ABSTRACT
Scarce and expensive iridium oxide is still the cornerstone catalyst of polymer-electrolyte membrane electrolyzers for green hydrogen production because of its exceptional stability under industrially relevant oxygen evolution reaction (OER) conditions. Earth-abundant transition metal oxides used for this task, however, show poor long-term stability. We demonstrate here the use of nitrogen-doped cobalt oxide as an effective iridium substitute. The catalyst exhibits a low overpotential of 240 mV at 10 mA cm-2 and negligible activity decay after 1000 h of operation in an alkaline electrolyte. Incorporation of nitrogen dopants not only triggers the OER mechanism switched from the traditional adsorbate evolution route to the lattice oxygen oxidation route but also achieves oxygen nonbonding (ONB) states as electron donors, thereby preventing structural destabilization. In a practical anion-exchange membrane water electrolyzer, this catalyst at anode delivers a current density of 1000 mA cm-2 at 1.78 V and an electrical efficiency of 47.8 kW-hours per kilogram hydrogen.
ABSTRACT
Reduction of carbon dioxide (CO2) by renewable electricity to produce multicarbon chemicals, such as ethylene (C2H4), continues to be a challenge because of insufficient Faradaic efficiency, low production rates, and complex mechanistic pathways. Here, we report that the rate-determining steps (RDS) on common copper (Cu) surfaces diverge in CO2 electroreduction, leading to distinct catalytic performances. Through a combination of experimental and computational studies, we reveal that CâC bond-making is the RDS on Cu(100), whereas the protonation of *CO with adsorbed water becomes rate-limiting on Cu(111) with a higher energy barrier. On an oxide-derived Cu(100)-dominant Cu catalyst, we reach a high C2H4 Faradaic efficiency of 72%, partial current density of 359 mA cm-2, and long-term stability exceeding 100 h at 500 mA cm-2, greatly outperforming its Cu(111)-rich counterpart. We further demonstrate constant C2H4 selectivity of >60% over 70 h in a membrane electrode assembly electrolyzer with a full-cell energy efficiency of 23.4%.
ABSTRACT
Anion-exchange membrane fuel cells provide the possibility to use platinum group metal-free catalysts, but the anodic hydrogen oxidation reaction (HOR) suffers from sluggish kinetics and its source is still debated. Here, over nickel-tungsten (Ni-W) alloy catalysts, we show that the Ni : W ratio greatly governs the HOR performance in alkaline electrolyte. Experimental and theoretical studies unravel that alloying with W can tune the unpaired electrons in Ni, tailoring the potential of zero charge and the catalytic surface to favor hydroxyl adsorption (OHad). The OHad species coordinately interact with potassium (K+) ions, which break the K+ solvation sheath to leave free water molecules, yielding an improved connectivity of hydrogen-bond networks. Consequently, the optimal Ni17W3 alloy exhibits alkaline HOR activity superior to the state-of-the-art platinum on carbon (Pt/C) catalyst and operates steadily with negligible decay after 10,000â cycles. Our findings offer new understandings of alloyed HOR catalysts and will guide rational design of next-generation catalysts for fuel cells.
ABSTRACT
Carbon-carbon coupling electrochemistry on a conventional copper (Cu) catalyst still undergoes low selectivity among many different multicarbon (C2+) chemicals, posing a grand challenge to achieve a single C2+ product. Here, we demonstrate a laser irradiation synthesis of a gerhardtite mineral, Cu2(OH)3NO3, as a catalyst precursor to make a Cu catalyst with abundant stacking faults under reducing conditions. Such structural perturbation modulates electronic microenvironments of Cu, leading to improved d-electron back-donation to the antibonding orbital of *CO intermediates and thus strengthening *CO adsorption. With increased *CO coverage on the defect-rich Cu, we report an acetate selectivity of 56 ± 2% (compared to 31 ± 1% for conventional Cu) and a partial current density of 222 ± 7 mA per square centimeter in CO electroreduction. When run at 400 mA per square centimeter for 40 h in a flow reactor, this catalyst produces 68.3 mmol of acetate throughout. This work highlights the value of a Cu-containing mineral phase in accessing suitable structures for improved selectivity to a single desired C2+ product.
