Impact of final rinse with saline or alcohol solution on root canal sealability.

Endodontic irrigation protocols are not only used to clean and disinfect the root canal system, but also to condition the canal wall dentine for subsequent root filling. In this study we tested whether a final irrigation step with saline solution or 80% ethanol improved root canal sealabilty by two popular sealers, an epoxy resin (AH Plus) and a hydraulic calcium silicate cement-based product (BioRoot RCS). Root canals in extracted single-rooted human teeth were instrumented and filled with a matched gutta-percha cone and sealer. During instrumentation and prior to root filling, sealer-specific irrigation protocols were applied. These involved a combined sodium hypochlorite/1-hydroxyethylidene-1,1-diphosphonic acid application, which was followed by irrigation with ethylenediaminetetraacetic acid (EDTA) for AH Plus. Protocols were followed by a 5-ml ultimate rinse with saline solution or 80% ethanol. No such final rinse was the control (N = 9). Canals were then dried with matched paper points. One week after root filling and storage of the teeth at 37°C in a humid environment, Rhodamine B was used to trace leakage. Two-way ANOVA revealed that the type of sealer had a significant (P < 0.05) impact on apical dye penetration while the final rinse did not (P > 0.05). AH Plus provided the slightly better seal (P < 0.05). Leakage occurred between the sealer and the dentin with AH Plus, and between the sealer-to-dentin as well as the sealer-to-gutta-percha interface with BioRoot RCS. In summary and under current conditions, there was no benefit from applying saline or ethanol as an ultimate rinsing solution prior to drying the canal with matched paper points.

Light-curable urushiol enhanced bisphenol A glycidyl dimethacrylate dentin bonding agent.

OBJECTIVES: The low durability of composite resin restorations can be attributed to the degradation of the resin dentin bonding interface. Owing to the presence of hydrophilic components in the adhesive, the integrity of the resin dentin bonding interface is easily compromised, which, in turn, leads to a reduction in bond strength. The hydrophilic nature of the adhesive leads to water sorption, phase separation, and leaching of the resin component. Therefore, hydrophobic adhesives could effectively be used to stabilize the integrity and durability of the resin dentin bonding interface. METHODS: We synthesized a novel hydrophobic dentin adhesive by partially replacing bisphenol A glycidyl dimethacrylate (Bis-GMA) with a light-curable urushiol monomer. The properties of the produced adhesive, including the degree of conversion, viscosity, contact angle, water sorption/solubility, and mechanical strength, were comprehensively examined and compared to those of the commercially adhesive Adper Single Bond2 as a positive control. The adhesive properties were determined using microtensile bond strength measurements, laser confocal microscopy, scanning electron microscopy observations, and nanoleakage tests. Finally, the novel adhesive was subjected to biocompatibility testing to determine its potential cytotoxicity. RESULTS: At a light-curable urushiol content of 20 %, the synthesized adhesive exhibited high degrees of conversion and hydrophobicity, low cytotoxicity, good mechanical properties, and outstanding adhesive strength. CONCLUSIONS: The introduction of the light-curable urushiol into dentin adhesives can significantly enhance their hydrophobic, mechanical, and bonding properties, demonstrating potential to significantly improve restoration longevity. CLINICAL SIGNIFICANCE: The integration of light-curable urushiol has endowed the experimental adhesives with several enhanced functionalities. These notable benefits underscore the suitability of this monomer for expanded applications in clinical practice.

Evaluation of Microleakage of Nanoparticle-incorporated Cyanoacrylate Root Canal Sealer Using the Radioisotopic Method: An In Vitro Study.

