ABSTRACT
Aqueous zinc-ion batteries (AZIBs) are highly regarded for their affordability, stability, safety, and eco-friendliness. Nevertheless, their practical application is hindered by severe side reactions and the formation of zinc (Zn) dendrites on the Zn metal anode surface. In this study, we employ tetrahydrofuran alcohol (THFA), an efficient and cost-effective alcohol ether electrolyte, to mitigate these issues and achieve ultralong-life AZIBs. Theoretical calculations and experimental findings demonstrate that THFA acts as both a hydrogen bonding donor and acceptor, effectively anchoring H2O molecules through dual-site hydrogen bonding. This mechanism restricts the activity of free water molecules. Moreover, the two oxygen (O) atoms in THFA serve as dual solvation sites, enhancing the desolvation kinetics of [Zn(H2O)6]2+ and improving the deposition dynamics of Zn2+ ions. As a result, even trace amounts of THFA significantly suppress adverse reactions and the formation of Zn dendrites, enabling highly reversible Zn metal anodes for ultralong-life AZIBs. Specifically, a Zn-based symmetric cell containing 2 % THFA achieves an ultralong cycle life of 8,800 h at 0.5 mA cm-2/0.5 mAh cm-2, while a Zn//VO2 full cell containing 2 % THFA maintains a remarkable 80.03 % capacity retention rate at 5 A g-1 over 2,000 cycles. This study presents a practical strategy to develop dendrite-free, cost-effective, and highly efficient aqueous energy storage systems by leveraging alcohol ether compounds with dual-site hydrogen bonding capabilities.
ABSTRACT
Aqueous zinc-ion batteries (AZIBs) have attracted significant attention owing to their inherent security, low cost, abundant zinc (Zn) resources and high energy density. Nevertheless, the growth of zinc dendrites and side reactions on the surface of Zn anodes during repeatedly plating/stripping shorten the cycle life of AZIBs. Herein, a simple organic molecule with abundant polar functional groups, 2,2,2-trifluoroether formate (TF), has been proposed as a high-efficient additive in the ZnSO4 electrolyte to suppress the growth of Zn dendrites and side reaction during cycling. It is found that TF molecules can infiltrate the solvated sheath layer of the hydrated Zn2+ to reduce the number of highly chemically active H2O molecules owing to their strong binding energy with Zn2+. Simultaneously, TF molecules can preferentially adsorb onto the Zn surface, guiding the uniform deposition of Zn2+ along the crystalline surface of Zn(002). This dual action significantly inhibits the formation of Zn dendrites and side reactions, thus greatly extending the cycling life of the batteries. Accordingly, the Zn//Cu asymmetric cell with 2 % TF exhibits stable cycling for more than 3,800 cycles, achieving an excellent average Columbic efficiency (CE) of 99.81 % at 2 mA cm-2/1 mAh cm-2. Meanwhile, the Zn||Zn symmetric cell with 2 % TF demonstrates a superlong cycle life exceeding 3,800 h and 2,400 h at 2 mA cm-2/1 mAh cm-2 and 5 mA cm-2/2.5 mAh cm-2, respectively. Simultaneously, the Zn//VO2 full cell with 2 % TF possesses high initial capacity (276.8 mAh/g) and capacity retention (72.5 %) at 5 A/g after 500 cycles. This investigation provides new insights into stabilizing Zn metal anodes for AZIBs through the co-regulation of Zn2+ solvated structure and surface crystallography.