ABSTRACT
Converting hydrogen chemical energy into electrical energy by fuel cells offers high efficiencies and environmental advantages, but ultrapure hydrogen (over 99.97%) is required; otherwise, the electrode catalysts, typically platinum on carbon (Pt/C), will be poisoned by impurity gases such as ammonia (NH3). Here we demonstrate remarkable NH3 resistivity over a nickel-molybdenum alloy (MoNi4) modulated by chromium (Cr) dopants. The resultant Cr-MoNi4 exhibits high activity toward alkaline hydrogen oxidation and can undergo 10,000 cycles without apparent activity decay in the presence of 2 ppm of NH3. Furthermore, a fuel cell assembled with this catalyst retains 95% of the initial peak power density even when NH3 (10 ppm)/H2 was fed, whereas the power output reduces to 61% of the initial value for the Pt/C catalyst. Experimental and theoretical studies reveal that the Cr modifier not only creates electron-rich states that restrain lone-pair electron donation but also downshifts the d-band center to suppress d-electron back-donation, synergistically weakening NH3 adsorption.
ABSTRACT
Large-scale deployment of proton exchange membrane (PEM) water electrolyzers has to overcome a cost barrier resulting from the exclusive adoption of platinum group metal (PGM) catalysts. Ideally, carbon-supported platinum used at cathode should be replaced with PGM-free catalysts, but they often undergo insufficient activity and stability subjecting to corrosive acidic conditions. Inspired by marcasite existed under acidic environments in nature, we report a sulfur doping-driven structural transformation from pyrite-type cobalt diselenide to pure marcasite counterpart. The resultant catalyst drives hydrogen evolution reaction with low overpotential of 67 millivolts at 10 milliamperes per square centimeter and exhibits no degradation after 1000 hours of testing in acid. Moreover, a PEM electrolyzer with this catalyst as cathode runs stably over 410 hours at 1 ampere per square centimeter and 60°C. The marked properties arise from sulfur doping that not only triggers formation of acid-resistant marcasite structure but also tailors electronic states (e.g., work function) for improved hydrogen diffusion and electrocatalysis.
ABSTRACT
ConspectusLow-temperature ion-exchange membrane hydrogen fuel cells, as zero-emission power sources, can largely preserve the merits of gasoline engines, including rapid fueling, extended cruising range, and low maintenance cost. To enable the widespread prevalence of fuel-cell automobiles, the U.S. Department of Energy (DOE) has set a long-term fuel-cell system cost target of US$30 kW-1. Over past decades, proton-exchange membrane fuel cell (PEMFC) technology has developed rapidly, resulting in the first commercial sales of fuel-cell-powered vehicles. Although there has been great success, the mass market penetration of PEMFCs is currently hindered by the excessive reliance on expensive platinum group metal (PGM) catalysts. Anion-exchange membrane fuel cells (AEMFCs), because of the alkaline environment that permits the use of PGM-free catalysts, have become an alternative technology with inherent long-term cost advantages. Thus far, significant progress has been made in the exploration of PGM-free catalysts for the oxygen reduction reaction at the AEMFC cathode, some of which have shown intrinsic catalytic properties comparable to PGM catalysts. However, the development of PGM-free catalysts for the anodic hydrogen oxidation reaction (HOR) has lagged behind, presumably owing to its sluggish kinetics in alkali. In alkaline media, the HOR kinetics is about 2 orders of magnitude slower than that in acid, which demands higher PGM loadings to reach similar fuel-cell performance in PEMFCs. Since Raney nickel (Ni) was explored for alkaline HOR catalysis in 1960s, research on Ni-based HOR catalysts has begun and now is flourishing, primarily thanks to their favorable adsorption energies of key HOR intermediates (e.g., Ni-Had and Ni-OHad). At present, a number of strategies have been developed to improve HOR performances of Ni-based materials, such as alloying, Ni nitridation, and alloy amorphization, which yield cost-effective HOR catalysts that rival or even exceed the activity and stability of PGM counterparts.In this Account, we describe our recent research endeavors toward the development of efficient Ni-based HOR catalysts for practical AEMFC anodes. First, we briefly highlight the important merits of AEMFC technology and why Ni-based materials are appealing for alkaline HOR catalysis. Critical innovations in the design of Ni-based nanostructured and bulky catalysts were then discussed, showing their great promise to catalyze alkaline HOR that traditionally relied on PGMs. To demonstrate utility, performances of the elaborately designed Ni-based catalysts under realistic fuel-cell conditions were examined, along with an initial effort to develop a CO-tolerant AEMFC anode. We conclude by outlining future research directions that allow access to next-generation PGM-free HOR catalysts for advanced AEMFCs.
