Quantitative examination of factors influencing the colour reproduction ability of lithium disilicate glass-ceramics.

BACKGROUND: Effects of ceramic translucency, layer thickness, and substrate colour on the shade of lithium disilicate glass-ceramic restorations proved to be significant in several studies, however, quantitative, numerical results on the relationship between the colour difference and these parameters are still lacking. The purpose of this in vitro study was to quantitatively determine how the colour reproduction ability of a lithium disilicate glass-ceramic is affected by its translucency, layer thickness, and substrate colour. METHODS: Ceramic samples were prepared from A2 shade IPS e.max CAD blocks with high and low translucencies (HT and LT) in a thickness range of 0.5-2.5 mm (+/- 0.05 mm). Layered samples were acquired utilizing composite substrates in 9 shades; transparent try-in paste was used. The spectral reflectance of the specimens was assessed under D65 standard illumination with a Konica Minolta CM-3720d spectrophotometer. The CIEDE2000 colour difference (ΔE00) between two samples was analysed using perceptibility and acceptability thresholds set at 50:50%. Statistical analysis involved linear regression analysis and the Kruskal-Wallis test. RESULTS: An increase in the thickness of 0.5 mm reduced the ΔE00 of the HT samples to 72.8%, and that of the T samples to 71.1% (p < 0.0001). 7 substrates with HT and LT specimens had significantly different results from the mean (p < 0.05). A thickness of 0.5 mm is not sufficient to achieve an acceptable result at any level of translucency, while the low translucency ceramic at a thickness of 1.5 mm gave acceptable results, except for severely discoloured substrates (ND8 and ND9). CONCLUSIONS: The colour reproduction ability of lithium disilicate glass-ceramics is significantly affected by their translucency, layer thickness, and 7 substrates out of 9 substrates examined.

Laboratory study of fracture resistance and failure mode of porcelain laminate veneers with different preparation depths in endodontically treated teeth.

PURPOSE: To compare the fracture resistance and failure mode of porcelain laminate veneers with different preparation depths in endodontically treated teeth. METHODS: Root canal treatment was performed for 40 maxillary central incisors, and then the teeth were divided into four groups (n= 10). The preparation depths were as follows: Group A: 0.9 mm, Group B: 0.6 mm, Group C: 0.3 mm, and in all three groups, 2 mm butt joint incisal reductions were performed; Group D was a control group with no preparation. Then 30 lithium disilicate porcelain veneers were milled by CAD- CAM method and cemented. After that, all specimens were subjected to cyclic loading and thermal cycling and finally were tested by a universal testing machine until failure occurred. RESULTS: The mean failure loads (N) after exposure to continuous load were as follows: Group A: 625.70 (401.45-1037.77), Group B: 780.32 (222.93-1391.82), Group C: 748.81 (239.68-1241.87) and Group D (control) : 509.88 (84.42-1025.85) and P= 0.216. Analysis of failure mode in four groups showed that P= 0.469. There was no significant difference between the control and the other groups. In this study, 0.3, 0.6 and 0.9 mm depths of preparation for porcelain laminate veneers for endodontically treated teeth had no significant difference in fracture resistance and failure mode with non-prepared teeth. CLINICAL SIGNIFICANCE: Reasonable consideration might be given to porcelain laminate veneer treatment for teeth that have become discolored and resistant to bleaching (such as instances where discoloration is severe following root canal treatment). This approach is considered to be on the conservative side, and has demonstrated that a labial preparation depth reduction of up to 0.9 mm does not have any impact on the failure mode or fracture resistance of endodontically-treated teeth.

Full-ceramic resin-bonded fixed dental prostheses: A systematic review.

Despite the development of implant-supported prostheses, there are still patients for whom conservative treatments such as resin-bonded fixed dental prostheses (RBFDPs) are more appropriate. This study's objective was to analyze the available research on full-ceramic RBFDPs. In this study, Web of Science, MEDLINE/PubMed, Scopus, Embase, Cochrane Library, and Google Scholar databases were searched for articles published in English between 2010 and 2020. A total of 14 studies were reviewed based on the eligibility criteria. The results showed that using a cantilever design with one abutment had an advantage over two abutments. Additionally, it was proposed that preparations designed with retentive aids, such as a proximal box, groove, and pinhole, could improve RBFDP survival rates. IPS e.max ZirCAD, In-Ceram alumina, and zirconia CAD/CAM were the most commonly used framework materials. Most studies used air abrasion, salinization, or hydrofluoric acid for surface treatment. Adhesive resin cements were the most frequently used type of cement. The survival rate of In-Ceram ceramics (85.3%-94.8%) was lower than that of In-Ceram zirconia and IPS e.max ZirCAD. Debonding, followed by framework fracture, was the leading cause of failure. Following 3-10 years follow-up, the survival percentage of all-ceramic RBFDPs ranged from 76% to 100%. Although RBFDPs have demonstrated satisfactory success as a conservative treatment, long-term follow-ups and higher sample sizes in clinical research are required to gain more reliable outcomes on the clinical success rate of various RBFDP designs.

