ABSTRACT
The challenge of dental ceramic degradation necessitates innovative technology, rigorous testing and proactive dental care, demanding collaboration between researchers, dentists and patients to ensure durable and reliable dental restorations.
Subject(s)
Ceramics , Humans , Dental Porcelain , Dental Materials , Dental Restoration Failure , Materials TestingABSTRACT
OBJECTIVE: The aim of the present study was to evaluate the influence of multidirectional brushing on the surface roughness, morphology, and bonding interface of resin-repaired CAD-CAM ceramic and composite restorations. MATERIALS AND METHODS: Twelve (N = 12) blocks (4 mm × 4 mm × 2 mm for parallel axis; 5 mm × 4 mm × 2 mm for perpendicular axis) of lithium disilicate glass-ceramic (IPS e.max CAD, Ivoclar AG) and CAD-CAM resin composite (Tetric CAD, Ivoclar AG) were obtained and repaired with direct resin composite (Clearfil AP-X, Kuraray). An abrasive slurry was prepared and the brushing was performed according to each restorative material and axis of brushing (n = 6; perpendicular to repair interface and parallel to repair interface) during 3,650 cycles (240 strokes per minute) to simulate 3 years of brushing. The surface roughness (Ra) and the profile variation for each material (restoration and direct repair resin composite) were measured at the baseline condition and after brushing, and the mean roughness and presence of steps at the repair interface were evaluated through factorial analysis of Variance (ANOVA). Scanning Electron Microscopy (SEM) images were taken to evaluate the surface topography of the repaired materials after brushing. RESULTS: The mean roughness of the repaired CAD-CAM restorations was affected by the brushing (P < .05), mainly when evaluating the repair material and the interface (P < .05), while the restorative CAD-CAM materials presented more stable values. The profile evaluation showed higher steps at the interface when repairing lithium disilicate than for CAD-CAM resin composite. CONCLUSION: Repaired CAD-CAM restorations were susceptible to wear after brushing simulation. The surface roughness of the direct resin composite was the most affected leading to step development at the interface, particularly in the repaired lithium disilicate samples. Cinical maintenance recalls and polishing protocols must be considered to enhance the longevity of such restorations.
ABSTRACT
OBJECTIVE: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites. MATERIALS AND METHODS: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis. RESULTS: The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups. CONCLUSION: The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material. CLINICAL RELEVANCE: The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.
Subject(s)
Dental Bonding , Methacrylates , Dental Bonding/methods , Surface Properties , Materials Testing , Composite Resins/chemistry , Zirconium/chemistry , Ceramics/chemistry , Shear Strength , Yttrium/chemistry , Resin Cements/chemistry , Dental Stress AnalysisABSTRACT
OBJECTIVES: The aim of the study was to evaluate the effect of surface treatment and resin cement on the bond strength of conventional and advanced lithium disilicates (ALDs). MATERIALS AND METHODS: Ceramic slices (2 × 13 × 15 mm) of conventional lithium disilicate (LD) (IPS e.max CAD) and ALD (CEREC Tessera) were sectioned, polished, and divided into 16 groups (n = 10) according to the factors: ceramic, surface treatment, and resin cement (Panavia V5 and Variolink Esthetic DC). Surface treatments consisted of hydrofluoric acid 4.9% etching for 20 seconds (Hf20) or 30 seconds (Hf30), self-etching ceramic primer (Se), and sandblasting (Sb). Then, a resin cement cylinder (Ø = 2.5 mm) was manufactured on each specimen's surface. The specimens were then submitted to a shear bond strength (SBS) test. Surface roughness was evaluated through a contact profilometer, and surface morphology was evaluated under scanning electron microscopy for qualitative analysis. STATISTICAL ANALYSIS: Two-way analysis of variance (ANOVA) was used to analyze the data of SBS and surface roughness. For bond strength, the effects of surface treatment, resin cement, and the interaction were analyzed for each ceramic. For roughness, analyzed factors include ceramic and surface treatment. RESULTS: ANOVA revealed that ceramic (p = 0.047) and surface treatment (p < 0.001) factors affected the bond strength, while the cements performed similarly. Both materials showed adequate bond strength (ALD 19.1 ± 7.7 MPa; LD 17.1 ± 7.9 MPa). Sb protocol showed the lowest mean value (9.6 ± 2.9 MPa) compared with Hf20 (22.0 ± 7.1 MPa), Hf30 (21.7 ± 7.4 MPa), and Se (19.3 ± 6.0 MPa). CONCLUSION: For both ceramics, the highest performance was obtained after applying Se and Hf20 or Hf30. Therefore, longer etching time is unnecessary. Sb protocol must be avoided.