ABSTRACT
Alkaline fuel cells can permit the adoption of platinum group metal-free (PGM-free) catalysts and cheap bipolar plates, thus further lowering the cost. With the exploration of PGM-free hydrogen oxidation reaction (HOR) catalysts, nickel-based compounds have been considered as the most promising HOR catalysts in alkali. Here we report an interfacial engineering through the formation of nickel-vanadium oxide (Ni/V2 O3 ) heterostructures to activate Ni for efficient HOR catalysis in alkali. The strong electron transfer from Ni to V2 O3 could modulate the electronic structure of Ni sites. The optimal Ni/V2 O3 catalyst exhibits a high intrinsic activity of 0.038â mA cm-2 and outstanding stability. Experimental and theoretical studies reveal that Ni/V2 O3 interface as the active sites can enable to optimize the hydrogen and hydroxyl bindings, as well as protect metallic Ni from extensive oxidation, thus achieving the notable activity and durability.
ABSTRACT
The bottleneck of large-scale implementation of electrocatalytic water-splitting technology lies in lacking inexpensive, efficient, and durable catalysts to accelerate the sluggish oxygen evolution reaction kinetics. Owing to more metallic features, transition metal telluride (TMT) with good electronic conductivity holds promising potential as an ideal type of electrocatalysts for oxygen evolution reaction (OER), whereas most TMTs reported up to now still show unsatisfactory OER performance that is far below corresponding sulfide and selenide counterparts. Here, the activation and stabilization of cobalt telluride (CoTe) nanoarrays toward OER through dual integration of sulfur (S) doping and surface oxidization is reported. The as-synthesized CoO@S-CoTe catalyst exhibits a low overpotential of only 246 mV at 10 mA cm-2 and a long-term stability of more than 36 h, outperforming commercial RuO2 and other reported telluride-based OER catalysts. The combined experimental and theoretical results reveal that the enhanced OER performance stems from increased active sites exposure, improved charge transfer ability, and optimized electronic state. This work will provide a valuable guidance to release the catalytic potential of telluride-based OER catalysts via interface modulating engineering.
ABSTRACT
Electrochemical generation of hydrogen peroxide (H2 O2 ) by two-electron oxygen reduction offers a green method to mitigate the current dependence on the energy-intensive anthraquinone process, promising its on-site applications. Unfortunately, in alkaline environments, H2 O2 is not stable and undergoes rapid decomposition. Making H2 O2 in acidic electrolytes can prevent its decomposition, but choices of active, stable, and selective electrocatalysts are significantly limited. Here, the selective and efficient two-electron reduction of oxygen toward H2 O2 in acid by a composite catalyst that is composed of black phosphorus (BP) nailed chemically on the metallic cobalt diselenide (CoSe2 ) surface is reported. It is found that this catalyst exhibits a 91% Faradic efficiency for H2 O2 product at an overpotential of 300 mV. Moreover, it can mediate oxygen to H2 O2 with a high production rate of ≈1530 mg L-1 h-1 cm-2 in a flow-cell reactor. Spectroscopic and computational studies together uncover a BP-induced surface charge redistribution in CoSe2 , which leads to a favorable surface electronic structure that weakens the HOO* adsorption, thus enhancing the kinetics toward H2 O2 formation.
ABSTRACT
Platinum on carbon (Pt/C) catalyst is commercially adopted in fuel cells but it undergoes formidable active-site poisoning by carbon monoxide (CO). In particular, given the sluggish kinetics of hydrogen oxidation reaction (HOR) in anion-exchange membrane fuel cell (AEMFC), the issues of Pt poisoning and slow rate would combine mutually, notably worsening the device performances. Here we overcome these challenges through incorporating cobalt (Co) into molybdenum-nickel alloy (MoNi4 ), termed Co-MoNi4 , which not only shows superior HOR activity over the Pt/C catalyst in alkali, but more intriguingly exhibits excellent CO tolerance with only small activity decay after 10 000 cycles in the presence of 500 parts per million (ppm) CO. When feeding with CO (250â ppm)/H2 , the AEMFC assembled by this catalyst yields a peak power density of 394â mW cm-2 , far exceeding the Pt/C catalyst. Experimental and computational studies reveal that weakened CO chemisorption originates from the electron-deficient Ni sites after Co incorporation that suppresses dâCO 2π* back-donation.
