ABSTRACT
In the last decade, among the emerging technologies in the area of bioplastics, additive manufacturing (AM), commonly referred to as 3D printing, stands out. This technology has gained great interest in the development of new products, mainly due to its capability to easily produce customized and low-cost plastic products. This work aims to evaluate the effect of supercritical foaming of 3D-printed parts based on a commercial PLA matrix loaded with calcium carbonate, for single-use sustainable food contact materials. 3D-printed PLA/CaCO3 parts were obtained by 3D printing with a 20% and 80% infill, and two infill patterns, rectilinear and triangular, were set for each of the infill percentages selected. Supercritical fluid foaming of PLA/CaCO3 composite printed parts was performed using a pressure of 25 MPa, a temperature of 130 °C for 23 min, with a fast depressurization rate (1 s). Closed-cell foams were achieved and the presence of CaCO3 did not influence the surface of the foams or the cell walls, and no agglomerations were observed. Foam samples with 80% infill showed subtle temperature fluctuations, and thermogravimetric analysis showed that samples were thermally stable up to ~300 °C, while the maximum degradation temperature was around 365 °C. Finally, tensile test analysis showed that for lower infill contents, the foams showed lower mechanical performance, while the 80% infill and triangular pattern produced foams with good mechanical performance. These results emphasize the interest in using the supercritical CO2 process to easily produce foams from 3D-printed parts. These materials represent a sustainable alternative for replacing non-biodegradable materials such as Expanded Polystyrene, and they are a promising option for use in many industrial applications, such as contact materials.
ABSTRACT
This article proposes a foaming method using supercritical carbon dioxide (scCO2) to obtain compostable bionanocomposite foams based on PLA and organoclay (C30B) where this bionanocomposite was fabricated by a previous hot melt extrusion step. Neat PLA films and PLA/C30B films (1, 2, and 3 wt.%) were obtained by using a melt extrusion process followed by a film forming process obtaining films with thicknesses between 500 and 600 µm. Films were further processed into foams in a high-pressure cell with scCO2 under constant conditions of pressure (25 MPa) and temperature (130 °C) for 30 min. Bionanocomposite PLA foams evidenced a closed cell and uniform cell structure; however, neat PLA presented a poor cell structure and thick cell walls. The thermal stability was significantly enhanced in the bionanocomposite foam samples by the good dispersion of nanoclays due to scCO2, as demonstrated by X-ray diffraction analysis. The bionanocomposite foams showed improved overall mechanical performance due to well-dispersed nanoclays promoting increased interfacial adhesion with the polymeric matrix. The water uptake behavior of bionanocomposite foams showed that they practically did not absorb water during the first week of immersion in water. Finally, PLA foams were disintegrated under standard composting conditions at higher rates than PLA films, showing their sustainable character. Thus, PLA bionanocomposite foams obtained by batch supercritical foaming seem to be a sustainable option to replace non-biodegradable expanded polystyrene, and they represent a promising alternative to be considered in applications such as food packaging and other products.