ABSTRACT
OBJECTIVE: To investigate fatigue fracture resistance and wear behavior of a polymer infiltrated ceramic network (PICN) material (ENAMIC, Vita Zahnfabrik). METHODS: Anatomically shaped ENAMIC monolithic crowns were milled using a CAD/CAM system. The crowns were cemented on aged dentin-like composite abutments (Z100, 3M ESPE) with resin-based cement (Vita DUO Cement, Vita). The specimens were subjected to 2 types of fatigue and wear tests: (1) accelerated sliding-contact mouth-motion step-stress fatigue test (n=24) in water; and (2) long-term sliding-contact mouth-motion fatigue/wear test using a clinically relevant load (P=200N, n=8) in water. Failure was designated as chip-off or bulk fracture. Optical and scanning electron microscopes were used to examine the occlusal surface and subsurface damage, as well as to reveal the material's microstructure. In addition, wear volume and depth were measured by X-ray micro-computed tomography. RESULTS: For accelerated mouth-motion step-stress fatigue testing, 3 out of the 24 ENAMIC crowns fractured following cyclic loading up to 1700N. Minor occlusal damage and contact-induced cone cracks were observed in all surviving specimens, but no flexural radial cracks were seen. For long-term mouth-motion fatigue/wear testing under a 200N load in water, a small wear scar without significant cracks was observed in all 8 tested ENAMIC crowns. SIGNIFICANCE: Monolithic CAD/CAM ENAMIC crowns showed superior resistance to sliding-contact fatigue fracture and wear.
Subject(s)
Dental Porcelain , Dental Restoration Failure , Dental Stress Analysis , Ceramics , Computer-Aided Design , Crowns , Humans , Materials Testing , Polymers , X-Ray MicrotomographyABSTRACT
OBJECTIVE: A major limiting factor for the widespread use of zirconia in prosthetic dentistry is its poor resin-cement bonding capabilities. We show that this deficiency can be overcome by infiltrating the zirconia cementation surface with glass. Current methods for assessing the fracture resistance of resin-ceramic bonds are marred by uneven stress distribution at the interface, which may result in erroneous interfacial fracture resistance values. We have applied a wedge-loaded double-cantilever-beam testing approach to accurately measure the interfacial fracture resistance of adhesively bonded zirconia-based restorative materials. METHODS: The interfacial fracture energy GC was determined for adhesively bonded zirconia, graded zirconia and feldspathic ceramic bars. The bonding surfaces were subjected to sandblasting or acid etching treatments. Baseline GC was measured for bonded specimens subjected to 7 days hydration at 37°C. Long-term GC was determined for specimens exposed to 20,000 thermal cycles between 5 and 55°C followed by 2-month aging at 37°C in water. The test data were interpreted with the aid of a 2D finite element fracture analysis. RESULTS: The baseline and long-term GC for graded zirconia was 2-3 and 8 times greater than that for zirconia, respectively. More significantly, both the baseline and long-term GC of graded zirconia were similar to those for feldspathic ceramic. SIGNIFICANCE: The interfacial fracture energy of feldspathic ceramic and graded zirconia was controlled by the fracture energy of the resin cement while that of zirconia by the interface. GC for the graded zirconia was as large as for feldspathic ceramic, making it an attractive material for use in dentistry.
Subject(s)
Dental Bonding , Dental Porcelain , Zirconium , Dental Stress Analysis , Materials Testing , Resin Cements , Stress, Mechanical , Surface PropertiesABSTRACT
OBJECTIVES: A recent 3-year randomized controlled trial (RCT) of tooth supported three- to five-unit zirconia-ceramic and metal-ceramic posterior fixed dental prostheses (FDPs) revealed that veneer chipping and fracture in zirconia-ceramic systems occurred more frequently than those in metal-ceramic systems [1]. This study seeks to elucidate the underlying mechanisms responsible for the fracture phenomena observed in this RCT using a descriptive fractographic analysis. METHODS: Vinyl-polysiloxane impressions of 12 zirconia-ceramic and 6 metal-ceramic FDPs with veneer fractures were taken from the patients at the end of a mean observation of 40.3±2.8 months. Epoxy replicas were produced from these impressions [1]. All replicas were gold coated, and inspected under the optical microscope and scanning electron microscope (SEM) for descriptive fractography. RESULTS: Among the 12 zirconia-ceramic FDPs, 2 had small chippings, 9 had large chippings, and 1 exhibited delamination. Out of 6 metal-ceramic FDPs, 5 had small chippings and 1 had large chipping. Descriptive fractographic analysis based on SEM observations revealed that fracture initiated from the wear facet at the occlusal surface in all cases, irrespective of the type of restoration. SIGNIFICANCE: Zirconia-ceramic and metal-ceramic FDPs all fractured from microcracks that emanated from occlusal wear facets. The relatively low fracture toughness and high residual tensile stress in porcelain veneer of zirconia restorations may contribute to the higher chipping rate and larger chip size in zirconia-ceramic FDPs relative to their metal-ceramic counterparts. The low veneer/core interfacial fracture energy of porcelain-veneered zirconia may result in the occurrence of delamination in zirconia-ceramic FDPs.