AIM OF THE STUDY: The study aimed to assess the microleakage of nanoparticle-based (NPB) cyanoacrylate sealer and epoxy resin-based (ERB) sealer using radioisotope method and confocal laser scanning microscopy (CLSM). MATERIALS AND METHODS: A total of 100 single-rooted teeth were collected; specimens were accessed, instrumented, and irrigated, and randomly distributed into 4 groups of 25 samples each: Group I: Positive control, group II: Negative control, group III: Obturated with NPB sealer, and group IV: Obturated with ERB sealer. All samples were immersed in 99mTc pertechnetate solution, for 3 hours after which radioactivity was estimated under a Gamma camera. The radioactivity released by specimens before and after nail varnish removal was statistically analyzed. After 2 weeks, the same samples were used for CLSM analysis. The sealer tubular penetration depth was measured at the deepest level for each group using ZEN lite 2012. Data collected was statistically evaluated. RESULTS: The amount of radioactivity observed at first in group III and group IV was 194.76 and 599.12 units, respectively, with p-value < 0.001, indicating significant interaction, and after nail varnish removal, it was 89.68 and 468.44 units, respectively, with a p-value < 0.001; again, indicating statistical significance. Hence, the radioactivity of NPB sealer was found to be lower than ERB sealer in both cases, indicating better sealing of the former. The photomicrographs show that mean value of dye penetration in NPB sealer in first, second, and third segment from apex was 85.06, 75.73, and 66.09, respectively; while in the case of ERB sealer, those were 597.28, 461.17, and 195.68, respectively; with p-value < 0.001; signifying that NPB sealer exhibited higher resistance to microleakage than ERB sealer. CONCLUSION: The NPB sealer can become a potential root canal sealer in future endodontics due to superior physiochemical properties attributed to the cyanoacrylate and incorporated nanoparticles. CLINICAL SIGNIFICANCE: The study clinically signifies that we can equally use the radioisotopic method along with confocal method while conducting the microleakage studies. In addition, NPB sealer can be an emerging replacement with better properties than gold standard root canal sealers for clinical use. How to cite this article: Shetty C, Qaiser S, Shetty A, et al. Evaluation of Microleakage of Nanoparticle-incorporated Cyanoacrylate Root Canal Sealer Using the Radioisotopic Method: An In Vitro Study. J Contemp Dent Pract 2024;25(4):335-341.

Microleakage of Silver-Modified Atraumatic Restorative Technique (SMART) Restorations Using Silver Diammine Fluoride and High-Viscosity Glass Ionomer.

Purpose: The purpose of this study was to investigate the microleakage of atraumatic glass ionomer restorations with and without silver diammine fluoride (SDF) application. Restorations with SDF are termed silver-modified atraumatic restorations (SMART). Methods: Sixty carious extracted permanent teeth were randomly allocated to two SMART groups and two control groups (n equals 15 per group) for a total of four groups. After selective caries removal, test specimens were treated with 38 percent SDF and polyacrylic acid conditioner was applied and rinsed; teeth were restored with Fuji IX GP® glass ionomer (n equals 15) or with SMART Advantage™ glass ionomer (SAGI; n equals 15). For control groups, specimens were restored with their respective GI material after selective caries removal, both without SDF. Restored teeth were placed in Dulbecco's Phosphate-Buffered Saline solution at 37 degrees Celsius for 24 hours. Teeth were thermocycled between five and 55 degrees Celsius for 1,000 cycles, stained with two percent basic fuchsin, sectioned, and visually inspected for microleakage utilizing stereomicroscopy on a four-point scale. Data were statistically analyzed using Kruskal-Wallis one-way analysis of variance on ranks using Dunn's method (P<0.05). Results: Microleakage between the two SMART restoration groups was insignificant. SAGI alone demonstrated significantly more microleakage than all other groups. There was no statistical significance between the Fuji IX GP® control group and the two SMART restoration groups. Conclusions: This in vitro study indicated that silver diammine fluoride placed before glass ionomer restoration does not increase microleakage. Polyacrylic acid may be used after SDF placement without increasing microleakage.

A feasible in vitro method to evaluate bacterial infiltration in three implant-abutment connection systems / Método in vitro factible para evaluar la infiltración bacteriana en tres sistemas de conexión implante-pilar

Introduction: Microorganism infiltration through the im-plant-abutment interface causes oral health problems such as periimplantitis, leading to implant loss. Materials and Methods: A feasible new method to quantify the Streptococcus mutans (S. mutans) infiltration through the implant-abutment interface gap is introduced in the present work. Internal hexagon (IH; n = 10), external hexagon (EH; n = 10), Morse taper (MT; n = 10), and a control for each group (n = 1) were tested. Bacteria suspension was prepared at 1.5x108 CFU/mL (CFU: colony forming units), and the implants were individually submerged up to the connection level, allowing the bacteria to contact it. The abutment was removed, and bacteria count was performed. Results: The implant sets were tested under normal bacterial growth and early and late biofilm growth conditions. Colony-forming units per mL were obtained, and the results were compared among groups. Differences in bacterial count between the MT and EH (p<0.001) and the MT and IH (p<0.001) groups were significantly higher in the MT-type implant. There was a significant increment of bacterial infiltration in the MTs submitted to late biofilm growth conditions. EH and IH connections are more effective in preventing bacterial infiltration independent of the growth condition. Conclusions: The proposed methodology is feasible to evaluate the infiltration of microorganisms through the implant-abutment interface.

