A novel BiOBr/rGO photocatalysts for degradation of organic and antibiotic pollutants under visible light irradiation: Tetracycline degradation pathways, kinetics, and mechanism insight.

In this study, the BiOBr/rGO nanocomposite photocatalysts are fabricated by a facile solvothermal method. The BiOBr growth on reduced graphene oxide (rGO) sheet could improve BiOBr's photocatalytic activity by increasing its adsorption ability, surface area, and charge carriers' separation efficiency. The prepared nanocomposites were characterized by XRD, Raman, FESEM, EDS, XPS, and UV-visible DRS. The BiOBr/rGO (BRG) nanocomposites showed improved photocatalytic activity for the photodegradation of Rhodamine B (RhB) dye and Tetracycline (TC) under visible light irradiation. Rhodamine B and tetracycline degradation efficiency were about 96% and 73% within 120 min under visible light irradiation. The PL analysis indicates that BiOBr/rGO nanocomposite exhibited maximum separation efficiency of photoinduced charge carriers. The trapping test confirmed that O2- and h+ are significant active photodegradation species. The GC-MS spectra detected the two plausible transformation routes of tetracycline degradation. The current work presented a low-cost and facile approach for fabricating Bi-based composites.

Highly Sensitive Ethanol Chemical Sensor Based on Novel Ag-Doped Mesoporous α-Fe2O3 Prepared by Modified Sol-Gel Process.

Mesoporous α-Fe2O3 has been synthesized via a simple sol-gel procedure in the presence of Pluronic (F-127) triblock copolymer as structure directing agent. Silver (Ag) nanoparticles were deposited onto α-Fe2O3 matrix by the photochemical reduction approach. Morphological analysis revealed the formation of Ag nanoparticles with small sizes < 20 nm onto the mesoporous structure of α-Fe2O3 possessing < 50 nm semi-spherical shape. The XRD, FTIR, Raman, UV-vis, PL, and N2 sorption isotherm studies confirmed the high crystallinity, mesoporosity, and optical characteristics of the synthesized product. The electrochemical sensing toward liquid ethanol has been performed using the current devolved Ag/α-Fe2O3-modified glassy carbon electrode (GCE) by cyclic voltammetry (CV) and current potential (I-V) techniques, and the obtained results were compared with bare GCE or pure α-Fe2O3. Mesoporous Ag/α-Fe2O3 was found to largely enhance the sensor sensitivity and it exhibited excellent sensing characteristics during the precision detection of low concentrations of ethanol. High and reproducible sensitivity of 41.27 µAmM- 1 cm- 2 at lower ethanol concentration region (0.05 to 0.8 mM) and 2.93 µAmM- 1 cm- 2 at higher concentration zone (0.8 to 15 mM), with a limit of detection (LOD) of 15.4 µM have been achieved. Investigation on reaction kinetics revealed a characteristic behavior of mixed surface and diffusion-controlled processes. Detailed sensing studies revealed also that the sensitivity toward ethanol was higher than that of methanol or isopropanol. With further effort in developing the synthesis and fabrication approaches, a proper utility for the current proposed protocol for fabricating a better sensor device performance is possible.