ABSTRACT
Mixed oxides of Rh-Cr (RhCrOx), containing Rh3+ and Cr3+ cations, are commonly used as cocatalysts for the hydrogen evolution reaction (HER) on particulate photocatalysts. The precise physicochemical mechanisms of the HER at the catalytic sites of these oxides are not well understood. In this study, model cocatalyst electrodes, composed of nanoparticulate RhCrOx, were fabricated to investigate the physicochemical mechanisms of the HER. Electroanalytical and X-ray photoelectron spectroscopic measurements revealed that nanoparticulate RhCrOx produces reduced Rh (Rh0) species by maintaining an electrode potential more negative than 0.03 V versus the reversible hydrogen electrode (VRHE). This results in significant enhancement of the HER activity. The catalytic activity for the HER stems from the reduced Rh species, and the inclusion of Cr3+ (CrOx) aided in the electron transfer process at the solid/liquid interface, resulting in a higher current density during the HER. To achieve a solar-to-hydrogen efficiency of over 3%, the conduction band minimum of the particulate photocatalyst should be positioned more negatively than -0.10 VRHE. Moreover, the formation of electron trap states at potentials more positive than 0.03 VRHE should be avoided. This study highlights the importance of understanding the catalytic sites on metal oxide cocatalysts. Moreover, it offers a design strategy for enhancing the efficiency of photocatalytic water splitting.
ABSTRACT
Some oxide-based particulate photocatalyst sheets exhibit excellent activity during the water-splitting reaction. The replacement of oxide photocatalysts with narrow-bandgap photocatalysts based on nonoxides could provide the higher solar-to-hydrogen energy conversion efficiencies that are required for practical implementation. Unfortunately, the activity of nonoxide-based photocatalyst sheets is low in many cases, indicating the need for strategies to improve the quality of nonoxide photocatalysts and the charge transfer process. In this work, single-crystalline particulate SrTaO2N is studied as an oxygen evolution photocatalyst for photocatalyst sheets applied to Z-scheme water splitting, in combination with La5Ti2Cu0.9Ag0.1O7S5 and Au as the hydrogen evolution photocatalyst and conductive layer, respectively. The loading of SrTaO2N with CoOx provided increases activity during photocatalytic water oxidation, giving an apparent quantum yield of 15.7% at 420 nm. A photocatalyst sheet incorporating CoOx-loaded SrTaO2N is also found to promote Z-scheme water splitting under visible light. Notably, the additional loading of nanoparticulate TiN on the CoOx-loaded SrTaO2N improves the water splitting activity by six times because the TiN promotes electron transfer from the SrTaO2N particles to the Au layer. This work demonstrates key concepts related to the improvement of nonoxide-based photocatalyst sheets based on facilitating the charge transfer process through appropriate surface modifications.
ABSTRACT
So-called Z-scheme systems permit overall water splitting using narrow-bandgap photocatalysts. To boost the performance of such systems, it is necessary to enhance the intrinsic activities of the hydrogen evolution photocatalyst and oxygen evolution photocatalyst, promote electron transfer from the oxygen evolution photocatalyst to the hydrogen evolution photocatalyst, and suppress back reactions. The present work develop a high-performance oxysulfide photocatalyst, Sm2Ti2O5S2, as an hydrogen evolution photocatalyst for use in a Z-scheme overall water splitting system in combination with BiVO4 as the oxygen evolution photocatalyst and reduced graphene oxide as the solid-state electron mediator. After surface modifications of the photocatalysts to promote charge separation and redox reactions, this system is able to split water into hydrogen and oxygen for more than 100 hours with a solar-to-hydrogen energy conversion efficiency of 0.22%. In contrast to many existing photocatalytic systems, the water splitting activity of the present system is only minimally reduced by increasing the background pressure to 90 kPa. These results suggest characteristics suitable for applications under practical operating conditions.