Introducción: La infiltración de microorganismos a través de la interfaz implante-pilar provoca problemas de salud bucal como la periimplantitis, que conduce a la pérdida del implante. Materiales y Métodos: En el presente trabajo se presenta un nuevo método factible para cuantificar la infiltración de Streptococcus mutans (S. mutans) a través de la brecha de la interfaz implante-pilar. Se probaron el hexágono interno (IH; n = 10), el hexágono externo (EH; n = 10), el cono Morse (MT; n = 10) y un control para cada grupo (n = 1). Se preparó una suspensión de bacterias a 1,5x108 UFC/mL y los implantes se sumergieron individualmente hasta el nivel de conexión, permitiendo que las bacterias entraran en contacto con él. Resultados: Se retiró el pilar y se realizó recuento de bacterias. Los conjuntos de implantes se probaron en condiciones de crecimiento bacteriano normal y de crecimiento temprano y tardío de biopelículas. Se obtuvieron unidades formadoras de colonias por ml y los resultados se compararon entre grupos. Las diferencias en el recuento bacteriano entre los grupos MT y EH (p<0,001) y MT e IH (p<0,001) fueron significativamente mayores en el implante tipo MT. Hubo un incremento significativo de la infiltración bacteriana en los MT sometidos a condiciones tardías de crecimiento de biopelículas. Las conexiones EH e IH son más efectivas para prevenir la infiltración bacteriana independientemente de las condiciones de crecimiento. Conclusión: La metodología propuesta es factible para evaluar la infiltración de microorganismos a través de la interfaz implante-pilar.

In Vitro Microleakage and Fracture Resistance of "Infinity Edge" and Cusp Reduction Preparation Designs for Moderate-sized Class II Composites.

AIM: This study aimed to evaluate the marginal microleakage and maximum occlusal fracture loads and fracture modes of two novel class II preparation designs, "infinity edge" and the "2.5 mm cusp reduction" preparations as compared to a traditional class II preparation without cuspal involvement. MATERIALS AND METHODS: Thirty extracted human mandibular molars were prepared for moderate-sized class II restorations with extensions into all occlusal grooves. Of these, ten class II preparations served as control. Ten were modified for a 2.5 mm even reduction of the cusps adjacent to the interproximal box. An additional 10 preparations were modified with an "infinity edge" bevel on the interproximal and occlusal portions. All teeth were restored utilizing a flowable bulk-fill composite in the apical portion of the interproximal box and 2-4 mm of heated bulk-fill composite in one increment for the remainder. All groups were cyclic loaded and thermocycled, then imaged with microcomputed tomography (µCT) before and after infiltration with a silver nitrate solution. Images were subtracted to obtain volumetric measurements of microleakage and reported as a percentage of the total volume from the apical extent of the proximal box. All groups were loaded to failure and fracture load and mode were recorded. RESULTS: No significant differences were found in microleakage volume as a percentage of total tooth volume; however, the "infinity edge" group had significantly greater microleakage in the proximal box compared to the traditional class II group. No significant differences were found in fracture load or mode between the groups. CONCLUSION: Traditional class II, 2.5 mm cuspal reduction, and "infinity edge" preparation designs have similar fracture loads as well as volumes of microleakage; however, an "infinity edge" preparation has a higher ratio of microleakage in the proximal box. CLINICAL SIGNIFICANCE: Clinicians should carefully consider the use of "infinity edge" margins, particularly on dentin in the apical extent of the proximal box. How to cite this article: Watson JC, Lien W, Raimondi JC, et al. In Vitro Microleakage and Fracture Resistance of "Infinity Edge" and Cusp Reduction Preparation Designs for Moderate-sized Class II Composites. J Contemp Dent Pract 2024;25(1):3-9.

Effect of protective coating agents on microleakage and flexural strength of glass ionomer cement and zirconomer. an in vitro study.