Laser debonding of ultrathin occlusal veneers fabricated from different CAD/CAM ceramic materials.

BACKGROUND: Erbium lasers safely offer the possibility of reuse for debonded restorations. Since these lasers have a high affinity for water molecules, they are absorbed by resin cement causing explosive ablation of the cement and thus, the restoration debonds. The efficiency of this process depends on many factors, including the ceramic type, its chemical composition and thickness. Therefore, this study was designed to test the time taken to debond ultrathin occlusal veneers made of three types of milled ceramic materials and evaluate the integrity of these restorations after debonding. METHODS: Three ceramic types were evaluated in this study: lithium disilicate (IPS Emax CAD), highly condensed lithium disilicate (GC initial®LiSi), and translucent zirconia (Katana zirconia STML). Each group consisted of 8 occlusal veneers of 0.5 mm thickness. The samples were cemented to the occlusal surfaces of the upper molar teeth. An Er; Cr: YSGG laser was applied to the occlusal veneers using the scanning method, and time until debonding was calculated. The debonded samples were then inspected under a stereomicroscope for possible damage. Numerical data are presented as the mean with 95% confidence interval (CI), standard deviation (SD), minimum (min.) and maximum (max.) values. Normality and variance homogeneity assumptions were confirmed using Shapiro-Wilk's and Levene's tests, respectively. Data were normally distributed and were analyzed using one-way ANOVA followed by Tukey's post hoc test. The significance level was set at p < 0.05 for all tests. Statistical analysis was performed with R statistical analysis software version 4.3.2 for Windows (R Core Team (2023). R: A language and environment for statistical computing. R Foundation for Statistical Computing, Vienna, Austria. URL https://www.R-project.org/). RESULTS: There was no significant difference in debonding time between the different materials (p = 0.995). The longest debonding time was found for Katana STML (87.52 ± 20.45) (seconds), followed by Emax (86.94 ± 20.63) (seconds), while the lowest value was found for LiSi initial (86.14 ± 25.16) (seconds). In terms of damage to the debonded veneers, The Emax and zirconia samples showed no damage. However, 40% of the LiSi samples fractured during debonding, and 20% exhibited cracks. Only 40% of the LiSi samples were sound after debonding. CONCLUSION: Er; Cr: YSGG laser can be used efficiently to remove ceramic occlusal veneers. However, its effect on LiSi restorations needs further research.

The fracture resistance of pulpotomized primary molars restored with zirconia crowns, lithium disilicate or resin based ceramic endocrowns.

BACKGROUND: Endocrown in pediatric dentistry was rooted in the fundamental principles of preserving healthy dental tissues, leveraging contemporary adhesive methodologies. AIM: This research aimed on assessing and comparing the fracture resistance of pulpotomized primary molars when rehabilitated with zirconia crowns and two distinct types of endocrowns, namely E-Max and Brilliant Crios. METHODS: The study involved thirty, anonymized, freshly extracted second primary molars that underwent pulpotomy. These teeth were then evenly divided into three groups, each consisting of ten specimens: the zirconia crown, the E-Max endocrown, and the Brilliant Crios endocrown groups. Post-pulpotomy, the teeth were prepared for their respective restorations. Subsequent to this preparation, the zirconia crowns, E-Max endocrowns, and Brilliant Crios endocrowns were secured. To evaluate the fracture resistance using a computer-controlled testing machine (Instron), a progressively increasing load was applied to each group until fracture occurred. The gathered data were then analyzed for outliers and subjected to normality testing using the Shapiro-Wilk and/or Kolmogorov-Smirnov tests, with a significance threshold set at 0.05. RESULTS: There was no statistically significant difference in fracture resistance of pulpotomized primary molars among lithium disilicate (E-Max) group (mean=1367.59N), Brilliant Crios group (mean=1349.73N) and zirconia group (mean=1240.82N). CONCLUSION: Endocrowns can be considered a promising restoration for pulpotomized primary molars.

