RESUMEN
The development and application of an electrochemical sensor is reported for detection of poly(3-hydroxybutyrate) (P3HB) - a bioplastic derived from agro-industrial residues. To overcome the challenges of molecular imprinting of macromolecules such as P3HB, this study employed methanolysis reaction to break down the P3HB biopolymer chains into methyl 3-hydroxybutyrate (M3HB) monomers. Thereafter, M3HB were employed as the target molecules in the construction of molecularly imprinted sensors. The electrochemical device was then prepared by electropolymerizing a molecularly imprinted poly (indole-3-acetic acid) thin film on a glassy carbon electrode surface modified with reduced graphene oxide (GCE/rGO-MIP) in the presence of M3HB. Electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), scanning electron microscopy with field emission gun (SEM-FEG), Raman spectroscopy, attenuated total reflection Fourier-transform infrared (ATR-FTIR) and X-ray Photoelectron Spectroscopy (XPS) were employed to characterize the electrode surface. Under ideal conditions, the MIP sensor exhibited a wide linear working range of 0.1 - 10 nM and a detection limit of 0.3 pM (n = 3). The sensor showed good repeatability, selectivity, and stability over time. For the sensor application, the bioproduction of P3HB was carried out in a bioreactor containing the Burkholderia glumae MA13 strain and sugarcane byproducts as a supplementary carbon source. The analyses were validated through recovery assays, yielding recovery values between 102 and 104%. These results indicate that this MIP sensor can present advantages in the monitoring of P3HB during the bioconversion process.
Asunto(s)
Burkholderia , Técnicas Electroquímicas , Electrodos , Grafito , Hidroxibutiratos , Polímeros Impresos Molecularmente , Poliésteres , Grafito/química , Poliésteres/química , Hidroxibutiratos/química , Burkholderia/química , Burkholderia/metabolismo , Técnicas Electroquímicas/métodos , Técnicas Electroquímicas/instrumentación , Polímeros Impresos Molecularmente/química , Límite de Detección , Oxidación-Reducción , PolihidroxibutiratosRESUMEN
Recent research focuses on fabricating scaffolds imitating the extracellular matrix (ECM) in texture, composition, and functionality. Moreover, specific nano-bio-particles can enhance cell differentiation. Decellularized ECM nanoparticles possess all of the mentioned properties. In this research, cartilage ECM, extracted from the cow's femur condyle, was decellularized, and ECM nanoparticles were synthesized. Finally, nanocomposite electrospun fibers containing polyhydroxybutyrate (PHB), chitosan (Cs) nanoparticles, and ECM nanoparticles were fabricated and characterized. TEM and DLS results revealed ECM nanoparticle sizes of 17.51 and 21.6 nm, respectively. Optimal performance was observed in the scaffold with 0.75 wt% ECM nanoparticles (PHB-Cs/0.75E). By adding 0.75 wt% ECM, the ultimate tensile strength and elongation at break increased by about 29 % and 21 %, respectively, while the water contact angle and crystallinity decreased by about 36° and 2 %, respectively. Uneven and rougher surfaces of the PHB-Cs/0.75E were determined by FESEM and AFM images, respectively. TEM images verified the uniform dispersion of nanoparticles within the fibers. After 70 days of degradation in PBS, the PHB-Cs/0.75E and PHB-Cs scaffolds demonstrated insignificant weight loss differences. Eventually, enhanced viability, attachment, and proliferation of the human costal chondrocytes on the PHB-Cs/0.75E scaffold, concluded from MTT, SEM, and DAPI staining, confirmed its potential for cartilage tissue engineering.