ABSTRACT
This in vitro study assessed the effectiveness of three cleaning protocols (air-water spray, 37% phosphoric acid, or Ivoclean) on lithium disilicate restorations' fatigue behavior after try-in paste application, compared to a clean condition. Lithium disilicate discs (IPS e.max CAD, Ivoclar) with Ø-= 12 mm and 1 mm thickness were prepared from prefabricated CAD-CAM blocks, polished, subjected to CAD-CAM milling topography simulation and crystallization. After, etching with 5% hydrofluoric acid and the application of try-in paste (Variolink try-in paste shade white; load of 2.5 N for 5 min) was performed. Discs that received try-in paste were divided into three groups according to the removal protocol: SPRAY - air-water spray for 30 s; HPO - active application of 37% phosphoric acid for 60 s; IVOC - application of Ivoclean for 20 s. Control group (CTRL group) did not receive the try-in paste application. Half of the specimens (n= 15) were tested in the baseline condition (24 h up to 7 days), and the others underwent 25,000 thermal cycles (5 - 55 °C) + 210 days of distilled water storage (37 °C). Additional specimens (n= 3) underwent monotonic testing (1 mm/min). Fatigue testing involved a cyclic fatigue approach (20 Hz, initial load = 100 N - 5000 cycles, step size = 50 N - 10,000 cycles) until a visible crack appeared. Fractographic and topographic analyses were performed. Fatigue data were statistically analyzed with two-way ANOVA, Kaplan-Meier log-rank (Mantel-Cox), and independent t-test (α= 0.05). In the baseline condition, the IVOC group resulted in a superior fatigue behavior compared to the CTRL and SPRAY groups, but similar to the HPO group. The HPO and SPRAY presented a similar fatigue behavior to the CTRL group. It was noticed a decrease in fatigue behavior after aging, which resulted in all the cleaning protocols leading to similar fatigue behavior compared to the CTRL group. On the SPRAY group surface, try-in pastes remnants were noticed. In summary, despite a detrimental impact at baseline conditions, all tested cleaning protocols seem proper to remove the try-in paste from the ceramic's surface in the long-term evaluation.
Subject(s)
Ceramics , Dental Porcelain , Phosphoric Acids , Surface Properties , Materials Testing , Ceramics/chemistry , Computer-Aided Design , Water , Dental Stress AnalysisABSTRACT
Objective: To evaluate the effect of different surface treatments on the morphology, shear bond, and flexural fatigue strength of a repaired translucent zirconia. Methods: Monolithic disc-shaped specimens of translucent zirconia were prepared and ground to simulate repair areas. Four groups underwent different treatments: Air-MDP (air-abrasion with alumina particles and 10-MDP primer), Si-Sil (silica-coated alumina particles with MDP-containing silane), Si-MDP (silica coating with 10-MDP primer), and Uni adhe (universal adhesive). After roughness measurements and treatments, repairs were done using resin composite. Shear bond and flexural (n = 15) fatigue tests were performed. Surface topography, interfacial analysis, fractographic, and finite element analysis were conducted. Results: The zirconia roughness was similar between the groups, however, the surface topography was modified according to the surface treatments. Si-Sil generated higher and more stable bond strength values (20.69 MPa) between translucent zirconia and resin composite when compared to Uni adhe (15.75 MPa) considering the fatigue bond strength scenario, while it was similar to Si-MDP (17.70 MPa) and Air-MDP (18.97 MPa). Regarding the mechanical behavior, Si-Sil (680.83 MPa) also showed higher and significantly different fatigue strength when compared to Uni adhe (584.55 MPa), while both were similar to Si-MDP (634.22 MPa) and Air-MDP (641.86 MPa). Conclusion: The association of mechanical and chemical approaches is essential for long-term bond strength and optimized mechanical behavior, being air-abrasion protocols and the use of silane and/or MDP-based primers suitable for zirconia repair protocols. It was found that relying solely on a universal adhesive was not as effective as other options available. Clinical significance: The surface treatment of repair protocols affects translucent zirconia's morphology. To enhance fatigue behavior in repaired monolithic zirconia, air abrasion is crucial. Exclusive use of a universal adhesive is less effective than other choices. A primer containing silane/MDP holds the potential for stable bond strength and optimized mechanical performance.
