ABSTRACT
Glass ceramics are widely used to manufacture esthetic veneers, inlays, onlays, and crowns. Although the clinical survival rates ofglass-ceramic restorations arefavorable,fractures or chips are common. Certain cases can be repaired with direct composite. AIM: The aim of this study was to investigate the interaction effect of different designs and surface treatments on the load-to-failure of lithium disilicate glass-ceramic repaired with nanofilled composite. MATERIALS AND METHOD: Lithium-disilicate glass-ceramic slabs (IPS e.max Press, Ivoclar Vivadent) with three different designs of the top surface (flat, single plateau, or doubleplateau) (n=U) received 'no treatment', '5% HF etching', or "AI2O3 sandblasting". HF-etched and sandblasted slabs also received silane and universal one-step adhesive application. All slabs were incrementally repaired with nanofilled composite (Filtek Z350, 3M ESPE) up to6 mm above the highest ceramic top plateau. Specimens were stored in artificial saliva at 37 °C for 21 days and then subjected to 1,000 thermocycles between 5 and 55 °C. The interface composite-ceramic of each specimen was tensile tested until failure in a universal testing machine and the mode of failure was determined under a stereomicroscope. The ceramic surface morphology of one representative tested specimen from each subgroup (design/surface treatment) was observed through scanning electron microscopy (SEM). RESULTS: Regardless of ceramic design, the absence of surface treatment resulted in significantly lower load-to-failure values. No significant differences in load-to-failure values were observed between HF-etched and sandblasted specimens for the flat design; however, HF etching resulted in significantly higher load-to-failure values than sandblasting for both single plateau and double plateau designs. The majority (60%) of HF-etched specimens with single plateau or double plateau presented mixed failures. SEM photomicrographs showed that HF-etched specimens had smoother surfaces than sandblasted specimens. CONCLUSION: The surface treatment of a defective lithium disilicate glass-ceramic restoration has more influence than its macroscopic design on the retention of the composite repair. HF etching seems to provide higher bond strength to the composite repair.
Embora fraturas e lascamento de restauragoes vitrocerámicas sejam comuns, alguns casos podem ser reparados com compósito direto. OBJETIVO: investigar o efeito da interagao de diferentes formas e tratamentos de superficie na carga de ruptura de uma vitrocerámica reforgada com dissilicato de litio reparada com compósito nanoparticulado. MATERIAIS E MÉTODOS: A superficie superior de espécimes de vitroceramica (IPS e.max Press, Ivoclar Vivadent) foi preparada com tres formas (plana, plato único, ou duplo) e recebeu (n=11): 'nenhum tratamento', 'condicionamento com ácido hidrofluoridrico 5%', ou 'jateamento com AfOf. Ambos espécimes condicionados e jateados receberam silano e adesivo universal. Todos os espécimes foram reparados incrementalmente com compósito (Filtek Z350, 3M ESPE) até6 mm acima do plato cerámico mais alto, armazenados em saliva artificial á 37 °C por 21 dias, e submetidos á 1.000 termociclos (5 e 55 °C). A interface compósito-cerámica de cada amostra foi testada á tragao até sua falha em máquina universal e o modo de falha foi determinado com estereomicroscópio. A morfologia da superficie de uma amostra representativa de forma/tratamento de superficie foi observada através de microscopia eletronica de varredura (MEV). RESULTADOS: Independentemente da forma ceramica, a ausencia de tratamento superficial resultou em valores de carga de ruptura significativamente menores. Nao foi observada differenga significativa entre os espécimes planos condicionados ou jateados; no entanto, o condicionamento resultou em valores significativamente maiores que o jateamento para espécimes com plato único e duplo. A maioria (60%) dos espécimes condicionados e com plato único ou duplo apresentou falhas mistas. Imagens SEM demonstraram rugosidade superficial mais regular dos espécimes condicionados que os jateados. CONCLUSÕES: O tratamento superficial de uma restauragao defeituosa de vitrocerámica reforgada por dissilicato de litio tem maior influencia na retengao do reparo de compósito do que sua forma macroscópica; ainda, o condicionamento com ácido hidrofluoridrico parece proporcionar maior resistencia de uniao ao reparo com compósito.
Subject(s)
Ceramics , Dental Porcelain , Surface Properties , Ceramics/chemistry , Dental Porcelain/chemistry , Materials Testing , Dental Restoration Failure , Composite Resins/chemistry , Dental Stress Analysis , Dental Prosthesis DesignABSTRACT
ABSTRACT Glass ceramics are widely used to manufacture esthetic veneers, inlays, onlays, and crowns. Although the clinical survival rates ofglass-ceramic restorations arefavorable,fractures or chips are common. Certain cases can be repaired with direct composite. Aim The aim of this study was to investigate the interaction effect of different designs and surface treatments on the load-to-failure of lithium disilicate glass-ceramic repaired with nanofilled composite. Materials and Method Lithium-disilicate glass-ceramic slabs (IPS e.max Press, Ivoclar Vivadent) with three different designs of the top surface (flat, single plateau, or doubleplateau) (n=U) received 'no treatment', '5% HF etching', or "AI2O3 sandblasting". HF-etched and sandblasted slabs also received silane and universal one-step adhesive application. All slabs were incrementally repaired with nanofilled composite (Filtek Z350, 3M ESPE) up to6 mm above the highest ceramic top plateau. Specimens were stored in artificial saliva at 37 °C for 21 days and then subjected to 1,000 thermocycles between 5 and 55 °C. The interface composite-ceramic of each specimen was tensile tested until failure in a universal testing machine and the mode of failure was determined under a stereomicroscope. The ceramic surface morphology of one representative tested specimen from each subgroup (design/surface treatment) was observed through scanning electron microscopy (SEM). Results Regardless of ceramic design, the absence of surface treatment resulted in significantly lower load-to-failure values. No significant differences in load-to-failure values were observed between HF-etched and sandblasted specimens for the flat design; however, HF etching resulted in significantly higher load-to-failure values than sandblasting for both single plateau and double plateau designs. The majority (60%) of HF-etched specimens with single plateau or double plateau presented mixed failures. SEM photomicrographs showed that HF-etched specimens had smoother surfaces than sandblasted specimens. Conclusion The surface treatment of a defective lithium disilicate glass-ceramic restoration has more influence than its macroscopic design on the retention of the composite repair. HF etching seems to provide higher bond strength to the composite repair.