Asunto(s)
Cartílago , Quitosano , Matriz Extracelular , Hidroxibutiratos , Nanopartículas , Ingeniería de Tejidos , Andamios del Tejido , Quitosano/química , Ingeniería de Tejidos/métodos , Andamios del Tejido/química , Matriz Extracelular/química , Matriz Extracelular/metabolismo , Nanopartículas/química , Animales , Hidroxibutiratos/química , Cartílago/citología , Cartílago/metabolismo , Poliésteres/química , Humanos , Bovinos , Condrocitos/citología , Condrocitos/metabolismo , PolihidroxibutiratosRESUMEN
Dental implant success is threatened by peri-implantitis, an inflammation leading to implant failure. Conventional treatments struggle with the intricate microbial and host factors involved. Antibacterial membranes, acting as barriers and delivering antimicrobials, may offer a promising solution. Thus, this study highlights the potential of developing antibacterial membranes of poly-3-hydroxybutyrate and silver nanoparticles (Ag Nps) to address peri-implantitis challenges, discussing design and efficacy against potential pathogens. Electrospun membranes composed of PHB microfibers and Ag Nps were synthesized in a blend of DMF/chloroform at three different concentrations. Various studies were conducted on the characterization and antimicrobial activity of the membranes. The synthesized Ag Nps ranged from 4 to 8 nm in size. Furthermore, Young's modulus decreased, reducing from 13.308 MPa in PHB membranes without Ag Nps to 0.983 MPa in PHB membranes containing higher concentrations of Ag Nps. This demonstrates that adding Ag Nps results in a less stiff membrane. An increase in elongation at break was noted with the rise in Ag Nps concentration, from 23.597 % in PHB membranes to 60.136 % in PHB membranes loaded with Ag Nps. The antibiotic and antibiofilm activity of the membranes were evaluated against Pseudomonas aeruginosa, Staphylococcus aureus, Streptococcus mutans, and Candida albicans. The results indicated that all PHB membranes containing Ag Nps exhibited potent antibacterial activity by inhibiting the growth of biofilms and planktonic bacteria. However, inhibition of C. albicans occurred only with the PHB-Ag Nps C membrane. These findings emphasize the versatility and potential of Ag Nps-incorporated membranes as a multifunctional approach for preventing and addressing microbial infections associated with peri-implantitis. The combination of antibacterial and antibiofilm properties in these membranes holds promise for improving the management and treatment of peri-implantitis-related complications.
Asunto(s)
Antibacterianos , Biopelículas , Hidroxibutiratos , Membranas Artificiales , Nanopartículas del Metal , Periimplantitis , Plata , Plata/química , Plata/farmacología , Biopelículas/efectos de los fármacos , Antibacterianos/farmacología , Antibacterianos/química , Nanopartículas del Metal/química , Periimplantitis/tratamiento farmacológico , Periimplantitis/microbiología , Hidroxibutiratos/química , Hidroxibutiratos/farmacología , Poliésteres/química , Pruebas de Sensibilidad Microbiana , Humanos , Staphylococcus aureus/efectos de los fármacos , Pseudomonas aeruginosa/efectos de los fármacos , Streptococcus mutans/efectos de los fármacos , PolihidroxibutiratosRESUMEN
A middle ear infection occurs due to the presence of several microorganisms behind the eardrum (tympanic membrane) and is very challenging to treat due to its unique location and requires a well-designed treatment. If not treated properly, the infection can result in severe symptoms and unavoidable side effects. In this study, excellent biocompatible ethyl cellulose (EC) and biodegradable polyhydroxybutyrate (PHB) biopolymer were used to fabricate drug-loaded nanofiber scaffolds using an electrospinning technique to overcome antibiotic overdose and insufficient efficacy of drug release during treatment. PHB polymer was produced from Halomonas sp., and the purity of PHB was found to around be 90 %. Additionally, ciprofloxacin (CIP) and amoxicillin (AMX) are highly preferable since both drugs are highly effective against gram-negative and gram-positive bacteria to treat several infections. Obtained smooth nanofibers were between 116.24 and 171.82 nm in diameter and the addition of PHB polymer and antibiotics improved the morphology of the nanofiber scaffolds. Thermal properties of the nanofiber scaffolds were tested and the highest Tg temperature resulted at 229 °C. The mechanical properties of the scaffolds were tested, and the highest tensile strength resulted in 4.65 ± 6.33 MPa. Also, drug-loaded scaffolds were treated against the most common microorganisms that cause the infection, such as S.aureus, E.coli, and P.aeruginosa, and resulted in inhibition zones between 10 and 21 mm. MTT assay was performed by culturing human adipose-derived mesenchymal stem cells (hAD MSCs) on the scaffolds. The morphology of the hAD MSCs' attachment was tested with SEM analysis and hAD MSCs were able to attach, spread, and live on each scaffold even on the day of 7. The cumulative drug release kinetics of CIP and AMX from drug-loaded scaffolds were analysed in phosphate-buffered saline (pH: 7.4) within different time intervals of up to 14 days using a UV spectrophotometer. Furthermore, the drug release showed that the First-Order and Korsmeyer-Peppas models were the most suitable kinetic models. Animal testing was performed on SD rats, matrix and collagen deposition occurred on days 5 and 10, which were observed using Hematoxylin-eosin and Masson's trichrome staining. At the highest drug concentration, a better repair effect was observed. Results were promising and showed potential for novel treatment.
