Sistema adesivo universal: análise da interface adesiva e degradação colagenolítica em dentina submetida à diferentes protocolos de condicionamento ácido / Universal adhesive system: analysis of adhesive interface and collagenolytic degradation of demineralized dentin submitted to different acid etching ptotocols

O objetivo desse estudo foi analisar a interface adesiva do sistema adesivo Single Bond Universal (SBU) em dentina submetida à diferentes protocolos de condicionamento ácido em 24 h e 12 meses. E a degradação colagenolítica (DC) mediada por metaloproteinases (MMPs) e Catepsina-K (CAT-K) em tempo imediato. Esse estudo foi conduzido em 3 etapas: 1) Caracterização química da dentina em FTIR; 2) DC por meio de fragmentos do Telelopeptídeo Carboxiterminal do Colágeno Tipo I (ICTP) e do Terminal C do Telopeptídeo ligado ao Colágeno Tipo I (CTX) e a resistência à tração (RT) da do colágeno; 3) Análise da interface adesiva através da resistência de união (RU), análise de fratura, microscopia eletrônica de varredura (MEV) e nanoinfiltração (NI). Para FTIR foram utilizados 6 discos de dentina, divididos em 2 grupos: 1) Ácido fosfórico 32 %15 s (AF), 2) Ácido poliacrílico 25 % 10 s (AP). Para análise da DC, 12 discos de dentina foram completamente desmineralizados e divididos em 3 grupos: 1) AF, 2) AP e 3) Água deionizada (Controle) 15 s. Após, foram incubados e armazenados por 1 semana. Seguindo-se a análise da concentração de proteína total (PT). 50 µl da solução de incubação foram utilizadas para analisar ICTP e CTX. As concentrações foram calculadas em relação à PT. Para RT, foram testados 36 palitos obtidos dos discos de colágeno. Para RU foram utilizados 48 dentes, divididos em 2 grupos, de acordo com o período de armazenamento, divididos em três subgrupos: 1) AF, 2) AP e 3) Autocondicionante SBU 20 s (SE). Os dentes foram restaurados e armazenados em água destilada 37 °C. Após, foram submetidos ao teste de microtração e análise de fraturas. Para as análises MEV e NI foram utilizados 2 espécimes de cada subgrupo. Para análise estatística utilizou-se ANOVA 1-Fator, ANOVA- 2 Fatores e teste de Tukey (α=0.05). Para FTIR, AF reduziu a quantidade de fosfato e carbonato quando comparado ao AP. Para DC, a liberação de ICTPPT para AF foi significantemente maior do que para AP (p < 0,05). Não houve diferença na liberação de CTXPT para AF e AP (p > 0,05). Para RT não houve diferença entre AP e Controle, porém, apresentaram valores maiores do que AF (p<0,05). Para RU em MPa, não houve diferença estatisticamente significativa para todos os tratamentos nos diferentes períodos de análise (p < 0,05). A análise de fraturas evidenciou a predominância de fraturas adesivas e mistas. MEV mostrou melhor qualidade da interface após 12 meses para AF e AP. Após 12 meses apenas SE não apresentou NI. Assim sendo, o autocondicionamento ainda parece ser a melhor opção para sistemas adesivos universais que possuam monômeros funcionais em sua composição.(AU)