A randomized controlled clinical trial on press and block lithium disilicate partial crowns: A 4-year recall.

PURPOSE: To evaluate clinical performances of two lithium disilicate systems (Initial LiSi press vs Initial LiSi Block, GC Co.) using modified United States Public Health Service (USPHS) evaluation criteria and survival rates after 4 years of clinical service. METHODS: Partial adhesive crowns on natural abutment posterior teeth were made on 60 subjects who were randomly divided into two groups: Group 1: Initial LiSi press and Group 2: Initial LiSi Block. Fabrication of partial crowns was made with full analog and digital procedure in Groups 1 and 2 respectively. The restorations were followed-up for 1 and 4 years, and the modified USPHS evaluation was performed at baseline and each recall together with periodontal evaluation. Contingency tables to assess for significant differences of success over time in each group and time-dependent Cox regression to test for differences between the two groups were used and the level of significance was set at P< 0.05. RESULTS: Regarding modified USPHS scores, all evaluated parameters showed Alpha or Bravo and no Charlie was recorded. No statistically significant difference emerged between the two groups in any of the assessed variables (P> 0.05). No statistically significant difference between scores recorded at the baseline and each recall. All modified USPHS scores were compatible with the outcome of clinical success and no one restoration was replaced or repaired, and the survival rate was 100% after 4 years of clinical service. No difference was found between traditional and digital procedure to fabricate the crowns. The two lithium disilicate materials showed similar results after 4 years of clinical service. CLINICAL SIGNIFICANCE: The crowns made with the two tested lithium disilicate materials with analog and digital procedures showed 100% survival after 4 years of clinical service with no statistically significant difference using the modified USPHS scores.

Long-term performance of ceramic in/-onlays vs. cast gold partial crowns - a retrospective clinical study.

OBJECTIVES: To assess the long-term clinical performance of ceramic in-/onlays (CIOs) and cast gold partial crowns (CGPCs) in posterior teeth in terms of success, survival, complications (biological, technical) and quality. MATERIAL AND METHODS: In a retrospective study, a total of 325 patients were recorded after up to 24.8 years (mean 13.9 ± 3.8 years) having (pre-)molars restored with CIO (Empress I, Ivoclar Vivadent, n = 161) and CGPC (Degunorm, DeguDent, n = 164) by supervised undergraduate students. A total of 296 restorations were assessed clinically and radiologically in healthy and endodontically treated teeth using modified United States Public Health Service (USPHS) criteria. Cumulative success and survival rates of the restorations were calculated using Kaplan-Meier estimates. Biological and technical complications were recorded. Status of oral health comprising caries risk and localized periodontitis were assessed. RESULTS: The cumulative success rates of CIOs were 92.1% and of CGPCs 84.2% after mean service times of 14.5 years. The annual failure rates of total service times were 0.5% in teeth restored with CIO (n = 155) and 0.7% in teeth restored with CGPC (n = 163). The cumulative survival rates of CIOs were 93.9% after a mean service time of 15.2 years and decreased to 91.7% after 23.5 years. The cumulative survival rates of CGPCs were 92.6% after a mean service time of 14.9 years and 91.8% after 23.5 years. Complications in CIOs (n = 149) were ceramic fracture (6.7%), secondary caries (4.7%), endodontic complication (2.7%) and tooth fracture (1.3%) compared to CGPCs (n = 147) with endodontic complication (8.8%), secondary caries (4.8%) and decementation (2.0%). Endodontically treated teeth restored with CIO or CGPC revealed significantly less often success compared with corresponding vital teeth (p = .02). CIOs and CGPCs revealed clinically and radiographically good and excellent qualities with 71.8% (107/149) and 68% (100/147) without any significant differences regarding type of restoration. CONCLUSIONS: Both CIOs and CGPCs achieved high survival rates up to 24.8 years when performed by supervised undergraduate students. The longevity of the restorations may benefit from the intraoral repair of accessible defects and, in case of pulp infection or necrosis, an adequate endodontic management. CLINICAL RELEVANCE: CIOs and CGPCs made by supervised undergraduate students are proper restoration types in posterior teeth in the long-term. An adequate preparation design, meticulous care in the inserting technique and constant biofilm removal due to proper oral hygiene combined with professional maintenance care are substantial. The clinical long-term performance was mostly limited by ceramic fractures in CIOs and endodontic complications in CGPCs.

