Electrowetting limits electrochemical CO2 reduction in carbon-free gas diffusion electrodes.

CO2 electrolysis might be a key process to utilize intermittent renewable electricity for the sustainable production of hydrocarbon chemicals without relying on fossil fuels. Commonly used carbon-based gas diffusion electrodes (GDEs) enable high Faradaic efficiencies for the desired carbon products at high current densities, but have limited stability. In this study, we explore the adaption of a carbon-free GDE from a Chlor-alkali electrolysis process as a cathode for gas-fed CO2 electrolysis. We determine the impact of electrowetting on the electrochemical performance by analyzing the Faradaic efficiency for CO at industrially relevant current density. The characterization of used GDEs with X-ray photoelectron spectroscopy (XPS) and X-Ray diffraction (XRD) reveals a potential-dependent degradation, which can be explained through chemical polytetrafluorethylene (PTFE) degradation and/or physical erosion of PTFE through the restructuring of the silver surface. Our results further suggest that electrowetting-induced flooding lets the Faradaic efficiency for CO drop below 40% after only 30 min of electrolysis. We conclude that the effect of electrowetting has to be managed more carefully before the investigated carbon-free GDEs can compete with carbon-based GDEs as cathodes for CO2 electrolysis. Further, not only the conductive phase (such as carbon), but also the binder (such as PTFE), should be carefully selected for stable CO2 reduction.

Direct Imaging of Local pH Reveals Bubble-Induced Mixing in a CO2 Electrolyzer.

Electrochemical CO2 reduction poses a promising pathway to produce hydrocarbon chemicals and fuels without relying on fossil fuels. Gas diffusion electrodes allow high selectivity for desired carbon products at high current density by ensuring a sufficient CO2 mass transfer rate to the catalyst layer. In addition to CO2 mass transfer, the product selectivity also strongly depends on the local pH at the catalyst surface. In this work, we directly visualize for the first time the two-dimensional (2D) pH profile in the catholyte channel of a gas-fed CO2 electrolyzer equipped with a bipolar membrane. The pH profile is imaged with operando fluorescence lifetime imaging microscopy (FLIM) using a pH-sensitive quinolinium-based dye. We demonstrate that bubble-induced mixing plays an important role in the Faradaic efficiency. Our concentration measurements show that the pH at the catalyst remains lower at -100 mA cm-2 than at -10 mA cm-2, implying that bubble-induced advection outweighs the additional OH- flux at these current densities. We also prove that the pH buffering effect of CO2 from the gas feed and dissolved CO2 in the catholyte prevents the gas diffusion electrode from becoming strongly alkaline. Our findings suggest that gas-fed CO2 electrolyzers with a bipolar membrane and a flowing catholyte are promising designs for scale-up and high-current-density operation because they are able to avoid extreme pH values in the catalyst layer.

Quinolinium-Based Fluorescent Probes for Dynamic pH Monitoring in Aqueous Media at High pH Using Fluorescence Lifetime Imaging.

Spatiotemporal pH imaging using fluorescence lifetime imaging microscopy (FLIM) is an excellent technique for investigating dynamic (electro)chemical processes. However, probes that are responsive at high pH values are not available. Here, we describe the development and application of dedicated pH probes based on the 1-methyl-7-amino-quinolinium fluorophore. The high fluorescence lifetime and quantum yield, the high (photo)stability, and the inherent water solubility make the quinolinium fluorophore well suited for the development of FLIM probes. Due to the flexible fluorophore-spacer-receptor architecture, probe lifetimes are tunable in the pH range between 5.5 and 11. An additional fluorescence lifetime response, at tunable pH values between 11 and 13, is achieved by deprotonation of the aromatic amine at the quinolinium core. Probe lifetimes are hardly affected by temperature and the presence of most inorganic ions, thus making FLIM imaging highly reliable and convenient. At 0.1 mM probe concentrations, imaging at rates of 3 images per second, at a resolution of 4 µm, while measuring pH values up to 12 is achieved. This enables the pH imaging of dynamic electrochemical processes involving chemical reactions and mass transport.

Inhomogeneities in the Catholyte Channel Limit the Upscaling of CO2 Flow Electrolysers.

