ABSTRACT
A series of Ti41Zr25Be34-xNix (x = 4, 6, 8, 10 at.%) and Ti41Zr25Be34-xCux (x = 4, 6, 8 at.%) bulk metallic glasses were investigated to examine the influence of Ni and Cu content on the viscosity, thermoplastic formability, and nanoindentation of Ti-based bulk metallic glasses. The results demonstrate that Ti41Zr25Be30Ni4 and Ti41Zr25Be26Cu8 amorphous alloys have superior thermoplastic formability among the Ti41Zr25Be34-xNix and Ti41Zr25Be34-xCux amorphous alloys due to their low viscosity in the supercooled liquid region and wider supercooled liquid region. The hardness and modulus exhibit obvious variations with increasing Ni and Cu content in Ti-based bulk metallic glasses, which can be attributed to alterations in atomic density. Optimal amounts of Ni and Cu in Ti-based bulk metallic glasses enhance thermoplastic formability and mechanical properties. The influence of Ni and Cu content on the hardness of Ti-based bulk metallic glasses is discussed from the perspective of the mean atomic distance.
ABSTRACT
Copper-coated graphite and copper mixture powders were deposited on AZ31B magnesium alloy and 6061 T6 aluminum alloy substrates under different process parameters by a solid-state cold spray technique. The microstructure of the copper-coated graphite and copper composite coatings was visually examined using photographs taken with an optical microscope and a scanning electron microscope. The surface roughness of the coatings was investigated with a 3D profilometer. The thickness of the coatings was determined through the analysis of the microstructure images, while the adhesion of the coatings was characterized using the scratch test method. The results indicate that the surface roughness of the coatings sprayed on the two different substrates gradually decreases as gas temperature and gas pressure increase. Additionally, the thickness and adhesion of the coatings deposited on the two different substrates both increase with an increase in gas temperature and gas pressure. Comparing the surface roughness, thickness, and adhesion of the coatings deposited on the two different substrates, the surface roughness and adhesion of the coatings on the soft substrate are greater than those of the coatings on the hard substrate, while the thickness of the coatings is not obviously affected by the hardness of the substrate. Furthermore, it is noteworthy that the surface roughness, thickness, and adhesion of the copper-coated graphite and copper composite coatings sprayed on the two different substrates exhibit a distinct linear relationship with particle velocity.
ABSTRACT
A silver precursor (silver 2-ethylhexanoate) and silver nanoparticles were synthesized and used to prepare a low sintering temperature nano-silver paste (PM03). We optimized the amount of silver 2-ethylhexanoate added and the sintering temperature to obtain the best performance of the nano-silver paste. The relationship between the microstructures and properties of the paste was studied. The addition of silver 2-ethylhexanoate resulted in less porosity, leading to lower resistivity and higher shear strength. Thermal compression of the paste PM03 at 250 °C with 10 MPa pressure for 30 min was found to be the proper condition for copper-to-copper bonding. The resistivity was (3.50 ± 0.02) × 10-7 Ωâm, and the shear strength was 57.48 MPa.