Static and dynamic stress analysis of different crown materials on a titanium base abutment in an implant-supported single crown: a 3D finite element analysis.

BACKGROUND: This Finite Element Analysis was conducted to analyze the biomechanical behaviors of titanium base abutments and several crown materials with respect to fatigue lifetime and stress distribution in implants and prosthetic components. METHODS: Five distinct designs of implant-supported single crowns were modeled, including a polyetheretherketone (PEEK), polymer-infiltrated ceramic network, monolithic lithium disilicate, and precrystallized and crystallized zirconia-reinforced lithium silicates supported by a titanium base abutment. For the static load, a 100 N oblique load was applied to the buccal incline of the palatal cusp of the maxillary right first premolar. The dynamic load was applied in the same way as in static loading with a frequency of 1 Hz. The principal stresses in the peripheral bone as well as the von Mises stresses and fatigue strength of the implants, abutments, prosthetic screws, and crowns were assessed. RESULTS: All of the models had comparable von Mises stress values from the implants and abutments, as well as comparable maximum and minimum principal stress values from the cortical and trabecular bones. The PEEK crown showed the lowest stress (46.89 MPa) in the cervical region. The prosthetic screws and implants exhibited the highest von Mises stress among the models. The lithium disilicate crown model had approximately 9.5 times more cycles to fatique values for implants and 1.7 times more cycles to fatique values for abutments than for the lowest ones. CONCLUSIONS: With the promise of at least ten years of clinical success and favorable stress distributions in implants and prosthetic components, clinicians can suggest using an implant-supported lithium disilicate crown with a titanium base abutment.

Adhesive Cementation of CAD/CAM Silica-based Ceramics: Effect of Adhesive Type and Long-term Aging on the Bond Strength to Composite Cement.

PURPOSE: To investigate the effect of adhesive type and long-term aging on the shear bond strength (SBS) between silica-based ceramics and composite cement (CC). MATERIALS AND METHODS: Lithium-silicate (LS), feldspathic (FD) and polymer-infiltrated ceramic (PIC) blocks were sectioned (10 x 12 x 2 mm) and divided into 24 groups considering the factors: "ceramics" (LS, FD, and PIC), "adhesive" (Ctrl: without adhesive; 2SC: 2-step conventional; 3SC: 3-step conventional; 1SU: 1-step universal), and "aging" (non-aged or aged [A]). After the surface treatments, CC cylinders (n = 15, Ø = 2 mm; height = 2 mm) were made and half of the samples were subjected to thermocycling (10,000) and stored in water at 37°C for 18 months. The samples were submitted to SBS testing (100 kgf, 1 mm/min) and failure analysis. Extra samples were prepared for microscopic analysis of the adhesive interface. SBS (MPa) data was analyzed by 3-way ANOVA and Tukey's test (5%). Weibull analysis was performed on the SBS data. RESULTS: All factors and interactions were significant for SBS (p<0.05). Before aging, there was no significant difference between the tested groups and the respective control groups. After aging, the LS_1SU (22.18 ± 7.74) and LS_2SC (17.32 ± 5.86) groups exhibited significantly lower SBS than did the LS_Ctrl (30.30 ± 6.11). Only the LS_1SU group showed a significant decrease in SBS after aging vs without aging. The LS_1SU (12.20) group showed the highest Weibull modulus, which was significantly higher than LS_2SC_A (2.82) and LS_1SU_A (3.15) groups. CONCLUSION: No type of adhesive applied after silane benefitted the long-term adhesion of silica-based ceramics to CC in comparison to the groups without adhesive.

Bonding of Composite Cements Containing 10-MDP to Zirconia Ceramics Without Dedicated Ceramic Primer.

