ABSTRACT
Simvastatin (SIM) is widely prescribed to treat hyperlipidemia, despite its limitations, such as a short half-life and low oral bioavailability. To overcome these drawbacks, the development of a controlled-release formulation is desirable. This study aims to develop a microparticulate system based on cellulose acetate (ACT) obtained from Agave sisalana Perrine to promote a controlled SIM release. SIM-loaded microparticles (SMP) were prepared using the solvent emulsification-evaporation method. Several parameters were evaluated, including particle size, surface charge, morphology, encapsulation efficiency, thermochemical characteristics, crystallinity, and in vitro release profile. ACT exhibited favorable flow properties after acetylation, with a degree of substitution values superior to 2.5, as confirmed by both the chemical route and H-NMR, indicating the formation of cellulose triacetate. The obtained SMP were spherical with an average size ranging from 1842 to 1857 nm, a zeta potential of -4.45 mV, and a high SIM incorporation efficiency (98%). Thermal and XRD analyses revealed that SIM was homogeneously dispersed into the polymeric matrix in its amorphous state. In vitro studies using dialysis bags revealed that the controlled SIM release from microparticles was higher under simulated intestinal conditions and followed the Higuchi kinetic model. Our results suggest that ACT-based microparticles are a promising system for SIM delivery, which can improve its bioavailability, and result in better patient compliance.
ABSTRACT
BACKGROUND: Neglected Tropical Diseases (NTD) are chronic infectious conditions that primarily affect marginalized populations. The chemotherapeutic arsenal available for treating NTD is limited and outdated, which poses a challenge in controlling and eradicating these diseases. This is exacerbated by the pharmaceutical industry's lack of interest in funding the development of new therapeutic alternatives. In addition, a considerable number of drugs used in NTD therapy have low aqueous solubility. To address this issue, solubility enhancement strategies, such as the use of inclusion complexes with cyclodextrins (CD) can be employed. OBJECTIVE: Therefore, this systematic review aims to present the application of CD in complexing with drugs and chemotherapeutic compounds used in the therapy of some of the most prevalent NTD worldwide and how these complexes can enhance the treatment of these diseases. METHODS: Two bibliographic databases, Science Direct and PubMed, were used to conduct the search. The selection of studies and the writing of this systematic review followed the criteria outlined by the PRISMA guidelines. RESULTS: From a total of 978 articles, 23 were selected after applying the exclusion criteria. All the studies selected were consistent with the use of CD as a strategy to increase the solubility of therapeutic agents used in NTD. CONCLUSION: The results indicate that CD can enhance the solubility of chemotherapeutic agents for the treatment of Neglected Tropical Diseases (NTD). This review presents data that clearly highlights the potential use of CD in the development of new treatments for neglected tropical diseases. It can assist in the formulation of future treatments that are more effective and safer.
ABSTRACT
OBJECTIVES: To assess the effects of different aging protocols on chemical, physical, and mechanical properties of an experimental ATZ composite compared to a zirconia. METHODS: Disc-shaped specimens were obtained through uniaxial pressing of commercial powders (Tosoh), ATZ comprised of 80%ZrO2/20%Al2O3 (TZ-3YS20AB) and 3Y-TZP (3Y-SBE). The specimens of each material were divided into different groups according to the aging protocol: immediate, autoclave aging and hydrothermal reactor aging. The aging protocols were performed at 134 ºC for 20 h at 2.2 bar. Crystalline evaluations were performed using X-Ray Diffraction. The nanoindentation tests measured the elastic modulus (Em) and hardness (H). Biaxial flexural strength was performed, and Weibull statistics were used to determine the characteristic strength and Weibull modulus. The probability of survival was also determined. The Em and H data were analyzed by one-way ANOVA and Tukey test. RESULTS: Diffractograms revealed the presence of monoclinic phase in both materials after aging. The hydrothermal reactor decreased the Em for ATZ compared to its immediate condition; and the H for both ATZ and 3Y-TZP regarding their immediate and autoclave aging conditions, respectively. The aging protocols significantly increased the characteristic strength for ATZ, while decreased for 3Y-TZP. No difference regarding Weibull modulus was observed, except for 3Y-TZP aged in reactor. For missions of up to 500 MPa, both materials presented a high probability of survival (>99 %) irrespective of aging condition. SIGNIFICANCE: The synthesized ATZ composite exhibited greater physical and microstructural stability compared to 3Y-TZP, supporting potential application of the experimental material for long-span reconstructive applications.
