ABSTRACT
In an actual economic context, the demand for scandium has grown due to its applications in top technologies. However, further development of new technologies will lead to an increase in the market for Sc related to such technologies. The present study aims to improve and upgrade existing technology in terms of efficient scandium recovery, proposing a new material with selective adsorptive properties for scandium recovery. To highlight the impregnation of Amberlite XAD7HP resin with tri-n-octylphosphine oxide extractant by the solvent-impregnated resin method, the obtained adsorbent material was characterized by physico-chemical techniques. Further, the specific surface of the adsorbent and the zero-point charge of the adsorbent surface have been determined. Different parameters, such as initial concentration, adsorbent amount, contact time, or temperature, have been studied. The initial pH effect was investigated when a maximum adsorption capacity of 31.84 mg g-1 was obtained at pH > 3, using 0.1 g of adsorbent and a contact time of 90 min and 298 K. An attempt was made to discuss and provide a clear representation of the studied adsorption process, proposing a specific mechanism for Sc(III) recovery from aqueous solutions through kinetic, thermodynamic, and equilibrium studies. Adsorption/desorption studies reveal that the prepared adsorbent material can be reused five times.
ABSTRACT
Industry represents a fundamental component of modern society, with the generation of massive amounts of industrial waste being the inevitable result of development activities in recent years. Red mud is an industrial waste generated during alumina production using the Bayer process of refining bauxite ore. It is a highly alkaline waste due to the incomplete removal of NaOH. There are several opinions in both the literature and legislation on the hazards of red mud. According to European and national legislation, this mud is not on the list of hazardous wastes; however, if the list of criteria are taken into account, it can be considered as hazardous. The complex processing of red mud is cost-effective because it contains elements such as iron, manganese, sodium, calcium, magnesium, zinc, strontium, lead, copper, cadmium, bismuth, barium and rare earths, especially scandium. Therefore, the selection of an extraction method depends on the form in which the element is present in solution. Extraction is one of the prospective separation and concentration methods. In this study, we evaluated the kinetic modelling of the solid-liquid acid extraction process of predominantly scandium as well as other elements present in red mud. Therefore, three acids (HCl, HNO3 and H2SO4) at different concentrations (10, 20 and 30%) were targeted for the extraction of Sc(III) from solid red mud. Specific parameters of the kinetics of the extraction process were studied, namely the solid:liquid ratio, initial acid concentration, contact time and temperature. The extraction kinetics of Sc(III) with acids was evaluated using first- and second-order kinetic models, involving kinetic parameters, rate constants, saturation concentration and activation energy. The second-order kinetic model was able to describe the mechanism of Sc(III) extraction from red mud. In addition, this study provides an overview on the mechanism of mass transfer involved in the acid extraction process of Sc(III), thereby enabling the design, optimization and control of large-scale processes for red mud recovery.
ABSTRACT
In this paper, we studied the scandium adsorption from aqueous solutions on the surface of low-temperature-activated alumina products (GDAH). The GDAH samples are industrially manufactured, coming from the Bayer production cycle of the Sierra Leone bauxite as aluminium hydroxide, and further, by drying, milling, classifying and thermally treating up to dehydroxilated alumina products at low temperature. All experiments related to hydroxide aluminium activation were conducted at temperature values of 260, 300 and 400 °C on samples having the following particle sizes: <10 µm, 20 µm, <45 µm and <150 µm, respectively. The low-temperature-activated alumina products were characterised, and the results were published in our previous papers. In this paper, we studied the scandium adsorption process on the above materials and related thermodynamic and kinetic studies.