Development and biomechanical analysis of an axially controlled compression spinal rod for lumbar spondylolysis.

BACKGROUND: To elucidate the differences in mechanical performance between a novel axially controlled compression spinal rod (ACCSR) for lumbar spondylolysis (LS) and the common spinal rod (CSR). METHODS: A total of 36 ACCSRs and 36 CSRs from the same batch were used in this study, each with a diameter of 6.0 mm. Biomechanical tests were carried out on spinal rods for the ACCSR group and on pedicle screw-rod internal fixation systems for the CSR group. The spinal rod tests were conducted following the guidelines outlined in the American Society for Testing and Materials (ASTM) F 2193, while the pedicle screw-rod internal fixation system tests adhered to ASTM F 1798-97 standards. RESULTS: The stiffness of ACCSR and CSR was 1559.15 ±â€…50.15 and 3788.86 ±â€…156.45 N/mm (P < .001). ACCSR's yield load was 1345.73 (1297.90-1359.97) N, whereas CSR's was 4046.83 (3805.8-4072.53) N (P = .002). ACCSR's load in the 2.5 millionth cycle of the fatigue four-point bending test was 320 N. The axial gripping capacity of ACCSR and CSR was 1632.53 ±â€…165.64 and 1273.62 ±â€…205.63 N (P = .004). ACCSR's torsional gripping capacity was 3.45 (3.23-3.47) Nm, while CSR's was 3.27 (3.07-3.59) Nm (P = .654). The stiffness of the pedicle screws of the ACCSR and CSR group was 783.83 (775.67-798.94) and 773.14 (758.70-783.62) N/mm (P = .085). The yield loads on the pedicle screws of the ACCSR and CSR group was 1345.73 (1297.90-1359.97) and 4046.83 (3805.8-4072.53) N (P = .099). CONCLUSION: Although ACCSR exhibited lower yield load, stiffness, and fatigue resistance compared to CSR, it demonstrated significantly higher axial gripping capacity and met the stress requirement of the human isthmus. Consequently, ACCSR presents a promising alternative to CSR for LS remediation.

Impact of the preservation media on ex vivo bone samples for full field mechanical testing.

The preservation method to store bone tissue for posterior analysis is a widespread practice. However, the method's potential influence on the material's mechanical properties is often overlooked during single-point experimentation. Saline and formaldehyde solutions are the most common among the employed preservation media. A full field analysis of the mice femoral bone deformation using non-destructive optical techniques is conducted to assess the influence of the storage media on the viscoelastic properties of the tissue. Three different groups are subjected to a standard three-point bending test. The first group is the control, with fresh post-mortem samples. The second and third groups used saline and formaldehyde solutions, respectively. During the mechanical test, the bone's surface and internal deformation are monitored simultaneously using digital holographic interferometry and Fourier-domain optical coherence tomography. A mechanical comparison among the three groups is presented. The results show that after 48 h of immersion in saline solution, the mice bones keep their viscoelastic behavior similar to fresh bones. Meanwhile, 48 h in formaldehyde modifies the response and affects the marrow structure. The high sensitivity of the optical phase also makes it possible to observe changes in the anisotropy of the samples. As a comparison, Raman spectroscopy analyzes the three bone groups to prove that the preservation media does not affect a single-point inspection.

Sensitivity of cartilage mechanical behaviour to spatial variations in material properties.

