RESUMEN
A novel red phosphor Lu3(1-x)Sc2Ga3O12: xEu3+(0 ≤ x ≤ 0.3) was successfully prepared by high temperature solid state method. The Lu2.4Sc2Ga3O12: 0.2Eu3+ phosphor shows strong high internal quantum efficiency and thermal stability with values of 64.79 % and 87.0 %, respectively. Based on Lu2.4Sc2Ga3O12: 0.2Eu3+ phosphor, the partial replacement of Lu3+ ions in the host by Gd3+ / Y3+ ions changes the local crystal field environment of Eu3+ ions, resulting in wonderful changes in the luminous center, and the luminous intensity at 593 nm is increased by 3.66 and 3.54 times, respectively. The decay time of Eu3+ ions is analyzed from the perspective of dynamics, and the reasons for the enhancement of luminescence after partial replacement of Lu3+ ions are discussed in detail from two aspects of phosphor structure and crystal field effect around Eu3+ ions. In addition, with the substitution of Gd3+ / Y3+ ions, the thermal stability of the sample is 90.3 %/89.4 % with excellent low thermal quenching. The thermal quenching mechanism is described by combining Debye temperature and activation energy. The sample also has a high internal quantum efficiency IQE=79.03 % / 78.24 %. Finally, under the excitation of 365 nm chip, the phosphors of Lu2.34Sc2Ga3O12: 0.2Eu3+, 0.02Gd3+ and Lu2.34Sc2Ga3O12: 0.2Eu3+, 0.02Y3+ synthesized R-LED device has extremely high color rendering index, Ra is 78.23/77.15 and color temperature is 1640.38 K/1642.97 K. The experimental results show that the Lu2.34Sc2Ga3O12: 0.2Eu3+, 0.02Gd3+ / Y3+ phosphors prepared has a wide application prospect in w-LED devices.
RESUMEN
LiYGeO4 phosphors doped with Dy3+ and Eu3+ ions were synthesized using the solid phase method, and their color characteristics were adjustable. The bandgap value of LiYGeO4 calculated by diffuse reflection data is very close to the theoretical value of 3.669 eV, indicating that LiYGeO4 is an ideal candidate for doped rare earth activated ions. The analysis of the emission spectra and fluorescence attenuation curves of Dy3+ and Eu3+ co-doped LiYGeO4 phosphors revealed a clear energy transfer process: energy transfer from Dy3+ to Eu3+. Analysis of emission spectra and fluorescence attenuation curves revealed a transfer of energy from Dy3+ to Eu3+. This transfer mechanism is attributed to the dipole-dipole interactions. In addition, by constantly adjusting the doping levels of Dy3+ and Eu3+, a warm white phosphor with a color temperature of 3881 K was obtained. Finally, the emission intensity of the LiYGeO4:0.015Dy3+,0.02Eu3+ phosphor at 423 K was 86%, indicating that the phosphor has excellent thermal stability and 40% internal quantum efficiency, which proves the potential application of the LiYGeO4 phosphor in white light-emitting diodes (w-LEDs).
RESUMEN
A series of Ca3Al2Ge3O12: xDy3+, yEu3+ phosphors were successfully prepared by the high-temperature solid-phase method. The phase and morphology of the phosphors were studied by means of Rietveld refinement and scanning electron microscopy. The results show that the phase is pure, and the crystal structure is the Ia3Ì d space group. In the Ca3Al2Ge3O12: xDy3+ phosphors, using 380 nm excitation, phosphors showed blue (4F9/2 â 6H15/2) and yellow (4F9/2 â 6H13/2) emission peaks at 481 and 581 nm, respectively. In Ca3Al2Ge3O12: xDy3+, yEu3+ phosphors, the energy transfer was inferred by the spectrum overlap of Dy3+ and Eu3+, and the lifetime attenuation was analyzed from the perspective of dynamics; finally, the band gap structure of the phosphors was analyzed by combining diffuse reflection spectra with the first principle, and the energy transfer mechanism and luminescence mechanism were elaborated by combining theory and practice. The transition from blue white light to red light can be achieved by tuning the range of y in Ca3Al2Ge3O12: 0.015Dy3+, yEu3+. Wherein, when y = 0.07, phosphors, the chromaticity coordinate of warm white CIE is (0.3932, 0.3203), the color temperature is 3093 K, and the warm white light is synthesized. The thermal stability of the synthesized warm white phosphors is 90.1% (423 K), the thermal sensing factors are Samax = 5.51 × 10-4 K-1 (303 K) and Srmax = 0.0359% K-1 (303 K), and the actual quantum efficiency is IQE = 52.48%. These results prove that Ca3Al2Ge3O12: Dy3+, Eu3+ have good application prospects as single-component warm w-LED devices.