PURPOSE: To measure zirconia-to-zirconia microtensile bond strength (µTBS) using composite cements with and without primer. MATERIALS AND METHODS: Two Initial Zirconia UHT (GC) sticks (1.8x1.8x5.0 mm) were bonded using four cements with and without their respective manufacturer's primer/adhesive (G-CEM ONE [GOne] and G-Multi Primer, GC; Panavia V5 [Pv5]), and Panavia SA Cement Universal [PSAu], and Clearfil Ceramic Plus, Kuraray Noritake; RelyX Universal (RXu) and Scotchbond Universal Plus [SBUp], 3M Oral Care). Specimens were trimmed to an hour-glass shaped specimen whose isthmus is circular in cross-section. After 1-week water storage, the specimens were either tested immediately (1-week µTBS) or first subjected to 50,000 thermocycles (50kTC-aged µTBS). The fracture mode was categorized as either adhesive interfacial failure, cohesive failure in composite cement, or mixed failure, followed by SEM fracture analysis of selected specimens. Data were analyzed using linear mixed-effects statistics (α = 0.05; variables: composite cement, primer/adhesive application, aging). RESULTS: The statistical analysis revealed no significant differences with aging (p = 0.3662). No significant difference in µTBS with/without primer and aging was recorded for GOne and PSAu. A significantly higher µTBS was recorded for Pv5 and RXu when applied with their respective primer/adhesive. Comparing the four composite cements when they were applied in the manner that resulted in their best performance, a significant difference in 50kTC-aged µTBS was found for PSAu compared to Pv5 and RXu. A significant decrease in µTBS upon 50kTC aging was only recorded for RXu in combination with SBUp. CONCLUSION: Adequate bonding to zirconia requires the functional monomer 10-MDP either contained in the composite cement, in which case a separate 10-MDP primer is no longer needed, or in the separately applied primer/adhesive.

Fabrication trueness and internal fit of different lithium disilicate ceramics according to post-milling firing and material type.

OBJECTIVES: To evaluate whether post-milling firing and material type affect the fabrication trueness and internal fit of lithium disilicate crowns. METHODS: A prefabricated cobalt chromium abutment was digitized to design a mandibular right first molar crown. This design file was used to fabricate crowns from different lithium disilicate ceramics (nano-lithium disilicate (AM), fully crystallized lithium disilicate (IN), advanced lithium disilicate (TS), and lithium disilicate (EX)) (n = 10). Crowns, the abutment, and the crowns when seated on the abutment were digitized by using an intraoral scanner. Fabrication trueness was assessed by using the root mean square method, while the internal fit was evaluated according to the triple scan method. These processes were repeated after the post-milling firing of AM, TS, and EX. Paired samples t-tests were used to analyze the effect of post-milling firing within AM, TS, and EX, while all materials were compared with 1-way analysis of variance and Tukey HSD tests (α = 0.05). RESULTS: Post-milling firing reduced the surface deviations and internal gap of AM and EX (P ≤ 0.014). AM mostly had higher deviations and internal gaps than other materials (P ≤ 0.030). CONCLUSIONS: Post-milling firing increased the trueness and internal fit of tested nano-lithium disilicate and lithium disilicate ceramics. Nano-lithium disilicate mostly had lower trueness and higher internal gap; however, the maximum meaningful differences among tested materials were small. Therefore, the adjustment duration and clinical fit of tested crowns may be similar. CLINICAL SIGNIFICANCE: Tested lithium disilicate ceramics may be suitable alternatives to one another in terms of fabrication trueness and internal fit, considering the small differences in measured deviations and internal gaps.

Evaluation of bond strength between zirconia milled ceramic material and veneered dental porcelain.

This study aimed at examining the bond strength between zirconia and ceramic veneer, following the ISO 9693 guidelines. A total of fifty specimens of zirconia/ceramic-veneer system were produced using two commercial zirconias (VITA YZ-HTWhite and Zolid HT+ White, referred to as Group A and Group B, respectively) and a ceramic-veneering material (Zirkonia 750). The microstructure (via x-ray diffraction analysis, XRD and Secondary Electron mode, SEM) and the mechanical properties (via 3-point bending tests) of the two groups were assessed. Then, experiments were conducted according to the ISO 9693 and conventional protocols applied for producing zirconia/ceramic-veneer restorations. Bond strength values, measured by 3-point bending tests, were 34.42 ± 7.60 MPa for Group A and 31.92 ± 6.95 MPa for Group B. SEM observations of the cohesively fractured surfaces (on the porcelain side) and the examination for normality using the Shapiro-Wilk test suggested the use of Weibull statistical analysis. Median strength (σ50%) for Group A and Group B was 34.76 and 32.22 MPa, while the characteristic strength (σ63.2%) was 35.78 and 33.14 MPa, respectively. The Weibull modulus disparity between groups (12.69 and 13.07) was not significant. Bond strength exceeded the ISO 9693 minimum of 20 MPa, suggesting satisfactory strength for clinical use.

Biomechanical reinforcement by CAD-CAM materials affects stress distributions of posterior composite bridges: 3D finite element analysis.