ABSTRACT
OBJECTIVE: The aim of the study was to evaluate the influence of surface polishing and printing layer orientation on the fatigue behaviour of 3 mol% yttria-stabilized zirconia (3Y-TZP) by stereolithography (SLA) in comparison with subtractive manufacturing. MATERIALS AND METHODS: 60 experimental zirconia bar-shaped specimens were 3D-printed (P) via SLA, and 30 specimens were milled (M) from commercial zirconia block (Lava™ Frame, 3 M ESPE AG). All specimens had the same dimensions (1 mm × 1 mm x 12 mm) after sintering. The 3D-printed specimens were randomly divided according to printing orientations: parallel or perpendicular to the tensile surface in the fatigue test. The specimens were subsequently submitted to two surface finishing protocols (n = 15/gr): unpolished or polished. Their phase compositions were analysed by X-ray diffraction. The fatigue behaviour was evaluated by a stepwise approach. RESULTS: The milled and both 3D-printed groups showed similar phase compositions for the as-sintered condition. Considerable amounts of rhombohedral phase were detected after polishing. Milled unpolished samples presented significantly higher fatigue strength than 3D-printed unpolished samples. Polishing did not improve the fatigue strength for milled zirconia but was advantageous for the 3D-printed specimens. 3D-printed specimens with parallel printing-layer orientation were significantly stronger than specimens with perpendicular layers regardless of surface finishing. CONCLUSION: The manufacturing techniques had a significant influence on the fatigue strength of 3Y-TZP, but not on the phase compositions of the surface. The polishing protocol showed different effects on 3Y-TZP fatigue strength and induced phase transition of the 3Y-TZP from Tetragonal to Rhombohedral. The best fatigue strength was achieved through milling using an unpolished surface and SLA-printed layers that were parallel to the tensile surface, followed by polishing.
Subject(s)
Yttrium , Zirconium , Materials Testing , Surface Properties , Printing, Three-Dimensional , Dental Materials , Dental Polishing , CeramicsABSTRACT
This study evaluated the mechanical behavior and risk of failure of three CAD-CAM crowns repaired with different resin composites through a three-dimensional (3D) finite element analysis. Three-dimensional models of different cusp-repaired (conventional nanohybrid, bulk-fill, and flowable resin composites) crowns made of zirconia, lithium disilicate, and CAD-CAM resin composite were designed, fixed at the cervical level, and loaded in 100 N at the working cusps, including the repaired one. The models were analyzed to determine the Maximum Principal and Maximum Shear stresses (MPa). Complementary, an in vitro shear bond strength test (n = 10) was performed to calculate the risk of failure for each experimental group. The stress distribution among the models was similar when considering the same restorative material. The crown material affected the stress concentration, which was higher for the ceramic models (±9 MPa for shear stress; ±3 MPa for tensile stress) than for the CAD-CAM composite (±7 MPa for shear stress; ±2 MPa for tensile stress). The shear bond strength was higher for the repaired CAD-CAM resin composite (±17 MPa) when compared to the ceramics (below 12 MPa for all groups), while the repair materials showed similar behavior for each substrate. The stress distribution is more homogenous for repaired resin composite crowns, and a flowable direct resin composite seems suitable to repair ceramic crowns with less risk of failure.