ABSTRACT
A long-standing trade-off exists between improving crystallinity and minimizing particle size in the synthesis of perovskite-type transition-metal oxynitride photocatalysts via the thermal nitridation of commonly used metal oxide and carbonate precursors. Here, we overcome this limitation to fabricate ATaO2N (A = Sr, Ca, Ba) single nanocrystals with particle sizes of several tens of nanometers, excellent crystallinity and tunable long-wavelength response via thermal nitridation of mixtures of tantalum disulfide, metal hydroxides (A(OH)2), and molten-salt fluxes (e.g., SrCl2) as precursors. The SrTaO2N nanocrystals modified with a tailored Ir-Pt alloy@Cr2O3 cocatalyst evolved H2 around two orders of magnitude more efficiently than the previously reported SrTaO2N photocatalysts, with a record solar-to-hydrogen energy conversion efficiency of 0.15% for SrTaO2N in Z-scheme water splitting. Our findings enable the synthesis of perovskite-type transition-metal oxynitride nanocrystals by thermal nitridation and pave the way for manufacturing advanced long-wavelength-responsive particulate photocatalysts for efficient solar energy conversion.
ABSTRACT
Photocatalytic water splitting is an ideal means of producing hydrogen in a sustainable manner, and developing highly efficient photocatalysts is a vital aspect of realizing this process. The photocatalyst Y2 Ti2 O5 S2 (YTOS) is capable of absorbing at wavelengths up to 650â nm and exhibits outstanding thermal and chemical durability compared with other oxysulfides. However, the photocatalytic performance of YTOS synthesized using the conventional solid-state reaction (SSR) process is limited owing to the large particle sizes and structural defects associated with this synthetic method. Herein, we report the synthesis of YTOS particles by a flux-assisted technique. The enhanced mass transfer efficiency in the flux significantly reduced the preparation time compared with the SSR method. In addition, the resulting YTOS showed improved photocatalytic H2 and O2 evolution activity when loaded with Rh and Co3 O4 co-catalysts, respectively. These improvements are attributed to the reduced particle size and enhanced crystallinity of the material as well as the slower decay of photogenerated carriers on a nanosecond to sub-microsecond time range. Further optimization of this flux-assisted method together with suitable surface modification is expected to produce high-quality YTOS crystals with superior photocatalytic activity.
ABSTRACT
The hydrogen evolution reaction (HER) of Rh nanoparticles (RhNP) coated with an ultrathin layer of Cr-oxides (CrOx ) was investigated as a model electrode for the Cr2 O3 /Rh-metal core-shell-type cocatalyst system for photocatalytic water splitting. The CrOx layer was electrodeposited over RhNP on a transparent conductive fluorine-doped tin oxide (FTO) substrate. The CrOx layer on RhNP facilitates the electron transfer process at the CrOx /RhNP interface, leading to the increased current density for the HER. Impedance spectroscopic analysis revealed that the CrOx layer transferred protons via the hopping mechanism to the RhNP surface for HER. In addition, CrOx restricted electron transfer from the FTO to the electrolyte and/or RhNP and suppressed the backward reaction by limiting oxygen migration. This study clarifies the crucial role of the ultrathin CrOx layer on nanoparticulate cocatalysts and provides a cocatalyst design strategy for realizing efficient photocatalytic water splitting.
ABSTRACT
The development of narrow-bandgap photocatalysts for one-step-excitation overall water splitting (OWS) remains a critical challenge in the field of solar hydrogen production. SrTaO2N is a photocatalytic material having a band structure suitable for OWS under visible light (λ ≤ 600 nm). However, the presence of defects in the oxynitride and the lack of cocatalysts to promote simultaneous hydrogen and oxygen evolution make it challenging to realize OWS using this material. The present work demonstrates a SrTaO2N-based particulate photocatalyst for OWS. This photocatalyst, which was composed of single crystals, was obtained by nitriding SrCl2 and Ta2O5 together with NaOH, with the latter added to control the formation of defects. The subsequent loading of bimetallic RuIrOx nanoparticles accelerated charge separation and allowed the SrTaO2N photocatalyst to exhibit superior OWS activity. This research presenting the strategies of controlling the oxygen sources and promoting the cocatalyst function is expected to expand the range of potential OWS-active oxynitride photocatalysts and permit the design of efficient cocatalysts for photocatalytic OWS.
ABSTRACT
The trade-off between light absorption and carrier transport in semiconductor thin film photoelectrodes is a major limiting factor of their solar-to-hydrogen efficiency for photoelectrochemical water splitting. Herein, we develop a heterogeneous doping strategy that combines surface doping with bulk gradient doping to decouple light absorption and carrier transport in a thin film photoelectrode. Taking La and Mg doped Ta3N5 thin film photoanode as an example, enhanced light absorption is achieved by surface La doping through alleviating anisotropic optical absorption, while efficient carrier transport in the bulk is maintained by the gradient band structure induced by gradient Mg doping. Moreover, the homojunction formed between the La-doped layer and the gradient Mg-doped layer further promotes charge separation. As a result, the heterogeneously doped photoanode yields a half-cell solar-to-hydrogen conversion efficiency of 4.07%, which establishes Ta3N5 as a leading performer among visible-light-responsive photoanodes. The heterogeneous doping strategy could be extended to other semiconductor thin film light absorbers to break performance trade-offs by decoupling light absorption and carrier transport.