Asunto(s)
Amoxicilina , Antibacterianos , Celulosa , Ciprofloxacina , Nanofibras , Celulosa/química , Celulosa/análogos & derivados , Ciprofloxacina/farmacología , Ciprofloxacina/química , Nanofibras/química , Animales , Ratas , Amoxicilina/farmacología , Amoxicilina/química , Antibacterianos/farmacología , Antibacterianos/química , Hidroxibutiratos/química , Hidroxibutiratos/farmacología , Humanos , Otitis Media/tratamiento farmacológico , Otitis Media/microbiología , Poliésteres/química , Liberación de Fármacos , Andamios del Tejido/química , Células Madre Mesenquimatosas/efectos de los fármacos , Células Madre Mesenquimatosas/citología , Prohibitinas , Portadores de Fármacos/química , MasculinoRESUMEN
Biogenic nanoparticles (NPs) have emerged as promising therapeutic formulations in effective drug delivery. Despite of various positive attributes, these NPs are often conjugated with various cytotoxic organic fluorophores for bioimaging, thereby reducing its effectiveness as a potential carrier. Herein, we aim to formulate biogenic fluorescent pigmented polyhydroxybutyrate (PHB) NPs from Rhodanobacter sp. strain KT31 (OK001852) for drug delivery. The bacterial strain produced 0.5 g L-1 of polyhydroxyalkanoates (PHAs) from 2.04 g L-1 of dry cell weight (DCW) under optimised conditions via submerged fermentation. Further, structural, thermal, and morphological charactersiation of the extracted PHAs was conducted using advance analytical technologies. IR spectra at 1719.25 cm-1 confirmed presence of C = O functional group PHB. NMR and XRD analysis validated the chemical structure and crystallinity of PHB. TG-DTA revealed Tm (168 °C), Td (292 °C), and Xc (35%) of the PHB. FE-SEM imaging indicated rough surface of the PHB film and the biodegradability was confirmed from open windro composting. WST1 assay showed no significant cell death (> 50%) from 100 to 500 µg/mL, endorsing non-cytotoxic nature of PHB. PHB NPs were uniform, smooth and spherical with size distribution and mean zeta potential 44.73 nm and 0.5 mV. IR and XRD peaks obtained at 1721.75 cm-1 and 48.42 Å denoted C = O and crystalline nature of PHB. Cell proliferation rate of PHB NPs was quite significant at 50 µg/mL, establishing the non-cytotoxic nature of NPs. Further, in vitro efficacy of the PHB NPs needs to be evaluated prior to the biomedical applications.
Asunto(s)
Nanopartículas , Polihidroxialcanoatos , Prohibitinas , Nanopartículas/química , Polihidroxialcanoatos/química , Polihidroxialcanoatos/metabolismo , Sistemas de Liberación de Medicamentos , Hidroxibutiratos/química , Hidroxibutiratos/metabolismo , Humanos , Rhodospirillaceae/metabolismo , Rhodospirillaceae/química , Portadores de Fármacos/químicaRESUMEN
Within bioplastics, natural poly(3-hydroxybutyrate) (PHB) stands out as fully biocompatible and biodegradable, even in marine environments; however, its high isotacticity and crystallinity limits its mechanical properties and hence its applications. PHB can also be synthesized with different tacticities via a catalytic ring-opening polymerization (ROP) of rac-ß-butyrolactone (BBL), paving the way to PHB with better thermomechanical and processability properties. In this work, the catalyst family is extended based on aluminum phenoxy-imine methyl catalyst [AlMeL2], that reveals efficient in the ROP of BBL, to the halogeno analogous complex [AlClL2]. As well, the impact on the ROP mechanism of different initiators is further explored with a particular focus in dimethylaminopyridine (DMAP), a hardly studied initiator for the ROP of BBL. A thorough mechanistic study is performed that evidences the presence of two concomitant DMAP-mediated mechanisms, that lead to either a DMAP or a crotonate end-capping group. Besides, in order to increase the possibilities of PHB post-polymerization functionalization, the introduction of a side-chain functionality is explored, establishing the copolymerization of BBL with ß-allyloxymethylene propiolactone (BPLOAll), resulting in well-defined P(BBL-co-BPLOAll) copolymers.
