ABSTRACT
Knowledge about the resistance of wood-polymer composites (WPCs) to biological attack is of high importance for purpose-oriented use in outdoor applications. To gain this knowledge, uniform test methods are essential. EN 15534-1 (2018) provides a general framework, including the recommendation of applying a pre-weathering procedure before the biological laboratory tests. However, the procedure's manner is not specified, and its necessity assumes that a durability test without such pre-weathering will not produce the structural changes that occur during outdoor use. To verify this assumption, this study examined the influence of natural, ground-level pre-weathering on the material properties of different WPC variants, which were tested at intervals of six months in four durability tests under laboratory conditions in accordance with EN 15534-1 (2018). Weathering factors were calculated from determined characteristic values such as mass loss, and loss in moduli of elasticity (MOE) and rupture (MOR). The weathering factors based on mechanical properties tended to decrease with increasing weathering duration. The expected negative influence of pre-weathering on these material properties was thus not confirmed. The weathering factors based on mass loss were subject to high variation. No significant effect of pre-weathering on mass loss due to fungal attack became evident. Overall, the necessity of a pre-weathering step in biological durability tests shall be questioned based on the presented results.
ABSTRACT
Wood in service is sequestering carbon, but it is principally prone to deterioration where different fungi metabolize wood, and carbon dioxide is released back to the atmosphere. A key prerequisite for fungal degradation of wood is the presence of moisture. Conversely, keeping wood dry is the most effective way to protect wood from wood degradation and for long-term binding of carbon. Wood is porous and hygroscopic; it can take up water in liquid and gaseous form, and water is released from wood through evaporation following a given water vapour pressure gradient. During the last decades, the perception of wood-water relationships changed significantly and so did the view on moisture-affected properties of wood. Among the latter is its susceptibility to fungal decay. This paper reviews findings related to wood-water relationships and their role for fungal wood decomposition. These are complex interrelationships not yet fully understood, and current knowledge gaps are therefore identified. Studies with chemically and thermally modified wood are included as examples of fungal wood substrates with altered moisture properties. Quantification and localization of capillary and cell wall water - especially in the over-hygroscopic range - is considered crucial for determining minimum moisture thresholds (MMThr) of wood-decay fungi. The limitations of the various methods and experimental set-ups to investigate wood-water relationships and their role for fungal decay are manifold. Hence, combining techniques from wood science, mycology, biotechnology and advanced analytics is expected to provide new insights and eventually a breakthrough in understanding the intricate balance between fungal decay and wood-water relations. KEY POINTS: ⢠Susceptibility to wood-decay fungi is closely linked to their physiological needs. ⢠Content, state and distribution of moisture in wood are keys for fungal activity. ⢠Quantification and localization of capillary and cell wall water in wood is needed. ⢠New methodological approaches are expected to provide new insights.