OBJECTIVES: This 3D finite element analysis study aimed to investigate the effect of reinforcing CAD-CAM bars on stress distribution in various components of a posterior composite bridge. METHODS: A virtual model mimicking the absence of an upper second premolar was created, featuring class II cavity preparations on the proximal surfaces of the adjacent abutment teeth surrounding the edentulous space. Five distinct finite element analysis (FEA) models were generated, each representing a CAD-CAM reinforcing bar material: 3-YTZP (IPS. emax ZirCAD MO; Zr), lithium disilicate (IPS e.max CAD; EX), nano-hybrid resin composite (Grandio Blocs; GB), Fibre-reinforced composite (Trilor; Tri), and polyetheretherketone (PEEK). A veneering resin composite was employed to simulate the replacement of the missing premolar (pontic). In the FEA, an axial force of 600 N and a transverse load of 20 N were applied at the center of the pontic. Subsequently, maximum von Mises (mvM) and maximum principal stresses (σmax) were computed across various components of the generated models. Additionally, shear stresses at the interface between the CAD-CAM bars and the veneering resin composite were determined. RESULTS: CAD-CAM materials with high modulus of elasticity, such as Zr and EX, exhibited the highest mvM stresses and shear stresses while transferring the lowest stress to the veneering resin composite in comparison to other materials. Conversely, PEEK demonstrated the lowest mvM stresses but produced the highest stresses within the veneering resin composite. There was a uniform distribution of mvM stresses in the remaining tooth structure among all groups, except for a noticeable elevation in the molar region of Zr and EX groups. SIGNIFICANCE: Reinforcing CAD-CAM bar materials with a high modulus of elasticity, such as Zr and EX, may result in debonding failures at the connector sites of posterior composite bridges. Conversely, GB, PEEK, and Tri have the potential to cause fracture failures at the connectors rather than debonding.

Fracture characteristics and translucency of multilayer monolithic zirconia crowns of various thicknesses.

OBJECTIVES: Multilayer monolithic zirconia (M-Zr) crowns can be engineered to achieve gradational translucency and color intensity. However, this modification may compromise the mechanical strength, raising concerns regarding the ability of M-Zr crowns to withstand occlusal stresses. The effects of M-Zr crown thickness on translucency and ability to endure occlusal forces were investigated at different tooth positions (incisors, premolars, and molars). The objective was to determine the minimal thickness of M-Zr crowns used in tooth preparation to meet aesthetic and functional demands. METHODS: M-Zr samples (Vita A1) with four thicknesses (0.5, 1.0, 1.5, and 2.0 mm) were prepared and subjected to translucency testing using a digital colorimeter by 3-third and 9-square division methods. Crown-shaped M-Zr samples with three thicknesses (1.0, 1.5, and 2.0 mm) and three tooth positions (incisor, premolar, and molar) were digitally designed, and 2.0 mm metal abutments were fabricated. The samples were bonded to the abutments; their fracture characteristics were evaluated using a universal testing machine, and their fracture surfaces examined using an optical microscope. Statistical analyses included the Shapiro-Wilk test, Pearson correlation, and one-way and two-way ANOVA with a post hoc Tukey HSD test (α = 0.05). RESULTS: Color analysis results revealed a significant negative correlation between thickness and translucency (r < -0.96, P < 0.01), with the highest values in the incisal region. Cross-sectional profiles confirmed the uniform thickness and morphology of the digitally designed M-Zr crowns. The results of fracture strength analysis showed position-dependent variability, a strong positive correlation with thickness (r > 0.96, P < 0.01), and fracture strengths consistently exceeding 1200 N across all tooth positions. Fracture patterns indicated that thinner crowns at the incisors and molars were more prone to cracking, whereas those at the premolars demonstrated significantly higher strength (4872.51 N, P < 0.05), only with crack or even no fracture occurring at 2.0 mm. CONCLUSIONS: Thickness significantly influenced both the translucency and fracture strength of M-Zr, with the tooth position playing an additional role, albeit to a lesser extent. Although thinner crowns exhibited lower strength at each tooth position, even at a thickness of 1.0 mm, fracture strength exceeding 1200 N was maintained, surpassing the typical occlusal forces. Thus, it can be asserted that M-Zr crowns with a minimum thickness of 1.0 mm can meet both aesthetic and functional requirements.

Influence of resin-coating techniques on the marginal adaptation and the bond strengths of CAD/CAM-fabricated hybrid ceramic inlays.

