Loading and thermal behaviour of ZIF-8 metal-organic framework-inorganic glass composites.

Here we describe the synthesis of a compositional series of metal-organic framework crystalline-inorganic glass composites (MOF-CIGCs) containing ZIF-8 and an inorganic phosphate glass, 20Na2O-10NaCl-70P2O5, to expand the library of host matrices for metal-organic frameworks. By careful selection of the inorganic glass component, a relatively high loading of ZIF-8 (70 wt%) was achieved, which is the active component of the composite. A Zn⋯O-P interfacial bond, previously identified in similar composites/hybrid blends, was suggested by analysis of the total scattering pair distribution function data. Additionally, CO2 and N2 sorption and variable-temperature PXRD experiments were performed to assess the composites' properties.

Mechanochemically-induced glass formation from two-dimensional hybrid organic-inorganic perovskites.

Hybrid organic-inorganic perovskites (HOIPs) occupy a prominent position in the field of materials chemistry due to their attractive optoelectronic properties. While extensive work has been done on the crystalline materials over the past decades, the newly reported glasses formed from HOIPs open up a new avenue for perovskite research with their unique structures and functionalities. Melt-quenching is the predominant route to glass formation; however, the absence of a stable liquid state prior to thermal decomposition precludes this method for most HOIPs. In this work, we describe the first mechanochemically-induced crystal-glass transformation of HOIPs as a rapid, green and efficient approach for producing glasses. The amorphous phase was formed from the crystalline phase within 10 minutes of ball-milling, and exhibited glass transition behaviour as evidenced by thermal analysis techniques. Time-resolved in situ ball-milling with synchrotron powder diffraction was employed to study the microstructural evolution of amorphisation, which showed that the crystallite size reaches a comminution limit before the amorphisation process is complete, indicating that energy may be further accumulated as crystal defects. Total scattering experiments revealed the limited short-range order of amorphous HOIPs, and their optical properties were studied by ultraviolet-visible (UV-vis) spectroscopy and photoluminescence (PL) spectroscopy.

Thermally activated structural phase transitions and processes in metal-organic frameworks.

The structural knowledge of metal-organic frameworks is crucial to the understanding and development of new efficient materials for industrial implementation. This review classifies and discusses recent advanced literature reports on phase transitions that occur during thermal treatments on metal-organic frameworks and their characterisation. Thermally activated phase transitions and procceses are classified according to the temperaturatures at which they occur: high temperature (reversible and non-reversible) and low temperature. In addition, theoretical calculations and modelling approaches employed to better understand these structural phase transitions are also reviewed.

Transient intermediate in the formation of an amorphous metal-organic framework.

Amorphous metal-organic frameworks are rarely formed via direct synthesis. Our limited understanding of their atomic assembly in solution prevents full exploitation of their unique structural complexity. Here, we use in situ synchrotron X-ray absorption spectroscopy with sub-second time resolution to probe the formation of the amorphous Fe-BTC framework. Using a combination of spectral fingerprinting, linear combination analysis, and principal component analysis coupled with kinetic analyses, we reveal a multi-stage formation mechanism that, crucially, proceeds via the generation of a transient intermediate species.

Control of ZIF-62 and agZIF-62 Film Thickness within Asymmetric Tubular Supports through Pressure and Dose Time Variation of Atomic Layer Deposition.

Thin-films of metal-organic frameworks (MOFs) have widespread potential applications, especially with the emergence of glass-forming MOFs, which remove the inherent issue of grain boundaries and allow coherent amorphous films to be produced. Herein, it is established that atomic layer deposition (ALD) of zinc oxide lends excellent control over the thickness and localization of resultant polycrystalline and glass zeolitic imidazole framework-62 (ZIF-62) thin-films within tubular α-alumina supports. Through the reduction of the chamber pressure and dose times during zinc oxide deposition, the resultant ZIF-62 films are reduced from 38 µm to 16 µm, while the presence of sporadic ZIF-62 (previously forming as far as 280 µm into the support) is prevented. Furthermore, the glass transformation shows a secondary reduction in film thickness from 16 to 2 µm.

Evidence of Organic Polymeric Behavior in the Glass Transition of Metal-Organic Frameworks.

The origin of the glass transition is still an open debate, especially for the new class of glasses, formed from metal-organic compounds. High-temperature in situ 2H Nuclear Magnetic Resonance (NMR) experiments are performed on deuterated samples of ZIF-62 (Zn(C3H4N2)2-x(C7H6N2)x, with x = 0.25 and x = 0.05), the prototypical metal-organic framework glass former. Using lineshape analysis, frequencies and angular amplitudes of oscillations of the imidazolate ring during heating up to the melt progressively increasing from ≈10 to 150 MHz, and from ≈5° to 25° are found. This behavior is compositionally dependent and points to the origin of the glass transition lying in organic linker movement, in a similar vein to that witnessed in some organics and contrary to the purely inorganic-based view of Metal-Organic Framework (MOF) glasses taken to date. This experimental approach shows the potential to elucidate the melting and/or decomposition process for a wide range of MOFs.

