Composite coatings containing reduced graphene oxide (rGO) and 3-(aminopropyl)triethoxysilane functionalised rGO (APTES-rGO) were prepared by sol-gel technology and deposited on Al 2024 T-3. Covalent functionalisation of GO by APTES occurred by formation of amide bonds, accompanied by GO reduction. The thin sheets were retained. The hydrophilicity of the coating increased when APTES-rGO was added. The opposite was observed when GO was added. A key finding is that the rGO flakes agglomerate and lie in a random orientation in the coating, whereas the APTES-rGO flakes are more evenly distributed in the matrix and appear to lie along the plane of the substrate.
We present a study of the surface effects and optical properties of the self-assembled nanostructures comprised of vertically aligned 5 nm-diameter Al nanowires embedded in an amorphous Si matrix (a-Si:Al). The controlled (partial) removal of Al nanowires in a selective etching process yielded nanoporous a-Si media with a variable effective surface area. Different spectroscopy techniques, such as X-ray photoelectron spectroscopy (XPS), UV-Vis spectrophotometry and photoluminescence (PL), have been combined to investigate the impact of such nanostructuring on optical absorption and emission properties. We also examine long-term exposure to air ambient and show that increasing level of surface oxidation determines the oxide defect-related nature of the dominant PL emission from the nanoporous structures. The role of bulk, nanosize and surface effects in optical properties has been separated and quantified, providing a better understanding of the potential of such nanoporous a-Si:Al structures for future device developments.