Articular cartilage tissue exhibits a spatial dependence in material properties that govern mechanical behaviour. A mathematical model of cartilage tissue under one dimensional confined compression testing is developed for normal tissue that takes account of these variations in material properties. Modifications to the model representative of a selection of mechanisms driving osteoarthritic cartilage are proposed, allowing application of the model to both physiological and pathophysiological, osteoarthritic tissue. Incorporating spatial variations into the model requires the specification of more parameters than are required in the absence of these variations. A global sensitivity analysis of these parameters is implemented to identify the dominant mechanisms of mechanical response, in normal and osteoarthritic cartilage tissue, to both static and dynamic loading. The most sensitive parameters differ between dynamic and static mechanics of the cartilage, and also differ between physiological and osteoarthritic pathophysiological cartilage. As a consequence changes in cartilage mechanics in response to alterations in cartilage structure are predicted to be contingent on the nature of loading and the health, or otherwise, of the cartilage. In particular the mechanical response of cartilage, especially deformation, is predicted to be much more sensitive to cartilage stiffness in the superficial zone given the onset of osteoarthritic changes to material properties, such as superficial zone increases in permeability and reductions in fixed charge. In turn this indicates that any degenerative changes in the stiffness associated with the superficial cartilage collagen mesh are amplified if other elements of osteoarthritic disease are present, which provides a suggested mechanism-based explanation for observations that the range of mechanical parameters representative of normal and osteoarthritic tissue can overlap substantially.

Influence of surface finishing on the outcome of a 3-point bending test in polymer-based dental composits assessed by qualitative and quantitative fractography.

OBJECTIVES: The aim of the study was to evaluate the influence of surface finishing in three polymer-based composits (composits) on the result of a 3-point bending test using quantitative and qualitative fractography as well as microstructural characteristics. MATERIALS AND METHODS: 270 rectangular specimens (n = 30) of three composits were prepared, stored and tested according to NIST No. 4877. Prior testing, the samples were subjected to three surface treatments: 1) no treatment, to preserve the oxygen inhibition layer, 2) with FEPA P1200 (ANSI equivalent grit 600) SiC paper abraded surface, and 3) polished surface. A three-point bending testing was employed, followed by quantitative (assessment of reason for failure and fracture pattern) and qualitative (fracture mirror measurements) fractography, 3D and 2D surface imaging, surface roughness, reliability and Fe-SEM analysis. The mirror radius that runs in the direction of constant stress was used to calculate the mirror constant (A) using Orr's equation. Uni- and multifactorial ANOVA, Tukey's post hoc test, and Weibull analysis was performed for statistical analysis. RESULTS: Surface finishing has less influence on the fracture pattern, reliability and mechanical parameters and has no influence on the mirror constant. The amount of inorganic filler has a direct impact on flexural strength and modulus, while the ranking of materials was independent of surface treatment. Failures initiated by volume defects were the most common failure mode (77.0%) with surface defects accounting for 14.9% (edge) and 7.7% (corner). Polishing resulted in lower peak-to valley height compared to no treatment, both 3-4 times lower compared to the 600 grit treatment. The increase in roughness within the analyzed range did not lead to an increase in surface-related failures. CONCLUSIONS: The clear dominance of volume defects in all examined materials as a cause of material fracture reduces the impact of roughness on the measured properties. This insight was only possible using qualitative and quantitative research fractography.

Passive mechanical properties of adipose tissue and skeletal muscle from C57BL/6J mice.

Skeletal muscle and adipose tissue are characterized by unique structural features finely tuned to meet specific functional demands. In this study, we investigated the passive mechanical properties of soleus (SOL), extensor digitorum longus (EDL) and diaphragm (DIA) muscles, as well as subcutaneous (SAT), visceral (VAT) and brown (BAT) adipose tissues from 13 C57BL/6J mice. Thereto, alongside stress-relaxation assessments we subjected isolated muscles and adipose tissues (ATs) to force-extension tests up to 10% and 30% of their optimal length, respectively. Peak passive stress was highest in the DIA, followed by the SOL and lowest in the EDL (p < 0.05). SOL displayed also the highest Young's modulus and hysteresis among muscles (p < 0.05). BAT demonstrated highest peak passive stress and Young's modulus followed by VAT (p < 0.05), while SAT showed the highest hysteresis (p < 0.05). When comparing data across all six biological specimens at fixed passive force intervals (i.e., 20-40 and 50-70 mN), skeletal muscles exhibited significantly higher peak stresses and strains than ATs (p < 0.05). Young's modulus was higher in skeletal muscles than in ATs (p < 0.05). Muscle specimens exhibited slower force relaxation in the first phase compared to ATs (p < 0.05), while there was no significant difference in behavior between muscles and AT in the second phase of relaxation. The study revealed distinctive mechanical behaviors specific to different tissues, and even between different muscles and ATs. These variations in mechanical properties are likely such to optimize the specific functions performed by each biological tissue.