Subject(s)
Aluminum Oxide , Flexural Strength , Materials Testing , X-Ray Diffraction , Zirconium , Zirconium/chemistry , Aluminum Oxide/chemistry , Elastic Modulus , Hardness , Surface Properties , Dental Materials/chemistry , Yttrium/chemistry , Dental Stress Analysis , Hot TemperatureABSTRACT
This study assessed the pharmacokinetics and pharmacodynamics of low-dose dexmedetomidine after IV bolus in dogs. Six healthy adult dogs (6.8 ± 3.0 kg) received dexmedetomidine (2 µg.kg-1 IV) over 2 min, using an infusion pump. Blood samples were collected totaling 5 h of monitoring. A validated UHPLC-MS/MS method was used to determine the plasma concentration of dexemedetomidine. For pharmacodynamics, HR, RR, oscillometric MBP, Grint END sedation score were evaluated at baseline (T0), every 3 min (T3 to T21), and after 30 (T30) and 60 (T60) minutes, with p < 0.05. T1/2 was 28.28 ± 6.14 min; the area under the curve was 467.44 ± 60.42 ng/mL/min. The total clearance was 5.46 ± 0.41 mL/min/kg, the Vdss was 146.19 ± 21.04 mL/kg, and the C max was 3.13 ± 1.15 ng/mL. HR (bpm) decreased significantly from T6 (79 ± 21) to T21 (78 ± 31) compared to T0 (116 ± 28). RR(mpm) decreased from T3 (43 ± 44) to T60 (41 ± 23), with T0 being 70 ± 48. The MBP (mmHg) increased at T18 (151 ± 34), T21 (152 ± 35), and T30 (140 ± 27), compared to T0 (111 ± 22). Sedation occurred at all times post-bolus, with a maximum peak at T12 (END 8 ± 6). The low dose of dexmedetomidine provided sedation in all animals, characterizing rapid metabolization and elimination. However, cardiovascular effects still may have negative repercussions in dogs with hemodynamic comorbidities, highlighting the caution and individualization of its use in certain patients.
Subject(s)
Dexmedetomidine , Humans , Dogs , Animals , Hypnotics and Sedatives/pharmacology , Tandem Mass Spectrometry/veterinary , Administration, Intravenous/veterinary , HemodynamicsABSTRACT
PURPOSE: To evaluate the reliability and failure modes of ultrathin (0.5 mm) lithium disilicate, translucent and ultra-translucent zirconia crowns for posterior teeth restorations. MATERIALS AND METHODS: Fifty-four mandibular first molar crowns of three ceramic materials: (1) Lithium disilicate (e.max CAD, Ivoclar Vivadent), (2) 3Y-TZP (Zirconn Translucent, Vipi), and (3) 5Y-PSZ (Cercon XT, Dentsply Sirona), with 0.5 mm of thickness were milled and cemented onto composite resin abutments. Eighteen samples of each group were tested under mouth-motion step-stress accelerated life testing in a humid environment using mild, moderate, and aggressive profiles. Data was subjected to Weibull statistics. Use level curves were plotted and reliability was calculated for a given mission of 100,000 cycles at 100, 200, and 300 N. Fractographic analyses of representative samples were performed in scanning electron microscope. RESULTS: Beta (ß) values suggest that failures were dictated by material's strength for lithium disilicate and by fatigue damage accumulation for both zirconias. No significant differences were detected in Weibull modulus and characteristic strength among groups. At a given mission of 100,000 cycles at 100 N, lithium disilicate presented higher reliability (98% CB: 95-99) regarding 3Y-TZP and 5Y-PSZ groups (84% CB: 65%-93% and 79% CB: 37&-94%, respectively). At 200 N, lithium disilicate reliability (82% CB: 66%-91%) was higher than 5Y-PSZ (20% CB: 4%-44%) and not significantly different from 3Y-TZP (54% CB: 32%-72%). Furthermore, at 300 N no significant differences in reliability were detected among groups, with a notable reduction in the reliability of all materials. Fractographic analyses showed that crack initiated at the interface between the composite core and the ceramic crowns due to tensile stress generated at the intaglio surface. CONCLUSIONS: Ultrathin lithium disilicate crowns demonstrated higher reliability relative to zirconia crowns at functional loads. Lithium disilicate and zirconia crown's reliability decreased significantly for missions at higher loads and similar failure modes were observed regardless of crown material. The indication of 0.5 mm thickness crowns in high-load bearing regions must be carefully evaluated. CLINICAL SIGNIFICANCE: Ultraconservative lithium disilicate and zirconia crowns of 0.5 mm thickness may be indicated in anterior restorations and pre-molars. Their clinical indication in high-load requirement regions must be carefully evaluated.
