ABSTRACT
A fast and sensitive aptasensor was developed using nanoplates with peroxidase activity as a novel approach. E. coli detection is described using a silver/platinum nanoplate (Ag/Pt NPL) that interacts with an oligonucleotide aptamer as a bioreceptor. The size of the Ag/Pt NPLs was about 42 nm according to the FE-SEM images. The EDS result indicates that a thin layer of Pt ions was coated on the surface of the Ag NPLs. This nanobiosensor has the ability to specifically bind to E. coli, increasing the peroxidase activity of the apt-Ag/Pt NPL. Finally, the blue color of the solution in the contaminated water samples was increased in the presence of 3,3',5,5'-tetramethylbenzidine (TMB) as a substrate and H2O2. The assay can be completed in 30 min and the presence of E. coli levels can be distinguished with the naked eye. The absorbance at 652 nm is proportional to pathogen concentration from 10 to 108 CFU·mL-1, with a detection limit of 10 CFU·mL-1. The percent recovery for the water samples spiked with E. coli is 95%. The developed assay should serve as a general platform for detecting other pathogenic bacteria which affect water and food quality. The proposed E. coli detection strategy has appealing characteristics such as high sensitivity, simple operation, short testing time, and low cost.
ABSTRACT
A newly developed water-soluble polymeric nano-additive termed "partially cross-linked nanoparticles graft copolymer (PCLNPG)" has been successfully synthesized and harnessed as a pore former for modifying a polyethersulfone ultrafiltration membrane for dyes removal. The PCLNPG content was varied in the PES polymeric matrix aiming to scrutinize its impact on membrane surface characteristics, morphological structure, and overall performance. Proposed interaction mechanism between methylene blue (MB), methyle orange (MO), and malachite green (MG) dyes with PES membrane was presented as well. Hydrophilicity and porosity of the novel membrane increased by 18 and 17 %, respectively, when manufactured with a 3 Wt. % PCLNPG, according to the findings. Besides this, the disclosed increased porosity, rather than the hydrophilic properties of the water-soluble PCLNPG, was the principal cause of the diminished contact angle. Meanwhile, raising the PCLNPG content in the prepared membrane made worthy shifts in its structure. A sponge-like region was materialized near the bottom surface as well. The membrane's pure water flux (PWF) synthesized with 3 Wt.% PCLNPG recorded 628 LMH, which is estimated 3.95 fold the pristine membrane. MG, MB, and MO dyes were rejected by 90.6, 96.3, and 97.87 %, respectively. These findings showed that the performance characteristics of the PES/PCLNPG membrane make it a potentially advantageous option to treat the textile wastewater.
ABSTRACT
In this research, poly terephthalic acid-co-glycerol-g-maleic anhydride (PTGM) graft co-polymer was used as novel water-soluble pore formers for polyethersulfone (PES) membrane modification. The modified PES membranes were characterized to monitor the effect of PTGM content on their pure water flux, hydrophilicity, porosity, morphological structure, composition, and performance. PTGM and PES/PTGM membranes were characterized by field emission scanning electron microscopy (FESEM), Fourier-transform infrared spectroscopy (FTIR), and contact angle (CA). The results revealed that the porosity and hydrophilicity of the fabricated membrane formed using a 5 wt.% PTGM ratio exhibited an enhancement of 20% and 18%, respectively. Similarly, upon raising the PTGM ratio in the casting solution, a more porous with longer finger-like structure was observed. However, at optimum PTGM content (i.e., 5%), apparent enhancements in the water flux, bovine serum albumin (BSA), and sodium alginate (SA) retention were noticed by values of 203 L/m2.h (LMH), 94, and 96%, respectively. These results illustrated that the observed separation and permeation trend of the PES/PTGM membrane may be a suitable option for applications of wastewater treatment. The experimental results suggest the promising potential of PTGM as a pore former on the membrane properties and performance.