ABSTRACT
Picturing the atomic migration pathways of catalysts in a reactive atmosphere is of central significance for uncovering the underlying catalytic mechanisms and directing the design of high-performance catalysts. Here, we describe a reduction-controlled atomic migration pathway that converts nanoparticles to single atom alloys (SAAs), which has remained synthetically challenging in prior attempts due to the elusive mechanism. We achieved this by thermally treating the noble-metal nanoparticles M (M = Ru, Rh, Pd, Ag, Ir, Pt, and Au) on metal oxide (CuO) supports with H2/Ar. Atomic-level characterization revealed such conversion as the synergistic consequence of noble metal-promoted H2 dissociation and concomitant CuO reduction. The observed atomic migration pathway offers an understanding of the dynamic mechanisms study of nanomaterials formation and catalyst design.
Subject(s)
Alloys , Metal Nanoparticles , CatalysisABSTRACT
The electrosynthesis of valuable multicarbon chemicals using carbon dioxide (CO2) as a feedstock has substantially progressed recently but still faces considerable challenges. A major difficulty lines in the sluggish kinetics of forming carbon-carbon (C-C) bonds, especially in neutral media. We report here that oxide-derived copper crystals enclosed by six {100} and eight {111} facets can reduce CO2 to multicarbon products with a high Faradaic efficiency of 74.9 ± 1.7% at a commercially relevant current density of 300 mA cm-2 in 1 M KHCO3 (pH â¼ 8.4). By combining the experimental and computational studies, we uncovered that Cu(100)/Cu(111) interfaces offer a favorable local electronic structure that enhances *CO adsorption and lowers C-C coupling activation energy barriers, performing superior to Cu(100) and Cu(111) surfaces, respectively. On this catalyst, no obvious degradation was observed at 300 mA cm-2 over 50 h of continuous operation.
ABSTRACT
Recently developed solid-state catalysts can mediate carbon dioxide (CO2) electroreduction to valuable products at high rates and selectivities. However, under commercially relevant current densities of > 200 milliamperes per square centimeter (mA cm-2), catalysts often undergo particle agglomeration, active-phase change, and/or element dissolution, making the long-term operational stability a considerable challenge. Here we report an indium sulfide catalyst that is stabilized by adding zinc in the structure and shows dramatically improved stability. The obtained ZnIn2S4 catalyst can reduce CO2 to formate with 99.3% Faradaic efficiency at 300 mA cm-2 over 60 h of continuous operation without decay. By contrast, similarly synthesized indium sulfide without zinc participation deteriorates quickly under the same conditions. Combining experimental and theoretical studies, we unveil that the introduction of zinc largely enhances the covalency of In-S bonds, which "locks" sulfur-a catalytic site that can activate H2O to react with CO2, yielding HCOO* intermediates-from being dissolved during high-rate electrolysis.
ABSTRACT
Most previous efforts are devoted to developing transition metals as electrocatalysts guided by the d-band center model. The metals of the s-block of the periodic table have so far received little attention in the application of oxygen reduction reactions (ORR). Herein, a carbon catalyst with calcium (Ca) single atom coordinated with N and O is reported, which displays exceptional ORR activities in both acidic condition (E1/2 = 0.77 V, 0.1 m HClO4 ) and alkaline condition (E1/2 = 0.90 V, 0.1 m KOH). The CaN, O/C exhibits remarkable performance in zinc-air battery with a maximum power density of 218 mW cm-2 , superior to a series of catalysts reported so far. X-ray absorption near-edge structure (XANES) characterization confirms the formation of N- and O-atom-coordinated Ca in the carbon matrix. Density functional theory (DFT) calculations reveal that the high catalytic activity of main-group Ca is ascribed to the fact that its p-orbital electron structure is regulated by N and O coordination so that the highest peak (EP ) of the projected density of states (PDOS) for the Ca atom is moved close to the Fermi level, thereby facilitating the adsorption of ORR intermediates and electron transfer.
