Hollow Porous VOx/C Nanoscrolls as High-Performance Anodes for Lithium-Ion Batteries.

Novel hollow porous VOx/C nanoscrolls are synthesized by an annealing process with the VOx/octadecylamine (ODA) nanoscrolls as both vanadium and carbon sources. In the preparation, the VOx/ODA nanoscrolls are first achieved by a two-phase solvothermal method using ammonium metavanadat as the precursor. Upon subsequent heating, the intercalated amines between the vanadate layers in the VOx/ODA nanoscrolls decompose into gases, which escape from inside the nanoscrolls and leave sufficient pores in the walls. As the anodes of lithium-ion batteries (LIBs), such hollow porous VOx/C nanoscrolls possess exceedingly high capacity and rate capability (904 mAh g-1 at 1 A g-1) and long cyclic stability (872 mAh g-1 after 210 cycles at 1 A g-1). The good performance is derived from the unique structural features of the hollow hierarchical porous nanoscrolls with low crystallinity, which could significantly suppress irreversible Li+ trapping as well as improve Li+ diffusion kinetics. This universal method of annealing amine-intercalated oxide could be widely applied to the fabrication of a variety of porous electrode materials for high-performance LIBs and supercapacitors.

Synthesis of Mesoporous Single Crystal Co(OH)2 Nanoplate and Its Topotactic Conversion to Dual-Pore Mesoporous Single Crystal Co3O4.

A new class of mesoporous single crystalline (MSC) material, Co(OH)2 nanoplates, is synthesized by a soft template method, and it is topotactically converted to dual-pore MSC Co3O4. Most mesoporous materials derived from the soft template method are reported to be amorphous or polycrystallined; however, in our synthesis, Co(OH)2 seeds grow to form single crystals, with amphiphilic block copolymer F127 colloids as the pore producer. The single-crystalline nature of material can be kept during the conversion from Co(OH)2 to Co3O4, and special dual-pore MSC Co3O4 nanoplates can be obtained. As the anode of lithium-ion batteries, such dual-pore MSC Co3O4 nanoplates possess exceedingly high capacity as well as long cyclic performance (730 mAh g(-1) at 1 A g(-1) after the 350th cycle). The superior performance is because of the unique hierarchical mesoporous structure, which could significantly improve Li(+) diffusion kinetics, and the exposed highly active (111) crystal planes are in favor of the conversion reaction in the charge/discharge cycles.