ABSTRACT
Natural fibers have emerged as a potential alternate to synthetic fibers, because of their excellent performance, biodegradability, renewability and sustainability. This research has focused on investigating the thermal, visco-elastic and fire-retardant properties of different hybrid Cytostachys Renda (CR)/kenaf fiber (K) (50/0; 35/ 15, 25/25, 15/ 35, 0/50)-reinforced MWCNT (multi-walled carbon nanotubes)-modified phenolic composites. The mass% of MWCNT-modified phenolic resin was maintained 50 mass% including 0.5 mass% of MWCNT. In order to achieve homogeneous dispersion ball milling process was employed to incorporate the MWCNT into phenolic resin (powder). Thermal results from thermogravimetric analysis and differential scanning calorimetric analysis revealed that the hybrid composites (35/15; 35 mass% CR and 15 mass% K) showed higher thermal stability among the composite samples. Visco-elastic results revealed that kenaf fiber-based MWCNT-modified composites (0/50; 0 mass% CR and 50 mass% K) exhibited higher storage and loss modulus due to high modulus kenaf fiber. Fire-retardant analysis (UL-94) showed that all the composite samples met H-B self-extinguishing rating and exhibited slow burning rate according to limiting oxygen index (LOI) test. However, (15/35; 15 mass% CR and 35 mass% K) hybrid composites showed the highest time to ignition, highest fire performance index, lowest total heat release rate, average mass loss rate, average fire growth rate index and maximum average rate of heat emission. Moreover, the smoke density of all hybrid composites was found to be less than 200 which meets the federal aviation regulations (FAR) 25.853d standard. Technique for Order Preference by Similarity to Ideal Solution (TOPSIS) was carried out to select an optimal composite sample considering the thermal, visco-elastic and fire-retardant behaviors. Through TOPSIS analysis, the hybrid (15/35; 15 mass% CR and 35 mass% K) composite sample has been selected as an optimal composite which can be used for high-temperature aircraft and automotive applications.
ABSTRACT
This research focuses on evaluating the effect of Cyrtostachys renda (CR) fiber and the impact of adding multi-walled carbon nanotubes (MWCNT) on the morphological, physical, mechanical, and flammability properties of phenolic composites. MWCNT were supplemented with phenolic resin through a dry dispersion ball milling method. Composites were fabricated by incorporating CR fiber in 0.5 wt.% MWCNT-phenolic matrix by hot pressing. Nevertheless, the void content, higher water absorption, and thickness swelling increased with fiber loading to the MWCNT/phenolic composites. The presence of MWCNT in phenolic enhanced the tensile, flexural, and impact strength by as much as 18%, 8%, and 8%, respectively, compared to pristine phenolic. The addition of CR fiber, however, strengthened MWCNT-phenolic composites, improving the tensile, flexural, and impact strength by as much as 16%, 16%, and 266%, respectively, for 50 wt.% loading of CR fiber. The CR fiber may adhere properly to the matrix, indicating that there is a strong interface between fiber and MWCNT-phenolic resin. UL-94 horizontal and limiting oxygen index (LOI) results indicated that all composite materials are in the category of self-extinguishing. Based on the technique for order preference by similarity to the ideal solution (TOPSIS) technique, 50 wt.% CR fiber-reinforced MWCNT-phenolic composite was chosen as the optimal composite for mechanical and flammability properties. This bio-based eco-friendly composite has the potential to be used as an aircraft interior component.
ABSTRACT
Adequate awareness of sustainable materials and eco-legislation have inspired researchers to identify alternative sustainable and green composites for synthetic fiber-reinforced polymer composites in the automotive and aircraft industries. This research focused on investigating the physical, mechanical, and morphological properties of different hybrid Cyrtostachys renda (CR)/kenaf fiber (K) (10C:0K, 7C:3K, 5C:5K, 3C:7K, 0C:10K) reinforced with 0.5 wt% MWCNT-phenolic composites. We incorporated 0.5 wt% of MWCNT into phenolic resin (powder) using a ball milling process for 25 h to achieve homogeneous distribution. The results revealed that CR fiber composites showed higher voids content (12.23%) than pure kenaf fiber composites (6.57%). CR fiber phenolic composite was more stable to the swelling tendency, resulting in the lowest percentage of swelling rate (4.11%) compared to kenaf composite (5.29%). The addition of kenaf fiber into CR composites had improved the tensile, flexural, and impact properties. The highest tensile and flexural properties were found for weight fraction of CR and kenaf fiber at 5C:5K (47.96 MPa) and 3C:7K (90.89 MPa) composites, respectively. In contrast, the highest impact properties were obtained for 0C:10K composites (9.56 kJ/m2). Based on the FE-SEM image, the CR fiber lumen was larger in comparison to kenaf fiber. The lumen of CR fiber was attributed to higher void and water absorption, lower mechanical properties compared to kenaf fiber. 5C:5K composite was selected as an optimal hybrid composite, based on the TOPSIS method. This hybrid composite can be used as an interior component (non-load-bearing structures) in the aviation and automotive sectors.
ABSTRACT
Natural renewable materials can play a big role in reducing the consumption of synthetic materials for environmental sustainability. Natural fiber-reinforced composites have attracted significant research and commercial importance due to their versatile characteristics and multi-dimensional applications. As the natural materials are easily rotten, flammable, and moisture absorbent, they require additional chemical modification for use in sustainable product development. In the present research, jute fibers were treated with rot-, fire-, and water-retardant chemicals and their corresponding polymer composites were fabricated using a compression molding technique. To identify the effects of the chemical treatments on the jute fiber and their polymeric composites, a Fourier transformed infrared radiation (FTIR) study was conducted and the results were analyzed. The presence of various chemicals in the post-treated fibers and the associated composites were identified through the FTIR analysis. The varying weight percentage of the chemicals used for treating the fibers affected the physio-mechanical properties of the fiber as well as their composites. From the FTIR analysis, it was concluded that crystallinity increased with the chemical concentration of the treatment which could be contributed to the improvement in their mechanical performance. This study provides valuable information for both academia and industry on the effect of various chemical treatments of the jute fiber for improved product development.