RESUMO Embora fraturas e lascamento de restauragoes vitrocerámicas sejam comuns, alguns casos podem ser reparados com compósito direto. Objetivo investigar o efeito da interagao de diferentes formas e tratamentos de superficie na carga de ruptura de uma vitrocerámica reforgada com dissilicato de litio reparada com compósito nanoparticulado. Materials e Método A superficie superior de espécimes de vitroceramica (IPS e.max Press, Ivoclar Vivadent) foi preparada com tres formas (plana, plato único, ou duplo) e recebeu (n=11): 'nenhum tratamento', 'condicionamento com ácido hidrofluoridrico 5%', ou 'jateamento com AfOf. Ambos espécimes condicionados e jateados receberam silano e adesivo universal. Todos os espécimes foram reparados incrementalmente com compósito (Filtek Z350, 3M ESPE) até6 mm acima do plato cerámico mais alto, armazenados em saliva artificial á 37 °C por 21 dias, e submetidos á 1.000 termociclos (5 e 55 °C). A interface compósito-cerámica de cada amostra foi testada á tragao até sua falha em máquina universal e o modo de falha foi determinado com estereomicroscópio. A morfologia da superficie de uma amostra representativa de forma/tratamento de superficie foi observada através de microscopia eletronica de varredura (MEV). Resultados Independentemente da forma ceramica, a ausencia de tratamento superficial resultou em valores de carga de ruptura significativamente menores. Nao foi observada differenga significativa entre os espécimes planos condicionados ou jateados; no entanto, o condicionamento resultou em valores significativamente maiores que o jateamento para espécimes com plato único e duplo. A maioria (60%) dos espécimes condicionados e com plato único ou duplo apresentou falhas mistas. Imagens SEM demonstraram rugosidade superficial mais regular dos espécimes condicionados que os jateados. Conclusoes O tratamento superficial de uma restauragao defeituosa de vitrocerámica reforgada por dissilicato de litio tem maior influencia na retengao do reparo de compósito do que sua forma macroscópica; ainda, o condicionamento com ácido hidrofluoridrico parece proporcionar maior resistencia de uniao ao reparo com compósito.
ABSTRACT
During the manufacture of ceramic restorations there is an important step of finishing and polishing and the effects of different types of these procedures on the surface characteristics of ceramics are not known for sure. AIM: To evaluate the effects of various surface treatments and immersion in coloring substances on the roughness, microhardness, and color stability of CAD-CAM monolithic ceramics. MATERIALS AND METHOD: The ceramics used were lithium disilicate reinforced with zirconium dioxide (Suprinity), lithium disilicate (E.max) or leucite (Empress). They were subjected to two surface treatments: glazing (group G) (n=20) or mechanical polishing (group P) (n=20). Then they were divided into two subgroups (n=10) to be treated with the staining substance (coffee or water). Roughness, microhardness and color were measured before and after treatment. Data were subjected to analysis of variance and multiple comparisons were performed with Tukey tests at 5% significance level. RESULTS: Roughness was lower in all tested ceramics after polishing than after glazing. Microhardness was the same for polished and glazed E.max, higher in glazed than polished Empress, and higher in polished than glazed Suprinity. Analysis of the effects of glazing and polishing on the individual ceramics showed that the ΔE2000 and ΔWID data of the E.max ceramic subjected to polishing showed greater change. Mechanical polishing is a good option for surface treatment of monolithic ceramics. CONCLUSION: Glazing was inferior and less satisfactory than polishing. Glazing generates changes that can lead to color instability.
Durante a confecção de restaurações cerâmicas existe uma importante etapa dos procedimentos de acabamento e polimento. Os efeitos de diferentes tipos desses procedimentos nas características superficiais das cerâmicas não são conhecidos com certeza. Objetivo: Avaliar os efeitos de vários tratamentos de superfície e imersão em substâncias corantes na rugosidade, microdureza e estabilidade de cor de cerâmicas monolíticas CAD-CAM. Materiais e Métodos: As cerâmicas utilizadas foram dissilicato de lítio reforçado com dióxido de zircônio (Suprinity), dissilicato de lítio (E.max) ou leucita (Empress). Foram submetidos a dois tratamentos de superfície: glazeamento (grupo G) (n=20) ou polimento mecânico (grupo P) (n=20). Em seguida, foram divididos em dois subgrupos (n=10) para serem tratados com a substância corante (café ou água). Rugosidade, microdureza e cor foram medidas antes e após o tratamento. Os dados foram submetidos à análise de variância e as comparações múltiplas foram realizadas com testes de Tukey ao nível de 5% de significância. Resultados: A rugosidade foi menor em todas as cerâmicas testadas após o polimento do que após o glazeamento. A microdureza foi a mesma para o E.max polido e vidrado, maior no Empress vidrado do que no polido, e maior no Suprinity polido do que no vidrado. A análise dos efeitos do esmaltação e polimento nas cerâmicas individuais mostrou que os dados ΔE2000 e ΔWID da cerâmica E.max submetida ao polimento apresentaram maior alteração. O polimento mecânico é uma boa opção para o tratamento superficial de cerâmicas monolíticas. Conclusão: A aplicação do glazing foi inferior e menos satisfatório que o polimento, gerando alterações que podem levar à instabilidade da cor.
