Reduced Defect Density in MOCVD-Grown MoS2 by Manipulating the Precursor Phase.

Advancements in the synthesis of large-area, high-quality two-dimensional transition metal dichalcogenides such as MoS2 play a crucial role in the development of future electronic and optoelectronic devices. The presence of defects formed by sulfur vacancies in MoS2 results in low photoluminescence emission and imparts high n-type doping behavior, thus substantially affecting material quality. Herein, we report a new method in which single-phase (liquid) precursors are used for the metal-organic chemical vapor deposition (MOCVD) growth of a MoS2 film. Furthermore, we fabricated a high-performance photodetector (PD) and achieved improved photoresponsivity and faster photoresponse in the spectral range 405-637 nm compared to those of PDs fabricated by the conventional MOCVD method. In addition, the fabricated MoS2 thin film showed a threshold voltage shift in the positive gate bias direction owing to the reduced number of S vacancy defects in the MoS2 lattice. Thus, our method significantly improved the synthesis of monolayer MoS2 and can expand the application scope of high-quality, atomically thin materials in large-scale electronic and optoelectronic devices.

Investigation on the Electrical Stability of 5,11-Bis(triethylsilylethynyl)anthradithiophene Thin-Film Transistors.

We investigate the effects of environmental conditions on the electrical stability of spin-coated 5,11-bis(triethylsilylethynyl)anthradithiophene (TES-ADT) thin-film transistors (TFTs) in which crosslinked poly(4-vinylphenol-co-methyl methacrylate) (PVP-co-PMMA) was utilized as a gate insulator layer. Atomic force microscopy observations show molecular terraces with domain boundaries in the spin-coated TEST-ADT semiconductor film. The TFT performance was observed to be superior in the ambient air condition. Under negative gate-bias stress, the TES-ADT TFTs showed a positive threshold voltage shift in ambient air and a negative threshold voltage shift under vacuum. These results are explained through a chemical reaction between water molecules in air and unsubstituted hydroxyl groups in the cross-linked PVP-co-PMMA as well as a charge-trapping phenomenon at the domain boundaries in the spin-coated TES-ADT semiconductor.