Prediction of the mechanical response of a 3D (bio)printed hybrid scaffold for improving bone tissue regeneration by structural finite element analysis.

Scaffolds for bone tissue engineering should be osteoinductive, osteoconductive, biocompatible, biodegradable, and, at the same time, exhibit proper mechanical properties. The present study investigated the mechanical properties of a coprinted hybrid scaffold made of polycaprolactone (PCL) and an alginate-based hydrogel, which was conceived to possess a double function of in vivo bio-integration (due to the ability of the hydrogel to release lyosecretome, a freeze-dried formulation of mesenchymal stem cell secretome with osteoinductive and osteoconductive properties) and withstanding loads (due to the presence of polycaprolactone, which provides mechanical resistance). To this end, an in-silico study was conducted to predict mechanical properties. Structural finite element analysis (FEA) of the hybrid scaffold under compression was performed to compare the numerical results with the corresponding experimental data. The impact of alginate inclusion and infill patterns on scaffold stiffness was investigated. Results show an increase in mechanical properties by changing the scaffold infill pattern (linear: 145.38±28.90 vs. honeycomb: 278.96±50.19, mean and standard deviation, n = 8), while alginate inclusion does not always impact the mechanical performance of the hybrid scaffold (stiffness: 145.38±28.90 vs. 195.42±38.68 N/mm, with vs without hydrogel inclusion, respectively). This is confirmed by FEA analysis, in which a good correspondence between experimental and numerical stiffness is shown (142±28.94 vs. 117.18, respectively, linear scaffold with hydrogel inclusion). In conclusion, the computational framework is a valid tool for predicting the mechanical performance of scaffolds and is promising for future clinical applications in the maxillofacial field.

Silk Fibroin Bioink for 3D Printing in Tissue Regeneration: Controlled Release of MSC extracellular Vesicles.

Sodium alginate (SA)-based hydrogels are often employed as bioink for three-dimensional (3D) scaffold bioprinting. They offer a suitable environment for cell proliferation and differentiation during tissue regeneration and also control the release of growth factors and mesenchymal stem cell secretome, which is useful for scaffold biointegration. However, such hydrogels show poor mechanical properties, fast-release kinetics, and low biological performance, hampering their successful clinical application. In this work, silk fibroin (SF), a protein with excellent biomechanical properties frequently used for controlled drug release, was blended with SA to obtain improved bioink and scaffold properties. Firstly, we produced a printable SA solution containing SF capable of the conformational change from Silk I (random coil) to Silk II (ß-sheet): this transition is a fundamental condition to improve the scaffold's mechanical properties. Then, the SA-SF blends' printability and shape fidelity were demonstrated, and mechanical characterization of the printed hydrogels was performed: SF significantly increased compressive elastic modulus, while no influence on tensile response was detected. Finally, the release profile of Lyosecretome-a freeze-dried formulation of MSC-secretome containing extracellular vesicles (EV)-from scaffolds was determined: SF not only dramatically slowed the EV release rate, but also modified the kinetics and mechanism release with respect to the baseline of SA hydrogel. Overall, these results lay the foundation for the development of SA-SF bioinks with modulable mechanical and EV-release properties, and their application in 3D scaffold printing.