Self-organising maps in the analysis of strains of human abdominal wall to identify areas of similar mechanical behaviour.

The study refers to the application of a type of artificial neural network called the Self-Organising Map (SOM) for the identification of areas of the human abdominal wall that behave in a similar mechanical way. The research is based on data acquired during in vivo tests using the digital image correlation technique (DIC). The mechanical behaviour of the human abdominal wall is analysed during changing intra-abdominal pressure. SOM allow to study simultaneously three variables in four time/load steps. The variables refer to the principal strains and their directions. SOM classifies all the abdominal surface data points into clusters that behave similarly in accordance with the 12 variables. The analysis of the clusters provides a better insight into abdominal wall deformation and its evolution under pressure than when observing a single mechanical variable. The presented results may provide a better understanding of the mechanics of the living human abdominal wall. It might be particularly useful when selecting proper implants as well as for the design of surgical meshes for the treatment of abdominal hernias, which would be mechanically compatible with identified regions of the human anterior abdominal wall, and possibly open the way for patient-specific solutions.

Effects of post-curing duration on the mechanical properties of complex 3D printed geometrical parts.

This study aims to assess the efficacy of post-curing guidance supplied by 3D printing resin manufacturers. Current guidance applies generically to all geometries with the caveat that post-curing should be extended for 'large' or 'complex' geometries but specific guidance is not provided. Two vat-polymerisation 3D printers (Form3B, Figure 4 Standalone) were used to print test models in 6 biocompatible resins (Pro Black, Med White, Med Amber, Biomed Black, Biomed White, Biomed Amber). The test model is of a complex geometry whilst also housing ISO 527 test specimens in concentric layers. Two separate intervals of curing were applied (100%, 500% stated guidance) creating different curing treatments of the specimens throughout the model. Post processed test models were disassembled and pull testing performed on each of the specimens to assess the mechanical properties. The analysis showed that extending the curing duration had significant effects on the mechanical properties of some materials but not all. The layers of the model had a significant effect except for elongation at break for the Med Amber material. This research demonstrates that generic post-curing guidance regarding UV exposures is not sufficient to achieve homogenous material strength properties for complex geometries. Large variations in mechanical properties throughout the models suggest some material was not fully-cured. This raises a query if such materials as originally marketed as biocompatible are fully cured and therefore safe to use for medical applications involving complex geometries.

Comparison of stress distribution in fully porous and dense-core porous scaffolds in dental implantation.

The aim of this study is to compare the stress distribution in porous scaffolds with different structures with similar geometric parameters to study a new approach in dental implantation. Three-dimensional finite element models of the fully porous and dense-core porous scaffolds with defined porosity parameters including space diameter and thickness with two porosity patterns were embedded in the jaw bone model with cortical and cancellous bone. The cylindrical shape was considered as the main shape of the scaffolds. To evaluate the mechanical performance, the Von Mises stress was compared in the models under static and dynamic masticatory loading. Incidentally, to validate the modeling results, experimental strain gauge tests were performed on four specimens fabricated from Ti6Al4V. Finally, the stress distribution in the models was compared with the results of previous studies on commercial implants. The results of the finite element analysis show that there are considerable differences in the magnitude of the equivalent stress in the models in static and dynamic phases. Also, changes in the defined geometric parameters have significant effects on the stress distribution in terms of Von Mises stress in the overall models. The experimental results indicated good agreement with those of the modeling. It can be concluded that some porous structures with optimal geometries can be proposed as a new structure for dental implants. However, considering the physiology of bone when confronted with porous structures, further studies such as in vivo experiments are needed in this field.