Asunto(s)
4-Butirolactona , Aluminio , Polihidroxialcanoatos , Polimerizacion , Catálisis , 4-Butirolactona/química , 4-Butirolactona/análogos & derivados , Polihidroxialcanoatos/química , Aluminio/química , Estructura Molecular , Hidroxibutiratos/química , PolihidroxibutiratosRESUMEN
Microbeads of biodegradable polyhydroxybutyrate (PHB) offer environmental benefits and economic competitiveness. The aim of this study was to encapsulate a water-soluble bioactive compound, niacinamide (NIA), in a pH-responsive natural matrix composed of PHB and cellulose acetate phthalate (CAP) by double emulsification (W1/O/W2) to improve the encapsulation efficiency (%EE) and loading capacity (%LC). PHB was produced in-house by Escherichia coli JM109 pUC19-23119phaCABA-04 without the inducing agent isopropyl ß-D-1-thiogalactopyranoside (IPTG). The influences of PHB and polyvinyl alcohol (PVA) concentrations, stirring rate, PHB/CAP ratio and initial NIA concentration on the properties of NIA-loaded pH-responsive microbeads were studied. The NIA-loaded pH-responsive PHB/CAP microbeads exhibited a spherical core-shell structure. The average size of the NIA-loaded pH-responsive microbeads was 1243.3 ± 11.5 µm. The EE and LC were 33.3 ± 0.5 % and 28.5 ± 0.4 %, respectively. The release profiles of NIA showed pH-responsive properties, as 94.2 ± 3.5 % of NIA was released at pH 5.5, whereas 99.3 ± 2.4 % of NIA was released at pH 7.0. The NIA-loaded pH-responsive PHB/CAP microbeads were stable for >90 days at 4 °C under darkness, with NIA remaining at 73.65 ± 1.86 %. A cytotoxicity assay in PSVK1 cells confirmed that the NIA-loaded pH-responsive PHB/CAP microbeads were nontoxic at concentrations lower than 31.3 µg/mL, in accordance with ISO 10993-5.
Asunto(s)
Celulosa , Emulsiones , Hidroxibutiratos , Microesferas , Niacinamida , Celulosa/química , Celulosa/análogos & derivados , Concentración de Iones de Hidrógeno , Hidroxibutiratos/química , Niacinamida/química , Agua/química , Poliésteres/química , Solubilidad , Liberación de Fármacos , Humanos , Prohibitinas , PolihidroxibutiratosRESUMEN
Paclitaxel (PTX) is a potent anticancer drug. However, PTX exhibits extremely poor solubility in aqueous solution along with severe side effects. Therefore, in this study, an inclusion complex was prepared between PTX and hydroxypropyl-ß-cyclodextrin (HPßCD) by solvent evaporation to enhance the drug's solubility. The HPßCD-PTX inclusion complex was then encapsulated in poly-3-hydroxybutyrate (PHB) to fabricate drug-loaded nanoparticles (HPßCD-PTX/PHB NPs) by nanoprecipitation. The HPßCD-PTX/PHB NPs depicted a higher release of PTX at pHâ¯5.5 thus demonstrating a pH-dependent release profile. The cytotoxic properties of HPßCD-PTX/PHB NPs were tested against MCF-7, MDA-MB-231 and SW-620 cell lines. The cytotoxic potential of HPßCD-PTX/PHB NPs was 2.59-fold improved in MCF-7 cells in comparison to free PTX. Additionally, the HPßCD-PTX/PHB NPs improved the antimitotic (1.68-fold) and apoptotic (8.45-fold) effects of PTX in MCF-7 cells in comparison to PTX alone. In summary, these pH-responsive nanoparticles could be prospective carriers for enhancing the cytotoxic properties of PTX for the treatment of breast cancer.
Asunto(s)
2-Hidroxipropil-beta-Ciclodextrina , Apoptosis , Portadores de Fármacos , Nanopartículas , Paclitaxel , Poliésteres , Prohibitinas , Humanos , Nanopartículas/química , Paclitaxel/farmacología , Paclitaxel/química , Concentración de Iones de Hidrógeno , Apoptosis/efectos de los fármacos , 2-Hidroxipropil-beta-Ciclodextrina/química , Portadores de Fármacos/química , Poliésteres/química , Células MCF-7 , Hidroxibutiratos/química , Hidroxibutiratos/farmacología , Línea Celular Tumoral , Liberación de Fármacos , Solubilidad , Supervivencia Celular/efectos de los fármacos , PolihidroxibutiratosRESUMEN
This study ventures into the exploration of potential poly-3-hydroxybutyrate (PHB) degradation in alpine environments. PHB-degrading bacteria were identified in both campus soil, representing a residential area, and Mt. Kurodake soil, an alpine region in Hokkaido, Japan. Next-generation sequencing analysis indicated that the campus soil exhibited higher microbial diversity, while Ralstonia insidiosa C1, isolated from Mt. Kurodake soil, displayed the highest proficiency in PHB degradation. R. insidiosa C1 efficiently degraded up to 3% (w/v) of PHB and various films composed of other biopolymers at 14 °C. This bacterium synthesized homopolymers using substrates such as 3-hydroxybutyric acid, sugars, and acetic acid, while also produced copolymers using a mixture of fatty acids. The analysis results confirmed that the biopolymer synthesized by strain C1 using glucose was PHB, with physical properties comparable to commercial products. The unique capabilities of R. insidiosa C1, encompassing both the production and degradation of bioplastics, highlight its potential to establish a novel material circulation model.