Subject(s)
Dental Polishing , Immersion , Materials Testing , Dental Polishing/methods , Surface Properties , Ceramics/chemistry , Dental Porcelain/chemistry , Computer-Aided Design , ColorABSTRACT
ABSTRACT During the manufacture of ceramic restorations there is an important step of finishing and polishing and the effects of different types of these procedures on the surface characteristics of ceramics are not known for sure. Aim: To evaluate the effects of various surface treatments and immersion in coloring substances on the roughness, microhardness, and color stability of CAD-CAM monolithic ceramics. Materials and Method: The ceramics used were lithium disilicate reinforced with zirconium dioxide (Suprinity), lithium disilicate (E.max) or leucite (Empress). They were subjected to two surface treatments: glazing (group G) (n=20) or mechanical polishing (group P) (n=20). Then they were divided into two subgroups (n=10) to be treated with the staining substance (coffee or water). Roughness, microhardness and color were measured before and after treatment. Data were subjected to analysis of variance and multiple comparisons were performed with Tukey tests at 5% significance level. Results: Roughness was lower in all tested ceramics after polishing than after glazing. Microhardness was the same for polished and glazed E.max, higher in glazed than polished Empress, and higher in polished than glazed Suprinity. Analysis of the effects of glazing and polishing on the individual ceramics showed that the ΔE2000 and ΔWID data of the E.max ceramic subjected to polishing showed greater change. Mechanical polishing is a good option for surface treatment of monolithic ceramics. Conclusion: Glazing was inferior and less satisfactory than polishing. Glazing generates changes that can lead to color instability.
RESUMO Durante a confecção de restaurações cerâmicas existe uma importante etapa dos procedimentos de acabamento e polimento. Os efeitos de diferentes tipos desses procedimentos nas características superficiais das cerâmicas não são conhecidos com certeza. Objetivo: Avaliar os efeitos de vários tratamentos de superfície e imersão em substâncias corantes na rugosidade, microdureza e estabilidade de cor de cerâmicas monolíticas CAD-CAM. Materiais e Métodos: As cerâmicas utilizadas foram dissilicato de lítio reforçado com dióxido de zircônio (Suprinity), dissilicato de lítio (E.max) ou leucita (Empress). Foram submetidos a dois tratamentos de superfície: glazeamento (grupo G) (n=20) ou polimento mecânico (grupo P) (n=20). Em seguida, foram divididos em dois subgrupos (n=10) para serem tratados com a substância corante (café ou água). Rugosidade, microdureza e cor foram medidas antes e após o tratamento. Os dados foram submetidos à análise de variância e as comparações múltiplas foram realizadas com testes de Tukey ao nível de 5% de significância. Resultados: A rugosidade foi menor em todas as cerâmicas testadas após o polimento do que após o glazeamento. A microdureza foi a mesma para o E.max polido e vidrado, maior no Empress vidrado do que no polido, e maior no Suprinity polido do que no vidrado. A análise dos efeitos do esmaltação e polimento nas cerâmicas individuais mostrou que os dados ΔE2000 e ΔWID da cerâmica E.max submetida ao polimento apresentaram maior alteração. O polimento mecânico é uma boa opção para o tratamento superficial de cerâmicas monolíticas. Conclusão: A aplicação do glazing foi inferior e menos satisfatório que o polimento, gerando alterações que podem levar à instabilidade da cor.
ABSTRACT
After ozone therapy for bleaching, it is important to evaluate enamel surface properties, to ensure that bleaching provides adequate conditions for sound dental substrate. Aim: The aim of this in vitro study was to evaluate the effects of a bleaching treatment with 10% carbamide peroxide (CP), with or without ozone (O), on the microhardness, roughness and micromorphology of the enamel surface. Materials and Method: Bovine enamel blocks were planed and distributed among the following three bleaching treatment groups (n=10): CP - 1 hour per day/14 days (Opalescence PF 10%/ Ultradent); O - 1 hour per day every 3 days/3 sessions (Medplus V Philozon, 60 mcg/mL and oxygen flow rate of 1 L/min); and OCP - CP with O, 1 hour per day every 3 days/3 sessions. Enamel surface microhardness (Knoop), roughness (Ra), and micromorphology by scanning electron microscopy (5,000x magnification) were determined before and after the treatments. Results: ANOVA and Tukey-Kramer's test showed that enamel microhardness remained unchanged by treatment with O and OCP (p=0.0087), but decreased by treatment with CP. Treatment with O promoted higher enamel microhardness than the other groups (p=0.0169). Generalized linear mixed models for repeated measures over time indicated treatment with CP increased enamel roughness more than OCP or O (p=0.0003). CP produced slight irregularities in enamel micromorphology after the whitening treatment. O, with or without CP, maintained the mechanical and physical properties of microhardness and enamel surface micromorphology, and either maintained or reduced surface roughness, compared to the conventional tray-delivered CP bleaching treatment. Conclusions: Treatment with 10% carbamide peroxide in trays promoted greater changes in enamel surface properties than treatments with ozone and with 10% ozonized carbamide peroxide in the office.
