Effect of fiber-reinforced direct restorative materials on the fracture resistance of endodontically treated mandibular molars restored with a conservative endodontic cavity design.

OBJECTIVE: This study aimed to evaluate the fracture strength of teeth restored using fiber-reinforced direct restorative materials after endodontic treatment with a conservative mesio-occlusal access cavity design. MATERIALS AND METHODS: A total of 100 extracted intact mandibular first molars were selected and distributed into a positive control group where teeth left intact and the following four test groups comprised of teeth with conservative mesio-occlusal access cavities that had undergone root canal treatment (n = 20/group): access cavity without restoration (negative control), bulk-fill resin composite with horizontal glass fiber post reinforcement, fiber-reinforced composite with bulk-fill resin and bulk-fill resin composite. Following thermocycling (10,000 cycles), fracture resistance was measured using a universal testing machine. Statistical analyses (one-way analysis of variance and the Tamhane test) were performed, and statistical significance was set at p < 0.05. RESULTS: Groups with minimally invasive access cavities had lower fracture strength than intact teeth, regardless of the restoration material (p < 0.05). Fiber-reinforced composite groups demonstrated higher fracture strength than bulk-fill resin composite alone (p < 0.05). Fracture types varied among groups, with restorable fractures predominant in the fiber-reinforced composite groups. CONCLUSION: This study suggests that using fiber-reinforced composite materials, especially in combination with bulk-fill resin composites, can effectively enhance the fracture strength of endodontically treated teeth with conservative access cavities. However, using only bulk-fill resin composite is not recommended based on the fracture strength results. CLINICAL SIGNIFICANCE: When teeth that undergo endodontic treatment are restored using a conservative access cavity design and fiber-reinforced composite materials, especially in combination with bulk-fill resin composites, the fracture strength of the teeth can be effectively increased.

The Effect of Gastric Acid on the Surface Properties of Different Universal Composites: A SEM Study.

The aim of this study is to compare surface roughness and microhardness changes of three monochromatic (Omnichroma, Vittra Unique, and Charisma Diamond One) and three universal shade (Neo Spectra ST, G-ænial A'CHORD, and Nova Compo C) resin composites after exposure to simulated gastric acid. A total of 144 disc-shaped specimens (24 discs of each composite resin) were prepared using plexiglass molds (R = 5 mm × h = 2 mm) for evaluation from each material. Specimens of each material were divided into two main groups for the evaluation of the microhardness and surface roughness and also two subgroups for 7- and 14-day exposures to simulated gastric acid. Initial microhardness and surface roughness measurements of all samples were measured before immersion (T1) followed by exposing the samples to simulated gastric acid for 7 days (T2) and 14 days (T3), and then, the microhardness and roughness measurements were repeated. Randomly selected specimens of each material for each of the time intervals (T1, T2, and T3) were evaluated with scanning electron microscopy (SEM). One-way ANOVA revealed that the surface roughness and hardness values of all tested composite resin restorative materials show no statistically significant difference for the initial (T1) value (p > 0.05). Regarding the 7th day (T2) and 14th day (T3) surface roughness and microhardness value of all composites, there are statistically significant differences between the groups (p < 0.05), while there was no statistically significant difference between the surface hardness reduction percentage between the time intervals (p > 0.05). As a result of this in vitro study, increase in surface roughness and decrease in microhardness of the tested universal composite materials when exposed to simulated gastric acid were statistically significant.

Management of root resorption with mineral trioxide aggregate complicated by a luxation injury: report of a case with six-year follow-up.

Trauma to the oral region occurs frequently, comprising 5% of all injuries. The most common dental injuries are lateral luxations which can be seen with a prevalence of up to 27% among dental injuries. Ectopic eruption of maxillary canines can lead to root resorption on maxillary lateral incisors especially on apical and middle thirds of the roots. Half of these resorbed lateral incisors show severe resorption, in which the pulp is exposed. This case report describes non-surgical treatment with mineral trioxide aggregate (MTA) and a six-year follow-up of a maxillary lateral incisor, resorbed by ectopic eruption of the canine and affected by lateral luxation injury. The tooth was asymptomatic, and radiographic examination showed that the resorbed region had been successfully repaired with new hard tissue deposition within the six-year follow-up. MTA can be considered an effective repair material in nonsurgical treatment of this type of root resorption.

A new familial case of Jalili syndrome caused by a novel mutation in CNNM4.

Jalili syndrome (JS) is a rare autosomal recessive disorder characterized by the combination of cone-rod dystrophy (CRD) and amelogenesis imperfecta. To date, 18 families with JS have been reported, 16 of which were found to have a mutation in CNNM4. We describe three siblings with clinical features of JS with a homozygous missense mutation in exon 4 of CNNM4, c.1781A>G (p.N594S). They demonstrated phenotypic variability in terms of ocular and dental findings. Although fundus examination and optical coherence tomography results were normal, the electroretinogram was compatible with CRD, supporting the diagnosis of JS. The dental phenotype severity also varied among the siblings.