This study aimed to evaluate the effects of different resin-coating technique strategies and dual-cure resin luting materials on proximal marginal adaptation and the microtensile bond strengths (µTBSs) of CAD/CAM hybrid ceramic inlays. Extracted human molars were classified into four groups, depending on the coating technique: No coating (None), single coating (1-coating), double coating (2-coating), and flowable resin-coating (Combination). The inlays were bonded with one of the three materials: Panavia V5 (V5), Rely X Ultimate (RXU), and Calibra Ceram (CC). The differences with regard to adaptation were not significant. In the case of µTBS data for V5, no significant differences were observed, whereas for RXU, µTBS values for Combination statistically exceeded those for None and 1-coating. For CC, µTBS values for Combination statistically exceeded those for None, 1-coating, and 2-coating. The coating techniques did not influence the adaptation but influenced the bond strength, and Combination performed the best.

Glass science behind lithium silicate glass-ceramics.

OBJECTIVES: Lithium silicate-based glass ceramics have evolved as a paramount restorative material in restorative and prosthetic dentistry, exhibiting outstanding esthetic and mechanical performance. Along with subtractive machining techniques, this material class has conquered the market and satisfied the patients' needs for a long-lasting, excellent, and metal-free alternative for single tooth replacements and even smaller bridgework. Despite the popularity, not much is known about the material chemistry, microstructure and terminal behaviour. METHODS: This article combines a set of own experimental data with extensive review of data from literature and other resources. Starting at manufacturer claims on unique selling propositions, properties, and microstructural features, the aim is to validate those claims, based on glass science. Deep knowledge is mandatory for understanding the microstructure evolution during the glass ceramic process. RESULTS: Fundamental glass characteristics have been addressed, leading to formation of time-temperature-transformation (TTT) diagrams, which are the basis for kinetic description of the glass ceramic process. Nucleation and crystallization kinetics are outlined in this contribution as well as analytical methods to describe the crystalline fraction and composition qualitatively and quantitatively. In relation to microstructure, the mechanical performance of lithium silicate-based glass ceramics has been investigated with focus on fracture strength versus fracture toughness as relevant clinical predictors. CONCLUSION: Fracture toughness has been found to be a stronger link to initially outlined manufacturer claims, and to more precisely match ISO recommendations for clinical indications.

Influence of Varied Silane Commercial Brands and Adhesive Application on Bond Strength and Stability to Lithium Disilicate Glass Ceramic.

OBJECTIVES: This study aimed to evaluate the impact of various commercial silane brands with varied chemical compositions with or without the application of an adhesive layer on the microshear bond strength and durability of a resin luting agent to lithium disilicate glass ceramic. METHODS AND MATERIALS: Lithium disilicate glass ceramic discs (EMX, IPS e.max Press, Ivoclar Vivadent) measuring 10 mm in diameter and 3 mm in thickness were fabricated (n=240). Surfaces were etched using 5% hydrofluoric acid and randomly assigned to 10 groups based on the commercial brand of silane used (n=24): [RP] RelyX Ceramic Primer (3M ESPE); [PS] Prosil (FGM); [SA] Silano (Angelus); [SM] Silano (Maquira); [SU] Silane (Ultradent); [GL] GLUMA Ceramic Primer (Kulzer); [CB] Ceramic Bond (VOCO); [MB] Monobond N (Ivoclar Vivadent); [CP] Clearfil Ceramic Primer (Kuraray); and [DE] 2-step silane (Dentsply Sirona). Half of the EMXs (n=12) received a thin adhesive layer (+) after the silane and prior to resin luting agent, while the other half (n=12) did not receive an adhesive layer (-). For the microshear bond strength test (µSBS), four light-cured resin luting agent cylinders (1 mm in diameter) were created on each EMX surface. Half of these specimens were tested after 24 hours, while the other half were stored in deionized water for 6 months. The µSBS test was conducted using a universal testing machine (DL 500, EMIC) at a crosshead speed of 1 mm/min until failure. The obtained data underwent statistical analysis using analysis of variance (ANOVA) and the Tukey test (α=0.05). RESULTS: There was significant influence of the silane commercial brand on bond strength. Notably, "universal primers" yielded lower bond strength results compared to "pure" silane solutions. Water storage had a detrimental effect on microshear bond strength for certain silane commercial brands. Additionally, the application of an adhesive layer negatively impacted bond strength results for all silanes. CONCLUSIONS: This study confirms the importance of both silane commercial brand and chemical composition in relation to bond strength of resin luting agents to lithium disilicate glass ceramic. Furthermore, the application of an adhesive layer may have an adverse effect on bond stability over time.

A comparative evaluation of the variations on the shades of pressable ceramic system with the layering technique after different number of firing cycles: An in vitro study.