ABSTRACT
Purpose: In case of need for esthetical improvement of zirconia restorations, an individualization using extrinsic staining can be applied. This study aimed to evaluate the surface roughness and fatigue strength (survival) of high-translucency zirconia (3Y-TZP, YZ®HT, Vita Zanhfabrik) with extrinsic characterization and/or glaze. Methods: Sixty (60) zirconia discs (12 × 1.2 mm) were obtained, sintered, and randomly distributed among three groups (n = 20) according to the surface finishing protocol: C (control), C + G (extrinsic characterization followed by a glaze layer), and G (glaze layer). The surface roughness (Ra) was analyzed with a contact profilometer. Subsequently, the specimens were subjected to a fatigue load profile starting at 120 N during 20,000 cycles at 4 Hz frequency, with a 5% increase at each step until failure. The failed specimens were evaluated under a stereomicroscope. Surface roughness analysis was evaluated by using one-way ANOVA and post hoc Tukey tests (95%); while fatigue survival probability was analyzed with Kaplan-Meier and Mantel-Cox (log- rank, 95%). Results: One-way ANOVA revealed that surface roughness was affected by the finishing protocol, where C + G showed the highest mean value (0.46 ± 0.18 µm)A followed by G (0.30 ± 0.10 µm)B, and C (0.19 ± 0.02 µm)C. While for fatigue strength, the G protocol presented a higher mean value (243.00, and 222.36-263.63)A, followed by C + G (192.75 and 186.61-198.88)B and C (172.50 and 159.43-185.56)C. Conclusion: Surface finishing protocols modify the surface roughness and fatigue strength of high-translucent zirconia. Regardless of the surface roughness, both glazing protocols improved the ceramic fatigue strength, favoring the restoration's long-term survival.
ABSTRACT
Objective: To evaluate the mechanical properties of different CAD/CAM ceramic systems and the post-fatigue fracture and stress distribution when used as cemented crowns. Materials and methods: Sixty (60) CAD/CAM monolithic crowns were milled using three different ceramic materials (FD - Feldspathic [Vita Mark II]), LE - Leucite-based ceramic [IPS Empress CAD] and LD - Lithium Disilicate [IPS e.max CAD]) and adhesively cemented on resin composite dyes. Specimens were stored in distillated water (37 °C) for 7 days. After, half of the crowns were submitted to immediate fracture load test while the other half was submitted to fatigue cycling. The average cement layer of approximately 80 µm was assessed using scanning electron microscopy (SEM). The average thickness was used in the three-dimensional (3D) Finite Element Analysis (FEA). For each ceramic material, the density, Poisson ratio, shear modulus, Young modulus, fracture toughness, and true hardness were assessed (n = 3). The data was used to assess the Maximum Principal Stress throughout 3D-FEA according to each material during load to fail and post-fatigue. Data were submitted to two-way ANOVA and Tukey test (α = 0.05). Results: LD showed the highest compression load, density, shear modulus, Young modulus, fracture toughness and true hardness values. While LE presented the lowest mechanical properties values. There is no difference in the Poisson ratio between the evaluated ceramics. Conclusion: LD was susceptible to aging process but presented stronger physicomechanical properties, showing the highest post-fatigue fracture load and highest stress magnitude.
ABSTRACT
This study evaluated the effect of pH and temperature on the ion (F- and Ca2+) release of a resin-based material containing alkaline fillers and a self-setting high-viscous glass ionomer cement. Disks were prepared according to manufacturers' instructions for both materials: the EF group (Equia Forte HT filling, GC) and the CN group (Cention N, Ivoclar). Specimens were immersed in 50 mL buffer solution with three different pHs (4.8, 6.8, and 8.8), and stored at 0°, 18°, 37°, and 44 °C. After 24 h, 7 d, and 28 d, cumulative F- and Ca2+ releases were analyzed by chromatography and mass spectrometry, and pH was measured. Both materials showed minimal changes in pH with final values after 28 d of 5.17 ± 0.56 for CN and 5.12 ± 0.24 for EF. In all experimental conditions, the percentages of ion release were higher for EF than for CF. In particular, both materials showed a significant difference in temperature in F- release. Regardless of the pH values, the highest Ca2+ ion release was after 28 days, with a significant difference in temperature for CN and EF. Within the limit of this study, the temperature storage influenced ion release and the high-viscous glass ionomer showed the maximum values.