É importante avaliar as propriedades da superfície do esmalte após a aplicação da ozonioterapia para clareamento, para garantir que o efeito clareador proporcione condições adequadas para um substrato dentário hígido. ultório. Objetivo: O objetivo deste estudo in vitro foi avaliar os efeitos de um tratamento clareador com peróxido de carbamida (PC) a 10%, associado ou não ao ozônio (O), na microdureza, rugosidade e micromorfologia da superfície do esmalte. Materiais e Método: Blocos de esmalte bovino foram aplainados e distribuídos entre três grupos de tratamento clareador (n=10): PC - 1 hora por dia/14 dias (Opalescence PF 10%/ Ultradent); O - 1 hora por dia a cada 3 dias/3 sessões (Medplus V Philozon, 60 mcg/mL e fluxo de oxigênio de 1 L/min); e PCO - CP com O, 1 hora por dia a cada 3 dias/3 sessões. A microdureza (Knoop), a rugosidade (Ra) e a micromorfologia da superfície do esmalte avaliada por microscopia eletrônica de varredura (aumento de 5.000x) foram analisadas antes e após os tratamentos. Resultados: ANOVA e teste de Tukey-Kramer mostraram que O e PCO mantiveram os valores de microdureza do esmalte ao final do tratamento (p=0,0087), enquanto PC promoveu diminuição da microdureza. O promoveu maiores valores de microdureza do esmalte do que os outros grupos ao final do tratamento (p=0,0169). Modelos lineares generalizados mistos para medidas repetidas no tempo indicaram um aumento na rugosidade da superfície para PC, levando a maior rugosidade do esmalte ao final do tratamento, em comparação com PCO ou O (p=0,0003). PC apresentou pequenas irregularidades na micromorfologia do esmalte após o tratamento clareador. O, com ou sem PC, manteve as propriedades mecânicas e físicas de microdureza e micromorfologia da superfície do esmalte, e manteve ou reduziu a rugosidade da superfície, em comparação com o tratamento clareador a base de PC aplicado em moldeira convencional. Conclusões: O tratamento com peróxido de carbamida a 10% para uso em moldeiras promoveu maiores alterações nas propriedades de superfície do esmalte do que aquelas observadas nos tratamentos com ozônio e com peróxido de carbamida ozonizado a 10% para uso em consultório.
Subject(s)
Ozone , Tooth Bleaching , Ozone/pharmacologyABSTRACT
ABSTRACT Aim: This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. Materials and Method: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope. Results: There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. Conclusions: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer.
RESUMO Objetivo: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. Resultados: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levo
ABSTRACT
Acidic conditions can cause hydrolysis and accelerate degradation of resin composites (RCs). Since there are limited and controversial data on the effect of acids on bulk-fill RCs, this study assessed the surface roughness (SR) and flexural strength (FS) of these RCs under simulated carious and erosion conditions. Bars of Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent), and Aura Bulk Fill (ABF, SDI) and a conventional RC [Filtek Z350XT (FZ, 3M/ESPE)] were allocated (n=15) to undergo caries or erosion conditions. The control group was kept in artificial saliva (AS). The bars were evaluated for SR change (final-baseline) and for three-point FS. Data were analyzed using ANOVA and Tukey's test. At the baseline (p <0.001), the SR of RCs ranked as follows: (TBF = XTF) < FBF (none differed from FZ) < ABF. The interplay between RCs and conditions affected SR change (p = 0.025). While after storage in AS, there was no difference among RCs, following carious and erosive conditions, ABF showed higher SR change. For FS (p <0.001), XTF > (FBF = FZ) > (TBF = FZ) > ABF, with no difference among control, carious and erosive conditions (p = 0.148). Depending on the restorative bulk-fill RCs, carious and erosive conditions roughen the surface but do not affect the FS of these materials.
Condições acídicas podem causar hidrólise e acelerar a degradação de resinas compostas (RCs). Como há dados limitados e controversos sobre os efeitos de ácidos sobre RCs bulk-fill, este estudo avaliou a rugosidade de superfície (RS) e a resistência flexural (RF) dessas RCs sob condições simuladas de cárie e erosão. Barras de Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent) e Aura Bulk Fill (ABF, SDI) e de uma RC convencional [Filtek Z350XT (FZ, 3M/ESPE)] foram alocadas (n=15) para estarem sob condições cariogênicas ou erosivas. O grupo controle foi mantido em saliva artificial saliva (SA). As barras foram avaliadas quanto à alteração de RS (final-inicial) e à RF de três pontos. Os dados foram analisados utilizando ANOVA e teste de Tukey. Inicialmente (p <0,001) a RS das RCs foi a seguinte: (TBF = XTF) < FBF (nenhuma diferiu de FZ)< ABF. A interação entre as RCs e as condições acídicas influenciou a alteração de RS (p = 0,025). Após armazenamento na SA, não houve diferença entre as RCs, enquanto após condições cariogênicas e erosivas a ABF mostrou a maior alteração de RS. Para FS (p < 0,001), XTF > (FBF = FZ) > (TBF = FZ) >ABF, sem diferença entre controle e condições cariogênicas e erosivas (p = 0,148). Dependendo da RC bulk-fill restauradora, condições cariogênicas e erosivas aumentam a RS, mas não alteram a RF desses materiais.
Subject(s)
Composite Resins , Dental Caries , Humans , Saliva, Artificial , Dental Caries/therapy , Materials TestingABSTRACT
ABSTRACT Acidic conditions can cause hydrolysis and accelerate degradation of resin composites (RCs). Since there are limited and controversial data on the effect of acids on bulk-fill RCs, this study assessed the surface roughness (SR) and flexural strength (FS) of these RCs under simulated carious and erosion conditions. Bars of Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent), and Aura Bulk Fill (ABF, SDI) and a conventional RC [Filtek Z350XT (FZ, 3M/ESPE)] were allocated (n=15) to undergo caries or erosion conditions. The control group was kept in artificial saliva (AS). The bars were evaluated for SR change (final-baseline) and for three-point FS. Data were analyzed using ANOVA and Tukey's test. At the baseline (p <0.001), the SR of RCs ranked as follows: (TBF = XTF) < FBF (none differed from FZ) < ABF. The interplay between RCs and conditions affected SR change (p = 0.025). While after storage in AS, there was no difference among RCs, following carious and erosive conditions, ABF showed higher SR change. For FS (p <0.001), XTF > (FBF = FZ) > (TBF = FZ) > ABF, with no difference among control, carious and erosive conditions (p = 0.148). Depending on the restorative bulk-fill RCs, carious and erosive conditions roughen the surface but do not affect the FS of these materials.