Biomechanical considerations of semi-anatomic glass fiber-reinforced (GFRC) composite implant for mandibular segmental defects: A technical note.

OBJECTIVES: The aim of this study was to investigate the selected biomechanical properties of semi-anatomic implant plate made of biostable glass fiber-reinforced composite (GFRC) for mandibular reconstruction. Two versions of GFRC plates were tested in vitro loading conditions of a mandible segmental defect model, for determining the level of mechanical stress at the location of fixation screws, and in the body of the plate. METHODS: GFRC of bidirectional S3-glass fiber weaves with dimethacrylate resin matrix were used to fabricate semi-anatomic reconstruction plates of two GFRC laminate thicknesses. Lateral surface of the plate followed the contour of the resected part of the bone, and the medial surface was concave allowing for placement of a microvascular bone flap in the next stages of the research. Plates were fixed with screws to a plastic model of the mandible with a large segmental defect in the premolar-molar region. The mandible-plate system was loaded from incisal and molar locations with loads of 10, 50, and 100 N and stress (microstrain, µÎµ) at the location of fixation screws and the body of the plate was measured by strain gauges. In total the test set-up had four areas for measuring the stress of the plate. RESULTS: No signs of fractures or buckling failures of the plates were found during loading. Strain values at the region of the fixation screws were higher with thick plate, whereas thin plates demonstrated higher strain at the body of the plate. Vertical displacement of the mandible-plate system was proportional to the loading force and was higher with incisal than molar loading locations but no difference was found between thin and thick plates. CONCLUSION: GFRC plates withstood the loading conditions up to 100 N even when loaded incisally. Thick plates concentrated the stress to the ramus mandibulae region of the fixation screws whereas the thin plates showed stress concentration in the angulus mandibulae region of the fixation and the plate itself. In general, thin plates caused a lower magnitude of stress to the fixation screw areas than thick plates, suggesting absorption of the loading energy to the body of the plate.

Evaluating stress and displacement in the craniomandibular complex using Twin Block appliances at varied angles: A finite element study.

OBJECTIVES: The objective of this investigation was to assess the stress and displacement pattern of the craniomandibular complex by employing finite element methodology to simulate diverse angulations of inclined planes that are incorporated in the Twin Block appliance. METHODS: A 3D finite element representation was established by use of Cone Beam Computed Tomography (CBCT) scans. This comprehensive structure included craniofacial skeletal components, the articular disc, a posterior disc elastic layer, dental elements, periodontal ligaments, and a Twin Block appliance. This investigation is the first to incorporated inclined planes featuring three distinct angulations (45, 60, and 70°) as the study models. Mechanical impacts were evaluated within the glenoid fossa, tooth, condylar, and articular disc regions. RESULTS: In all simulations, the stress generated by the Twin Block appliance was distributed across teeth and periodontal ligament, facilitating the anterior movement of mandibular teeth and the posterior displacement of maxillary teeth. Within the temporomandibular joint region, compressive forces on the superior and posterior facets of the condyle diminished, coinciding with the stress configuration that fosters condylar and mandibular growth. Stress dispersion homogenized in the condylar anterior facet and articular disc, with considerable tensile stress in the glenoid fossa's posterior aspect conforming to stress distribution that promote fossa reconfiguration. The 70° inclined plane exerts the highest force on the tissues. The condyle's maximum and minimum principal stresses are 0.36 MPa and -0.15 MPa, respectively, while those of the glenoid fossa are 0.54 MPa and -0.23 MPa. CONCLUSION: Three angled appliances serve the purpose of advancing the mandible. A 45° inclined plane relative to the occlusal plane exerts balanced anteroposterior and vertical forces on the mandibular arch. Steeper angles yield greater horizontal forces, which may enhance forward growth and efficient repositioning.