ABSTRACT
Efficient water vapor splitting opens a new strategy to develop scalable and corrosion-free solar-energy-harvesting systems. This study demonstrates highly efficient overall water splitting under vapor feeding using Al-doped SrTiO3 (SrTiO3:Al)-based photocatalyst decorated homogeneously with nano-membrane TiOx or TaOx thin layers (<3 nm). Here, we show the hygroscopic nature of the metal (hydr)oxide layer provides liquid water reaction environment under vapor, thus achieving an AQY of 54 ± 4%, which is comparable to a liquid reaction. TiOx coated, CoOOH/Rh loaded SrTiO3:Al photocatalyst works for over 100 h, under high pressure (0.3 MPa), and with no problems using simulated seawater as the water vapor supply source. This vapor feeding concept is innovative as a high-pressure-tolerant photoreactor and may have value for large-scale applications. It allows uniform distribution of the water reactant into the reactor system without the potential risk of removing photocatalyst powders and eluting some dissolved ions from the reactor.
ABSTRACT
Interface engineering is a proven strategy to improve the efficiency of thin film semiconductor based solar energy conversion devices. Ta3N5 thin film photoanode is a promising candidate for photoelectrochemical (PEC) water splitting. Yet, a concerted effort to engineer both the bottom and top interfaces of Ta3N5 thin film photoanode is still lacking. Here, we employ n-type In:GaN and p-type Mg:GaN to modify the bottom and top interfaces of Ta3N5 thin film photoanode, respectively. The obtained In:GaN/Ta3N5/Mg:GaN heterojunction photoanode shows enhanced bulk carrier separation capability and better injection efficiency at photoanode/electrolyte interface, which lead to a record-high applied bias photon-to-current efficiency of 3.46% for Ta3N5-based photoanode. Furthermore, the roles of the In:GaN and Mg:GaN layers are distinguished through mechanistic studies. While the In:GaN layer contributes mainly to the enhanced bulk charge separation efficiency, the Mg:GaN layer improves the surface charge inject efficiency. This work demonstrates the crucial role of proper interface engineering for thin film-based photoanode in achieving efficient PEC water splitting.
ABSTRACT
Solar-powered one-step-excitation overall water splitting (OWS) using semiconducting materials is a simple means of achieving scalable and sustainable hydrogen production. While tantalum oxynitride (TaON) is one of the few photocatalysts capable of promoting OWS via single-step visible-light excitation, the efficiency of this process remains extremely poor. The present work employed 15â nm amorphous Ta2 O5 â 3.3 H2 O nanoparticles as a new precursor together with Zr doping and an optimized nitridation duration to synthesize a TaON-based photocatalyst with reduced particle sizes and low defect densities. Upon loading with Ru/Cr2 O3 /IrO2 cocatalysts, this material exhibited stoichiometric water splitting into hydrogen and oxygen, with an order of magnitude improvement in efficiency. Our findings demonstrate the importance of inventing/selecting the appropriate synthetic precursor and of defect control for fabricating active OWS photocatalysts.
ABSTRACT
While self-healing is considered a promising strategy to achieve long-term stability for oxygen evolution reaction (OER) catalysts, this strategy remains a challenge for OER catalysts working in highly alkaline conditions. The self-healing of the OER-active nickel iron layered double hydroxides (NiFe-LDH) has not been successful due to irreversible leaching of Fe catalytic centers. Here, we investigate the introduction of cobalt (Co) into the NiFe-LDH as a promoter for in situ Fe redeposition. An active borate-intercalated NiCoFe-LDH catalyst is synthesized using electrodeposition and shows no degradation after OER tests at 10 mA cm-2 at pH 14 for 1000 h, demonstrating its self-healing ability under harsh OER conditions. Importantly, the presence of both ferrous ions and borate ions in the electrolyte is found to be crucial to the catalyst's self-healing. Furthermore, the implementation of this catalyst in photoelectrochemical devices is demonstrated with an integrated silicon photoanode. The self-healing mechanism leads to a self-limiting catalyst thickness, which is ideal for integration with photoelectrodes since redeposition is not accompanied by increased parasitic light absorption.