Asunto(s)
Biodegradación Ambiental , Hidroxibutiratos , Polihidroxialcanoatos , Ralstonia , Microbiología del Suelo , Ralstonia/metabolismo , Ralstonia/genética , Polihidroxialcanoatos/metabolismo , Hidroxibutiratos/metabolismo , Hidroxibutiratos/química , Poliésteres/metabolismo , Poliésteres/química , Japón , PolihidroxibutiratosRESUMEN
The objective of this study was to prepare biocomposites through the solution casting method followed by compression moulding in which bacterial cellulose (BC) deposited flax fabric (FF) produced through fermentation is coated with minimal amount of polylactic acid (PLA) and polyhydroxybutyrate (PHB). Biocomposites incorporated with 60 % of PLA or PHB (% w/w) show enhanced tensile strength. Cross-sectional morphology showed good superficial interaction of these biopolymers with fibres of FF thereby filling up the gaps present between the fibres. The tensile strength of biocomposites at 60 % PLA and 60 % PHB improved from 37.97 MPa (i.e., BC deposited FF produced in presence of honey) to 67.17 MPa and 56.26 MPa, respectively. Further, 0.25 % of nalidixic acid (NA) (% w/w) and 6 % of oleic acid (OA) (% w/w) incorporation into the biocomposites imparted prolonged antibacterial activity against Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa. The in vitro cytotoxicity of biocomposites was determined using L929 mouse fibroblast cells. The 3-(4,5-cime- thylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide cytotoxicity tests showed that the PHB derived biocomposites along with antibacterial compounds in it were non-toxic. In vitro degradation of biocomposites was measured for up to 8 weeks in the mimicked physiological environment that showed a gradual rate of degradation over the period.
Asunto(s)
Antibacterianos , Celulosa , Lino , Hidroxibutiratos , Poliésteres , Poliésteres/química , Celulosa/química , Celulosa/farmacología , Antibacterianos/farmacología , Antibacterianos/química , Ratones , Animales , Hidroxibutiratos/química , Hidroxibutiratos/farmacología , Lino/química , Resistencia a la Tracción , Textiles , Staphylococcus aureus/efectos de los fármacos , Pruebas de Sensibilidad Microbiana , Escherichia coli/efectos de los fármacos , Línea CelularRESUMEN
Ethyl (S)-4-chloro-3-hydroxybutyrate ((S)-CHBE) is an important chiral intermediate in the synthesis of the cholesterol-lowering drug atorvastatin. Studying the use of SpyTag/SpyCatcher and SnoopTag/SnoopCatcher systems for the asymmetric reduction reaction and directed coupling coenzyme regeneration is practical for efficiently synthesizing (S)-CHBE. In this study, Spy and Snoop systems were used to construct a double-enzyme directed fixation system of carbonyl reductase (BsCR) and glucose dehydrogenase (BsGDH) for converting 4-chloroacetoacetate (COBE) to (S)-CHBE and achieving coenzyme regeneration. We discussed the enzymatic properties of the immobilized enzyme and the optimal catalytic conditions and reusability of the double-enzyme immobilization system. Compared to the free enzyme, the immobilized enzyme showed an improved optimal pH and temperature, maintaining higher relative activity across a wider range. The double-enzyme immobilization system was applied to catalyze the asymmetric reduction reaction of COBE, and the yield of (S)-CHBE reached 60.1% at 30 °C and pH 8.0. In addition, the double-enzyme immobilization system possessed better operational stability than the free enzyme, and maintained about 50% of the initial yield after six cycles. In summary, we show a simple and effective strategy for self-assembling SpyCatcher/SnoopCatcher and SpyTag/SnoopTag fusion proteins, which inspires building more cascade systems at the interface. It provides a new method for facilitating the rapid construction of in vitro immobilized multi-enzyme complexes from crude cell lysate.
