The role of chitosan grafted copolymer/zeolite Schiff base nanofiber in adsorption of copper and zinc cations from aqueous media.

The objective of this research was to develop and assess chitosan-grafted copolymer/HZSM5 zeolite Schiff base nanofibers for Cu2+ and Zn2+ adsorption from aqueous media. Nanofibers were prepared via electrospinning and characterized using XRD, FTIR, 1H NMR, FESEM, TGA, BET, and XPS. The study evaluated the effect of unmodified HZSM5 and Schiff base functionalization on adsorption capacities. Incorporating 10.0 wt% zeolite Schiff base as the optimum content into the chitosan-grafted copolymer significantly enhanced adsorption, achieving increases of 98.2 % for Zn2+ and 42.2 % for Cu2+. Specifically, Zn2+ adsorption increased from 27.6 to 54.7 mg/g, and Cu2+ from 67.1 to 95.4 mg/g. Factors such as temperature, pH, adsorption time, and initial cation concentration were analyzed. Kinetic studies revealed a double-exponential model, and isotherm analysis indicated a good fit with the Redlich-Peterson model, showing maximum monolayer capacities of 310.1 mg/g for Cu2+ and 97.8 mg/g for Zn2+ (pH 6.0, 240 min, 45 °C). The adsorption thermodynamics indicated a spontaneous and endothermic adsorption. Reusability tests showed minimal capacity loss (4.91 % for Cu2+ and 5.59 % for Zn2+) after five cycles. The nanofiber displayed greater selectivity for Cu2+ over Zn2+ in multi-ion systems and real electroplating wastewater, highlighting its potential for targeted heavy metal removal.

Functionalization of a cast NaAl/binary ZnO/SiO2 nanohybrid with amine and Schiff base ligands as an adsorbent of divalent cations in water system.

Casting method was used to synthesize a novel sodium alginate nanohybrid functionalized with aminated ZnO/SiO2 Schiff base for adsorption of nickel (Ni2+) and copper (Cu2+) divalent cations in single and binary water systems. The cast Schiff base nanohybrids were investigated using FESEM, XRD, BET, FTIR, TGA, and XPS analyses. The influence of unfunctionalized binary ZnO/SiO2 nano oxides and aminated Schiff base ligands formed by the reaction between salicylaldehyde and O-phenylenediamine on the adsorption of Ni2+ and Cu2+ cations was evaluated. The results confirmed that the aminated Schiff base ligands led to a higher adsorption ability of the cast nanohybrids containing interaction of divalent cations with nitrogen and oxygen atoms, as well as carboxyl and hydroxyl groups. The adsorption kinetics and isotherm for both cations followed a double-exponential model and the Redlich-Peterson model, respectively. The maximum monolayer capacity was found to be 249.8 mg/g for Cu2+ cation and 96.4 mg/g for Ni2+ cation. Thermodynamic analysis revealed an endothermic and spontaneous adsorption process with an increase in entropy. Furthermore, the synthesized Schiff base adsorbent could be easily reused over five times. The simultaneous adsorption in binary system exhibited a higher adsorption selectivity of the cast Schiff base nanohybrid for Cu2+ cation compared to Ni2+ cation. It was found that the removal percentages of Cu2+ and Ni2+ from industrial electroplating wastewater were 91.3 and 64.5%, respectively. Lastly, cost analysis of the synthesized nanohybrid was investigated.