Subject(s)
Crowns , Dental Porcelain , Reproducibility of Results , Materials Testing , Ceramics , Zirconium , Dental Stress Analysis , Dental Restoration Failure , Computer-Aided DesignABSTRACT
OBJECTIVE: To evaluate the effect of different hydrofluoric acid concentrations and etching times on the surface, chemical composition and microstructure of lithium disilicate. MATERIAL AND METHODS: Ninety specimens of pressed lithium disilicate (LDS) were obtained (IPS e.max Press, Rosetta SP and LiSi Press). The specimens of each material were divided in two groups according to the hydrofluoric acid concentration: 5% and 10% (n = 15/group), and subdivided according to the etching time: 20, 40 and 60 s (n = 5/group). Crystalline evaluations and chemical composition were performed through x-ray diffraction (XRD) and energy-dispersive x-ray spectroscopy (EDS), respectively. Microstructural analyses were performed by scanning electron microscope (SEM), surface roughness (Ra), and material thickness removal evaluation. Thickness removal and Ra data were analyzed by ANOVA and Tukey test (p < 0.05). RESULTS: XRD demonstrated characteristic peaks of lithium disilicate crystals, lithium phosphate and of a vitreous phase for all materials. EDS identified different compositions and SEM confirmed different surface responses to acid etching protocols. Material and etching time influenced Ra and material thickness removal (p < 0.05). CONCLUSION: Hydrofluoric acid concentration and etching time affect the surface characteristics of LDS differently. LiSi Press presented higher resistance to hydrofluoric acid etching compared to e.max Press and Rosetta SP. CLINICAL SIGNIFICANCE: Applying the appropriate etching protocol is pivotal to avoid excessive material removal and to prevent jeopardize the mechanical and optical properties of the material.
Subject(s)
Dental Bonding , Hydrofluoric Acid , Hydrofluoric Acid/chemistry , Materials Testing , Dental Porcelain/chemistry , Ceramics/chemistry , Surface Properties , Dental Bonding/methods , Resin Cements/chemistryABSTRACT
BACKGROUND: Morus nigra L. is a plant with significant potential for drug development due to the presence of numerous bioactive compounds in its various parts. OBJECTIVES: This article aims to compile the technological perspectives of Morus nigra L. towards drug development and therapeutic indications based on registered patents in databases. METHODS: The study analyzed patents published within the last five years, focusing on products derived from different parts of the Morus nigra L. plant. Patent databases such as the European Patent Office (EPO), the United States Patent and Trademark Office (USPTO), the World Intellectual Property Organization (WIPO), and the National Institute of Industrial Property Databases (INPI) were examined. RESULTS: A total of 45 patents were categorized by country of origin, type of applicant, extraction method, and therapeutic indications. China had the highest number of patent filings (43.48%), and private companies were the primary technology patent holders (38.64%). Noteworthy extraction methods included ultrasound-assisted extraction, decoction, infusion, and maceration. The most utilized plant parts were leaves (44.44%), followed by fruits (35.56%), root bark (15.56%), and stems (4.44%). The main therapeutic indications identified were the treatment of hyperglycemia and dyslipidemia (43.33%), along with digestive problems, cosmetics, nutrition, and cleaning applications. CONCLUSION: The study of patents covers discoveries and advancements often absent in scientific articles, making a review focused on this advanced information crucial for expanding existing scientific knowledge. Even if some therapies have been explored previously, patents can reveal innovative approaches and fresh perspectives that contribute to sustained scientific progress.