Asunto(s)
Enzimas Inmovilizadas , Glucosa 1-Deshidrogenasa , Glucosa 1-Deshidrogenasa/metabolismo , Glucosa 1-Deshidrogenasa/química , Enzimas Inmovilizadas/química , Enzimas Inmovilizadas/metabolismo , Biocatálisis , Concentración de Iones de Hidrógeno , Hidroxibutiratos/química , Temperatura , Catálisis , Oxidorreductasas de Alcohol/química , Oxidorreductasas de Alcohol/metabolismo , Carbonil Reductasa (NADPH)/metabolismo , Carbonil Reductasa (NADPH)/químicaRESUMEN
Due to their excellent properties, polyhydroxyalkanoates are gaining increasing recognition in the biodegradable polymer market. These biogenic polyesters are characterized by high biodegradability in multiple environments, overcoming the limitation of composting plants only and their versatility in production. The most consolidated techniques in the literature or the reference legislation for the physical, chemical and mechanical characterisation of the final product are reported since its usability on the market is still linked to its quality, including the biodegradability certificate. This versatility makes polyhydroxyalkanoates a promising prospect with the potential to replace fossil-based thermoplastics sustainably. This review analyses and compares the physical, chemical and mechanical properties of poly-ß-hydroxybutyrate and poly-ß-hydroxybutyrate-co-ß-hydroxyvalerate, indicating their current limitations and strengths. In particular, the copolymer is characterised by better performance in terms of crystallinity, hardness and workability. However, the knowledge in this area is still in its infancy, and the selling prices are too high (9-18 $ kg-1). An analysis of the main extraction techniques, established and in development, is also included. Solvent extraction is currently the most widely used method due to its efficiency and final product quality. In this context, the extraction phase of the biopolymer production process remains a major challenge due to its high costs and the need to use non-halogenated toxic solvents to improve the production of good-quality bioplastics. The review also discusses all fundamental parameters for optimising the process, such as solubility and temperature.
Asunto(s)
Biodegradación Ambiental , Poliésteres , Polihidroxialcanoatos , Polihidroxibutiratos , Poliésteres/química , Solventes/química , Hidroxibutiratos/químicaRESUMEN
Dental implant surgery is a procedure that replaces damaged or missing teeth with an artificial implant. During this procedure, guided bone regeneration (GBR) membranes are commonly used to inhibit the migration of epithelium and GBR at the surgical sites. Due to its biodegradability, good biocompatibility, and unique biological properties, gelatin (GT) is considered a suitable candidate for guiding periodontal tissue regeneration. However, GT-based membranes come with limitations, such as poor mechanical strength and mismatched degradation rates. To confront this challenge, a series of GT/poly(4-hydroxybutyrate) (P4HB) composite membranes are fabricated through electrospinning technology. The morphology, composition, wetting properties, mechanical properties, biocompatibility, and in vivo biodegradability of the as-prepared composite membranes are carefully characterized. The results demonstrate that all the membranes present excellent biocompatibility. Moreover, the in vivo degradation rate of the membranes can be manipulated by changing the ratio of GT and P4HB. The results indicate that the optimized GT/P4HB membranes with a high P4HB content (75%) may be suitable for periodontal tissue engineering because of their good mechanical properties and biodegradation rate compatible with tissue growth.
Asunto(s)
Gelatina , Membranas Artificiales , Gelatina/química , Animales , Poliésteres/química , Poliésteres/farmacología , Hidroxibutiratos/química , Hidroxibutiratos/farmacología , Materiales Biocompatibles/química , Materiales Biocompatibles/farmacología , Ensayo de Materiales , Ingeniería de Tejidos/métodos , Implantes AbsorbiblesRESUMEN
As an energy-storage substance of microorganisms, polyhydroxybutyrate (PHB) is a promising alternative to petrochemical polymers. Under appropriate fermentation conditions, PHB-producing strains with metabolic diversity can efficiently synthesize PHB using various carbon sources. Carbon-rich wastes may serve as alternatives to pure sugar substrates to reduce the cost of PHB production. Genetic engineering strategies can further improve the efficiency of substrate assimilation and PHB synthesis. In the downstream link, PHB recycling strategies based on green chemistry concepts can replace PHB extraction using chlorinated solvents to enhance the economics of PHB production and reduce the potential risks of environmental pollution and health damage. To avoid carbon loss caused by biodegradation in the traditional sense, various strategies have been developed to degrade PHB waste into monomers. These monomers can serve as platform chemicals to synthesize other functional compounds or as substrates for PHB reproduction. The sustainable potential and cycling value of PHB are thus reflected. This review summarized the recent progress of strains, substrates, and fermentation approaches for microbial PHB production. Analyses of available strategies for sustainable PHB recycling were also included. Furthermore, it discussed feasible pathways for PHB waste valorization. These contents may provide insights for constructing PHB-based comprehensive biorefinery systems.