RESUMO Condições acídicas podem causar hidrólise e acelerar a degradação de resinas compostas (RCs). Como há dados limitados e controversos sobre os efeitos de ácidos sobre RCs bulk-fill, este estudo avaliou a rugosidade de superfície (RS) e a resistência flexural (RF) dessas RCs sob condições simuladas de cárie e erosão. Barras de Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent) e Aura Bulk Fill (ABF, SDI) e de uma RC convencional [Filtek Z350XT (FZ, 3M/ESPE)] foram alocadas (n=15) para estarem sob condições cariogênicas ou erosivas. O grupo controle foi mantido em saliva artificial saliva (SA). As barras foram avaliadas quanto à alteração de RS (final-inicial) e à RF de três pontos. Os dados foram analisados utilizando ANOVA e teste de Tukey. Inicialmente (p <0,001) a RS das RCs foi a seguinte: (TBF = XTF) < FBF (nenhuma diferiu de FZ)< ABF. A interação entre as RCs e as condições acídicas influenciou a alteração de RS (p = 0,025). Após armazenamento na SA, não houve diferença entre as RCs, enquanto após condições cariogênicas e erosivas a ABF mostrou a maior alteração de RS. Para FS (p < 0,001), XTF > (FBF = FZ) > (TBF = FZ) >ABF, sem diferença entre controle e condições cariogênicas e erosivas (p = 0,148). Dependendo da RC bulk-fill restauradora, condições cariogênicas e erosivas aumentam a RS, mas não alteram a RF desses materiais.
ABSTRACT
AIM: This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. MATERIALS AND METHOD: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope. RESULTS: There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. CONCLUSIONS: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer.
OBJETIVO: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. RESULTADOS: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levou a uma menor permeabilidade dentinária e a mais irregularidades na superfície da camada adesiva.
Subject(s)
Chitosan , Dental Bonding , Humans , Chitosan/pharmacology , Composite Resins/chemistry , Dental Cements , Dentin , Dentin Permeability , Dentin-Bonding Agents/pharmacology , Dentin-Bonding Agents/chemistry , Materials Testing , Resin Cements/chemistry , Tensile StrengthABSTRACT
The aim of this study was to compare low- and high-viscosity bulk-fill composites for Knoop microhardness (KHN), microtensile bond strength (MTBS) to dentin in occlusal cavities, and fracture strength (FS) in molars with mesialocclusal- distal restoration. Disk-shaped samples with different thicknesses (2 or 4 mm) of low-viscosity (SDR Flow, Dentsply) and high-viscosity bulk-fill composites (Filtek BulkFill, 3M ESPE; and Tetric-N Ceram Bulk Fill, Ivoclar Vivadent) were prepared for top and bottom KHN analysis (n=10). MTBS to dentin and fracture pattern was evaluated in human molars with occlusal cavities restored with (n=10): conventional nanocomposite (Z350XT, 3M ESPE), low-viscosity (Filtek Bulk-fill Flow, 3M ESPE) or high-viscosity bulk-fill composites (Filtek BulkFill). The FS and fracture pattern of human molar with mesial-occlusal-distal restorations submitted or not to thermomechanical cycling were investigated (n=10) using: intact tooth (control), and restoration based on conventional microhybrid composite (Z250, 3M ESPE), low-viscosity (SDR Flow) or high-viscosity bulk-fill composites (Filtek BulkFill). The data were submitted to split-plot ANOVA (KHN), one-way ANOVA (MTBS), two-way ANOVA (FS) followed by Tukey's test (α=0.05). For KHN, there was no significant difference for the resin composites between the top and bottom. For MTBS, no significant differences among the materials were detected; however, the low-viscosity composite presented lower frequency of adhesive failures. For FS, there was no significant difference between composites and intact tooth regardless of thermomechanical cycling. Low- and high-viscosity bulk-fill composites have comparable microhardness and microtensile bond strength when used in occlusal restorations. Likewise, the bulk-fill composites present similar fracture strength in molars with mesio-occlusal-distal restorations.
O objetivo deste estudo foi comparar resinas compostas bulk- -fill de baixa e alta viscosidade quanto à microdureza Knoop (KHN), resistência de união a microtração (MTBS) em cavidades oclusais e carga à fratura (FS) em molares com restauração mesio-oclusal-distal. Amostras em forma de disco com diferentes espessuras (2 ou 4 mm) de resinas bulk-fill de baixa viscosidade (SDR Flow, Dentsply) e alta viscosidade (Filtek BulkFill, 3M ESPE; e Tetric-N Ceram Bulk Fill, Ivoclar Vivadent) foram obtidas para análise de KHN no topo e na base (n = 10). A MTBS em dentina e o padrão de fratura foram avaliados em molares humanos com cavidades oclusais restauradas com (n = 10): resina composta nanoparticulada convencional (Z350XT, 3M ESPE), resinas bulk-fill de baixa viscosidade (Filtek Bulk-fill Flow, 3M ESPE) ou alta viscosidade (Filtek BulkFill). Foram investigados a FS e o padrão de fratura de molares humanos em restaurações mesial-ocluso-distais sub metidas ou não à ciclagem termomecânica (n = 10), sendo: dente íntegro (controle), e restaurações baseadas em resina composta microhíbrida convencional (Z250, 3M ESPE); resinas bulk-fill de baixa viscosidade (SDR Flow) ou alta viscosidade (Filtek BulkFill). Os dados foram submetidos a split-plot ANOVA (KHN), one-way ANOVA (MTBS), two-way ANOVA (FS) seguidos do teste de Tukey (α = 0,05). Para KHN, não houve diferença significativa entre o topo e a base para as resinas compostas. Para MTBS, não foram detectadas diferenças significativas entre os materiais; entretanto, a resina bulk-fill de baixa viscosidade apresentou menor frequência de falhas adesivas. Para FS, não houve diferença significativa entre os materiais e o dente íntegro, independentemente da ciclagem termomecânica. As resinas bulk-fill de baixa e alta viscosidade têm microdureza e resistência à microtração comparáveis quando usados em restaurações oclusais. Da mesma forma, as resinas bulk-fill apresentam resistência à fratura semelhante em molares com restaurações mesio-oclusal-distais.