Subject(s)
Morus , Databases, Factual , Intellectual Property , Patents as Topic , Technology , United StatesABSTRACT
The aim of this study was to evaluate the effect of two finishing techniques, glazing or polishing, in comparison with the as-cut condition, on the biaxial-flexural-strength (BFS) of a zirconia-reinforced lithium silicate ceramic (ZLS). Cylinders were milled from CAD/CAM blocks and sliced to obtain disc-shaped specimens (ISO6872:2015). Polished and glazed specimens were processed following the manufacturer's instructions. Thirty-three specimens were obtained for each condition and microstructural and BFS/fractographic characterizations were performed. BFS and roughness data were analyzed using Weibull statistics and ANOVA one-way with Tukey post-hoc test, respectively. While a rougher surface was observed for as-cut specimens, smoother surfaces were observed for polished and glazed ZLS at microscopical evaluation and confirmed through surface-roughness evaluation. X-ray spectra depicted a glass phase for all groups and characteristic metasilicate, lithium disilicate, and lithium phosphate peaks for the as-cut and polished specimens. Glazed specimens showed higher characteristic strength than polished and as-cut specimens, which did not differ significantly. While higher Weibull-modulus was observed for the polished than for the as-cut specimens, no statistically significant differences were noted between glazed and polished, and between glazed and as-cut specimens. ZLS presents higher strength when glazed, and polishing increases the structural reliability of the material relative to the as-cut condition. Both finishing techniques reduced surface roughness similarly.
Subject(s)
Ceramics , Lithium , Reproducibility of Results , Materials Testing , Surface Properties , Ceramics/chemistry , Dental Porcelain/chemistry , Zirconium/chemistry , Silicates , Computer-Aided DesignABSTRACT
This study aimed to develop a recycling process for the remnants of milled 3Y-TZP and enhance their properties using glass infiltration. 3Y-TZP powder was gathered from the vacuum system of CAD-CAM milling equipment, calcined and sieved (x < 75 µm). One hundred twenty discs were fabricated and pre-sintered at 1000 °C/h. These specimens were then divided into four groups, categorized by glass infiltration (non-infiltrated [Zr] or glass-infiltrated [Zr-G]) and sintering temperature (1450 °C [Zr-1450] or 1550 °C [Zr-1550]/2h). After sintering, the specimens were characterized by X-Ray Diffraction (XRD), relative density measurement, and scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS). The biaxial flexural strength test was performed according to the ISO 6872 and followed by fractographic analysis. Subsequent results were analyzed using Weibull statistics. Relative density values of the sintered specimens from Zr-1450 and Zr-1550 groups were 86.7 ± 1.5% and 92.2 ± 1.7%, respectively. Particle size distribution revealed particles within the range of 0.1-100 µm. XRD analysis highlighted the presence of the ZrO2-tetragonal in both the Zr-1450 and Zr-1550 groups. Glass infiltration, however, led to the formation of the ZrO2-monoclinic of 9.84% (Zr-1450-G) and 18.34% (Zr-1550-G). SEM micrographs demonstrated similar microstructural characteristics for Zr-1450 and Zr-1550, whereas the glass-infiltrated groups exhibited comparable infiltration patterns. The highest characteristic strength was observed in the glass-infiltrated groups. Fractographic analyses suggested that fracture origins were related to defects on the tensile side, which propagated to the compression side of the samples. Both the sintering temperature and glass infiltration significantly influenced the mechanical properties of the 3Y-TZP recycled.