Structural insights into hybrid immiscible blends of metal-organic framework and sodium ultraphosphate glasses.

Recently, increased attention has been focused on amorphous metal-organic frameworks (MOFs) and, more specifically, MOF glasses, the first new glass category discovered since the 1970s. In this work, we explore the fabrication of a compositional series of hybrid blends, the first example of blending a MOF and inorganic glass. We combine ZIF-62(Zn) glass and an inorganic glass, 30Na2O-70P2O5, to combine the chemical versatility of the MOF glass with the mechanical properties of the inorganic glass. We investigate the interfacial interactions between the two components using pair distribution function analysis and solid state NMR spectroscopy, and suggest potential interactions between the two phases. Thermal analysis of the blend samples indicated that they were less thermally stable than the starting materials and had a Tg shifted relative to the pristine materials. Annular dark field scanning transmission electron microscopy tomography, X-ray energy dispersive spectroscopy (EDS), nanoindentation and 31P NMR all indicated close mixing of the two phases, suggesting the formation of immiscible blends.

Interfacial Bonding between a Crystalline Metal-Organic Framework and an Inorganic Glass.

The interface within a composite is critically important for the chemical and physical properties of these materials. However, experimental structural studies of the interfacial regions within metal-organic framework (MOF) composites are extremely challenging. Here, we provide the first example of a new MOF composite family, i.e., using an inorganic glass matrix host in place of the commonly used organic polymers. Crucially, we also decipher atom-atom interactions at the interface. In particular, we dispersed a zeolitic imidazolate framework (ZIF-8) within a phosphate glass matrix and identified interactions at the interface using several different analysis methods of pair distribution function and multinuclear multidimensional magic angle spinning nuclear magnetic resonance spectroscopy. These demonstrated glass-ZIF atom-atom correlations. Additionally, carbon dioxide uptake and stability tests were also performed to check the increment of the surface area and the stability and durability of the material in different media. This opens up possibilities for creating new composites that include the intrinsic chemical properties of the constituent MOFs and inorganic glasses.

Unravelling the Molecular Structure and Confining Environment of an Organometallic Catalyst Heterogenized within Amorphous Porous Polymers.

The catalytic activity of multifunctional, microporous materials is directly linked to the spatial arrangement of their structural building blocks. Despite great achievements in the design and incorporation of isolated catalytically active metal complexes within such materials, a detailed understanding of their atomic-level structure and the local environment of the active species remains a fundamental challenge, especially when these latter are hosted in non-crystalline organic polymers. Here, we show that by combining computational chemistry with pair distribution function analysis, 129 Xe NMR, and Dynamic Nuclear Polarization enhanced NMR spectroscopy, a very accurate description of the molecular structure and confining surroundings of a catalytically active Rh-based organometallic complex incorporated inside the cavity of amorphous bipyridine-based porous polymers is obtained. Small, but significant, differences in the structural properties of the polymers are highlighted depending on their backbone motifs.

Metal-organic framework glass composites.

The melting phenomenon in metal-organic frameworks (MOFs) has been recognised as one of the fourth generation MOF paradigm behaviours. Molten MOFs have high processibility for producing mechanically robust glassy MOF macrostructures, and they also offer highly tunable interfacial characteristics when combined with other types of functional materials, such as crystalline MOFs, inorganic glass and metal halide perovskites. As a result, MOF glass composites have emerged as a family of functional materials with dynamic properties and hierarchical structural control. These nanocomposites allow for sophisticated materials science studies as well as the fabrication of next-generation separation, catalysis, optical, and biomedical devices. Here, we review the approaches for designing, fabricating, and characterising MOF glass composites. We determine the key application opportunities enabled by these composites and explore the remaining hurdles, such as improving thermal and chemical compatibility, regulating interfacial properties, and scalability.

Survival of Zirconium-Based Metal-Organic Framework Crystallinity at Extreme Pressures.