The aim of this study was to analyze the adhesive interface of the Single Bond Universal (SBU) to dentin submitted to different acid etching protocols in 24 h and 12 months, and the collagenolytic degradation (CD) by matrix metalloproteinases (MMPs) and Cathepsin-K (CAT-K) in the immediate time. This study was divided into three stages: 1) Dentin chemical characterization by FTIR; 2) CD by release of the collagen telopeptide fragment cross-linked carboxyterminal telopeptide of type I collagen (ICTP), and C-terminal crosslinked telopeptide of type I collagen (CTX) and ultimate tensile strength (UTS); 3) Analysis of the adhesive interface by microtensile bond strength (µTBS), failure mode, scanning electron microscopy (SEM) of the AI, and nanoleakage by SEM (NL). For FTIR, six dentin disks were divided into two groups: 1) Phosphoric acid 15 s (PA), 2) Polyacrylic acid 10 s (PAA). For CD twelve dentin disks were completely demineralized, then were divided into 3 groups 1) PA, 2) PAA, and 3) deionized water (Control) for 15 s. All disks were incubated in a buffered solution (BS) for 1 week. Total protein (TP) concentrations were measured using Nanodrop™ at 280 nm. 50 µl of BS was used to analyze solubilized telopeptide fragments using ICTP and CTX . ICTP and CTX average ratios were calculated in relation to TP concentration (ICTPtp and CTXtp). For UTS, 36 dentin beams obtained from collagen disks were tested. For µTBS, forty-eight teeth were divided into two groups according to the period of storage, then subdivided into three subgroups: 1) PA, 2) PAA, and 3) Self-etch 20 s (SE). After, composite build up, the specimens were stored in distilled water at 37 °C. Two specimens of each group were used for SEM analysis of AI and NL. Data were analyzed by one-way ANOVA, two-way ANOVA and Tukey tests (p<0.05). According to the results of the FTIR etching with PA reduced the amount of phosphate and carbonate when compared to PAA. ICTPtp release of PA was significantly higher A than PAA (p > 0,05). CTXtp showed no difference between the PA and PAA (p < 0,05). For UTS there was no difference between PAA and control, but they were significantly higher (p<0.05) than PA. For µTBS in MPa, there is no statistical difference among all the etching protocols tested, as well in both storage periods of analysis (p < 0,05). The most prevalent failure mode were adhesives associated with mixed. SEM analysis highlighted a better quality of AI after 12 months for PA and PAA. However, after 12 months only SE did not show NL. Then, the self-etching protocol seems to be a better choice regarding universal adhesive systems which have functional monomers in their blend(AU)

Avaliação das metaloproteinases de matriz -2 e -9 em gatos com desmineralização óssea secundária à tirotoxicose induzida / Evaluation of matrix metalloproteinases -2 and -9 in cats under bone demineralization secondary to induced thyrotoxicosis

Observou-se significativo aumento de atividade das formas ativas das metaloproteinases -2 e -9 em gatos com tirotoxicose induzida e desmineralização óssea. As formas pró e intermediária da metaloproteinase -2 elevaram-se com 14 dias de administração hormonal, porém, posteriormente, houve uma tendência de queda. Observou-se correlação negativa entre a forma ativa das metaloproteinases de matriz -2 e -9 e a densidade mineral óssea da extremidade distal do rádio. Os resultados sugerem aumento da degradação da matriz colágena secundária com a elevação dos hormônios tiroidianos.(AU)

Significant increase of activity of active forms of matrix metalloproteinases -2 and -9 in cats under induced thyrotoxicosis and bone demineralization was observed. Pro and intermediated forms of matrix metalloproteinases -2 and -9 increased at 14 days of hormonal treatment, followed by decrease tendency. A negative correlation between active forms of matrix metalloproteinases -2 and -9 and bone mineral density of radius distal extremity was also observed. The results suggest an increase of collagen matrix degradation secondary to high levels of thyroid hormones.(AU)

Avaliação das metaloproteinases de matriz -2 e -9 em gatos com desmineralização óssea secundária à tirotoxicose induzida / Evaluation of matrix metalloproteinases -2 and -9 in cats under bone demineralization secondary to induced thyrotoxicosis

Observou-se significativo aumento de atividade das formas ativas das metaloproteinases -2 e -9 em gatos com tirotoxicose induzida e desmineralização óssea. As formas pró e intermediária da metaloproteinase -2 elevaram-se com 14 dias de administração hormonal, porém, posteriormente, houve uma tendência de queda. Observou-se correlação negativa entre a forma ativa das metaloproteinases de matriz -2 e -9 e a densidade mineral óssea da extremidade distal do rádio. Os resultados sugerem aumento da degradação da matriz colágena secundária com a elevação dos hormônios tiroidianos.

Significant increase of activity of active forms of matrix metalloproteinases -2 and -9 in cats under induced thyrotoxicosis and bone demineralization was observed. Pro and intermediated forms of matrix metalloproteinases -2 and -9 increased at 14 days of hormonal treatment, followed by decrease tendency. A negative correlation between active forms of matrix metalloproteinases -2 and -9 and bone mineral density of radius distal extremity was also observed. The results suggest an increase of collagen matrix degradation secondary to high levels of thyroid hormones.