Subject(s)
Flexural Strength , Zirconium , Temperature , Materials Testing , Zirconium/chemistry , Yttrium/chemistry , Surface Properties , Dental Materials , Ceramics/chemistryABSTRACT
Objetivo: descrever a experiência de enfermeiros sobre o uso do capacete ELMO para o tratamento de pacientes com a COVID-19. Métodos: relato de experiência em unidade de pronto-atendimento localizada numa cidade metropolitana do Ceará, Brasil, no período de 15 de março a 22 de junho de 2021. Utilizou-se a Análise de Conteúdo para a organização e a análise por meio de referencial da área. Resultados: foram observadas as potencialidades do cuidado durante o uso do capacete ELMO, como a diminuição das indicações de intubação orotraqueal, melhora de desconforto respiratório e diminuição da morbidade, mas, também as fragilidades como a comunicação paciente-profissional de saúde diminuída, necessidade de criteriosa avaliação do tempo de uso e a resposta do paciente, o risco de instabilidade psicológica e de broncoaspiração; além disso, aspectos colaborativos da equipe de saúde como comunicação intraequipe aumentada, interação efetiva e maior tomada de decisão foram registrados. Conclusão: importantes resultados no tratamento da COVID-19 podem advir da empregabilidade dessa ferramenta, no entanto, há a necessidade de acompanhamento rígido para que se evitem as complicações respiratórias maiores, assim como as sequelas físicas e psicológicas pelo uso do ELMO. Descritores: Cuidados de enfermagem. Equipe de assistência ao paciente. Práticas interdisciplinares. COVID-19
Objective:to describe nurses' experience with the use of the ELMO helmet for the treatment of patients with COVID-19. Methods:experience report in an emergency care unit located in a metropolitan city of Ceará, Brazil, in the period from March 15 to June 22, 2021. Content Analysis was used for organization and analysis through references in the area. Results:the potentialities of care during the ELMO helmet use were observed, such as a decrease in indications for orotracheal intubation, improvement in respiratory distress, and decrease in morbidity, but also weaknesses such as diminished patient-healthcare professional communication, need for careful evaluation of the time of use and patient response, risk of psychological instability, and risk of broncho-aspiration; moreover, health teams collaborative aspects such as increased intra-team communication, effective interaction, and greater decision-making were registered. Conclusion:important results in treating COVID-19 can result from the use of this tool; however, there is a need for strict monitoring in order to avoid major respiratory complications as well as physical and psychological sequelae from the wearing of ELMO.Descriptors:Nursing Care. Patient Care Team. Interdisciplinary Placement. COVID-19
Subject(s)
Patient Care Team , Interdisciplinary Placement , COVID-19 , Nursing CareABSTRACT
Dental zirconias have been broadly utilized in dentistry due to their high mechanical properties and biocompatibility. Although initially introduced in dentistry as an infrastructure material, the high rate of technical complications related to veneered porcelain has led to significant efforts to improve the optical properties of dental zirconias, allowing for its monolithic indication. Modifications in the composition, processing methods/parameters, and the increase in the yttrium content and cubic phase have been presented as viable options to improve zirconias' translucency. However, concerns regarding the hydrothermal stability of partially stabilized zirconia and the trade-off observed between optical and mechanical properties resulting from the increased cubic content remain issues of concern. While the significant developments in polycrystalline ceramics have led to a wide diversity of zirconia materials with different compositions, properties, and clinical indications, the implementation of strong, esthetic, and sufficiently stable materials for long-span fixed dental prostheses has not been completely achieved. Alternatives, including advanced polycrystalline composites, functionally graded structures, and nanosized zirconia, have been proposed as promising pathways to obtain high-strength, hydrothermally stable biomaterials. Considering the evolution of zirconia ceramics in dentistry, this manuscript aims to present a critical perspective as well as an update to previous classifications of dental restorative ceramics, focusing on polycrystalline ceramics, their properties, indications, and performance.
ABSTRACT
To assess the influence of dentifrices with different abrasiveness levels on the properties of dental reconstructive materials. Forty-eight cylinders were obtained from four polymeric materials, being two CAD/CAM acrylic resins (Ivotion-Dent and Ivotion-Base), one injected acrylic resin (IvoBase-Hydrid) and one light-cured resin composite (Empress Direct). Specimens were allocated to four subgroups for toothbrushing simulation according to the dentifrice relative dentin abrasivity (RDA) and silica content: (i) RDA 0 = 0%; (ii) RDA 50 = 3%; (iii) RDA 100 = 10%; and (iv) RDA 120 = 25%. Specimens were then subjected to toothbrushing. Surface analyses [surface roughness Ra (SR) and scanning electron microscopy (SEM)] along with hardness and optical properties [translucency parameter (TP) and contrast ratio (CR)] were evaluated before and after toothbrushing. Statistical analyses were performed using ANOVA and Tukey test. A significant increase in SR was observed after toothbrushing with higher RDA toothpastes for Ivotion-Dent (100 and 120) and IvoBase-Hybrid (120). Ivotion-Base and Empress Direct presented no significant differences in SR when analyzed as a function of timepoint and RDA levels. Hardness was not influenced by toothbrushing with different RDA dentifrices, except for Empress Direct with RDA 0 toothpaste, where a decrease in the hardness was observed. TP of Ivotion-Dent and Empress Direct significantly decreased after toothbrushing with higher RDA dentifrices and CR of Ivotion-Dent, Empress Direct and IvoBase-Hybrid significantly increased with higher RDA dentifrices. The levels of dentifrice abrasiveness affected differently the SR, hardness and optical properties of polymeric reconstructive materials after toothbrushing.