Asunto(s)
Polihidroxibutiratos , Polímeros , Polímeros/química , Fermentación , Carbohidratos , Carbono/química , Hidroxibutiratos/análisis , Hidroxibutiratos/química , Hidroxibutiratos/metabolismoRESUMEN
This study investigates the effects of SCG embedded into biodegradable polymer blends and aimed to formulate and characterise biomass-reinforced biocomposites using spent coffee ground (SCG) as reinforcement in PHB/PLA polymer blend. The effect of SCG filler loading and varying PHB/PLA ratios on the tensile properties and morphological characteristics of the biocomposites were examined. The results indicated that tensile properties reduction could be due to its incompatibility with the PHB/PLA matrixSCG aggregation at 40â¯wt% content resulted in higher void formation compared to lower content at 10â¯wt%. A PHB/PLA ratio of 50/50 with SCG loading 20â¯wt% was chosen for biocomposites with treated SCG. Biological treatment of SCG using Phanerochaete chrysosporium CK01 and Aspergillus niger DWA8 indicated P. chrysosporium CK01 necessitated a higher moisture content for optimum growth and enzyme production, whereas the optimal conditions for enzyme production (50-55â¯%, w/w) differed from those promoting A. niger DWA8 growth (40â¯%, w/w). SEM micrographs highlighted uniform distribution and effective wetting of treated SCG, resulting in improvements of tensile strength and modulus of biocomposites, respectively. The study demonstrated the effectiveness of sustainable fungal treatment in enhancing the interfacial adhesion between treated SCG and the PHB/PLA matrix.
Asunto(s)
Aspergillus niger , Café , Hidroxibutiratos , Poliésteres , Poliésteres/química , Hidroxibutiratos/química , Café/química , Aspergillus niger/efectos de los fármacos , Resistencia a la Tracción , Polímeros/químicaRESUMEN
This study investigated the effect of polymer blending of microbially produced poly[(R)-lactate-co-(R)-3-hydroxybutyrate] copolymers (LAHB) with poly(lactate) (PLA) on their mechanical, thermal, and biodegradable properties. Blending of high lactate (LA) content and high molecular weight LAHB significantly improved the tensile elongation of PLA up to more than 250 % at optimal LAHB composition of 20-30 wt%. Temperature-modulated differential scanning calorimetry and dynamic mechanical analysis revealed that PLA and LAHB were immiscible but interacted with each other, as indicated by the mutual plasticization effect. Detailed morphological characterization using scanning probe microscopy, small-angle X-ray scattering, and solid-state NMR confirmed that PLA and LAHB formed a two-phase structure with a characteristic length scale as small as 20 nm. Because of mixing in this order, the polymer blends were optically transparent. The biological oxygen demand test of the polymer blends in seawater indicated an enhancement of PLA biodegradation during biodegradation of the polymer blends.
Asunto(s)
Poliésteres , Poliésteres/química , Poliésteres/metabolismo , Polímeros/química , Polímeros/metabolismo , Hidroxibutiratos/química , Hidroxibutiratos/metabolismo , Temperatura , Peso Molecular , Biodegradación AmbientalRESUMEN
This article addresses the entire life cycle of the all-green fibrous materials based on poly(3-hydroxybutyrate) (PHB) containing a natural biocompatible additive Hemin (Hmi): from preparation, service life, and the end of life upon in-soil biodegradation. Fibrous PHB/Hmi materials with a highly developed surface and interconnected porosity were prepared by electrospinning (ES) from Hmi-containing feed solutions. Structural organization of the PHB/Hmi materials (porosity, uniform structure, diameter of fibers, surface area, distribution of Hmi within the PHB matrix, phase composition, etc.) is shown to be governed by the ES conditions: the presence of even minor amounts of Hmi in the PHB/Hmi (below 5 wt %) serves as a powerful tool for the control over their structure, performance, and biodegradation. Service characteristics of the PHB/Hmi materials (wettability, prolonged release of Hmi, antibacterial activity, breathability, and mechanical properties) were studied by different physicochemical methods (scanning electron microscopy, Fourier transform infrared spectroscopy, energy-dispersive X-ray spectroscopy, differential scanning calorimetry, contact angle measurements, antibacterial tests, etc.). The effect of the structural organization of the PHB/Hmi materials on their in-soil biodegradation at the end of life was analyzed, and key factors providing efficient biodegradation of the PHB/Hmi materials at all stages (from adaptation to mineralization) are highlighted (high surface area and porosity, thin fibers, release of Hmi, etc.). The proposed approach allows for target-oriented preparation and structural design of the functional PHB/Hmi nonwovens when their structural supramolecular organization with a highly developed surface area controls both their service properties as efficient antibacterial materials and in-soil biodegradation upon the end of life.