A new approach to identify wear regions on bearing surfaces of retrieved endoprostheses.

Although total hip replacements (THR) can be considered one of the most successful implantable medical devices in history, wear remains the ultimate challenge in order to further increase clinical success. Wear assessment on retrieved implants is the most reliable way to perform research into failure mechanisms. Therefor the bearing surface of the explant is measured geometrically by coordinate measuring machine (CMM). Wear determination in geometrical data is carried out in 3 steps: (1) identifying the worn area, (2) reconstructing the pre-wear geometry and (3) quantify wear as the difference between worn area and pre-wear geometry. In previous studies, assumptions to pre-wear geometry had been made for wear determination (step 2) and the worn area was identified by deviations between measured data and assumed form. Thus, the original form of the retrieved endoprostheses, including form deviations due to the manufacturing process and implantation, was not considered which leads to uncertainties in the wear computed. This work introduces a method which allows to identify the wear area without making assumptions to the original form. Instead, the curvature of the bearing surface obtained by simple computations on the measurement data is analysed and the edge of the wear region is recognized by its deviation in curvature. The method is applied to a retrieved Metal-on-Metal prosthetic head and the results are compared to those of the well-known method introduced by Jaeger et al., in 2013. With the new approach the wear region is identified more accurately.

Identification of constitutive materials of bi-layer soft tissues from multimodal indentations.

The personalisation of finite element models is an important problem in the biomechanical fields where subject-specific analyses are fundamental, particularly in studying soft tissue mechanics. The personalisation includes the choice of the constitutive law of the model's material, as well as the choice of the material parameters. In vivo identification of the material properties of soft tissues is challenging considering the complex behaviour of soft tissues that are, among other things, non-linear hyperelastic and heterogeneous. Hybrid experimental-numerical methods combining in vivo indentations and inverse finite element analyses are common to identify these material parameters. Yet, the uniqueness and the uncertainty of the multi-material hyperelastic model have not been evaluated. This study presents a sensitivity analysis performed on synthetic indentation data to investigate the identification uncertainties of the material parameters in a bi-material thigh phantom. Synthetic numerical data, used to replace experimental measurements, considered several measurement modalities: indenter force and displacement, stereo-camera 3D digital image correlation of the indented surface, and ultrasound B-mode images. A finite element model of the indentation was designed with either Ogden-Moerman or Mooney-Rivlin constitutive laws for both materials. The parameters' identifiability (i.e. the possibility of converging to a unique parameter set within an acceptable margin of error) was assessed with various cost functions formulated using the different synthetic data sets. The results underline the need for multiple experimental modalities to reduce the uncertainty of the identified parameters. Additionally, the experimental error can impede the identification of a unique parameter set, and the cost function depends on the constitutive law. This study highlights the need for sensitivity analyses before the design of the experimental protocol. Such studies can also be used to define the acceptable range of errors in the experimental measurement. Eventually, the impact of the evaluated uncertainty of the identified parameters should be further investigated according to the purpose of the finite element modelling.

A new method for determining the ogden parameters of soft materials using indentation experiments.

A full understanding of the material properties of skin tissue is crucial for exploring its tribo-mechanical behaviour. It has been widely accepted that the mechanical behaviour of skin tissue for both small and large deformations can be accurately described using a hyperelastic model, such as the one developed by Ogden. However, obtaining these Ogden parameters for in-vivo skin by in-vivo experiments no matter the indentation or suction tests is a significant challenge. The mathematical model used to describe the material behaviour during the test should consider not only the material nonlinearity but also the geometrical confinement of the tissue, the large deformations induced, and the fact that the specimens are relatively thin. A range of contact models is available to describe the contact behaviour during the indentation test. However, none of them can be used for hyperelastic materials with small thickness under large deformations. Simultaneously explaining material nonlinearity and geometric nonlinearity, either through theoretical equations or numerical calculations, poses a significant challenge. In this research, we propose a pragmatic method to obtain Ogden parameters for in-vivo skin tissue by combining experimental indentation results and numerical simulations. The indentation tests were used to obtain the force-indentation depth curves, while the numerical simulations were used to obtain the strain fields. The method assumes the material behaviour of specimens can be linearized in each small deformation increment, and the contact model developed by Hayes can be applied to accommodate each increment. Then, the linear elastic behaviour in each increment can be described by the elastic modulus E which were obtained using Hayes model, and the principal stresses in each increment were subsequently obtained using Hooke's law. By combining all stress fields, overall stress-strain curves can be constructed, from which the hyperelastic Ogden parameters can be obtained. A second numerical simulation of the hyperelastic indentation was then performed using the obtained Ogden parameters, allowing a comparison of the experimental and simulated relationships between force and indentation.