ABSTRACT
This study aimed to monitor the effects of dipyrone following multiple administrations in northeastern donkeys. Ten castrated male donkeys, aged 6.4 ± 3 years and weighing 130.6 ± 9.8 kg, were administered dipyrone (25 mg/kg IV) every 12 h, resulting in six administrations (D1 to D6) per animal. Blood samples were collected over a 72 h monitoring period. A validated UHPLC-MS/MS method was employed to determine the plasma concentrations of the 4- methylaminoantipyrine (4-MAA) and 4-aminoantipyrine (4-AA). The calculated pharmacokinetic variables of 4-MAA after D1 and D6 were, respectively: Cmax (µg/mL) = 163.60 ± 179.72 and 178.79 ± 196.94; T1/2beta (h) = 2.65 ± 0.65 and 3.37 ± 1.03; and AUC0-t (µg/mL × h) = 240.38 ± 130.87 and 373.52 ± 78.85. The same variables for 4-AA were: Cmax, (µg/mL) = 0.44 ± 0.27 and 0.90 ± 0.31, T1/2beta (h) = 14.77 ± 13.13 and 35.97 and AUC0-t (µg/mL × h) = 3.20 ± 0.43 and 27.73 ± 11.99. Concentrations of 4-MAA exceeded the minimum concentration required for 50% inhibition of cyclooxygenases 1 and 2. However, an accumulation of 4-AA, was observed. Further clinical studies are necessary to ascertain the implications of these findings on the pharmacodynamic response to dipyrone in northeastern donkeys.
Subject(s)
Dipyrone , Equidae , Male , Animals , Dipyrone/pharmacokinetics , Brazil , Tandem Mass Spectrometry/veterinary , Ampyrone/pharmacokineticsABSTRACT
STATEMENT OF PROBLEM: The bonding of implant-supported prostheses is determined by abutment material, convergence angle, height, surface treatment, and luting agents. However, studies evaluating the bonding of luting agents to titanium base abutments with different heights under fatigue conditions are scarce. PURPOSE: The purpose of this in vitro study was to evaluate the retention of zirconia crowns bonded with different luting agents to titanium base abutments of different heights before and after fatigue testing. MATERIAL AND METHODS: Zirconia crowns were designed, milled, and distributed into 4 experimental groups according to the luting agents (G-Multi Primer/G-Cem LinkForce [MP/GC] and Scotchbond Universal/RelyX Ultimate [SU/RU]) and titanium base abutment heights (2.5 mm and 4 mm) (n=10). Pull-out testing was performed in a universal testing machine at a crosshead speed of 1 mm/min until crown displacement. Fatigue testing was performed by an electric precision fatigue simulator (1×106 cycles; 100 N; and 15 Hz), followed by pull-out testing of fatigued specimens. Collected data were statistically evaluated by using a linear mixed model after post hoc comparisons by the least significant difference test (α=.05). RESULTS: Luting agents, abutment heights, and fatigue influenced the bonding retention of zirconia crowns to titanium base abutments. SU/RU agents promoted higher pull-out compared with MP/GC for both abutment heights before and after fatigue. Higher abutment height increased pull-out regarding lower abutment height for SU/RU materials before and after fatigue testing. Although fatigue had no significant effect on the pull-out of MP/GC, lower bond retention was observed for SU/RU after fatigue, regardless of abutment height. CONCLUSIONS: Luting agent composition and the interaction with abutment height and fatigue influenced the retention of zirconia crowns to titanium base abutments.
