ABSTRACT
In this work, the endurance characteristics of Al-doped HfO2(HAO)-based metal-ferroelectric-metal (MFM) capacitors (which were annealed at 1000 °C) with various doping concentrations were investigated. The doping concentration was optimized for the high annealing temperature (1000 °C) process. To investigate the impact of cycling pulses on the endurance characteristics of HAO-based MFM capacitor, the rise/fall time (tr/f) and hold time (th) for the cycling pulses were varied. Moreover, by adopting the recoverable fatigue process, the endurance characteristics under repetitive wake-up/fatigue processes were studied. The HAO capacitors achieved the remnant polarization (2Pr) of 23.767µC cm-2at pristine state under the high annealing temperature. Furthermore, it was demonstrated that the endurance characteristics (â¼108cycles) of the HAO capacitors were comparable to them of other HfO2-based ferroelectric capacitors. Lastly but not least, it turned out that the amount of oxygen and oxygen vacancies in the HAO thin film was dependent of doping concentrations for the film. The impact of oxygen and oxygen vacancies was quantitatively analyzed, in detail, with TEM, XPS and GIXRD analysis.
ABSTRACT
The endurance characteristic of Zr-doped HfO2 (HZO)-based metal-ferroelectric-metal (MFM) capacitors fabricated under various deposition/annealing temperatures in the atomic layer deposition (ALD) process was investigated. The chamber temperature in the ALD process was set to 120 °C, 200 °C, or 250 °C, and the annealing temperature was set to 400 °C, 500 °C, 600 °C, or 700 °C. For the given annealing temperature of 700 °C, the remnant polarization (2Pr) was 17.21 µC/cm2, 26.37 µC/cm2, and 31.8 µC/cm2 at the chamber temperatures of 120 °C, 200 °C, and 250 °C, respectively. For the given/identical annealing temperature, the largest remnant polarization (Pr) was achieved when using the chamber temperature of 250 °C. At a higher annealing temperature, the grain size in the HZO layer becomes smaller, and thereby, it enables to boost up Pr. It was observed that the endurance characteristics for the capacitors fabricated under various annealing/chamber temperatures were quite different. The different endurance characteristics are due to the oxygen and oxygen vacancies in ferroelectric films, which affects the wakeup/fatigue behaviors. However, in common, all the capacitors showed no breakdown for an externally applied pulse (up to 108 cycles of the pulse).
ABSTRACT
In this work, the measured electrical characteristics of a fully depleted silicon-on-insulator (FDSOI) device and fin-shaped field-effect transistor (FinFET), whose gate electrode is connected in series to the bottom electrode of a ferroelectric capacitor (FE-FDSOI/FE-FinFET), are experimentally studied. The hysteretic property in input transfer characteristic of those devices is desirable for memory device applications, so that the understanding and modulating the hysteresis window is a key knob in designing the devices. It is experimentally observed that the hysteresis window of FE-FDSOI/FE-FinFET is decreased with (i) increasing the area of the ferroelectric capacitor and/or (ii) decreasing the gate area of baseline FET. The way how to control the hysteresis window of FE-FDSOI/FE-FinFET is proposed and discussed in detail.
ABSTRACT
Threshold voltage adjustment in threshold switching (TS) devices with HfO2/Al2O3 superlattice (by means of changing the cycle ratio of HfO2 to Al2O3 in atomic layer deposition) is investigated to implement a transparent cross-point array. TS devices with different cycle ratios (i.e., 3:1, 3:2, and 3:3) were fabricated and studied. The threshold voltage of the devices was increased from 0.9 V to 3.2 V, as the relative contents of Al2O3 layer in the superlattice were increased. At the same time, it is demonstrated that the off-resistance values of the devices were enhanced from 2.6 109 to 6 1010 as the atomic layer deposition (ALD) cycle ratio of HfO2 to Al2O3 layer was adjusted from 3:1 to 3:3. However, the hold voltage and the on-current values were almost identical for the three devices. These results can be understood using the larger barrier height of Al2O3 layer than that of HfO2 layer.