Subject(s)
Composite Resins , Flexural Strength , Humans , Materials Testing , Molar , ViscosityABSTRACT
The aim of this in vitro study was to evaluate the effect of bleaching protocols on the surface roughness (Ra), color change and surface micromorphology of a low-viscosity bulk-fill composite (Filtek Bulk Fill Flow, 3M ESPE), a highviscosity bulk-fill composite (Filtek Bulk Fill, 3M ESPE) and a conventional nanoparticulate composite resin (control) (Filtek Z350 XT, 3M ESPE). Forty samples of each composite (disks 5 mm in diameter and 2 mm thick) were randomly divided into four groups (n=10), according to bleaching protocol: a) 10% carbamide peroxide gel (Opalescence, Ultradent Products) (2 h/ day, for 14 days); b) 40% hydrogen peroxide gel (Opalescence Boost, Ultradent Products) (three bleaching sessions, once a week, 45 min/session); c) whitening rinse (Listerine Whitening Extreme, Johnson & Johnson) (2 min/day, for 14 days); and d) distilled water (control). The samples were submitted to triplicate readings (Ra and color [CIELAB parameters]) before and after contact with bleaching protocols. Micromorphology was analyzed in a scanning electron microscope (SEM). Ra and color parameters (ΔL, Δa, Δb and ΔE) were analyzed by generalized linear models (α=0.05). The Ra of the high-viscosity bulk-fill was significantly higher than that of the other composites (p<0.05). Ra increased significantly (p<0.05) and surface became more irregular (SEM analysis) in all the composite resins, regardless of the bleaching protocol (p<0.05). The high-viscosity bulk-fill composite resin group had significantly lower ΔE (p<0.05) than the nanoparticulate composite resin group immersed in distilled water. It was concluded that the characteristics of each resin significantly influenced the Ra more than the bleaching protocol. The high-viscosity bulk-fill resin presented minor color change.
Este estudo in vitro teve objetivo de avaliar o efeito de protocolos clareadores sobre a rugosidade de superfície (Ra), alteração de cor e micromorfologia de resina bulk-fill de baixa viscosidade (Filtek Bulk Fill Flow, 3M ESPE), alta viscosidade (Filtek Bulk Fill, 3M ESPE) e de uma resina composta nanoparticulada (controle) (Filtek Z350 XT, 3M ESPE). Quarenta amostras de cada resin composta (discos de 5 mm de diâmetro e 2 mm de espessura) foram aleatoriamente divididas em quatro grupos , de acordo com protocolo clareador (n=10): a) Gel de peróxido de carbamida (Opalescence, Ultradent Products) (2 horas/dia, por 14 dias); b) Gel de peróxido de hidrogênio (Opalescence Boost, Ultradent Products) (3 sessões de clareamento, uma por semana, 45 min/sessão); enxaguatório clareador (Listerine Whitening Extreme, Johnson & Johnson) (2 min/dia, por 14 dias); d) água destilada (controle). As amostras foram submetidas a leituras, em triplicata (Ra e cor (parâmetros CIELab) antes e depois do contato com os protocolos clareadores. A micromorfologia de superfície foi conduzida em microscópio eletrônico de varredura (MEV). Ra e parâmetros de cor (ΔL, Δa, Δb e ΔE) foram analisados por modelos lineares generalizados (α=0.05). A Ra da resina bulk-fill de alta viscosidade foi significantemente superior do que para os outros compósitos (p<0.05). A Ra aumentou significantemente (p<0.05) e a superfície ficou mais irregular (MEV) para todos os compósitos, independente do protocolo clareador (p<0,05). A resina bulk-fill de alta viscosidade obteve menor ΔE (p<0.05) do que a resina composta nanoparticulada, imersa em água destilada. Pode-se concluir que as características de cada resina composta influenciaram de forma mais significativa a Ra do que o protocolo clareador. A resina bulk fill de alta viscosidade apresentou menor alteração de cor.
Subject(s)
Composite Resins/chemistry , Hydrogen Peroxide/chemistry , Tooth Bleaching Agents/chemistry , Tooth Bleaching/methods , Tooth Discoloration/drug therapy , Viscosity/drug effects , Color , Humans , Materials TestingABSTRACT
ABSTRACT The aim of this in vitro study was to evaluate the effect of bleaching protocols on the surface roughness (Ra), color change and surface micromorphology of a low-viscosity bulk-fill composite (Filtek Bulk Fill Flow, 3M ESPE), a highviscosity bulk-fill composite (Filtek Bulk Fill, 3M ESPE) and a conventional nanoparticulate composite resin (control) (Filtek Z350 XT, 3M ESPE). Forty samples of each composite (disks 5 mm in diameter and 2 mm thick) were randomly divided into four groups (n=10), according to bleaching protocol: a) 10% carbamide peroxide gel (Opalescence, Ultradent Products) (2 h/ day, for 14 days); b) 40% hydrogen peroxide gel (Opalescence Boost, Ultradent Products) (three bleaching sessions, once a week, 45 min/session); c) whitening rinse (Listerine Whitening Extreme, Johnson & Johnson) (2 min/day, for 14 days); and d) distilled water (control). The samples were submitted to triplicate readings (Ra and color [CIELAB parameters]) before and after contact with bleaching protocols. Micromorphology was analyzed in a scanning electron microscope (SEM). Ra and color parameters (ΔL, Δa, Δb and ΔE) were analyzed by generalized linear models (α=0.05). The Ra of the high-viscosity bulk-fill was significantly higher than that of the other composites (p<0.05). Ra increased significantly (p<0.05) and surface became more irregular (SEM analysis) in all the composite resins, regardless of the bleaching protocol (p<0.05). The high-viscosity bulk-fill composite resin group had significantly lower ΔE (p<0.05) than the nanoparticulate composite resin group immersed in distilled water. It was concluded that the characteristics of each resin significantly influenced the Ra more than the bleaching protocol. The high-viscosity bulk-fill resin presented minor color change.