ABSTRACT
Background: This study investigated the impact of luting procedure and restoration thicknesses on the flexural strength of CAD/CAM restorations. Traditional luting agents have been questioned in favor of pre-heated resin composites or flowable composites. Materials and Methods: 400 disc-shaped restorations (lithium disilicate [IPS e.max CAD] or resin composite [Tetric CAD, Ivoclar]) were cemented onto dentin analog discs using different procedures (n = 20): dual-curing resin cement (Panavia V5), light-curing resin cement (Panavia Veneer LC), pre-heated resin composite (Clearfil™ AP-X) with or without pre-heated restoration, and high-filled flowable composite (Clearfil Majesty™ Flow). The biaxial flexural strength was calculated. Results: There were significant effects of material, thickness, and luting procedure on flexural strength (p < 0.001). Resin composite specimens exhibited lower flexural strength (90 MPa) compared to lithium disilicate specimens (571 MPa), with thicker restorations (338 MPa) being stronger than thinner ones (323 MPa). Light-curing cement showed the highest strength (408.8 MPa)A, followed by dual-curing cement (362 MPa)B, pre-heated cement with pre-heated composite (318 MPa)C, pre-heated composite (304 MPa)C, and flowable resin composite (259 MPa)D. The light-curing cement yielded similar results to the pre-heated resin composite associated or not with the pre-heated crown for the thicker lithium disilicate specimens, whereas for the thinner lithium disilicate specimens all luting procedures performed similarly. Thin resin composite discs showed higher flexural strength when luted with light-curing cement, whereas the luting procedure had less influence for the thicker restorations. Conclusion: Luting procedures impact the flexural strength of CAD/CAM lithium disilicate and resin composite restorations. Pre-heated resin composite, with or without pre-heated restoration, can replace dual-curing cement. Nevertheless, light-curing cement is superior for resin composite and 1.5 mm lithium disilicate restorations.
Different luting procedures significantly impact the flexural strength of CAD/CAM lithium disilicate and resin composite restorations, with light-curing cement demonstrating superior performance for specific thicknesses.Pre-heated resin composites, either with or without pre-heated restorations, offer a viable alternative to conventional dual-curing cement for bonding indirect restorations, presenting potential clinical advantages.Restoration thickness plays a crucial role in the mechanical response of restorations, with thinner resin composite restorations benefiting from dual- or light-curing, while thicker ones are less sensitive to luting procedure variations.
ABSTRACT
Com base no desenvolvimento da odontologia adesiva, restaurações minimamente invasivas em cerâmica são utilizadas como alternativas para restaurar um dente. As cerâmicas odontológicas são amplamente aplicadas na área odontológica principalmente devido à sua estética e resistência mecânica. Uma das propriedades da cerâmica a ser bem conhecida antes de seu uso, é a resistência ao desgaste que deve ser compatível com o comportamento de desgaste do antagonista para evitar desempenhos indesejados. Portanto, vários métodos têm sido realizados para avaliar o comportamento do desgaste dos materiais cerâmicos considerando diferentes condições presentes no complexo meio oral. Este estudo teve como objetivo compilar os métodos utilizados para investigar o desgaste das cerâmicas odontológicas e descrever os mecanismos de desgaste envolvidos nos mesmos. A obtenção e análise de dados também é abordada para discutir os resultados obtidos a partir de diferentes métodos, bem como a análise clínica do desgaste e perspectivas futuras sobre esse tema. Em conclusão, muitas metodologias estão disponíveis para medir o desgaste cerâmico. Portanto, os métodos devem ser selecionados com base na relevência clínica de cada estudo e devem seguir parâmetros previamente relatados para padronização, permitindo a comparação da literatura (AU)
