ABSTRACT
<p><b>OBJECTIVE</b>To study the characteristics of cationic polymers polyethylenimine-β-cyclodextrin (PEI-CyD), polyethylenimine-poly-(3-hydroxypropyl)-aspartamide (PEI-PHPA), N,N-Dimethyldipropylenetriamine-Bis(3-aminopropyl)amine-aspartamide (PEE-PHPA) in vitro and in vivo.</p><p><b>METHODS</b>PEI-PHPA, PEI-CyD and PEE-PHPA were synthesized and the chemistry structure of PEI-PHPA, PEI-CyD and PEE-PHPA was confirmed by (1)H-NMR. The particle size and zeta potential of these polymers were measured, and capacity of plasmid DNA condensation was tested. The inhibition of COS-7, A549, HEK293 and C6 cells was measured by MTT assay. The transfection efficiency was determined in HEK293 cell lines. The toxicity, tissue distribution and transfection efficiency of cationic polymers were tested in vivo.</p><p><b>RESULTS</b>When the N/P of polymers/DNA at 30, the particle sizes were close 250 nm and the zeta-potential were near 35 mv. They were able to condense DNA at N/P ratio < 5. The MTT assay showed that the IC(50) of PEE-PHPA was 21.5, 20.2, 7.30 and 37.1 μg/ml, and that of PEI25kD was 15.8, 18.3, 11.4 and 36.7 μg/ml in C6, COS-7, A549 and HEK293cell lines, respectively. The cell viability of PEI-CyD and PEI-PHPA in above cell lines was over 60%. They had high transfection efficiency in HEK293 cell lines. The LD(50) of PEI25Kd, PEI-CyD, PEI-PHPA and PEE-PHPA in vivo was 19.50, 100.4, 521.2 and 630.0, respectively by intraperitoneal (ip) injection. The contractions of these polymers were higher in kidney than in other organs and tissues.PEE-PHPA had slight effect on kidney and liver function.</p><p><b>CONCLUSION</b>PEE and PEI25kD have higher transfection efficiency and higher toxicity; while PC and PHPA-PEI have lower toxicity and higher transfection efficiency to be used as non-viral gene vector.</p>
Subject(s)
Humans , Cations , Cell Line, Tumor , Genetic Vectors , Polyethyleneimine , Polymers , Transfection , beta-CyclodextrinsABSTRACT
<p><b>OBJECTIVE</b>To develop a drug delivery system triptolide-polyethylenimine-cyclodextrin and to evaluate its anticancer activity in vitro.</p><p><b>METHODS</b>Triptolide was conjugated to polyethylenimine-cyclodextrin by N, N'-carbonyldiimidazole to form triptolide-polyethylenimine-cyclodextrin. (1)H-NMR, FT-IR and XRD were used to confirm its structure. The anticancer effect of the polymer was assessed by MTT assay, erasion trace test and hematoxylin-eosin staining. The potential to condense siRNA and to delivery siRNA into cytoplasm was demonstrated by gel retardation assay, zeta-potential determination and fluorescence staining.</p><p><b>RESULTS</b>Triptolide was successfully conjugated to polyethylenimine-cyclodextrin and the conjugation rate of triptolide was 10% (w/w). siRNA was effectively condensed by the polymer at the N/P ratio of 5, and its particle size was 300 ±15 nm and zeta potential was 8 ±2.5 mV. MTT assay, erasion trace test and hematoxylin-eosin staining revealed that triptolide-polyethylenimine-cyclodextrin had anticancer effect and low cytotoxicity to normal cells. The polymer was able to deliver siRNA to the cytoplasm effectively as demonstrated by fluorescence staining.</p><p><b>CONCLUSION</b>Triptolide-polyethylenimine-cyclodextrin is able to inhibit the growth and migration of cancer cells in vitro and to carry siRNA into cells effectively. It is potential to be used as a novel prodrug for co-delivery of gene and drug in cancer treatment.</p>