PURPOSE: The objective of this study was to assess the microleakage and flexural strength of glass ionomer cement (GIC) and modified GIC (Zirconomer) when coated with protective coating agents such as COAT-IT and G-COAT plus. METHODS: Sixty tooth specimens were grouped into two groups based on the type of restorations (GIC (n = 30) and Zirconomer (n = 30)). The samples were further divided into three subgroups (n = 10) based on the protective coating agent (Petroleum jelly, G-COAT Plus, or COAT IT) applied. This study evaluated the microleakage at the occlusal and cervical margins of class V restoration after being subjected to dye penetration and sectioning. Each specimen was viewed under a 40 × microscope and was given scores based on the depth of dye penetration. They were statistically analyzed using the Kruskal-Wallis test and compared within the groups using the Mann- Whitney Test. In addition, flexural strength was assessed using standardized cuboid (25 × 2 × 2 mm) specimens of restorative materials with and without protective coating agents. The mean flexural strength data of all the subgroups were statistically evaluated using a one-way analysis of variance (ANOVA) and compared within the subgroups using the student t test. RESULTS: A statistically significant difference was found when occlusal margin microleakage scores were evaluated with G-COAT Plus demonstrating the lowest occlusal margin microleakage when applied over GIC restoration. The increasing order of occlusal margin microleakage scores is as follows: GIC with G-COAT Plus, Zirconomer with COAT-IT, GIC with COAT-IT, GIC, Zirconomer with G-COAT Plus, and Zirconomer. However, the cervical margin microleakage scores revealed no significant difference. While flexural strength was found to be highest for the GIC group coated with G-COAT Plus, it was observed that there was a significant improvement in the flexural strength of both GIC and Zirconomer when coated with either of the protective coating agents. CONCLUSION: Within the limitations of this in vitro study, it was observed that the application of protective coating agents can significantly reduce the potential microleakage and improve the flexural strength of the restorative material especially when zirconia-reinforced GIC is the restorative material.

Protocolo para la medición de espacios vacíos dentro de la obturación endodóntica con microtomografía / A protocol for the measurement of voids within the endodontic filling with microtomography

La microtomografía es un estudio que utiliza la ra-diación X para obtener imágenes de tamaños de mi-lésimas de milímetros y de alta resolución. Las imá-genes 2D son procesadas por diferentes softwares para lograr obtener volúmenes capaces de ser ana-lizados tridimensionalmente. La microtomografía es el estudio de elección a la hora de evaluar caracte-rísticas muy pequeñas con gran precisión. La obtu-ración endodóntica buscar lograr un sellado que no tenga espacios vacíos dentro de la masa de obtura-ción. Esto es importante debido a que los poros pue-den permitir, si están en contacto con la pared den-tinaria, la entrada de microorganismos al conducto radicular. El objetivo de este trabajo fue describir el procedimiento para el análisis y visualización de los espacios vacíos dentro de la obturación endodónti-ca, utilizando la microtomografía de rayos x, y esta-blecer un protocolo para ser utilizado por cualquier investigador(AU)

Microtomography is a study that uses X-radiation to obtain high-resolution images of sizes of thousandths of millimeters. The 2D images are processed by different software to obtain volumes capable of being analyzed three-dimensionally. Microtomography is the study of choice when evaluating very small features with great precision. Endodontic filling seeks to achieve a seal that does not have voids within the filling obturation. This is important because the voids can allow, if they are in contact with the dentin wall, the entry of microorganisms into the root canal. The objective of this work was to describe the procedure for the analysis and visualization of voids within the endodontic filling using microtomography and to establish the protocol to be used by any researcher (AU)

Evaluating the effect of three fissure preparation techniques on microleakage of a colored flowable composite used as a fissure sealant.

Pit and fissure sealants play an essential role in preventive dentistry. This study evaluates the microleakage levels of a new and colored flowable composite applied as a sealant after three preparation techniques. A total of 24 non-carious mandibular permanent molars with deep pits and fissures were included in the study. Pit and fissures were prepared with 37% phosphoric acid, tungsten carbide bur and fissurotomy burs (SS WHITE Dental, New Jersey, USA) using conventional, enameloplasty and fissurotomy techniques. All samples were thermocycled following the placement of Rainbow Flow (PPH CERKAMED Wojciech Pawlowski, Poland) as a sealant and sections were taken after immersion in methylene blue dye. The microleakage levels of the samples were examined under a stereomicroscope (Olympus SZX-7 Olympus SZ-61 Stereo Microscope) at 2.8× magnification to analyze the dye penetration of the flowable composite. The 144 sections were examined and scoring for microleakage was done by examining the dye penetration from the occlusal border to the base of the fissure. Considering all sections regardless of the preparation technique, it was found that 16.6% of the sections have no leakage. Regarding the microleakage scores, the mean score of the conventional group was 1.87 ± 0.98, the mean score of the enameloplasty group was 1.88 ± 1.14, and the mean score of the fissurotomy group was 1.81 ± 1.1. The median scores of the conventional, enameloplasty and fissurotomy groups were 2, 2 and 1.5, respectively. The present study reports no difference between the microleakage level of a colored flowable composite material used as a pit and fissure sealant following three fissure preparation techniques and supports the clinical use of this material.