Based on the development of adhesive dentistry, minimally invasive restorations in ceramics are used as alternatives to restore a tooth. Dental ceramics are largely applied in the dentistry field mainly due to their esthetic and mechanical strength. One of the ceramic properties to be well known before its use is the wear resistance that should be compatible with the antagonist wear behavior to avoid unwanted performance. Therefore, several methods have been performed to assess the ceramic materials wear behavior considering different conditions present in the complex oral medium. This study aimed to compile the methods used to investigate dental ceramics wear and to describe the wear mechanisms involved on them. Obtaining and analyzing data is also addressed to discuss the results obtained from different methods, as well as the clinical analysis of wear and future perspectives on this topic. In conclusion, many methodologies are available to measure the ceramic wear. Therefore, the methods must be selected based on the clinical significance of each study and should follow previously reported parameters for standardization, allowing literature comparison. (AU)
Subject(s)
Metal Ceramic Alloys , Dental Restoration Wear , Dental Materials , Tooth Wear , MethodsABSTRACT
OBJECTIVES: This article evaluated the effect of substrates rigidities on the post-fatigue fracture resistance of adhesively cemented simplified restorations in lithium disilicate glass ceramic. METHODS: Precrystalized computer-aided design/computer-aided manufacturing ceramic blocks were processed into disc-shaped specimens (n = 10, Ø = 10 mm), mimicking a simplified restoration at two thicknesses (0.5 and 1.0 mm). Thereafter, the discs were cemented onto different base substrates (dentin analogue [control], dentin analogue with a central core build-up of resin composite [RC], or glass ionomer cement [GIC]). The specimens were subjected to mechanical cycling in a chewing simulator (100 N, 1 × 106 cycles, 4 Hz) and then subjected to thermocycling aging (10,000 cycles, 5/37/55°C, 30 seconds). After the fatigue protocol, the specimens were loaded until failure (N) in a universal testing machine. Finite element analysis calculated the first principal stress at the center of the adhesive interface. RESULTS: The results showed that "restoration thickness," "type of substrate," and their interaction were statistically significant (one-way analysis of variance; p < 0.001). Regardless the restoration thickness a higher fracture load was observed for specimens cemented to dentin analogue. Among the base materials, RC build-up presented the highest fracture load and lower stress magnitude for both restoration thicknesses in comparison with GIC build-up. The 0.5-mm restoration showed higher stress peak and lower fracture load when submitted to the compressive test. CONCLUSION: More flexible base material reduces the fracture load and increases the stress magnitude of adhesively cemented lithium disilicate restorations regardless the ceramic thickness. Therefore, more rigid substrates are suggested to be used to prevent restoration mechanical failures.
ABSTRACT
OBJECTIVE: This investigation evaluated the effect of two sintering modes of a translucent zirconia (Y-TZP) on its surface roughness, topography, phase-transformation (t â m), translucency and biaxial flexure fatigue strength. MATERIALS AND METHODS: To do so, 50 Y-TZP discs (Ø = 15 mm; thickness = 1.2 mm; IPS e.max ZirCAD LT) were prepared and divided into two groups: Standard mode (SM) and Fast mode (FM). Staircase fatigue testing was performed (piston-on-three balls set-up, ISO 6872:2015), as well as surface roughness, profilometry, scanning electron microscopy (SEM-FEG), energy dispersive X-ray spectroscopy (EDX), phase transformation (t â m) using X-ray diffraction analysis (XRD), translucency parameter analysis (TP and TP00 ) and fractography. RESULTS: The results showed no statistical significant differences for roughness parameters (p > 0.05, SM: Ra = 0.13 ± 0.02, Rz = 1.21 ± 0.26 and RSm = 24.91 ± 2.19; FM: Ra = 0.14 ± 0.03, Rz = 1.32 ± 0.25 and RSm = 24.68 ± 2.16) or flexural fatigue strength (SM: 512 (464-560) MPa; FM: 542 (472-611) MPa) between the groups. In addition, similarity in surface morphological features (SEM and profilometry), composition and phases (EDX and XRD) was observed between the firing protocols. Fractography showed that the failure origin occurred on the tensile side. Sintering mode did not affect the TP (F = 0.001, p = 0.97) and TP00 (F = 0.12, p = 0.72). CONCLUSIONS: Therefore, the fast-sintering mode is suggested as a viable alternative to the standard mode since it does not influence the evaluated surface morphology, microstructure, fatigue strength and translucency of a translucent monolithic zirconia. CLINICAL SIGNIFICANCE: The fast sintering mode is a viable alternative for zirconia without compromising its topography, microstructure, mechanical performance or translucency.
