ABSTRACT
In this work, copper (Cu) matrix composite reinforced with titanium carbide (TiC) was fabricated by powder metallurgy (PM) method with the varying TiC content from 0% to 12% by weight in the step of 4%. The required weight percentage of powders was milled in an indigenously developed ball milling setup. Green compacts were made using a computer-controlled hydraulic press (400 kN) and sintered in a muffle furnace at a temperature of 950°C. Scanning electron microscope (SEM) was used to analyze the distribution of TiC particles in Cu matrix in as-sintered conditions. X-ray diffraction (XRD) analysis resulted in the existence of respective phases in the produced composites. The structural characteristics such as stress, strain, dislocation density, and grain size of the milled composites were evaluated. Cold upsetting was conducted for the sintered composites at room temperature to evaluate the axial (σ z ), hoop (σ Ó© ), hydrostatic (σ m ), and effective (σ eff ) true stresses. These stresses were analyzed against true axial strain (ε z ). Results showed that the increase in the inclusion of weight percentage of TiC into the Cu matrix increases density, hardness, (σ z ), (σ Ó© ), (σ m ), (σ eff ), and stress ratio parameters such as (σ z /σ eff ), (σ θ /σ eff ), (σ m /σ eff ), and (σ z /σ θ ) of the composites.
ABSTRACT
The ternary blends consisting of Chitosan (CS), Nylon 6 (Ny 6) and Montmorillonite clay (MM clay) were prepared by the solution blending method with glutaraldehyde. The prepared ternary blends were characterization by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Thermo gravimetric analysis (TGA), Differential scanning calorimetry (DSC) and Scanning electron microscope (SEM). The FTIR results showed that the strong intermolecular hydrogen bondings were established between chitosan, nylon 6 and montmorillonite clay. TGA showed the thermal stability of the blend is enhanced by glutaraldehyde as Crosslink agent. Results of XRD indicated that the relative crystalline of the pure chitosan film was reduced when the polymeric network was reticulated by glutaraldehyde. Finally, the results of scanning electron microscopy (SEM) indicated that the morphology of the blend was rough and heterogenous. Further, it confirms the interaction between the functional groups of the blend components. The extent of removal of the trace metals was found to be almost the same. The removal of these metals at different pH was also done and the maximum removal of the metals was observed at pH 4.5 for both trace metals. Adsorption studies and kinetic analysis have also been made. Moreover, the protonation of amine groups is induced an electrostatic repulsion of cations. When the pH of the solution was more than 5.5, the sorption rate began to decrease. Besides, the quantity of adsorbate on absorbent was fitted as a function in Langmuir and Freundlich isotherm. The sorption kinetics was tested for pseudo first order and pseudo second order reaction. The kinetic experimental data correlated with the second order kinetic model and rate constants of sorption for kinetic models were calculated and accordingly, the correlation coefficients were obtained.