Three-axis load analysis of high-speed handpiece on dental training teeth and computer-aided design/computer-aided manufacturing blocks.

This study aimed to evaluate and compare the mechanical properties of dental training teeth with subtractive and additive computer-aided design/computer-aided manufacturing (CAD/CAM) materials used to fabricate dental simulation models. Therefore, the three-axis load generated during cutting movements, including drilling and milling performed using a dental handpiece, was measured and compared. The samples were cut vertically downward by 1.5 mm, horizontally by 6 mm, and vertically upward at a constant speed (1 mm/s), while the rotational speed of the bur was maintained at 200,000 rotations per minute. A three-axis load cell was used to measure the X-, Y-, and Z-axis loads on the specimen. The median value of the X-, Y-, and Z-axis measurements and the resultant load during the vertical-downward, horizontal, and vertical-upward movements were compared using a one-way analysis of variance and Tukey's post hoc test. For vertical downward movement, the drilling force of the dental training teeth was lower than that of Vita Enamic® and similar to that of Lava™ Ultimate. In contrast to subtractive CAD/CAM blocks, the drilling force of the dental training teeth was higher than that of 3D-printed resin blocks. Regarding horizontal movement, the milling force of dental training teeth was lower than that of Vita Enamic®. In contrast, the milling force of Nissin was similar to that of Lava™ Ultimate, while that of Frasaco was lower. Furthermore, compared to additive CAD/CAM blocks, the milling force of the dental training teeth was higher than that of 3D-printed resin blocks. Regarding vertical upward movement, the resultant loads of dental training teeth was lower than that of Vita Enamic®. Similarly, the resultant load of Nissin was similar to that of Lava™ Ultimate, while that of Frasaco was lower. Additionally, compared to additive CAD/CAM blocks, the resultant loads of the dental training teeth were similar to those of the 3D-printed resin blocks.

Effect of gastric acids on the mechanical properties of conventional and CAD/CAM resin composites - An in-vitro study.

OBJECTIVES: Dental erosion in patients with gastroesophageal reflux disease (GERD) is a current and frequent condition that may compromise the mechanical properties and clinical durability of resin-based composites (RBCs). This study assessed the mechanical properties of conventional and computer-aided design/computer-aided manufacturing (CAD/CAM) RBCs subsequent to simulated gastric acid aging. MATERIALS AND METHOD: Three conventional and three CAD/CAM composites were assessed. They were divided into an experimental group (exposed to simulated gastric acid aging) and a control group (no aging). Both groups were analyzed for Vickers microhardness (VHN), wear and flexural strength over a period of six months. The failure rate probability for each RBC was calculated through the Weibull cumulative distribution function (m). Statistical analysis was conducted using repeated measures ANOVA, 3-way ANOVA, a non-parametric Kruskal-Wallis and U Mann-Whitney tests (α = 0.05). RESULTS: The mechanical properties of all the RBCs dropped significantly after aging (p < 0.05). Lower VHN and flexural strength values, along with greater wear values were evident in the experimental groups, though the effects of the treatment varied between RBCs. The Weibull m of all the RBCs decreased over time. CONCLUSION: Conventional RBCs might show greater reduction in mechanical properties compared to CAD/CAM RBCs when exposed to gastric acid attack. Thus, CAD/CAM composites may represent a suitable choice for the treatment of patients presenting erosive issues.