Subject(s)
Ceramics , Yttrium , Yttrium/chemistry , Ceramics/chemistry , Materials Testing , Surface Properties , Zirconium/chemistry , Dental Materials/chemistryABSTRACT
Mouthguards (MG) are protective devices that can reduce the risks of facial trauma. However, many athletes do not use them. Additionally, MG wear with coincidental parafunctional activity has not been considered. The aim of this study was to evaluate the stress distribution as a consequence of a direct impact comparing a conventional MG with a novel hybrid appliance (HMG). Using computer-aided design (CAD) software, a human skull was modeled with the teeth inserted into their respective alveolus. The models were divided according to the MG type (conventional or hybrid). The geometries were exported to the computer-aided engineering (CAE) software and the materials were considered isotropic. Fixation was defined at the base of the maxilla. The load was applied using a hockey puck. The total deformation (mm) and the von Mises stress (MPa) results were obtained for the MGs (conventional and hybrid), upper teeth, lower teeth, and maxillary bone. Despite the presence of an MG, it is still possible to observe generated stress in all structures. However, the hybrid design was more efficient than the conventional design in reducing the displacement during the impact and consequently the stress on the upper teeth, lower teeth, and maxillary bone. Higher stress magnitude was more concentrated at the inner portion of the hybrid design than the conventional device. The HMG appliance decreased the stress concentration in the teeth and in the bone, limiting the areas susceptible to injuries to the regions directly impacted by the hockey puck. Although the novel HMG may mitigate injury, some stress will still result, and any possible injury should be evaluated by a dental professional.
ABSTRACT
The present investigation evaluated the effect of the combination of different dental filling materials in Class I cavities under occlusal loading using three-dimensional finite elements analysis (FEA). Six computer-generated and restored models of a lower molar were created in the CAD software and compared according to the biomechanical response during chewing load condition. Two adhesively bonded bulk restorative materials [bulk-fill resin composite (BF) or Alkasite (Alk)] were evaluated with or without the presence of a base material below (flowable resin composite or glass ionomer cement). A food bolus was placed on the occlusal surface mimicking the compressive occlusal load (600 N) during the static linear analysis. The maximum principal stress (tensile) was calculated as stress criteria in enamel, dentin and restoration. All models showed high stresses along the enamel/restoration margin with a similar stress trend for models restored with the same upper-layer material. Stress values up to 12.04 MPa (Alk) or up to 11.12 MPa (BF) were recorded at the enamel margins. The use of flexible polymeric or ionic base material in combination with bulk-fill resin composite or Alk did not reduce the stress magnitude in dentine and enamel. Class I cavities adhesively restored with bulk-fill resin composite showed lighter stress concentration as well as Alk. Therefore, adhesively bonded Alk restoration showed a promising mechanical behavior when used with different base materials or as a bulk restoration for posterior Class I cavity.
ABSTRACT
This study evaluated the influence of distal implants angulation and framework material in the stress concentration of an All-on-4 full-arch prosthesis. A full-arch implant-supported prosthesis 3D model was created with different distal implant angulations and cantilever arms (30° with 10-mm cantilever; 45° with 10-mm cantilever and 45° with 6-mm cantilever) and framework materials (Cobalt-chrome [CoCr alloy], Yttria-stabilized tetragonal zirconia polycrystal [Y-TZP] and polyetheretherketone [PEEK]). Each solid was imported to computer-aided engineering software, and tetrahedral elements formed the mesh. Material properties were assigned to each solid with isotropic and homogeneous behavior. The contacts were considered bonded. A vertical load of 200 N was applied in the distal region of the cantilever arm, and stress was evaluated in Von Misses (σVM) for prosthesis components and the Maximum (σMAX) and Minimum (σMIN) Principal Stresses for the bone. Distal implants angled in 45° with a 10-mm cantilever arm showed the highest stress concentration for all structures with higher stress magnitudes when the PEEK framework was considered. However, distal implants angled in 45° with a 6-mm cantilever arm showed promising mechanical responses with the lowest stress peaks. For the All-on-4 concept, a 45° distal implants angulation is only beneficial if it is possible to reduce the cantilever's length; otherwise, the use of 30° should be considered. Comparing with PEEK, the YTZP and CoCr concentrated stress in the framework structure, reducing the stress in the prosthetic screw.
