Polyethersulfone Blended with Titanium Dioxide Nanoribbons/Multi-Wall Carbon Nanotubes for Strontium Removal from Water.

Nanofiltration methods were used and evaluated for strontium removal from wastewater. The phase inversion method was used to create a variety of polyethersulfone (PES)/TiO2 nanoribbons (TNRs)-multi-walled carbon nanotubes (MWCNTs) membranes with varied ratios of TNR-MWCNT nanocomposite. The hydrothermal technique was applied to synthesize the nanocomposite (TNRs-MWCNTs), which was then followed by chemical vapor deposition (CVD). The synthesized membranes were characterized by scanning electron microscopy (SEM), transmission electron microscopy, and FTIR. TNR macrovoids are employed as a support for the MWCNT growth catalyst, resulting in a TNR-MWCNT network composite. The hydrophilicity, mechanical properties, porosity, filtration efficiency of the strontium-containing samples, water flux, and fouling tendency were used to assess the performance of the synthesized membranes. The effect of feed water temperature on water flux was investigated as well as its effect on salt rejection. As the temperature increased from 30 to 90 °C, the salt rejection decreased from 96.6 to 82% for the optimized 0.7 PES/TNR-MWCNT membrane, whereas the water flux increased to ≈150 kg/m2. h. Double successive filtration was evaluated for its high efficiency of 1000 ppm strontium removal, which reached 82.4%.

Enhanced photoelectrochemical water splitting activity of carbon nanotubes@TiO2 nanoribbons in different electrolytes.

Hydrogen production from water splitting by a photocatalytic process is one way that can be used to solve global problems related to energy depletion and environmental pollution. This work aims to design and characterize a novel photocatalyst nanohybrid carbon nanotubes@TiO2 nanoribbons (CNTs@TNRs) for enhanced photoelectrochemical (PEC) water splitting in different electrolytes under visible light irradiance. Here, hydrothermal and chemical vapor deposition (HT-CVD) were combined to grow CNTs @ the nanopits of TNRs producing network of nanohybrid CNTs@TNRs. The structural, morphological, optical, and photocatylatic properties of the TNRs and CNTs@TNRs nanohybrid were characterized by different techniques. The crystallite size is increased from 14.86 nm for TNRs to 21.61 nm for CNTs@TNRs nanohybrid. The CNTs@TNRs nanohybrid has well-resolved nanopits on the surface of the TNRs with an average diameter of 10 nm. The absorption edge of CNTs@TNRs relative to TNRs was strongly shifted to the visible light region. The band gap values are 3.78 and 2.07 eV for TNRs and CNTs@TNRs, respectively. The TNRs and CNTs@TNRs were used for the photocatalytic water splitting under visible light irradiance in Na2S2O3, HCl and KOH electrolytes of different concentrations. The calculated incident photon-to-current conversion efficiency (IPCE) was 97% at 510 nm. These values are higher than those previously reported for different photoelectrodes. The number of hydrogen moles was calculated to be 300 µmol h-1 cm-2. Therefore, our work demonstrates a feasible route for efficient PEC water splitting under sunlight irradiation utilizing the novel CNTs@TNRs photocatalyst.

TiO2 Nanoribbons/Carbon Nanotubes Composite with Enhanced Photocatalytic Activity; Fabrication, Characterization, and Application.

TiO2 nanoribbons (TiO2 NRs) loaded with FeCo-Al2O3 catalyst were synthesized and used as a precursor in the synthesis of TiO2 nanoribbons/carbon nanotubes (TiO2 NRs/CNTs) composite by a chemical vapor deposition (CVD) method. TiO2 NRs and TiO2 NRs/CNTs composite were characterized by XRD, FT-IR, TEM, SEM, EDX and UV-Vis spectrophotometer. The results revealed the formation of TiO2-B and hydrogen titanate nanoribbon like structures by the hydrothermal treatment. After loading TiO2 NRs by FeCo-Al2O3 catalyst and the CVD growth of carbon nanotubes, the synthetic TiO2 nanoribbons converted entirely to TiO2-B nanoribbons with nanopits structure. The composite composed of tube-like nanostructures forming an interlocked network from CNTs and TiO2-B NRs. The composite shows a relatively red-shifted band gap (3.09 eV), broader and stronger UV absorption band relative to TiO2 NRs. The photocatalytic properties of TiO2 NRs and TiO2 NRs/CNTs composite were studied under sunlight irradiation. The photocatalytic degradation of methylene blue (MB) dye was investigated as a function of contact time, dye concentration, and catalyst dose. The kinetics and mechanisms of degradation were discussed. TiO2 NRs/CNTs composite showed higher stability after six runs and 50% shorter irradiation time than TiO2 NRs photocatalyst.