ABSTRACT
Electrosynthesis of hydrogen peroxide (H2 O2 ) in the acidic environment could largely prevent its decomposition to water, but efficient catalysts that constitute entirely earth-abundant elements are lacking. Here we report the experimental demonstration of narrowing the interlayer gap of metallic cobalt diselenide (CoSe2 ), which creates high-performance catalyst to selectively drive two-electron oxygen reduction toward H2 O2 in an acidic electrolyte. The enhancement of the interlayer coupling between CoSe2 atomic layers offers a favorable surface electronic structure that weakens the critical *OOH adsorption, promoting the energetics for H2 O2 production. Consequently, on the strongly coupled CoSe2 catalyst, we achieved Faradaic efficiency of 96.7 %, current density of 50.04â milliamperes per square centimeter, and product rate of 30.60â mg cm-2 h-1 . Moreover, this catalyst shows no sign of degradation when operating at -63 milliamperes per square centimeter over 100â hours.
ABSTRACT
There has been great interest in phospholipids (PLs) from marine by-products due to their long-chain polyunsaturated fatty acids with unique health and functional properties. Here, marine PLs from squid viscera and gonads were comprehensively characterized and compared by UPLC-Q-Exactive Orbitrap/MS-based lipidomics analysis. A total of thirteen phospholipid classes including 1223 molecular species were identified and quantified in both resources. PC, PE and SM were further isolated from the total PLs of squid viscera and gonads, respectively. All isolated squid PL components were first evaluated for anti-inflammatory, antioxidant and cardiovascular effects using in vivo zebrafish models. Our results showed the diversity, content and physiological functions of PLs from squid by-products, which provided a basis for their future application in the nutritional and pharmaceutical industry.
Subject(s)
Decapodiformes/chemistry , Phospholipids/chemistry , Animals , Anti-Inflammatory Agents/administration & dosage , Anti-Inflammatory Agents/chemistry , Antioxidants/administration & dosage , Antioxidants/chemistry , Arrhythmias, Cardiac/drug therapy , Cardiovascular Agents/administration & dosage , Cardiovascular Agents/chemistry , Chromatography, High Pressure Liquid , Fibrinolytic Agents/administration & dosage , Fibrinolytic Agents/chemistry , Gonads/chemistry , Humans , Lipidomics , Mass Spectrometry , Phospholipids/administration & dosage , Thrombosis/drug therapy , Viscera/chemistry , ZebrafishABSTRACT
Operating fuel cells in alkaline environments permits the use of platinum-group-metal-free (PGM-free) catalysts and inexpensive bipolar plates, leading to significant cost reduction. Of the PGM-free catalysts explored, however, only a few nickel-based materials are active for catalyzing the hydrogen oxidation reaction (HOR) in alkali; moreover, these catalysts deactivate rapidly at high anode potentials owing to nickel hydroxide formation. Here we describe that a nickel-tungsten-copper (Ni5.2WCu2.2) ternary alloy showing HOR activity rivals Pt/C benchmark in alkaline electrolyte. Importantly, we achieved a high anode potential up to 0.3 V versus reversible hydrogen electrode on this catalyst with good operational stability over 20 h. The catalyst also displays excellent CO-tolerant ability that Pt/C catalyst lacks. Experimental and theoretical studies uncover that nickel, tungsten, and copper play in synergy to create a favorable alloying surface for optimized hydrogen and hydroxyl bindings, as well as for the improved oxidation resistance, which result in the HOR enhancement.
ABSTRACT
Copper is currently the material with the most promise as catalyst to drive carbon dioxide (CO2) electroreduction to produce value-added multicarbon (C2+) compounds. However, a copper catalyst on a carbon-based gas diffusion layer electrode often has poor stability-especially when performing at high current densities-owing to electrolyte flooding caused by the hydrophobicity decrease of the gas diffusion layer during operation. Here, we report a bioinspired copper catalyst on a gas diffusion layer that mimics the unique hierarchical structuring of Setaria's hydrophobic leaves. This hierarchical copper structure endows the CO2 reduction electrode with sufficient hydrophobicity to build a robust gas-liquid-solid triple-phase boundary, which can not only trap more CO2 close to the active copper surface but also effectively resist electrolyte flooding even under high-rate operation. We consequently achieved a high C2+ production rate of 255 ± 5.7 mA cm-2 with a 64 ± 1.4% faradaic efficiency, as well as outstanding operational stability at 300 mA cm-2 over 45 h in a flow reactor, largely outperforming its wettable copper counterparts.