ABSTRACT
ABSTRACT: To evaluate the stresses generated in upper premolars rehabilitated with ceramic fragments (table-top) of lithium disilicate on the occlusal surface. An upper premolar was modeled following its anatomical references using computer aided design software (Rhinoceros version 5.0 SR8, USA). The dental tissues were individually designed containing enamel, dentin and periodontal ligament. The main anatomical points were used as parameters for model creation. Ceramic fragments were modeled varying their maximum thicknesses as: 0.5 mm, 1.0 mm and 1.5 mm. Solid geometries were exported to the analysis software (ANSYS 17.2, USA) in STEP format. The materials were considered isotropic, homogeneous and linear, and the values of the elastic modulus of the materials and structures were used to perform a static structural mechanical analysis. The set was submitted to 200 N load. The system fixation was defined on the basis of the three- dimensional model, and the results were obtained in MPa according to the failure criteria of the analyzed materials (tensile stress). Occlusal restoration was not detrimental to mechanical behavior. Stress distribution in the internal region of the restoration was similar between the groups. Thicker fragments presented a lower concentration of tensile stress, therefore suggesting better prognosis in attenuating tensile stresses in the tooth region. More conservative occlusal ceramic fragments presented worse prognosis. However, all evaluated thickness for table-tops support the occlusal rehabilitation of upper premolars when submitted to 200 N loading.
RESUMEN: El objetivo fue evaluar las tensiones generadas en los premolares superiores rehabilitados con fragmentos cerámicos (tablero) de disilicato de litio en la superficie oclusal. Se modeló un premolar superior siguiendo sus referencias anatómicas utilizando un software de diseño asistido por computadora (Rhinoceros versión 5.0 SR8, EE. UU.). Los tejidos dentales se moldearon individualmente conteniendo esmalte, dentina y ligamento periodontal. Los principales puntos anatómicos se utilizaron como parámetros para la creación del modelo. Los fragmentos cerámicos se modelaron variando sus espesores máximos como: 0,5 mm, 1,0 mm y 1,5 mm. Las geometrías sólidas se exportaron al software de análisis (ANSYS 17.2, EE. UU.) En formato STEP. Los materiales se consideraron isotrópicos, homogéneos y lineales, y los valores del módulo elástico de los materiales y estructuras se utilizaron para realizar un análisis mecánico estructural estático. El conjunto se sometió a una carga de 200 N. La fijación del sistema se definió a partir del modelo tridimensional, y los resultados se obtuvieron en MPa según los criterios de falla de los materiales analizados (tensión de tracción). La restauración oclusal no perjudica el comportamiento mecánico. La distribución de la tensión en la región interna de la restauración es similar entre los grupos. Los fragmentos más gruesos presentaron una menor concentración de tensión de tracción, lo que sugiere un mejor pronóstico en la atenuación de las tensiones de tracción en la región dentaria. Los fragmentos cerámicos oclusales más conservadores presentaron peor pronóstico. Sin embargo, todos los espesores evaluados para tableros de mesa en disilicato de litio apoyan la rehabilitación oclusal de los premolares superiores cuando se someten a una carga de 200 N.
ABSTRACT
Evidence regarding the effect of the onlay preparation design for different CAD/CAM restorative materials considering the preservation of cusps is lacking. Molars were 3D-modeled in four preparation designs for onlay restoration: traditional design with functional cusp coverage (TFC), non-retentive design with functional cusp coverage (NFC), traditional design with non-functional cusp coverage (TNFC) and non-retentive design with non-functional cusp coverage (NNFC). The restorations were simulated with two CAD/CAM restorative materials: LD-lithium disilicate (IPS e.max CAD) and RC-resin composite (GrandioBloc). A 100 N axial load was applied to the occlusal surface, simulating the centric contact point. Von Mises (VM) and maximum principal (Pmax) stress were evaluated for restorations, cement layer and dental substrate. The non-retentive preparation design reduced the stress concentration in the tooth structure in comparison to the conventional retentive design. For LD onlays, the stress distribution on the restoration intaglio surface showed that the preparation design, as well as the prepared cusp, influenced the stress magnitude. The non-retentive preparation design provided better load distribution in both restorative materials and more advantageous for molar structure. The resin composite restoration on thenon-functional cusp is recommended when the functional cusp is preserved in order to associate conservative dentistry and low-stress magnitude.