The use of gas diffusion electrodes that supply gaseous CO2 directly to the catalyst layer has greatly improved the performance of electrochemical CO2 conversion. However, reports of high current densities and Faradaic efficiencies primarily come from small lab scale electrolysers. Such electrolysers typically have a geometric area of 5 cm2, while an industrial electrolyser would require an area closer to 1 m2. The difference in scales means that many limitations that manifest only for larger electrolysers are not captured in lab scale setups. We develop a 2D computational model of both a lab scale and upscaled CO2 electrolyser to determine performance limitations at larger scales and how they compare to the performance limitations observed at the lab scale. We find that for the same current density larger electrolysers exhibit much greater reaction and local environment inhomogeneity. Increasing catalyst layer pH and widening concentration boundary layers of the KHCO3 buffer in the electrolyte channel lead to higher activation overpotential and increased parasitic loss of reactant CO2 to the electrolyte solution. We show that a variable catalyst loading along the direction of the flow channel may improve the economics of a large scale CO2 electrolyser.

Narrow Pressure Stability Window of Gas Diffusion Electrodes Limits the Scale-Up of CO2 Electrolyzers.

Electrochemical CO2 reduction is a promising process to store intermittent renewable energy in the form of chemical bonds and to meet the demand for hydrocarbon chemicals without relying on fossil fuels. Researchers in the field have used gas diffusion electrodes (GDEs) to supply CO2 to the catalyst layer from the gas phase. This approach allows us to bypass mass transfer limitations imposed by the limited solubility and diffusion of CO2 in the liquid phase at a laboratory scale. However, at a larger scale, pressure differences across the porous gas diffusion layer can occur. This can lead to flooding and electrolyte breakthrough, which can decrease performance. The aim of this study is to understand the effects of the GDE structure on flooding behavior and CO2 reduction performance. We approach the problem by preparing GDEs from commercial substrates with a range of structural parameters (carbon fiber structure, thickness, and cracks). We then determined the liquid breakthrough pressure and measured the Faradaic efficiency for CO at an industrially relevant current density. We found that there is a trade-off between flooding resistance and mass transfer capabilities that limits the maximum GDE height of a flow-by electrolyzer. This trade-off depends strongly on the thickness and the structure of the carbon fiber substrate. We propose a design strategy for a hierarchically structured GDE, which might offer a pathway to an industrial scale by avoiding the trade-off between flooding resistance and CO2 reduction performance.

Automation and Microfluidics for the Efficient, Fast, and Focused Reaction Development of Asymmetric Hydrogenation Catalysis.

Automation and microfluidic tools potentially enable efficient, fast, and focused reaction development of complex chemistries, while minimizing resource- and material consumption. The introduction of automation-assisted workflows will contribute to the more sustainable development and scale-up of new and improved catalytic technologies. Herein, the application of automation and microfluidics to the development of a complex asymmetric hydrogenation reaction is described. Screening and optimization experiments were performed using an automated microfluidic platform, which enabled a drastic reduction in the material consumption compared to conventional laboratory practices. A suitable catalytic system was identified from a library of RuII -diamino precatalysts. In situ precatalyst activation was studied with 1 H/31 P nuclear magnetic resonance (NMR), and the reaction was scaled up to multigram quantities in a batch autoclave. These reactions were monitored using an automated liquid-phase sampling system. Ultimately, in less than a week of total experimental time, multigram quantities of the target enantiopure alcohol product were provided by this automation-assisted approach.

When Flooding Is Not Catastrophic-Woven Gas Diffusion Electrodes Enable Stable CO2 Electrolysis.

Electrochemical CO2 reduction has the potential to use excess renewable electricity to produce hydrocarbon chemicals and fuels. Gas diffusion electrodes (GDEs) allow overcoming the limitations of CO2 mass transfer but are sensitive to flooding from (hydrostatic) pressure differences, which inhibits upscaling. We investigate the effect of the flooding behavior on the CO2 reduction performance. Our study includes six commercial gas diffusion layer materials with different microstructures (carbon cloth and carbon paper) and thicknesses coated with a Ag catalyst and exposed to differential pressures corresponding to different flow regimes (gas breakthrough, flow-by, and liquid breakthrough). We show that physical electrowetting further limits the flow-by regime at commercially relevant current densities (≥200 mA cm-2), which reduces the Faradaic efficiency for CO (FECO) for most carbon papers. However, the carbon cloth GDE maintains its high CO2 reduction performance despite being flooded with the electrolyte due to its bimodal pore structure. Exposed to pressure differences equivalent to 100 cm height, the carbon cloth is able to sustain an average FECO of 69% at 200 mA cm-2 even when the liquid continuously breaks through. CO2 electrolyzers with carbon cloth GDEs are therefore promising for scale-up because they enable high CO2 reduction efficiency while tolerating a broad range of flow regimes.