Orifice barriers to prevent coronal microleakage after root canal treatment: systematic review and meta-analysis.

AIMS: This systematic review aimed to compare the efficiency of orifice barriers in preventing coronal microleakage in vitro. METHODS: Articles published in English, German and Chinese were searched for studies describing microleakage assays for the bacterial penetration of root canal-treated teeth in vitro. The final sample included 18 articles for review and meta-analysis. Risk ratios and confidence intervals were determined for dichotomous variables. Ten publications using bacterial leakage models contributed to the meta-analysis. RESULTS: The addition of orifice barriers to a root canal filling was overall effective, shown by risk ratios (RR) and 95% confidence intervals (CI) demonstrating reduced microleakage with glass ionomer cement (GIC) (RR 0.37, 95% CI 0.26-0.53, P < 0.001), resin-modified GIC (RR 0.32, 95% CI 0.15-0.67, P = 0.01), composite resin (RR 0.54, 95% CI 0.38-0.75, P < 0.001), mineral trioxide aggregate (MTA) (RR 0.25, 95% CI 0.12-0.52, P < 0.001) and Cavit (RR 0.23, 95% CI 0.14-0.39, P < 0.001). There were no significant differences between GIC, resin-modified GIC, composite resin and MTA orifice barriers. CONCLUSIONS: Placement of an orifice barrier over the root canal filling is effective in the prevention of coronal microleakage in vitro. Other parameters may also affect the effectiveness of orifice barriers, including thickness and duration of exposure to the oral environment. © 2023 Australian Dental Association.

Effect of three different conditioning agents on cavosurface microleakage and bond strength of glass ionomer restorations - An in vitro study.

Aim: This study aimed to investigate the conditioning effects of phosphoric acid/5.25% sodium hypochlorite (NaOCl) mixture, 2% chlorhexidine (CHX) digluconate, and 10% polyacrylic acid on cavosurface microleakage and bond strength of glass ionomer (GI) restorations. Materials and Methods: Out of 68 extracted premolars, 34 teeth were selected for microleakage and 34 for bond strength evaluation. The samples were divided into the following four groups. Group 1: pretreatment with 50/50 volume% mixture of 5.25% NaOCl solution and 37% phosphoric acid (H3PO4), Group 2:pretreatment with 2% CHX digluconate, Group 3: pretreatment with 10% polyacrylic acid (positive control), and Group 4: no pretreatment (negative control). All the samples were then restored with glass ionomer cement (GIC). Microleakage was evaluated using a stereomicroscope and rhodamine-B dye penetration test. For bond strength, flat dentin surface was exposed and pretreated as mentioned previously and restored with GIC and was evaluated using universal testing machine. Results: Among all the four groups, Group 1 showed least microleakage and highest bond strength when compared with other groups. Whereas the Group 4 samples which were not pretreated with any of the conditioning agent showed the least shear bond strength with greatest cavosurface microleakage when compared to the groups which were pretreated with the conditioning agents. Conclusions: A combination of 50/50 volume % mixture of 37% H3PO4 and 5.25% NaOCl can be a good choice for surface pretreatment of GI restorations.

Impact of access cavity cleaning on the seal of postendodontic composite restorations in vitro.

AIM: The aim of the study was to investigate the influence of cavity cleaning and conditioning on marginal integrity of directly placed post-endodontic composite class-I-restorations in vitro. METHODOLOGY: A total of 168 fully intact teeth without caries or fillings received pre-endodontic composite restorations (class-II) after their extraction. Occlusal endodontic access-cavities were prepared, and root canals were instrumented and filled with gutta-percha and an epoxy resin-based sealer. Prior to post-endodontic class-I-restoration, access cavities were completely contaminated with sealer, cleaned with alcohol and pre-treated as follows: cleaner only (alcohol), glycine-polishing, Al2 O3 sandblasting, carbide bur (immediate as well as delayed restoration). A positive control (not contaminated with sealer and adhesive used) and negative control (cleaner used but no adhesive) were established. Half of the teeth from each group were subjected to thermocycling and mechanical loading (TCML). Marginal integrity of post-endodontic restoration was evaluated in oro-vestibular or mesio-distal sections after AgNO3 dye penetration (DP) by standardized photomacroscopic imaging and expressed in per cent of margin length along all segments and separately for enamel, dentine and composite, respectively. Results were analysed non-parametrically (α = .05). RESULTS: No restorations or teeth fractured or debonded completely. Without TCML, the median DP of all segments was significantly higher for the negative control compared with all other groups in oro-vestibular cutting direction (53%; p = .002) and in mesio-distal cutting direction (51%; p ≤ .041). The other groups without TCML revealed 16%-24% DP (oro-vestibular) and 12%-24% DP (mesio-distal). With TCML, the median DP in oro-vestibular cutting direction for all segments ranged between 48% and 62% for all groups, a significant difference was only observed between glycine-polishing and carbide bur (p = .041). In mesio-distal cutting direction, the median DP in negative control was 69% with TCML and significantly higher compared with all other groups (p = .002). For all other groups, the median DP of all segments ranged between 28% and 40% with TCML without significant differences. Error rates method (k = 7) revealed a significant influence of TCML in general on penetration of all segments in both oro-vestibular and mesio-distal cutting directions. CONCLUSION: Additional access cavity pre-treatment after alcohol cleaning did not improve the marginal integrity of post-endodontic composite restorations. Thorough cleaning of the access cavity with alcohol seems to assure an acceptable marginal integrity to the tooth and restorative composite.