Biomechanical assessment of mandibular fracture fixation using finite element analysis validated by polymeric mandible mechanical testing.

The clinical finite element analysis (FEA) application in maxillofacial surgery for mandibular fracture is limited due to the lack of a validated FEA model. Therefore, this study aims to develop a validated FEA model for mandibular fracture treatment, by assessing non-comminuted mandibular fracture fixation. FEA models were created for mandibles with single simple symphysis, parasymphysis, and angle fractures; fixated with 2.0 mm 4-hole titanium miniplates located at three different configurations with clinically known differences in stability, namely: superior border, inferior border, and two plate combinations. The FEA models were validated with series of Synbone polymeric mandible mechanical testing (PMMT) using a mechanical test bench with an identical test set-up. The first outcome was that the current understanding of stable simple mandibular fracture fixation was reproducible in both the FEA and PMMT. Optimal fracture stability was achieved with the two plate combination, followed by superior border, and then inferior border plating. Second, the FEA and the PMMT findings were consistent and comparable (a total displacement difference of 1.13 mm). In conclusion, the FEA and the PMMT outcomes were similar, and hence suitable for simple mandibular fracture treatment analyses. The FEA model can possibly be applied for non-routine complex mandibular fracture management.

Insights into the Mechanical Characterization of Mouse Brain Tissue Using Microindentation Testing.

Indentation testing is the most common approach to quantify mechanical brain tissue properties. Despite a myriad of studies conducted already, reported stiffness values vary extensively and continue to be subject of study. Moreover, the growing interest in the relationship between the brain's spatially heterogeneous microstructure and local tissue stiffness warrants the development of standardized measurement protocols to enable comparability between studies and assess repeatability of reported data. Here, we present three individual protocols that outline (1) sample preparation of a 1000-µm thick coronal slice, (2) a comprehensive list of experimental parameters associated with the FemtoTools FT-MTA03 Micromechanical Testing System for spherical indentation, and (3) two different approaches to derive the elastic modulus from raw force-displacement data. Lastly, we demonstrate that our protocols deliver a robust experimental framework that enables us to determine the spatially heterogeneous microstructural properties of (mouse) brain tissue. © 2024 Wiley Periodicals LLC. Basic Protocol 1: Mouse brain sample preparation Basic Protocol 2: Indentation testing of mouse brain tissue using the FemtoTools FT-MTA03 Micromechanical Testing and Assembly System Basic Protocol 3: Tissue stiffness identification from force-displacement data.

Validation of a double-semicircular notched configuration for mechanical testing of orthodontic thermoplastic aligner materials.

The potential of using specimens with a double-semicircular-notched configuration for performing tensile tests of orthodontic thermoplastic aligner materials was explored. Unnotched and double-semicircular-notched specimens were loaded in tension using a universal testing machine to determine their tensile strength, while finite element analysis (FEA) and digital image correlation (DIC) were used to estimate stress and strain, respectively. The shape did affect the tensile strength, demonstrating the importance of unifying the form of the specimen. During the elastic phase under tension, double-semicircular-notched specimens showed similar behavior to unnotched specimens. However, great variance was observed in the strain patterns of the unnotched specimens, which exhibited greater chance of end-failure, while the strain patterns of the double-semicircular-notched specimens showed uniformity. Considerable agreement between the theoretical (FEA) and practical models (DIC) further confirmed the validity of the double-semicircular-notched models.

How do different intraoral scanners and milling machines affect the fit and fatigue behavior of lithium disilicate and resin composite endocrowns?