RESUMO Este estudo in vitro teve objetivo de avaliar o efeito de protocolos clareadores sobre a rugosidade de superfície (Ra), alteração de cor e micromorfologia de resina bulk-fill de baixa viscosidade (Filtek Bulk Fill Flow, 3M ESPE), alta viscosidade (Filtek Bulk Fill, 3M ESPE) e de uma resina composta nanoparticulada (controle) (Filtek Z350 XT, 3M ESPE). Quarenta amostras de cada resin composta (discos de 5 mm de diâmetro e 2 mm de espessura) foram aleatoriamente divididas em quatro grupos , de acordo com protocolo clareador (n=10): a) Gel de peróxido de carbamida (Opalescence, Ultradent Products) (2 horas/dia, por 14 dias); b) Gel de peróxido de hidrogênio (Opalescence Boost, Ultradent Products) (3 sessões de clareamento, uma por semana, 45 min/sessão); enxaguatório clareador (Listerine Whitening Extreme, Johnson & Johnson) (2 min/dia, por 14 dias); d) água destilada (controle). As amostras foram submetidas a leituras, em triplicata (Ra e cor (parâmetros CIELab) antes e depois do contato com os protocolos clareadores. A micromorfologia de superfície foi conduzida em microscópio eletrônico de varredura (MEV). Ra e parâmetros de cor (ΔL, Δa, Δb e ΔE) foram analisados por modelos lineares generalizados (α=0.05). A Ra da resina bulk-fill de alta viscosidade foi significantemente superior do que para os outros compósitos (pp<0.05). A Ra aumentou significantemente (p<0.05) e a superfície ficou mais irregular (MEV) para todos os compósitos, independente do protocolo clareador (pp<0,05). A resina bulk-fill de alta viscosidade obteve menor ΔE (pp<0.05) do que a resina composta nanoparticulada, imersa em água destilada. Pode-se concluir que as características de cada resina composta influenciaram de forma mais significativa a Ra do que o protocolo clareador. A resina bulk fill de alta viscosidade apresentou menor alteração de cor.
Subject(s)
Humans , Tooth Bleaching/methods , Tooth Discoloration/drug therapy , Viscosity/drug effects , Composite Resins/chemistry , Tooth Bleaching Agents/chemistry , Hydrogen Peroxide/chemistry , Materials Testing , ColorABSTRACT
PURPOSE: To perform a clinical and radiographic evaluation comparing Filtek Bulk Fill high viscosity bulk-fill resins with Filtek Z350 XT nanoparticulate for 1 year. METHODS: 58 restorations were performed for each material (bulk-fill and nanoparticulate), for a total of 116 restorations. Among these, 42 Class I and 16 Class II restorations were performed for each group, in molars and premolars. Clinical evaluation was performed 7 days (baseline), 6 months and 1 year after restorations, using the World Dental Federation (FDI) criteria. Radiographs were obtained at 7 days and 1 year after the restoration was placed and the radiopacity was measured using Image J software at the same time interval. RESULTS: Of the 70 restorations available for evaluation at 1 year, the Mann-Whitney and Friedman tests showed no statistically significant difference for the FDI criteria analyzed. Greater radiopacity was observed for bulk-fill resin compared to nanoparticulate (two-way ANOVA, P= 0.022). This same test showed no difference in radiopacity between the groups in the two evaluation periods (P= 0.062). The high viscosity bulk-fill resin composite presented similar clinical performance to nanoparticulate resin in this evaluation period and higher radiopacity was observed for this material when compared to nanoparticulate resin, in both time periods. CLINICAL SIGNIFICANCE: The high viscosity bulk-fill resin composite showed similar performance to the nanoparticulate resin during the evaluation period of 1 year. Radiopacity showed high values for the bulk-fill resin when compared to nanoparticulate resin. The bulk-fill resin has potential to be used in posterior teeth.
Subject(s)
Dental Materials , Dental Restoration, Permanent , Bicuspid , Composite Resins , Molar , ViscosityABSTRACT
PURPOSE: To evaluate the influence of ceramic laminate on color stability, surface microhardness, water sorption, and solubility of resin luting agents. METHODS: Disk-shaped specimens (10 × 2 mm) of dual-cured resin cements (RelyX ARC or RelyX Ultimate) were obtained, and a light-cured luting agent (RelyX Veneer) was used. In Experiment 1, disk-shaped resin cements (n = 10) were submitted to: I) polymerization with or without ceramic laminate (0.7 mm), and II) immersion in distilled water or coffee, 3 hours daily for 20 days. The surface microhardness loss (%SML) was determined, and the color variables were assessed by the CIE L*a*b* system (ΔE, ΔL*) and the shade guide units (ΔSGU). In Experiment 2, other disk-shaped specimens (n = 5) were submitted to polymerization with or without ceramic laminate to assess their water sorption (WS) and solubility (S). Statistical analysis was performed using 3-way ANOVA and Tukey's test for ΔE, ΔL* and %SML; Mann-Whitney, Kruskal-Wallis, and Dunn's tests for ΔSGU; and 2-way ANOVA and Tukey's test for WS and S. The significance level was set at 5%. RESULTS: No statistically significant differences among the resin cements was observed for %SML, WS, or S, regardless of stain exposure or presence of ceramic laminate during light activation. Coffee caused a significant decrease in ΔL* values. All the resin cements presented visually detectable color alteration for ΔE; however, RelyX Ultimate showed less color change after coffee exposure. RelyX ARC showed the greatest color change in water. RelyX Veneer presented the highest values of ΔSGU, compared with the other resin cements. The WS, S, and %SML of resin cements were not influenced by the staining solution or the presence of ceramic laminate during light activation; however, RelyX Ultimate resin cement presented the best color stability. CLINICAL SIGNIFICANCE: Resin cements can present color changes over time, affecting the long-term esthetic success of laminate ceramic restorations. RelyX Ultimate resin cement presented the best color stability, thus making it a suitable indication for cementing ceramic laminates.