AIM: The main aim of the present study was to compare and evaluate the effect of repetitive firings on different shades of a pressable all ceramic system layered with veneering porcelain. SETTING AND DESIGN: In-vitro comparative study. MATERIALS AND METHODS: An in vitro comparative study was conducted, and a total of 60 disc shaped specimens (15 mm in diameter and 0.8 mm in thickness) were made of heat pressed ceramic of shades A2, A3, and B2 (20 discs of each shade) grouped as Group I, II, and III, respectively, using the lost wax technique. The discs were subsequently layered with veneering porcelain followed by glazing and overglazing and underwent a firing cycle at each step until six times combined. CIE L*a*b* measurements were noted on each sample after the third, fourth, fifth, and sixth firing using VITA Easyshade Advance 4.0 spectrophotometer. STATISTICAL ANALYSIS USED: Statistical Analysis was done by SPSS 17.0 software. One way analysis of variance, multiple comparisons using the Tukey test, and descriptive statistical analysis were done for all the groups in the study. P <0.05 was statistically significant. RESULTS: The mean color differences for the repeated firings were imperceptible (ΔE <1.67) to the human eye for all ceramic samples tested except between the fourth and fifth firing of Group II (shade A3). CONCLUSION: The analysis revealed that although repeated firings lead to changes in L*, a*, and b* values, the mean color difference was below the clinically acceptable color change (ΔE <3.7).

How do different intraoral scanners and milling machines affect the fit and fatigue behavior of lithium disilicate and resin composite endocrowns?

The aim of this in vitro study was to evaluate the effect of the combinations of two different intraoral scanners (IOS), two milling machines, and two restorative materials on the marginal/internal fit and fatigue behavior of endocrowns produced by CAD-CAM. Eight groups (n= 10) were considered through the combination of TRIOS 3 (TR) or Primescan (PS) IOS; 4-axes (CR; CEREC MC XL) or 5-axes (PM; PrograMill PM7) milling machines; and lithium disilicate (LD; IPS e.max CAD) or resin composite (RC; Tetric CAD) restorative materials. Specific surface treatments were applied to each material, and the bonding to its corresponding Endocrown-shaped fiberglass-reinforced epoxy resin preparations was performed (Variolink Esthetic DC). Computed microtomography (µCT) was performed to assess the marginal/internal fit, as well as a mechanical fatigue test (20 Hz, initial load = 100 N/5000 cycles; step-size = 50 N/10,000 cycles until a threshold of 1500 N, then, the step-size was increased if needed to 100 N/10,000 cycles until failure or a threshold of 2800 N) to evaluate the restorations long-term behavior. Complementary analysis of the fracture features and surface topography in scanning electron microscopy was performed. Three-way ANOVA and Kaplan-Meier test (α = 0.05) were performed for marginal/internal fit, and fatigue behavior data, respectively. PS scanner, CR milling machine, and RC endocrowns resulted in a better marginal fit compared to their counterparts. Still, the PM machine resulted in a better pulpal space fit compared to the CR milling machine. Regardless of the scanner and milling machine, RC endocrowns exhibited superior fatigue behavior than LD ones. LD endocrowns presented margin chipping regardless of the milling machine used. Despite minor differences in terms of fit, the 'IOS' and 'milling machine' factors did not impair the fatigue behavior of endocrowns. Resin-composite restorations resulted in a higher survival rate compared to glass-ceramic ones, independently of the digital devices used in the workflow.

Influence of attaching mechanical retentive devices onto frameworks on fracture resistance of implant-supported zirconia crowns.

This study investigated the fracture load of implant-supported zirconia crowns (IZCs), in which indirect composite resin or feldspathic porcelain was layered onto zirconia frameworks with mechanical retentive devices. Three different zirconia frameworks were assessed: attaching mechanical retentive devices on glaze and opaque porcelain materials (GL and OP groups, respectively), and no attaching mechanical retentive devices (ND group). The frameworks were layered using feldspathic porcelain (FP veneer) and indirect composite resin (IC veneer). Fracture load of the specimens was measured. In FP veneer, the GL group recorded the highest fracture load. In the IC veneer, the GL and OP groups had significantly higher fracture load than the ND group. The fracture resistance of IZCs can be enhanced by applying glaze material before attaching mechanical retentive devices for porcelain layering. The mechanical retentive devices effectively yielded mechanical interlocking between the zirconia frameworks and the IC veneer in GL and OP groups.