Sealing Behavior of a New Material Combination in Two-Part Dental Implant Systems: An In Vitro Examination.

PURPOSE: To test a newly introduced implant-abutment material combination against bacterial endotoxin leakage in a human whole blood assay. MATERIALS AND METHODS: Two dental implant systems with internal connections and the following material combinations at the implant-abutment interface (IAI) were used (implant material/abutment material): yttrium-stabilized tetragonal zirconium dioxide (Y-TZP)/polyetherketoneketone (PEKK), and titanium (Ti/Ti). Test implants were inoculated with lipopolysaccharide (LPS) and sealed and submerged in human whole blood. Untreated implants served as the control groups. Changes in gene expression levels of inflammatory markers indicating LPS leakage were assessed after 1, 8, and 24 hours using quantitative real-time polymerase chain reaction. RESULTS: In the Y-TZP/PEKK test group, a significant influence of the implant system (P < .001) on increases in gene expression indicating leakage were detected after 8 hours for TLR-4 and after 24 hours for interleukin 1-ß and nuclear factor kappa-light-chain-enhancer of activated B-cells (NF-κB), indicating microleakage of LPS at the IAI. In the Ti/Ti test group, differences in gene expression were found only for NF-κB after 8 hours. CONCLUSION: The internal hexalobe IAI of two-piece dental implants fabricated from Y-TZP and PEKK do not prevent LPS molecular microleakage.

Marginal microleakage and modified microtensile bond strength of Activa Bioactive, in comparison with conventional restorative materials.

OBJECTIVES: This study aimed to assess the enamel and dentin marginal microleakage and dentin microtensile bond strength (µTBS) of ACTIVA BioACTIVE Restorative with and without a bonding agent compared with conventional restorative materials. MATERIAL AND METHODS: For enamel and dentin microleakage, Class II boxes were prepared in the mesial (1 mm under the cementoenamel junction) and distal (1 mm above the cementoenamel junction) surfaces of 90 extracted human third molars. The teeth were randomly divided into five groups (n = 18): Group Z (G-Premio Bond + Filtek Z250 XT), Group X (G-Premio Bond + X-tra fil bulk-fill), Group AA (G-Premio Bond + Activa Bioactive restorative), Group A (Activa Bioactive restorative), and Group G (dentin conditioner + Fuji II LC Improve). The teeth were thermocycled, and their microleakage was quantified using the dye penetration test under a stereomicroscope. For dentin µTBS measurement, 12 specimens were fabricated in metal molds (1 × 1 × 12 mm³) for each group mentioned above, and a universal testing machine measured their µTBS. Data were analyzed using one-way analysis of variance (ANOVA), the Kruskal-Wallis test, and multiple comparisons tests. RESULTS: Significant differences were noted among the groups in marginal microleakage and µTBS (p < .001). The highest mean microleakage scores at the enamel and dentin margins were noted in Group A, which had significant differences with other groups (p < .001). The highest µTBS was found in Group X, with significant differences with Group G and Group A (p < .05). The lowest µTBS was noted in Group A, with significant differences with Groups X, Group AA, and Group Z (p < .001). CONCLUSIONS: Activa Bioactive without a bonding agent showed significantly lower µTBS to dentin, and higher microleakage at the enamel and dentin margins. Application of adhesive resin with Activa Bioactive provided a dentine bond strength and marginal seal comparable to other restorative materials.

Microgap and microleakage of a hybrid connection platform-switched implant system in the absence or presence of a silicone-based sealing agent.

