ABSTRACT
This study aimed to compare the amount of fluoride uptake and the recharge and release characteristics of conventional glass ionomer cement (GIC) without any additives in comparison to conventional glass ionomer cement supplemented with silver nanoparticles (AgNPs) at two concentrations: 0.1% and 0.2% (w/w). A total of 60 specimens were used in this in vitro study. The sample was divided into six groupsincluding three groups without fluoride charge: Group 1 (conventional GIC), Group 2 (GIC with 0.1% silver nanoparticles), and Group 3 (GIC with 0.2% silver nanoparticles; and three groups with fluoride charge: Group 4 (conventional GIC with fluoride); Group 5 (GIC with 0.1% silver nanoparticles with fluoride); Group 6 (GIC with 0.2% silver nanoparticles with fluoride), where Group 1 is considered the control group and the other five groups are used as the test groups. The amount of fluoride released was measured on days 1, 2, 7, 15, and 30. The comparisons were made between the groups with and without fluoride and among all the groups. A significant difference in the amount of fluoride released was observed between the groups, with the highest amount occurring in Group 1, followed by Group 2; the lowest amount of fluoride released was observed in Group 3 (p < 0.05). The groups with fluoride recharge (Groups 4, 5, and 6) exhibited a higher amount of fluoride release than the groups with no recharge (Groups 1, 2, and 3); however, Group 1 has more fluoride release compared to all other groups on days 1, 2, 7, 15, and 30 (p < 0.05). The amount of released fluoride decreased from day 1 to day 30 in all of the groups in the study. Despite the antimicrobial and anticariogenic benefits of adding silver nanoparticles to GIC, it seems that fluoride release characteristics are significantly affected by the addition of this material. This may force the clinician to a compromise between the antimicrobial benefit of silver nanoparticles and the remineralizing advantage of fluoride.
ABSTRACT
Background: The nanotechnologies have been applied for dental restorative materials manufacturing such as glass ionomer cement, composites, tooth regeneration, and endodontic sealers. The study aimed to investigate the chemical bond of conventional glass ionomer cement and to evaluate the addition of different concentrations of silver nanoparticles (AgNPs) on the quality of the chemical bond of glass ionomer cement to primary dentin. Methods: Silver nanoparticle (AgNP) powder was added in concentrations of 0.2, 0.4, and 0.6% to the conventional powder of GIC Fuji II. Then, the powder was added to the liquid and mixed with the recommended powder/liquid ratio of 3.6:1 g. The Fourier-transform infrared spectra (FTIR) of teeth with 0.2%, 0.4%, and 0.6% w/w of silver nanoparticles in GIC fills and the control tooth were obtained. The conventional glass ionomer was used as a control group. The control and the plain silver tooth were subjected to FTIR analysis using an ATR-FTIR spectrophotometer (ThermoFisher Scientific, Waltham, MA, United States) with zinc selenide (ZnSe) ATR crystal (attenuated total reflection) and OPUS v7.5 software. All spectra were recorded in the range of 500-3,500 cm-1 in the transmission mode with an ATR module. Results: The AgNPs added at 0.2, 0.4, and 0.6% concentration to GIC provided some information in the context of bond interaction with the dentin. Various bond peaks were seen for calcium, carbonate, phosphate, and amide. In our study, only the amide and phosphate were generated. The amide peaks were almost similar to the control, 0.2%, 0.4%, and 0.6%, with the peaks in the range of 1250-1650 cm-1. There was a clear shift in the phosphate peak from the control, 0.2, and 0.4%, which was about 1050 cm-1, whereas for 0.6%, there was a clear shift from 1050 cm-1 to 880 cm-1. Conclusion: GIC supplemented with AgNPs showed that a concentration above 0.4% of AgNPs altered the bond quality in dentin interaction. In conclusion, adding AgNPs at a minimal level improves the mechanical properties and maintains the same bond quality as GIC.