The aim of this in vitro study was to evaluate the effect of the combinations of two different intraoral scanners (IOS), two milling machines, and two restorative materials on the marginal/internal fit and fatigue behavior of endocrowns produced by CAD-CAM. Eight groups (n= 10) were considered through the combination of TRIOS 3 (TR) or Primescan (PS) IOS; 4-axes (CR; CEREC MC XL) or 5-axes (PM; PrograMill PM7) milling machines; and lithium disilicate (LD; IPS e.max CAD) or resin composite (RC; Tetric CAD) restorative materials. Specific surface treatments were applied to each material, and the bonding to its corresponding Endocrown-shaped fiberglass-reinforced epoxy resin preparations was performed (Variolink Esthetic DC). Computed microtomography (µCT) was performed to assess the marginal/internal fit, as well as a mechanical fatigue test (20 Hz, initial load = 100 N/5000 cycles; step-size = 50 N/10,000 cycles until a threshold of 1500 N, then, the step-size was increased if needed to 100 N/10,000 cycles until failure or a threshold of 2800 N) to evaluate the restorations long-term behavior. Complementary analysis of the fracture features and surface topography in scanning electron microscopy was performed. Three-way ANOVA and Kaplan-Meier test (α = 0.05) were performed for marginal/internal fit, and fatigue behavior data, respectively. PS scanner, CR milling machine, and RC endocrowns resulted in a better marginal fit compared to their counterparts. Still, the PM machine resulted in a better pulpal space fit compared to the CR milling machine. Regardless of the scanner and milling machine, RC endocrowns exhibited superior fatigue behavior than LD ones. LD endocrowns presented margin chipping regardless of the milling machine used. Despite minor differences in terms of fit, the 'IOS' and 'milling machine' factors did not impair the fatigue behavior of endocrowns. Resin-composite restorations resulted in a higher survival rate compared to glass-ceramic ones, independently of the digital devices used in the workflow.

3D printed, subtractive, and conventional acrylic resins: Evaluation of monotonic versus fatigue behavior and surface characteristics.

This study assessed the mechanical properties and surface characteristics of dental prosthetic acrylic resin fabricated by 3D printing, comparing it with subtractive, pressing, and molding techniques. Bar-shaped specimens (N= 90; 65 × 10 × 3.3 mm; ISO:207951) were prepared and assigned into six groups: PRINT (3D printing vis stereolithography with PriZma 3D Bio Denture, Makertech Labs); SUB (subtractive manufacturing with Vipiblock Trilux, Vipi); PRESS Base (pressing using muffle with Thermo Vipi Wave, Vipi for base); PRESS Tooth (pressing with Onda-cryl, Clássico for tooth); MOLD Base (molding using addition silicone with Vipi Flash, Vipi for base); and MOLD Tooth (molding with Dencor, Clássico for tooth). Monotonic flexural strength (FS) and elastic modulus (E) were measured using a three-point bending approach (n= 5) on a universal testing machine at a crosshead speed of 5 mm/min. Fatigue testing (n= 10) followed similar geometry and settings, with a frequency of 2 Hz, initial stress level at 20 MPa, and stress increments of 5 MPa every 2,500 cycles. Surface roughness (n= 10) was assessed through profilometry, and fractographic and topographic analyses were conducted. Statistical analyses included One-Way ANOVA for monotonic FS, roughness, and E, along with Kaplan-Meier with Mantel-Cox post-hoc and Weibull analysis for fatigue strength. PRINT showed lower monotonic FS than the SUB and PRESS Tooth but comparable fatigue strength to these groups and superior to PRESS Base and MOLD (Base and Tooth) groups. All groups had similar Weibull moduli. Surface roughness of the PRINT group was comparable to most techniques but higher than the PRESS Tooth group. Fractographic analysis revealed fractures originating from surface defects under tensile stress, with SEM showing scratch patterns in all groups except PRINT, which had a more uniform surface. Despite its lower monotonic strength, 3D printed resin demonstrated comparable fatigue strength to subtractive and pressing methods and similar surface roughness to most methods, indicating its potential as a viable option for dental prosthesis.