength reached 426.1 ± 4.7 MPa. In situ tensile tests showed that the reinforced alloys still broke from the grain boundary. Continuous and discontinuous dynamic recrystallization during severe plastic deformation produced many recrystallized grains. During deformation, the dislocation density of the alloy first increased and then decreased, and the texture strength of the (0001) direction increased with deformation. Analysis of the mechanism of alloy strengthening showed that the strength and plasticity enhancement of Zn-Li alloys after macro deformation was a combination of dislocation strengthening, weave strengthening, and grain refinement rather than only fine-grain strengthening as observed in conventional macro-deformed Zn alloys.

Identification of pimavanserin tartrate as a potent Ca2+-calcineurin-NFAT pathway inhibitor for glioblastoma therapy.

Glioblastoma multiforme (GBM) is the most common and malignant type of primary brain tumor, and 95% of patients die within 2 years after diagnosis. In this study, aiming to overcome chemoresistance to the first-line drug temozolomide (TMZ), we carried out research to discover a novel alternative drug targeting the oncogenic NFAT signaling pathway for GBM therapy. To accelerate the drug's clinical application, we took advantage of a drug repurposing strategy to identify novel NFAT signaling pathway inhibitors. After screening a set of 93 FDA-approved drugs with simple structures, we identified pimavanserin tartrate (PIM), an effective 5-HT2A receptor inverse agonist used for the treatment of Parkinson's disease-associated psychiatric symptoms, as having the most potent inhibitory activity against the NFAT signaling pathway. Further study revealed that PIM suppressed STIM1 puncta formation to inhibit store-operated calcium entry (SOCE) and subsequent NFAT activity. In cellula, PIM significantly suppressed the proliferation, migration, division, and motility of U87 glioblastoma cells, induced G1/S phase arrest and promoted apoptosis. In vivo, the growth of subcutaneous and orthotopic glioblastoma xenografts was markedly suppressed by PIM. Unbiased omics studies revealed the novel molecular mechanism of PIM's antitumor activity, which included suppression of the ATR/CDK2/E2F axis, MYC, and AuroraA/B signaling. Interestingly, the genes upregulated by PIM were largely associated with cholesterol homeostasis, which may contribute to PIM's side effects and should be given more attention. Our study identified store-operated calcium channels as novel targets of PIM and was the first to systematically highlight the therapeutic potential of pimavanserin tartrate for glioblastoma.

Ultrafine- and uniform-grained biodegradable Zn-0.5Mn alloy: Grain refinement mechanism, corrosion behavior, and biocompatibility in vivo.

An ultrafine- and uniform-grained Zn-0.5Mn alloy (D3 alloy, stands for deformation rate of 99.5%) is fabricated via multi-pass drawing. The alloy features excellent ductility and elongation properties (up to 245.0% ± 9.0% at room temperature). Zn-0.5Mn alloys are composed of two phases, namely, Zn and MnZn13. The MnZn13 phase confers multiple effects during refinement by inducing and pinning low-angle boundaries within grains. Meanwhile, the presence of these phases along grain boundaries prevents the growth of new refined grains. D3 shows uniform corrosion behaviors in c-SBF solution on account of the even distribution of the MnZn13 phase in its microstructure. Animal implantation experiments indicate that D3 has good biocompatibility; it does not cause damage to bone tissue or other organs. Taking the results together, D3 may be developed into a new type of biodegradable material with remarkable elongation and corrosion properties and satisfactory biocompatibility for medical applications.

[Impact of a Sewage Treatment Plant on the Accumulation of Microplastics in Freshwater Organisms in the Lijiang River of the Guilin Urban Section].

Microplastics (MPs, particle size<5 mm), as a new pollutant, have attracted wide attention in recent years. The distributions of MPs in effluent of a sewage treatment plant (STP) were examined. Surface water, sediment, and freshwater organism samples were taken from the STP discharge outlet in the Lijiang River tributary (S1), the confluence of tributaries and main streams in the Lijiang River (S2), and downstream locations in the Lijiang River (S3). The impact of STP discharge effluent on the characteristics and spatial distribution of MPs pollution in freshwater organisms was studied. The results showed that the freshwater organisms had a probability of uptake of MPs by 94.2%. The mean abundance of MPs in S1 (2.7 n·ind-1) was significantly higher than that of S3 (1.9 n·ind-1, P<0.05). The MPs found in S1 and S3 were mainly <0.10 mm, accounting for 46.0% and 30.5%, respectively. The fiber type of MPs was observed in the body of freshwater organisms. Polyethylene terephthalate was the major polymer form in S1 organisms, while polypropylene was the major polymer form in S3. The effluent discharged from the STP led to the accumulation of MPs in freshwater organisms.