Subject(s)
Dental Cements , Dental Implants , Dental Cements/chemistry , Titanium/chemistry , Crowns , Zirconium/chemistry , Materials Testing , Dental Abutments , Dental Stress AnalysisABSTRACT
To assess the reliability and failure modes of Ti-base abutments supported by narrow and wide-diameter implant systems. Narrow (Ø3.5 × 10 mm) and wide (Ø5 × 10 mm) implant systems of two different manufacturers with internal conical connections (16°) and their respective Ti-base abutments (3.5 and 4.5 mm) were evaluated. Ti-base abutments were torqued to the implants, standardized metallic maxillary incisor crowns were cemented, and step stress accelerated life testing of eighteen assemblies per group was performed in three loading profiles: mild, moderate, and aggressive until fracture or suspension. Reliability for missions of 100,000 cycles at 100 and 150 N was calculated, and fractographic analysis was performed. For missions at 100 N for 100,000 cycles, both narrow and wide implant systems exhibited a high probability of survival (≥99%, CI: 94-100%) without significant differences. At 150 N, wide-diameter implants presented higher reliability (≥99%, CI: 99-100%) compared to narrow implants (86%, CI: 61-95%), with no significant differences among manufacturers. Failure mode predominantly involved Ti-base abutment fractures at the abutment platform. Ti-base abutments supported by narrow and wide implant systems presented high reliability for physiologic masticatory forces, whereas for high load-bearing applications, wide-diameter implants presented increased reliability. Failures were confined to abutment fractures.
ABSTRACT
The present study aimed to identify tick and flea species infesting captive tapirs (Tapirus terrestris and Tapirus kabomani) in the Brazilian Amazon. Ectoparasites were collected from tapirs chemically restrained in Zoo-botanical Parks, breeding facilities, conservationists and, environmental compensation areas in the states of Amapá, Amazonas, and Pará. After collection, the tick and flea specimens were placed in plastic pots containing isopropanol and identified according to dichotomous keys. Ectoparasite infestations were observed in 55% (18/33) tapirs, of which 61% (11/18) were single infestations with ticks or fleas, and 39% (7/18) were mixed infestations with different species of ticks and/or fleas. In total, 227 ticks (15 larvae, 107 nymphs, 38 females and 67 males) and 14 fleas (eight females and six males) were collected, identifying four tick species (Amblyomma cajennense sensu stricto , Amblyomma naponense, Amblyomma oblongoguttatum, and Amblyomma pacae) and three flea species and/or subspecies (Ctenocephalides felis felis, Rhopalopsyllus australis australis, and Tunga penetrans). In conclusion, infestations with Ixodidae ticks and Rhopalopsyllidae, Pulicidae and Tungidae fleas were found in captive tapirs in the Brazilian Amazon, and A. cajennense s.s. was the most frequent species. Additionally, the present study reports new associations between A. pacae and R. a. australis with T. terrestris and between A. cajennense s.s. with T. kabomani.
Subject(s)
Flea Infestations , Ixodidae , Siphonaptera , Tick Infestations , Ticks , Male , Female , Animals , Brazil/epidemiology , Perissodactyla , Flea Infestations/epidemiology , Flea Infestations/veterinary , Flea Infestations/parasitology , Tick Infestations/epidemiology , Tick Infestations/veterinary , Tick Infestations/parasitologyABSTRACT
This study aimed to develop films of chitosan (CSF) associated with pentoxifylline (PTX) for healing cutaneous wounds. These films were prepared at two concentrations, F1 (2.0 mg/mL) and F2 (4.0 mg/mL), and the interactions between the materials, structural characteristics, in vitro release, and morphometric aspects of skin wounds in vivo were evaluated. The formation of the CSF film with acetic acid modifies the polymeric structure, and the PTX demonstrates interaction with the CSF, in a semi-crystalline structure, for all concentrations. The release for all films was proportional to the concentration, with two phases: a fast one of ≤2 h and a slow one of >2 h, releasing 82.72 and 88.46% of the drug after 72 h, being governed by the Fickian diffusion mechanism. The wounds of the mice demonstrate a reduction of up to 60% in the area on day 2 for F2 when compared to CSF, F1, and positive control, and this characteristic of faster healing speed for F2 continues until the ninth day with wound reduction of 85%, 82%, and 90% for CSF, F1, and F2, respectively. Therefore, the combination of CSF and PTX is effective in their formation and incorporation, demonstrating that a higher concentration of PTX accelerates skin-wound reduction.
