Antimony Selenide Solar Cells Fabricated by Hybrid Reactive Magnetron Sputtering.

The fabrication of Sb2Se3 thin-film solar cells deposited by a pulsed hybrid reactive magnetron sputtering (PHRMS) was proposed and examined for different growth conditions. The influence of growth temperature and Se pulse period were studied in terms of morphology, crystal structure, and composition. The Sb2Se3 growth showed to be dependent on the growth temperature, with a larger crystal size for growth at 270 °C. By controlling the Se pulse period, the crystal structure and crystal size could be modified as a function of the supplied Se amount. The solar cell performance for Sb2Se3 absorbers deposited at various temperatures, Se pulse periods and thicknesses were assessed through current-voltage characteristics. A power conversion efficiency (PCE) of 3.7% was achieved for a Sb2Se3 solar cell with 900 nm thickness, Sb2Se3 deposited at 270 °C and Se pulses with 0.1 s duration and period of 0.5 s. Finally, annealing the complete solar cell at 100 °C led to a further improvement of the Voc, leading to a PCE of 3.8%, slightly higher than the best reported Sb2Se3 solar cell prepared by sputtering without post-selenization.

In Vitro and In Vivo Pharmaco-Toxicological Characterization of 1-Cyclohexyl-x-methoxybenzene Derivatives in Mice: Comparison with Tramadol and PCP.

1-cyclohexyl-x-methoxybenzene is a novel psychoactive substance (NPS), first discovered in Europe in 2012 as unknown racemic mixture of its three stereoisomers: ortho, meta and para. Each of these has structural similarities with the analgesic tramadol and the dissociative anesthetic phencyclidine. In light of these structural analogies, and based on the fact that both tramadol and phencyclidine are substances that cause toxic effects in humans, the aim of this study was to investigate the in vitro and in vivo pharmacodynamic profile of these molecules, and to compare them with those caused by tramadol and phencyclidine. In vitro studies demonstrated that tramadol, ortho, meta and para were inactive at mu, kappa and delta opioid receptors. Systemic administration of the three stereoisomers impairs sensorimotor responses, modulates spontaneous motor activity, induces modest analgesia, and alters thermoregulation and cardiorespiratory responses in the mouse in some cases, with a similar profile to that of tramadol and phencyclidine. Naloxone partially prevents only the visual sensorimotor impairments caused by three stereoisomers, without preventing other effects. The present data show that 1-cyclohexyl-x-methoxybenzene derivatives cause pharmaco-toxicological effects by activating both opioid and non-opioid mechanisms and suggest that their use could potentially lead to abuse and bodily harm.

Charge carrier-selective contacts for nanowire solar cells.

Charge carrier-selective contacts transform a light-absorbing semiconductor into a photovoltaic device. Current record efficiency solar cells nearly all use advanced heterojunction contacts that simultaneously provide carrier selectivity and contact passivation. One remaining challenge with heterojunction contacts is the tradeoff between better carrier selectivity/contact passivation (thicker layers) and better carrier extraction (thinner layers). Here we demonstrate that the nanowire geometry can remove this tradeoff by utilizing a permanent local gate (molybdenum oxide surface layer) to control the carrier selectivity of an adjacent ohmic metal contact. We show an open-circuit voltage increase for single indium phosphide nanowire solar cells by up to 335 mV, ultimately reaching 835 mV, and a reduction in open-circuit voltage spread from 303 to 105 mV after application of the surface gate. Importantly, reference experiments show that the carriers are not extracted via the molybdenum oxide but the ohmic metal contacts at the wire ends.

Quantifying losses and thermodynamic limits in nanophotonic solar cells.

Nanophotonic engineering shows great potential for photovoltaics: the record conversion efficiencies of nanowire solar cells are increasing rapidly and the record open-circuit voltages are becoming comparable to the records for planar equivalents. Furthermore, it has been suggested that certain nanophotonic effects can reduce costs and increase efficiencies with respect to planar solar cells. These effects are particularly pronounced in single-nanowire devices, where two out of the three dimensions are subwavelength. Single-nanowire devices thus provide an ideal platform to study how nanophotonics affects photovoltaics. However, for these devices the standard definition of power conversion efficiency no longer applies, because the nanowire can absorb light from an area much larger than its own size. Additionally, the thermodynamic limit on the photovoltage is unknown a priori and may be very different from that of a planar solar cell. This complicates the characterization and optimization of these devices. Here, we analyse an InP single-nanowire solar cell using intrinsic metrics to place its performance on an absolute thermodynamic scale and pinpoint performance loss mechanisms. To determine these metrics we have developed an integrating sphere microscopy set-up that enables simultaneous and spatially resolved quantitative absorption, internal quantum efficiency (IQE) and photoluminescence quantum yield (PLQY) measurements. For our record single-nanowire solar cell, we measure a photocurrent collection efficiency of >90% and an open-circuit voltage of 850 mV, which is 73% of the thermodynamic limit (1.16 V).