Subject(s)
Dental Porcelain , Resin Cements , Ceramics , Color , Materials Testing , Solubility , WaterABSTRACT
PURPOSE: To evaluate the effect of a zinc chloride (ZnCl2) solution (2% wt), incorporated into a two-step etch-and-rinse adhesive system (AS), on microtensile bond strength (µTBS) to caries-affected dentin (CAD). METHODS: First, the degree of conversion (DC) of the AS with and without the ZnCl2 solution was evaluated by Fourier transform infrared spectroscopy (FTIR). Second, beam-shaped samples (7 mm × 2 mm × 1 mm) were prepared with the AS containing the ZnCl2 solution to perform flexural strength (FS) tests. For µTBS testing purposes, CAD surfaces were etched with phosphoric acid and randomly divided into three groups (n=10) : ZnCl2- AS with ZnCl2; NT (no treatment)- AS without ZnCl2; and CHX - pretreatment with 2% chlorhexidine solution. AS (Adper Single Bond 2) was applied according to the manufacturer's instructions, and resin composite restorations were built up. After 24 hours, the resin-dentin blocks were sectioned into specimens (0.8 mm2), and then subjected to micro;TBS testing immediately following, or after 6 or 12 months of water storage (WS). The adhesive interface was evaluated by scanning electron microscope. Both µTBS and FS tests were performed using a universal testing machine ( 0.5 mm/minute). FS and DC data were submitted to the Student t-test, and µTBS data were subjected to two-way ANOVA and Tukey's test (α= 0.05). RESULTS: DC was not affected by ZnCl2 incorporation into AS (P= 0.2527). Higher FS values were obtained in the group with ZnCl2 added to AS. Regarding µTBS, the mean of the NT group was statistically higher than that of the ZnCl2 or the CHX groups (P< 0.001(, regardless of WS, but the latter groups did not differ from each other. µTBS at 24 hours was statistically superior to that of 6 and 12 months of WS (P< 0.001).
Subject(s)
Dental Bonding , Dentin-Bonding Agents , Acid Etching, Dental , Bisphenol A-Glycidyl Methacrylate , Chlorides , Composite Resins , Dental Stress Analysis , Dentin , Flexural Strength , Humans , Materials Testing , Resin Cements , Tensile Strength , Zinc CompoundsABSTRACT
The aim of this in vitro study was to evaluate the effects of dental bleaching with ozone (O3) on color change and enamel microhardness. Enamel blocks (3 x 3 x 3mm) were randomly distributed for treatments (n=10). Color change (ΔE) and Knoop microhardness of the enamel blocks were evaluated before and after the following treatments: C - deionized water (control); HP - 37.5% hydrogen peroxide (Pola Office+/ SDI); PLA - placebo gel; O3 - ozone; and O2 - oxygen. Four 8-minute applications were used for HP and PLA, and one 19-minute application for O3 and O2.One-way ANOVA revealed that ΔE was not significantly influenced by the treatment (p = 0.112). For the treatments with HP, PLA, O3 andO2, ΔE was greater than 3.3. The paired t test showed significant decrease in microhardness after treatments (p < 0.001) but no significant difference between treatments (ANOVA; p = 0.313). Dental bleaching treatments with O3, HP, O2 and PLA induced enamel color changes that may be clinically discernible, although enamel microhardeness decreased.
O objetivo deste estudo in vitro foi avaliar os efeitos do clareamento dental com ozônio (O3) quanto à alteração de cor e microdureza do esmalte. Blocos de esmalte (3 x 3 x 3mm) foram aleatoriamente distribuídos entre os tratamentos (n=10). Alteração de cor (ΔE) e microdureza Knoop foram avaliados antes e após cada um dos seguintes tratamentos: C água deionizada (controle); PH peróxido de hidrogênio a 37,5% (Pola Office+/ SDI); PLA gel placebo; O3 ozônio; O2 oxigênio. Quatro aplicações de PH e PLA foram realizadas por 8 minutos cada e uma aplicação de O3 e O2 foram realizados por 19 minutos em cada bloco de esmalte. ANOVA a um critério mostrou que os valores de ΔE não foram significativamente influenciados pelo tratamento (p = 0,112). Para os tratamentos com PH, PLA, O3 e O2, o ΔE foi maior que 3,3. O teste t pareado mostrou diminução significativa dos valores de microdureza no final do tratamento quando comparado com o tempo baseline (p < 0,001), mas não houve diferença significativa entre os tratamentos (ANOVA; p = 0,313). O tratamento com O3, PH, O2 e PLA levou a alteração de cor do esmalte clinicamente perceptível, embora tenha sido observada diminuição da microdureza do esmalte com a realização dos tratamentos.
Subject(s)
Dental Enamel/drug effects , Ozone/pharmacology , Tooth Bleaching/methods , Hardness/drug effects , Humans , In Vitro Techniques , Random AllocationABSTRACT
The saliva of patients undergoing orthodontic treatment with fixed appliances can potentially present a delay in the diluting, clearing, and buffering of dietary acids due to an increased number of retention areas. The aim of this clinical trial was to compare salivary pH kinetics of patients with and without orthodontic treatment, following the intake of an acidic beverage. Twenty participants undergoing orthodontic treatment and 20 control counterparts had their saliva assessed for flow rate, pH, and buffering capacity. There was no significant difference between salivary parameters in participants with or without an orthodontic appliance. Salivary pH recovery following acidic beverage intake was slower in the orthodontic subjects compared to controls. Patients with fixed orthodontic appliances, therefore, seem to be at higher risk of dental erosion, suggesting that dietary advice and preventive care need to be implemented during orthodontic treatment.