The present study aims to characterize, for the first time, the microgap and bacterial microleakage of a platform-switched implant system with hybrid connection, screwed at distinct torque values (manufacturer recommended torque-25 N cm-and a reduced torque-5 N cm-mimicking the long-term functional use), in the absence or presence of a silicon-based sealing agent. Microgap was determined through scanning electron microscopy and bacterial microleakage was evaluated in vitro, upon Enterococcus faecalis colonization of the system. The sealing efficacy was evaluated in the absence or presence of a commercially available silicon-based sealer. The cytotoxicity of the sealer was further addressed in vitro, with a fibroblastic cell line, in accordance with reference standards. A low microgap of the implant system was verified, regardless of the applied torque load-maximal values ranged around 0.25 and 1.25 µm, for 25 and 5 N cm torques, respectively. No bacterial microleakage was reported at 25 N cm, while at 5 N cm, leakage was verified on 38% of the samples. The application of a silicon-based sealer-with an adequate cytocompatible profile-was effective on preventing the bacterial microleakage on the assayed experimental setting. The assayed platform-switched implant system with hybrid connection presented a low interfacial misfit and an effective sealing capability at manufacturer recommended torque. Despite the increased microleakage at low torque conditions, the application of a cytocompatible silicon-based sealing agent restored the sealing effectiveness of the system. The use of a silicon-based sealing agent can assist on the maintenance of the sealing effectiveness even at low torque conditions.

Quantitative Microbial Leakage Evaluation of Restorative Materials with/without Antibacterial Primer as an Intracoronal Barrier: An Ex Vivo Study.

AIM: Aim of this research was to assess the microbial leakage of restorative materials with/without antibacterial primer as an intracoronal barrier. MATERIALS AND METHODS: Fifty-five extracted single-rooted teeth were included in this study. The canals were cleaned, shaped, and obturated with gutta-percha and AH plus sealer at the established working length. After removing 2 mm of coronal gutta-percha, the teeth were incubated for 24 hours. The teeth were divided into groups according to the materials used as intracoronary orifice barriers as follows: • Group I: Clearfil Protect Bond/Clearfil AP-X • Group II: Xeno IV/Clearfil AP-X • Group III: Chemflex (glass ionomer) • Group IV: Positive control (no barrier) • Group V: Negative control (no barrier and inoculated with sterile broth) Sterile 2 chambers bacterial technique was used to assess the microleakage and Enterococcus faecalis was considered as a microbial marker. The percentage of samples leaked, the time taken for leakage, and the number of colony-forming units (CFUs) in the leaked samples were calculated and analyzed statistically. RESULTS: There was no statistically significant difference found in bacterial penetration among the three investigated materials after 120 days of use as an intracoronal orifice barrier. This study can also infer that the leaked sample from the Clearfil Protect Bond showed the least mean number of CFUs (43 CFUs) followed by Xeno IV (61 CFUs) and glass ionomer cement (GIC) (63 CFUs). CONCLUSION: This study concluded that all three experimental antibacterial primers performed better as intracoronal barrier. However, Clearfil Protect Bond with an antibacterial primer showed promising results as an intracoronal orifice barrier in reducing the number of bacterial leakages. CLINICAL SIGNIFICANCE: The significance of intracoronal orifice barriers in the success of endodontic treatment depends on the ability of the materials to prevent microleakage. This helps clinicians to provide successful antibacterial therapy against endodontic anaerobes.

Comparison of sealing ability of MTA and retroplast as root end filling materials evaluated under a stereomicroscope using rhodamine B dye: An In vitro study.

Aim: The aim of the study was to compare the sealing ability of Mineral Trioxide Aggregate (MTA) and Retroplast as root end filling materials using the Rhodamine B dye penetration method in vitro. Methodology: Forty freshly extracted human single-rooted teeth were randomly divided into two groups of 20 teeth each, and standard root-end cavities were prepared in all teeth. The cavities were filled with MTA and Retroplast in groups 1 and 2, respectively. The specimens were then stored in 1% Rhodamine B dye for a week, following which the dye penetration with all samples was analysed under a stereomicroscope and scored according to Tronstad's criteria. The observations were compared with Chi square test at a 0.220 level of significance. Results: 5% of the samples in both the groups showed no significant leakage. The leakage was deeper with the Retroplast group than with the MTA group; however, there was no statistically significant difference between the two groups. Conclusion: Both MTA and Retroplast are similar in their sealing potential as root-end cavity fillings with Retroplast reporting slightly deeper microleakage than MTA within the limits of the present study.