Influence of growth conditions on the performance of InP nanowire solar cells.

Nanowire based solar cells have attracted great attention due to their potential for high efficiency and low device cost. Photovoltaic devices based on InP nanowires now have characteristics comparable to InP bulk solar cells. A detailed and direct correlation of the influence of growth conditions on performance is necessary to improve efficiency further. We explored the effects of the growth temperature, and of the addition of HCl during growth, on the efficiency of nanowire array based solar cell devices. By increasing HCl, the saturation dark current was reduced, and thereby the nanowire solar cell efficiency was enhanced from less than 1% to 7.6% under AM 1.5 illumination at 1 sun. At the same time, we observed that the solar cell efficiency decreased by increasing the tri-methyl-indium content, strongly suggesting that these effects are carbon related.

Nanowire Arrays as Cell Force Sensors To Investigate Adhesin-Enhanced Holdfast of Single Cell Bacteria and Biofilm Stability.

Surface attachment of a planktonic bacteria, mediated by adhesins and extracellular polymeric substances (EPS), is a crucial step for biofilm formation. Some pathogens can modulate cell adhesiveness, impacting host colonization and virulence. A framework able to quantify cell-surface interaction forces and their dependence on chemical surface composition may unveil adhesiveness control mechanisms as new targets for intervention and disease control. Here we employed InP nanowire arrays to dissect factors involved in the early stage biofilm formation of the phytopathogen Xylella fastidiosa. Ex vivo experiments demonstrate single-cell adhesion forces up to 45 nN, depending on the cell orientation with respect to the surface. Larger adhesion forces occur at the cell poles; secreted EPS layers and filaments provide additional mechanical support. Significant adhesion force enhancements were observed for single cells anchoring a biofilm and particularly on XadA1 adhesin-coated surfaces, evidencing molecular mechanisms developed by bacterial pathogens to create a stronger holdfast to specific host tissues.

High-Yield Growth and Characterization of ⟨100⟩ InP p-n Diode Nanowires.

Semiconductor nanowires are nanoscale structures holding promise in many fields such as optoelectronics, quantum computing, and thermoelectrics. Nanowires are usually grown vertically on (111)-oriented substrates, while (100) is the standard in semiconductor technology. The ability to grow and to control impurity doping of ⟨100⟩ nanowires is crucial for integration. Here, we discuss doping of single-crystalline ⟨100⟩ nanowires, and the structural and optoelectronic properties of p-n junctions based on ⟨100⟩ InP nanowires. We describe a novel approach to achieve low resistance electrical contacts to nanowires via a gradual interface based on p-doped InAsP. As a first demonstration in optoelectronic devices, we realize a single nanowire light emitting diode in a ⟨100⟩-oriented InP nanowire p-n junction. To obtain high vertical yield, which is necessary for future applications, we investigate the effect of the introduction of dopants on the nanowire growth.

Photoelectrochemical hydrogen production on InP nanowire arrays with molybdenum sulfide electrocatalysts.

Semiconductor nanowire arrays are expected to be advantageous for photoelectrochemical energy conversion due to their reduced materials consumption. In addition, with the nanowire geometry the length scales for light absorption and carrier separation are decoupled, which should suppress bulk recombination. Here, we use vertically aligned p-type InP nanowire arrays, coated with noble-metal-free MoS3 nanoparticles, as the cathode for photoelectrochemical hydrogen production from water. We demonstrate a photocathode efficiency of 6.4% under Air Mass 1.5G illumination with only 3% of the surface area covered by nanowires.

Reversible switching of InP nanowire growth direction by catalyst engineering.

We demonstrate high yield vapor-liquid-solid (VLS) growth of [100]-oriented InP nanowire arrays. The highest yield (97%) is obtained when the catalyst droplet is filled with indium prior to nanowire nucleation to the equilibrium composition during nanowire growth. Using these [100] wires as a template we can reversibly switch between a [100] and a [111] growth direction by varying the indium content of the droplet. Modeling VLS growth by a kinetic nucleation model indicates that the growth direction is governed by the liquid-vapor interface energy that is strongly affected by the indium concentration in the catalyst droplet.

Efficiency enhancement of InP nanowire solar cells by surface cleaning.

We demonstrate an efficiency enhancement of an InP nanowire (NW) axial p-n junction solar cell by cleaning the NW surface. NW arrays were grown with in situ HCl etching on an InP substrate patterned by nanoimprint lithography, and the NWs surfaces were cleaned after growth by piranha etching. We find that the postgrowth piranha etching is critical for obtaining a good solar cell performance. With this procedure, a high diode rectification factor of 10(7) is obtained at ±1 V. The resulting NW solar cell exhibits an open-circuit voltage (Voc) of 0.73 V, a short-circuit current density (Jsc) of 21 mA/cm(2), and a fill factor (FF) of 0.73 at 1 sun. This yields a power conversion efficiency of up to 11.1% at 1 sun and 10.3% at 12 suns.