ABSTRACT
Magnesium (Mg) is a promising conductive metallic biomaterial due to its desirable mechanical properties for load bearing and biodegradability in human body. Controlling the rapid degradation of Mg in physiological environment continues to be the key challenge toward clinical translation. In this study, we investigated the effects of conductive poly(3,4-ethylenedioxythiophene) (PEDOT) coating on the degradation behavior of Mg substrates and their cytocompatibility. Human embryonic stem cells (hESCs) were used as the in vitro model system to study cellular responses to Mg degradation because they are sensitive and can potentially differentiate into many cell types of interest (e.g., neurons) for regenerative medicine. The PEDOT was deposited on Mg substrates using electrochemical deposition. The greater number of cyclic voltammetry (CV) cycles yielded thicker PEDOT coatings on Mg substrates. Specifically, the coatings produced by 2, 5, and 10 CV cycles (denoted as 2×-PEDOT-Mg, 5×-PEDOT-Mg, and 10×-PEDOT-Mg) had an average thickness of 31, 63, and 78 µm, respectively. Compared with non-coated Mg samples, all PEDOT coated Mg samples showed slower degradation rates, as indicated by Tafel test results and Mg ion concentrations in the post-culture media. The 5×-PEDOT-Mg showed the best coating adhesion and slowest Mg degradation among the tested samples. Moreover, hESCs survived for the longest period when cultured with the 5×-PEDOT-Mg samples compared with the non-coated Mg and 2×-PEDOT-Mg. Overall, the results of this study showed promise in using PEDOT coating on biodegradable Mg-based implants for potential neural recording, stimulation and tissue engineering applications, thus encouraging further research.
Subject(s)
Bridged Bicyclo Compounds, Heterocyclic/chemistry , Coated Materials, Biocompatible , Embryonic Stem Cells/cytology , Magnesium/chemistry , Neurons/cytology , Polymers/chemistry , Humans , Microscopy, Electron, ScanningABSTRACT
In an attempt to develop biodegradable, mechanically strong, biocompatible, and conductive nerve guidance conduits, pure magnesium (Mg) was used as the biodegradable substrate material to provide strength while the conductive polymer, poly(3,4-ethylenedioxythiophene) (PEDOT) was used as a conductive coating material to control Mg degradation and improve cytocompatibility of Mg substrates. This study explored a series of electrochemical deposition conditions to produce a uniform, consistent PEDOT coating on large three-dimensional Mg samples. A concentration of 1 M 3,4-ethylenedioxythiophene in ionic liquid was sufficient for coating Mg samples with a size of 5 × 5 × 0.25 mm. Both cyclic voltammetry (CV) and chronoamperometry coating methods produced adequate coverage and uniform PEDOT coating. Low-cost stainless steel and copper electrodes can be used to deposit PEDOT coatings as effectively as platinum and silver/silver chloride electrodes. Five cycles of CV with the potential ranging from -0.5 to 2.0 V for 200 s per cycle were used to produce consistent coatings for further evaluation. Scanning electron micrographs showed the micro-porous structure of PEDOT coatings. Energy dispersive X-ray spectroscopy showed the peaks of sulfur, carbon, and oxygen, indicating sufficient PEDOT coating. Adhesion strength of the coating was measured using the tape test following the ASTM-D 3359 standard. The adhesion strength of PEDOT coating was within the classifications of 3B to 4B. Tafel tests of the PEDOT coated Mg showed a corrosion current (I(CORR)) of 6.14 × 10(-5) A as compared with I(CORR) of 9.08 × 10(-4) A for non-coated Mg. The calculated corrosion rate for the PEDOT coated Mg was 2.64 mm/year, much slower than 38.98 mm/year for the non-coated Mg.
Subject(s)
Coated Materials, Biocompatible/chemistry , Coated Materials, Biocompatible/chemical synthesis , Electroplating , Magnesium/chemistry , Absorbable Implants , Bridged Bicyclo Compounds, Heterocyclic/chemistry , Coated Materials, Biocompatible/pharmacology , Corrosion , Electric Conductivity , Electrochemical Techniques , Electroplating/methods , Guided Tissue Regeneration/instrumentation , Guided Tissue Regeneration/methods , Magnesium/pharmacology , Materials Testing , Models, Biological , Neural Conduction/drug effects , Neural Conduction/physiology , Polymers/chemical synthesis , Polymers/chemistry , Polymers/pharmacology , Surface Properties/drug effectsABSTRACT
Bacterial infection often causes clinical complications and failure of indwelling medical devices. This is a major problem of current ureteral stents, which are used clinically to treat the blockage of ureteral canals. This study investigates the effectiveness and applicability of magnesium as a novel biodegradable ureteral stent material that has inherent antimicrobial properties. Incubating Escherichia coli with the magnesium samples showed a decrease in the bacterial cell density as compared with the currently used commercial polyurethane stent. Magnesium degradation in the immersion solutions (artificial urine, luria bertani broth, and deionized water) resulted in an alkaline pH shift. Antimicrobial and biodegradation properties of magnesium make it an attractive alternative as next-generation ureteral stent material.