Asunto(s)
Materiales Biocompatibles , Hemina , Animales , Materiales Biocompatibles/química , Polihidroxibutiratos , Hidroxibutiratos/química , Antibacterianos/química , Estadios del Ciclo de Vida , Muerte , SueloRESUMEN
BACKGROUND: Polyhydroxybutyrate is a biopolymer produced by bacteria and archaea under nitrogen-limiting conditions. PHB is an essential polymer in the bioplastic sector because of its biodegradability, eco-friendliness, and adaptability. The characterization of PHB is a multifaceted process for studying the structure and its properties. This entire aspect can assure the long-term viability and performance attributes of the PHB. The characteristics of PHB extracted from the halophile Brachybacterium paraconglomeratum were investigated with the objective of making films for application in healthcare. RESULTS: This was the first characterization study on PHB produced by a rare halophile, Brachybacterium paraconglomeratum (MTCC 13074). In this study, the strain produced 2.72 g/l of PHB for.5.1 g/l of biomass under optimal conditions. Methods are described for the determination of the physicochemical properties of PHB. The prominent functional groups CH3 and C = O were observed by FT-IR and the actual chemical structure of the PHB was deduced by NMR. GCMS detects the confirmation of four methyl ester derivatives of the extracted PHB in the sample. Mass spectrometry revealed the molecular weight of methyl 3-hydroxybutyric acid (3HB) present in the extract. The air-dried PHB films were exposed to TGA, DSC and a universal testing machine to determine the thermal profile and mechanical stability. Additionally, the essential property of biopolymers like viscosity was also assessed for the extracted PHB. CONCLUSIONS: The current study demonstrated the consistency and quality of B. paraconglomeratum PHB. Therefore, Brachybacterium sps are also a considerable source of PHB with desired characteristics for industrial production.
Asunto(s)
Actinobacteria , Actinomycetales , Polihidroxibutiratos , Espectroscopía Infrarroja por Transformada de Fourier , Polímeros , Biopolímeros , Hidroxibutiratos/químicaRESUMEN
The production of poly-3-hydroxybutyrate (PHB) on an industrial scale remains a major challenge due to its higher production cost compared to petroleum-based plastics. As a result, it is necessary to develop efficient fermentative processes using low-cost substrates and identify high-value-added applications where biodegradability and biocompatibility properties are of fundamental importance. In this study, grape residues, mainly grape skins, were used as the sole carbon source in Azotobacter vinelandii OP cultures for PHB production and subsequent nanoparticle synthesis based on the extracted polymer. The grape residue pretreatment showed a high rate of conversion into reducing sugars (fructose and glucose), achieving up to 43.3 % w w-1 without the use of acid or external heat. The cultures were grown in shake flasks, obtaining a biomass concentration of 2.9 g L-1 and a PHB accumulation of up to 37.7 % w w-1. PHB was characterized using techniques such as Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). The formation of emulsified PHB nanoparticles showed high stability, with a particle size between 210 and 240 nm and a zeta potential between -12 and - 15 mV over 72 h. Owing to these properties, the produced PHB nanoparticles hold significant potential for applications in drug delivery.
Asunto(s)
Polihidroxibutiratos , Vitis , Carbono , Poliésteres/química , Polímeros , Hidroxibutiratos/químicaRESUMEN
Traditional Chinese medicine residue (TCMR) was utilized as an inexpensive carbon source for the production of poly(3-hydroxybutyrate) (PHB) using the newly isolated Bacillus altitudinis HBU-SI7. The results showed that Yu Ping Feng TCMR could be directly hydrolysed by cellulase to obtain a high proportion of glucose (99 % of total sugar) without pretreatment, achieving an enzymatic hydrolysis rate of up to 89.2 %. B. altitudinis could grow and produce PHB when using enzymatically hydrolysed TCMR in a 5-L fermenter. After 20 h of fermentation, the maximum concentration of PHB was 11.2 g/L, and the highest cell dry weight (CDW) was 15.4 g/L, with 72.7 % of the PHB fraction in CDW. Moreover, this strain could utilize enzymatic hydrolysates from various herbal formulas to produce high levels of PHB. This novel approach aims to accumulate PHB from TCMR hydrolysates, offering an effective and environmentally friendly method to reduce production costs and achieve mass production.