Recent research on metal-organic frameworks (MOFs) has shown a shift from considering only the crystalline high-porosity phases to exploring their amorphous counterparts. Applying pressure to a crystalline MOF is a common method of amorphization, as MOFs contain large void spaces that can collapse, reducing the accessible surface area. This can be either a desired change or indeed an unwanted side effect of the application of pressure. In either case, understanding the MOF's pressure response is extremely important. Three such MOFs with varying pore sizes (UiO-66, MOF-808, and NU-1000) were investigated using in situ high-pressure X-ray diffraction and Raman spectroscopy. Partial crystallinity was observed in all three MOFs above 10 GPa, along with some recovery of crystallinity on return to ambient conditions if the frameworks were not compressed above thresholds of 13.3, 14.2, and 12.3 GPa for UiO-66, MOF-808, and NU-1000, respectively. This threshold was marked by an unexpected increase in one or more lattice parameters with pressure in all MOFs. Comparison of compressibility between MOFs suggests penetration of the pressure-transmitting oil into MOF-808 and NU-1000. The survival of some crystallinity above 10 GPa in all of these MOFs despite their differing pore sizes and extents of oil penetration demonstrates the importance of high-pressure characterization of known structures.

Mapping nanocrystalline disorder within an amorphous metal-organic framework.

Intentionally disordered metal-organic frameworks (MOFs) display rich functional behaviour. However, the characterisation of their atomic structures remains incredibly challenging. X-ray pair distribution function techniques have been pivotal in determining their average local structure but are largely insensitive to spatial variations in the structure. Fe-BTC (BTC = 1,3,5-benzenetricarboxylate) is a nanocomposite MOF, known for its catalytic properties, comprising crystalline nanoparticles and an amorphous matrix. Here, we use scanning electron diffraction to first map the crystalline and amorphous components to evaluate domain size and then to carry out electron pair distribution function analysis to probe the spatially separated atomic structure of the amorphous matrix. Further Bragg scattering analysis reveals systematic orientational disorder within Fe-BTC's nanocrystallites, showing over 10° of continuous lattice rotation across single particles. Finally, we identify candidate unit cells for the crystalline component. These independent structural analyses quantify disorder in Fe-BTC at the critical length scale for engineering composite MOF materials.

ZIF-62 glass foam self-supported membranes to address CH4/N2 separations.

Membranes with ultrahigh permeance and practical selectivity could greatly decrease the cost of difficult industrial gas separations, such as CH4/N2 separation. Advanced membranes made from porous materials, such as metal-organic frameworks, can achieve a good gas separation performance, although they are typically formed on support layers or mixed with polymeric matrices, placing limitations on gas permeance. Here an amorphous glass foam, agfZIF-62, wherein a, g and f denote amorphous, glass and foam, respectively, was synthesized by a polymer-thermal-decomposition-assisted melting strategy, starting from a crystalline zeolitic imidazolate framework, ZIF-62. The thermal decomposition of incorporated low-molecular-weight polyethyleneimine evolves CO2, NH3 and H2O gases, creating a large number and variety of pores. This greatly increases pore interconnectivity but maintains the crystalline ZIF-62 ultramicropores, allowing ultrahigh gas permeance and good selectivity. A self-supported circular agfZIF-62 with a thickness of 200-330 µm and area of 8.55 cm2 was used for membrane separation. The membranes perform well, showing a CH4 permeance of 30,000-50,000 gas permeance units, approximately two orders of magnitude higher than that of other reported membranes, with good CH4/N2 selectivity (4-6).

Glass Formation in Hybrid Organic-Inorganic Perovskites.

Crystalline materials have governed the development of hybrid organic-inorganic perovskites (HOIPs), giving rise to a variety of fascinating applications such as solar cells and optoelectronic devices. With increasing interest in non-crystalline systems, the glassy state of HOIPs has recently been identified. Here, the basic building blocks of crystalline HOIPs appear to be retained, though their glasses lack long-range periodic order. The emerging family of glasses formed from HOIPs exhibits diverse properties, complementary to their crystalline state. This mini review describes the chemical diversity of both three-dimensional and two-dimensional crystalline HOIPs and demonstrates how glasses are produced from these materials. Specifically, current achievements in melt-quenched glasses formed from HOIPs are highlighted. We conclude with our perspective on the future of this new family of materials.

Brittle-to-ductile transition and theoretical strength in a metal-organic framework glass.