ABSTRACT
The unprecedented impact of human activity on Earth's climate and the ongoing increase in global energy demand have made the development of carbon-neutral energy sources ever more important. Hydrogen is an attractive and versatile energy carrier (and important and widely used chemical) obtainable from water through photocatalysis using sunlight, and through electrolysis driven by solar or wind energy1,2. The most efficient solar hydrogen production schemes, which couple solar cells to electrolysis systems, reach solar-to-hydrogen (STH) energy conversion efficiencies of 30% at a laboratory scale3. Photocatalytic water splitting reaches notably lower conversion efficiencies of only around 1%, but the system design is much simpler and cheaper and more amenable to scale-up1,2-provided the moist, stoichiometric hydrogen and oxygen product mixture can be handled safely in a field environment and the hydrogen recovered. Extending our earlier demonstration of a 1-m2 panel reactor system based on a modified, aluminium-doped strontium titanate particulate photocatalyst4, we here report safe operation of a 100-m2 array of panel reactors over several months with autonomous recovery of hydrogen from the moist gas product mixture using a commercial polyimide membrane5. The system, optimized for safety and durability, and remaining undamaged on intentional ignition of recovered hydrogen, reaches a maximum STH of 0.76%. While the hydrogen production is inefficient and energy negative overall, our findings demonstrate that safe, large-scale photocatalytic water splitting, and gas collection and separation are possible. To make the technology economically viable and practically useful, essential next steps are reactor and process optimization to substantially reduce costs and improve STH efficiency, photocatalyst stability and gas separation efficiency.
ABSTRACT
The simultaneous control of the defect species and surface properties of semiconducting materials is a crucial aspect of improving photocatalytic performance, yet it remains challenging. Here, we synthesized Mg-Zr-codoped single-crystalline Ta3N5 (Ta3N5:Mg+Zr) nanoparticles by a brief NH3 nitridation process, exhibiting photocatalytic water reduction activity 45 times greater than that of pristine Ta3N5 under visible light. A coherent picture of the relations between the defect species (comprising reduced Ta, nitrogen vacancies and oxygen impurities), surface properties (associated with dispersion of the Pt cocatalyst), charge carrier dynamics, and photocatalytic activities was drawn. The tuning of defects and simultaneous optimization of surface properties resulting from the codoping evidently resulted in the generation of high concentrations of long-lived electrons in this material as well as the efficient migration of these electrons to evenly distributed surface Pt sites. These effects greatly enhanced the photocatalytic activity. This work highlights the importance and feasibility of improving multiple properties of a catalytic material via a one-step strategy.
ABSTRACT
Charge separation is crucial for an efficient artificial photosynthetic process, especially for narrow-bandgap metal sulfides/selenides. The present study demonstrates the application of a p-n junction to particulate metal selenides to enhance photocatalytic Z-scheme overall water splitting (OWS). The constructed p-n junction of CdS-(ZnSe)0.5(CuGa2.5Se4.25)0.5 significantly boosted charge separation. A thin TiO2 coating layer also was introduced to inhibit photocorrosion of CdS and suppress the backward reaction of water formation from hydrogen and oxygen. By employing Pt-loaded TiO2/CdS-(ZnSe)0.5(CuGa2.5Se4.25)0.5 as a hydrogen evolution photocatalyst (HEP), we assembled a Z-scheme OWS system, together with BiVO4:Mo and Au as an oxygen evolution photocatalyst and electron mediator, respectively. An apparent quantum yield of 1.5% at 420 nm was achieved, which is by far the highest among reported particulate photocatalytic Z-scheme OWS systems with metal sulfides/selenides as HEPs. The present work demonstrates that a well-tailored p-n junction structure is effective for promoting charge separation in photocatalysis and opens new pathways for the development of efficient artificial photosynthesis systems involving narrow bandgap photocatalysts.