ABSTRACT
Com base no desenvolvimento da odontologia adesiva, restaurações minimamente invasivas em cerâmica são utilizadas como alternativas para restaurar um dente. As cerâmicas odontológicas são amplamente aplicadas na área odontológica principalmente devido à sua estética e resistência mecânica. Uma das propriedades da cerâmica a ser bem conhecida antes de seu uso, é a resistência ao desgaste que deve ser compatível com o comportamento de desgaste do antagonista para evitar desempenhos indesejados. Portanto, vários métodos têm sido realizados para avaliar o comportamento do desgaste dos materiais cerâmicos considerando diferentes condições presentes no complexo meio oral. Este estudo teve como objetivo compilar os métodos utilizados para investigar o desgaste das cerâmicas odontológicas e descrever os mecanismos de desgaste envolvidos nos mesmos. A obtenção e análise de dados também é abordada para discutir os resultados obtidos a partir de diferentes métodos, bem como a análise clínica do desgaste e perspectivas futuras sobre esse tema. Em conclusão, muitas metodologias estão disponíveis para medir o desgaste cerâmico. Portanto, os métodos devem ser selecionados com base na relevência clínica de cada estudo e devem seguir parâmetros previamente relatados para padronização, permitindo a comparação da literatura (AU)
Based on the development of adhesive dentistry, minimally invasive restorations in ceramics are used as alternatives to restore a tooth. Dental ceramics are largely applied in the dentistry field mainly due to their esthetic and mechanical strength. One of the ceramic properties to be well known before its use is the wear resistance that should be compatible with the antagonist wear behavior to avoid unwanted performance. Therefore, several methods have been performed to assess the ceramic materials wear behavior considering different conditions present in the complex oral medium. This study aimed to compile the methods used to investigate dental ceramics wear and to describe the wear mechanisms involved on them. Obtaining and analyzing data is also addressed to discuss the results obtained from different methods, as well as the clinical analysis of wear and future perspectives on this topic. In conclusion, many methodologies are available to measure the ceramic wear. Therefore, the methods must be selected based on the clinical significance of each study and should follow previously reported parameters for standardization, allowing literature comparison. (AU)
Subject(s)
Metal Ceramic Alloys , Dental Restoration Wear , Dental Materials , Tooth Wear , MethodsABSTRACT
OBJECTIVE: To assess potential antagonist wear and survival probability of silica-infiltrated zirconia compared to glass-graded, glazed, and polished zirconia. METHODS: Table top restorations made of 3Y-TZP (3Y), 5Y-PSZ (5Y), and lithium disilicate (LD) were bonded onto epoxy resin preparations. Each zirconia was divided into five groups according to the surface treatment: polishing; glaze; polishing-glaze; glass infiltration; and silica infiltration. The LD restorations received a glaze layer. Specimens were subjected to sliding fatigue wear using a steatite antagonist (1.25 ×106 cycles, 200 N). The presence of cracks, fractures, and/or debonding was checked every one/third of the total number of cycles was completed. Roughness, microstructural, Scanning electron microscopy, wear and residual stress analyses were conducted. Kaplan-Meier, Mantel-Cox (log-rank) and ANOVA tests were performed for statistical analyses. RESULTS: The survival probability was different among the groups. Silica infiltration and polishing-glaze led to lower volume loss than glaze and glass-infiltration. Difference was observed for roughness among the zirconia and surface treatment, while lithium disilicate presented similar roughness compared to both glazed zirconia. Scanning electron microscopy revealed the removal of the surface treatment after sliding fatigue wear in all groups. Compressive stress was detected on 3Y surfaces, while tensile stress was observed on 5Y. SIGNIFICANCE: 3Y and 5Y zirconia behaved similarly regarding antagonist wear, presenting higher antagonist wear than the glass ceramic. Silica-infiltrated and polished-glazed zirconia produced lower antagonist volume loss than glazed and glass-infiltrated zirconia. Silica-infiltrated 3Y and lithium disilicate restorations were the only groups to show survival probabilities lower than 85%.