Metal-organic framework (MOF) glasses, a new type of melt-quenched glass, show great promise to deal with the alleviation of greenhouse effects, energy storage and conversion. However, the mechanical behavior of MOF glasses, which is of critical importance given the need for long-term stability, is not well understood. Using both micro- and nanoscale loadings, we find that pillars of a zeolitic imidazolate framework (ZIF) glass have a compressive strength falling within the theoretical strength limit of ≥E/10, a value which is thought to be unreachable in amorphous materials. Pillars with a diameter larger than 500 nm exhibited brittle failure with deformation mechanisms including shear bands and nearly vertical cracks, while pillars with a diameter below 500 nm could carry large plastic strains of ≥20% in a ductile manner with enhanced strength. We report this room-temperature brittle-to-ductile transition in ZIF-62 glass for the first time and demonstrate that theoretical strength and large ductility can be simultaneously achieved in ZIF-62 glass at the nanoscale. Large-scale molecular dynamics simulations have identified that microstructural densification and atomistic rearrangement, i.e., breaking and reconnection of inter-atomistic bonds, were responsible for the exceptional ductility. The insights gained from this study provide a way to manufacture ultra-strong and ductile MOF glasses and may facilitate their processing toward real-world applications.

Fabrication of Super-Sized Metal Inorganic-Organic Hybrid Glass with Supramolecular Network via Crystallization-Suppressing Approach.

Metal coordination compound (MCC) glasses [e.g., metal-organic framework (MOF) glass, coordination polymer glass, and metal inorganic-organic complex (MIOC) glass] are emerging members of the hybrid glass family. So far, a limited number of crystalline MCCs can be converted into glasses by melt-quenching. Here, we report a universal wet-chemistry method, by which the super-sized supramolecular MIOC glasses can be synthesized from non-meltable MOFs. Alcohol and acid were used as agents to inhibit crystallization. The MIOC glasses demonstrate unique features including high transparency, shaping capability, and anisotropic network. Directional photoluminescence with a large polarization ratio (≈47 %) was observed from samples doped with organic dyes. This crystallization-suppressing approach enables fabrication of super-sized MCC glasses, which cannot be achieved by conventional vitrification methods, and thus allows for exploring new MCC glasses possessing photonic functionalities.

An Upper Bound Visualization of Design Trade-Offs in Adsorbent Materials for Gas Separations: CO2 , N2 , CH4 , H2 , O2 , Xe, Kr, and Ar Adsorbents.

The last 20 years have seen many publications investigating porous solids for gas adsorption and separation. The abundance of adsorbent materials (this work identifies 1608 materials for CO2 /N2 separation alone) provides a challenge to obtaining a comprehensive view of the field, identifying leading design strategies, and selecting materials for process modeling. In 2021, the empirical bound visualization technique was applied, analogous to the Robeson upper bound from membrane science, to alkane/alkene adsorbents. These bound visualizations reveal that adsorbent materials are limited by design trade-offs between capacity, selectivity, and heat of adsorption. The current work applies the bound visualization to adsorbents for a wider range of gas pairs, including CO2 , N2 , CH4 , H2 , Xe, O2 , and Kr. How this visual tool can identify leading materials and place new material discoveries in the context of the wider field is presented. The most promising current strategies for breaking design trade-offs are discussed, along with reproducibility of published adsorption literature, and the limitations of bound visualizations. It is hoped that this work inspires new materials that push the bounds of traditional trade-offs while also considering practical aspects critical to the use of materials on an industrial scale such as cost, stability, and sustainability.

Formation of a meltable purinate metal-organic framework and its glass analogue.

The chemistries that can be incorporated within melt-quenched zeolitic imidazolate framework (ZIF) glasses are currently limited. Here we describe the preparation of a previously unknown purine-containing ZIF which we name ZIF-UC-7. We find that it melts and forms a glass at one of the lowest temperatures reported for 3D hybrid frameworks.

Thermal Expansion of Metal-Organic Framework Crystal-Glass Composites.

Metal-organic framework crystal-glass composites (MOF CGCs) are a class of materials comprising a crystalline framework embedded within a MOF glass matrix. Herein, we investigate the thermal expansion behavior of three MOF CGCs, incorporating two flexible (MIL-53(Al) and MIL-118) and one rigid (UL-MOF-1) MOF within a ZIF-62 glass matrix. Specifically, variable-temperature powder X-ray diffraction data and thermomechanical analysis show the suppression of thermal expansivity in each of these three crystalline MOFs when suspended within a ZIF-62 glass matrix. In particular, for the two flexible frameworks, the average volumetric thermal expansion (ß) was found to be near-zero in the crystal-glass composite. These results provide a route to engineering thermal expansivity in stimuli-responsive MOF glass composites.

Formation of new crystalline qtz-[Zn(mIm)2] polymorph from amorphous ZIF-8.

The structure of a new ZIF-8 polymorph with quartz topology (qtz) is reported. This qtz-[Zn(mIm)2] phase was obtained by mechanically amorphising crystalline ZIF-8, before heating the resultant amorphous phase to between 282 and 316 °C. The high-temperature phase structure was obtained from powder X-ray diffraction, and its thermal behaviour, CO2 gas sorption properties and dye adsorption ability were investigated.