Efficacy of Various Implant Abutment Screw Access Channel Sealing Materials in Preventing Microleakage: A Systematic Review.

The aim of this systematic review is to evaluate the effectiveness of different materials used for sealing dental implant abutment screw access channel (ASAC), in preventing microleakage. As per the searched indexed English literature, this study is the first review of its kind. Indexed English literature published up to February 20, 2021 was systematically searched on relevant electronic databases. The recommendations specified by the Preferred Reporting Items for Systematic Reviews and Meta-Analysis (PRISMA) were applied for constructing framework, and reporting the current review. The focused PICO (Participant, Intervention, Comparison, Outcome) question was: "Which material (C) is more effective in sealing (I) implant ASAC (P) in terms of causing minimal microbial leakage (O)". Quality of articles was assessed with modified CONSORT scale for in vitro studies. Five in vitro studies were selected for qualitative analysis after final stage screening. Modified CONSORT scale suggested that out of the 5 selected studies, 1 each was of low and high quality, whereas 3 studies were of moderate quality. Included studies had contrasting results related to the efficacy these materials as sealants in ASAC. Sealing capacity against microleakage should be considered as one of the important criteria while selecting the material to fill implant ASAC. Definitive conclusions asserting superiority of a single material over others are difficult to draw, due to nonhomogeneity in study design of the included papers. More studies should be conducted in the near future to investigate the efficacy of various combination of materials in preventing microleakage.

Assessment of Penetration Depth and Microleakage of Different Pit and Fissure Sealants Using Dye Penetration Method: An In Vitro Study.

AIM AND OBJECTIVE: The aim of this study was to evaluate the depth of penetration as well as the microleakage of three different pit and fissure sealant materials employing the dye penetration method. MATERIALS AND METHODS: Sixty healthy human mandibular premolar teeth without dental caries that were extracted for orthodontic treatment constituted the study samples. These 60 premolar samples were subjected to an equal division (20 in every group) into three groups. Group I: self-adhering flowable composite, group II: flowable nanocomposites, group III: classical pit and fissure sealants. Every sample tooth underwent thermocycling amid 4°C ± 2°C and 60°C ± 2°C for 1,000 cycles. The samples were placed in 1% methylene blue solution for 24 hours to permit diffusion of the dye into probable gaps in between the restoration and the tooth. The teeth were sectioned and evaluated below a stereomicroscope at 10× magnification with image analysis software. RESULTS: Flowable nanocomposites (3.69 ± 0.10) exhibited a slightly greater mean depth of penetration as compared to classical pit and fissure sealants (3.58 ± 0.16) and self-adhering flowable composites (3.51 ± 0.13) in that order. This difference between the three sealants was not significant statistical. Amid the three sealant study groups, the lowest mean marginal microleakage was exhibited by the flowable nanocomposites (1.06 ± 0.03), followed by self-adhering flowable composites (1.98 ± 0.06), and classical pit and fissure sealants (2.74 ± 0.11). Analysis of variance revealed statistically significant differences among the three sealants that were studied. CONCLUSION: This study concludes that flowable nanocomposites depicted enhanced penetration and reduced marginal leakage as compared to the self-adhering flowable composites and classical pit and fissure sealants. CLINICAL SIGNIFICANCE: An efficient approach to preventing dental caries on the occlusal surfaces of teeth is the use of pit and fissure sealants. The efficiency of sealants chiefly depends on the morphological characteristics of the fissures and properties of dental materials used.

Bacterial leakage assessment in root canals sealed with AH Plus sealer modified with silver nanoparticles.

BACKGROUND: Successful endodontic therapy requires prevention of bacterial leakage between the root canal filing and root-canal walls. Sealing quality of a root canal filling depends strongly on the sealing ability of the sealer used. The present study aimed to evaluate the bacterial leakage resistance of AH Plus sealer modified with silver nanoparticles. METHODS: Forty sound teeth were obturated using lateral compaction technique except for five teeth as the negative controls. After considering five teeth as the positive controls (filled without sealer), the remaining teeth were assigned to two groups (n = 15) in terms of the sealer used (AH Plus sealer and silver nanoparticle-modified AH Plus). Bacterial leakage was evaluated in saliva using the two-chamber technique in every 24 h. When all the samples in the test groups were contaminated, the study was terminated. The data were analyzed with log-rank statistical test. RESULTS: All samples in both experimental groups were contaminated during the 3-months period of observation. There was no significant difference in contamination time between study groups (P > 0.05). CONCLUSIONS: Silver nanoparticles used in tested concentration did not improve the bacterial leakage resistance of AH Plus sealer.