ABSTRACT
Zn and its alloys are increasingly under consideration for biodegradable bone fracture fixation implants owing to their attractive biodegradability and mechanical properties. However, their clinical application is a challenge for osteoporotic bone fracture healing, due to their uneven degradation mode, burst release of zinc ions, and insufficient osteo-promotion and osteo-resorption regulating properties. In this study, a type of Zn2+ coordinated zoledronic acid (ZA) and 1-hydroxyethylidene-1,1-diphosphonic acid (HEDP) metal-organic hybrid nanostick was synthesized, which was further mixed into zinc phosphate (ZnP) solution to mediate the deposition and growth of ZnP to form a well-integrated micro-patterned metal-organic/inorganic hybrid coating on Zn. The coating protected noticeably the Zn substrate from corrosion, in particular reducing its localized occurrence as well as suppressing its Zn2+ release. Moreover, the modified Zn was osteo-compatible and osteo-promotive and, more important, performed osteogenesis in vitro and in vivo of well-balanced pro-osteoblast and anti-osteoclast responses. Such favorable functionalities are related to the nature of its bioactive components, especially the bio-functional ZA and the Zn ions it contains, as well as its unique micro- and nano-scale structure. This strategy provides not only a new avenue for surface modification of biodegradable metals but also sheds light on advanced biomaterials for osteoporotic fracture and other applications. STATEMENT OF SIGNIFICANCE: Developing appropriate biodegradable metallic materials is of clinical relevance for osteoporosis fracture healing, whereas current strategies are short of good balance between the bone formation and resorption. Here, we designed a micropatterned metal-organic nanostick mediated zinc phosphate hybrid coating modified Zn biodegradable metal to fulfill such a balanced osteogenicity. The in vitro assays verified the coated Zn demonstrated outstanding pro-osteoblasts and anti-osteoclasts properties and the coated intramedullary nail promoted fracture healing well in an osteoporotic femur fracture rat model. Our strategy may offer not only a new avenue for surface modification of biodegradable metals but also shed light on better understanding of new advanced biomaterials for orthopedic application among others.
Subject(s)
Osteoporotic Fractures , Rats , Animals , Zoledronic Acid , Osteoporotic Fractures/drug therapy , Osteoporotic Fractures/surgery , Biocompatible Materials/chemistry , Phosphates , Alloys/pharmacology , Alloys/chemistry , Zinc/pharmacology , Absorbable Implants , Corrosion , Materials TestingABSTRACT
The medical applications of porous Mg scaffolds are limited owing to its rapid corrosion, which dramatically decreases the mechanical strength of the scaffold. Mimicking the bone structure and composition can improve the mechanical and biological properties of porous Mg scaffolds. The Mg structure can also be coated with HA by an aqueous precipitation coating method to enhance both the corrosion resistance and the biocompatibility. However, due to the brittleness of HA coating layer, cracks tend to form in the HA coating layer, which may influence the corrosion and biological functionality of the scaffold. Consequently, in this study, hybrid poly(ether imide) (PEI)-SiO2 layers were applied to the HA-coated biomimetic porous Mg to impart the structure with the high corrosion resistance associated with PEI and excellent bioactivity with SiO2. The porosity of the Mg was controlled by adjusting the concentration of the sodium chloride (NaCl) particles used in the fabrication via the space-holder method. The mechanical measurements showed that the compressive strength and stiffness of the biomimetic porous Mg increased as the portion of the dense region increased. In addition, following results show that HA/(PEI-SiO2) hybrid-coated biomimetic Mg is a promising biodegradable scaffold for orthopedic applications. In-vitro testing revealed that the proposed hybrid coating reduced the degradation rate and facilitated osteoblast spreading compared to HA- and HA/PEI-coating scaffolds. Moreover, in-vivo testing with a rabbit femoropatellar groove model showed improved tissue formation, reduced corrosion and degradation, and improved bone formation on the scaffold. STATEMENT OF SIGNIFICANCE: Porous Mg is a promising biodegradable scaffold for orthopedic applications. However, there are limitations in applying porous Mg for an orthopedic biomaterial due to its poor mechanical properties and susceptibility to rapid corrosion. Here, we strategically designed the structure and coating layer of porous Mg to overcome these limitations. First, porous Mg was fabricated by mimicking the bone structure which has a combined structure of dense and porous regions, thus resulting in an enhancement of mechanical properties. Furthermore, the biomimetic porous Mg was coated with HA/(PEI-SiO2) hybrid layer to improve both corrosion resistance and biocompatibility. As the final outcome, with tunable mechanical and biodegradable properties, HA/(PEI-SiO2)-coated biomimetic porous Mg could be a promising candidate material for load-bearing orthopedic applications.
Subject(s)
Biomimetic Materials , Bone Regeneration/drug effects , Bone Substitutes , Coated Materials, Biocompatible , Magnesium , Materials Testing , Animals , Biomimetic Materials/chemistry , Biomimetic Materials/pharmacology , Bone Substitutes/chemistry , Bone Substitutes/pharmacology , Cell Line , Coated Materials, Biocompatible/chemistry , Coated Materials, Biocompatible/pharmacology , Compressive Strength , Corrosion , Magnesium/chemistry , Magnesium/pharmacology , Male , Mice , Osteogenesis/drug effects , Porosity , RabbitsABSTRACT
The durability of denture base resins with a new type of organic-inorganic hybrid coating was examined after long-term water im-mersion.After water immersion for 1 80 days at constant temperature of 37 ℃ the flexural strength and elastic modulus of the samples with the coating were qualified with the national standerds,the controls were not.