ABSTRACT
Oxynitride photocatalysts hold promise for renewable solar hydrogen production via water splitting owing to their intense visible light absorption. Cocatalyst loading is essential for activation of such oxynitride photocatalysts. However, cocatalyst nanoparticles form aggregates and exhibit weak interaction with photocatalysts, which prevents eliciting their intrinsic photocatalytic performance. Here, we demonstrate efficient utilization of photoexcited electrons in a single-crystalline particulate BaTaO2N photocatalyst prepared with the assistance of RbCl flux for H2 evolution reactions via sequential decoration of Pt cocatalyst by impregnation-reduction followed by site-selective photodeposition. The Pt-loaded BaTaO2N photocatalyst evolves H2 over 100 times more efficiently than before, with an apparent quantum yield of 6.8% at the wavelength of 420 nm, from a methanol aqueous solution, and a solar-to-hydrogen energy conversion efficiency of 0.24% in Z-scheme water splitting. Enabling uniform dispersion and intimate contact of cocatalyst nanoparticles on single-crystalline narrow-bandgap particulate photocatalysts is a key to efficient solar-to-chemical energy conversion.
ABSTRACT
Overall water splitting, evolving hydrogen and oxygen in a 2:1 stoichiometric ratio, using particulate photocatalysts is a potential means of achieving scalable and economically viable solar hydrogen production. To obtain high solar energy conversion efficiency, the quantum efficiency of the photocatalytic reaction must be increased over a wide range of wavelengths and semiconductors with narrow bandgaps need to be designed. However, the quantum efficiency associated with overall water splitting using existing photocatalysts is typically lower than ten per cent1,2. Thus, whether a particulate photocatalyst can enable a quantum efficiency of 100 per cent for the greatly endergonic water-splitting reaction remains an open question. Here we demonstrate overall water splitting at an external quantum efficiency of up to 96 per cent at wavelengths between 350 and 360 nanometres, which is equivalent to an internal quantum efficiency of almost unity, using a modified aluminium-doped strontium titanate (SrTiO3:Al) photocatalyst3,4. By selectively photodepositing the cocatalysts Rh/Cr2O3 (ref. 5) and CoOOH (refs. 3,6) for the hydrogen and oxygen evolution reactions, respectively, on different crystal facets of the semiconductor particles using anisotropic charge transport, the hydrogen and oxygen evolution reactions could be promoted separately. This enabled multiple consecutive forward charge transfers without backward charge transfer, reaching the upper limit of quantum efficiency for overall water splitting. Our work demonstrates the feasibility of overall water splitting free from charge recombination losses and introduces an ideal cocatalyst/photocatalyst structure for efficient water splitting.
ABSTRACT
Photoelectrochemical (PEC) water splitting using visible-light-responsive photoelectrodes is the preferred approach to converting solar energy into hydrogen as a renewable energy source. A transparent Ta3 N5 photoanode embedded within a PEC cell having a tandem configuration is a promising configuration that may provide a high solar-to-hydrogen energy conversion efficiency. Ta3 N5 thin films are typically prepared by heating precursor films in an NH3 flow at high temperatures, which tends to degrade the transparent conductive layer, such that producing efficient Ta3 N5 transparent photoanodes is challenging. Herein, the direct preparation of transparent Ta3 N5 photoanodes on insulating quartz substrates was demonstrated without the insertion of a transparent conductive layer. The resulting devices generated a photocurrent of 6.0â mA cm-2 at 1.23â V vs. a reversible hydrogen electrode under simulated sunlight. This study provides a new strategy for the preparation of transparent photoelectrodes that mitigates current challenges.
ABSTRACT
It is important to improve the apparent quantum yields (AQYs) of narrow bandgap photocatalysts to achieve efficient H2 production. The present work demonstrates a particulate solid solution of zinc selenide and copper gallium selenide (denoted as ZnSe:CGSe) that evolves H2 efficiently and is responsive to visible light up to 725 nm. This material was synthesized using a flux-assisted method and was found to comprise single-crystalline tetrahedral particles. The coloading of Ni and Rh, Pt, Pd or Ru as cocatalysts further improved the photocatalytic H2 evolution rate over this photocatalyst. With the optimal coloading of a Ni-Ru composite cocatalyst, an AQY of 13.7% was obtained at 420 nm during a sacrificial H2 evolution reaction, representing the highest value yet reported for a photocatalyst with an absorption edge longer than 700 nm. The present study demonstrates that the preparation of single-crystalline particles and the rational assembly of composite cocatalysts are effective strategies that allow the efficient utilization of long wavelengths by metal selenide photocatalysts for solar fuel production.