ABSTRACT
STATEMENT OF PROBLEM: Studies of composite resin repairs of yttrium-tetragonal zirconia polycrystal (Y-TZP) are usually performed in its tetragonal phase, but it may be partially transformed into a monoclinic phase in a clinical fracture. PURPOSE: The purpose of this in vitro study was to evaluate the effect of airborne-particle abrasion (APA) and a bonding agent on the shear bond strength (SBS) between a composite resin and hydrothermally aged Y-TZP. MATERIAL AND METHODS: Specimens (7.0×7.0×1.7 mm, N=112) of Y-TZP Lava were obtained, and 50% were aged in an autoclave at 134°C at 300 kPa for 8 hours. The surfaces were treated with APA 50-µm Al2O3 particles (ALU) or Rocatec Soft (30 µm) (ROC) followed by Clearfil SE Bond Primer (10-methacryloyloxydecyl dihydrogen phosphate [10-MDP]) plus Clearfil porcelain bond activator (3-methacryloxypropyl-trimethoxy silane [3-MPS]) (CLE) or RelyX Ceramic Primer plus a layer of RelyX U100 adhesive-resin cement (REL). Composite resin cylinders were built on the Y-TZP treated surfaces. After thermocycling (6000 cycles, 5°C and 55°C, 30-second dwell time), an SBS test was carried out (n=14). Data were analyzed by 3-way ANOVA and the Tukey honest significant differences test (α=.05). The failure mode was analyzed. RESULTS: The 3-way ANOVA was not significant for aging (P>.05), but the APA (P<.001), bonding agent (P<.001), and their interaction (P<.001) were significant. APA with ALU or ROC did not influence the SBS of the groups bonded with CLE, but the REL APA with ROC provided higher SBS. The failure mode was adhesive for all specimens. CONCLUSIONS: Adhesion was not different on monoclinic partially transformed Y-TZP. The APA with ROC followed by REL was the most effective treatment for repairing Y-TZP.
Subject(s)
Composite Resins/therapeutic use , Dental Prosthesis Repair/methods , Yttrium , Zirconium , Dental Bonding/methods , Dental Etching/methods , Dental Stress Analysis , Humans , In Vitro Techniques , Yttrium/adverse effects , Yttrium/therapeutic use , Zirconium/adverse effects , Zirconium/therapeutic useABSTRACT
Crowns made from an yttria-stabilized tetragonal zirconia polycrystals (3Y-TZP) core with a porcelain veneer have shown high clinical failure rates. Manifestations of clinical failure in veneering ceramic ranges from a single chip to an extended fracture. Core failures are uncommon but usually are catastrophic. This article examines the possible causes of failure in zirconia systems and presents a case report involving the diagnosis and repair of three different types of failure in six 3Y-TZP/porcelain crowns.