Early monitoring of inlay wear after total knee arthroplasty on plain radiographs using model-based wear measurement.

Wear of the ultra-high molecular-weight polyethylene (UHMWPE) component in total knee arthroplasty contributes to implant failure. It is often detected late, when patients experience pain or instability. Early monitoring could enable timely intervention, preventing implant failure and joint degeneration. This study investigates the accuracy and precision (repeatability) of model-based wear measurement (MBWM), a novel technique that can estimate inlay thickness and wear radiographically. Six inlays were milled from non-crosslinked UHMWPE and imaged via X-ray in anteroposterior view at flexion angles 0°, 30°, and 60° on a phantom knee model. MBWM measurements were compared with reference values from a coordinate measurement machine. Three inlays were subjected to accelerated wear generation and similarly evaluated. MBWM estimated inlay thickness with medial and lateral accuracies of 0.13 ± 0.09 and 0.14 ± 0.09 mm, respectively, and linear wear with an accuracy of 0.07 ± 0.06 mm. Thickness measurements revealed significant lateral differences at 0° and 30° (0.22 ± 0.08 mm vs. 0.06 ± 0.06 mm, respectively; t-test, p = 0.0002). Precision was high, with average medial and lateral differences of - 0.01 ± 0.04 mm between double experiments. MBWM using plain radiographs presents a practical and promising approach for the clinical detection of implant wear.

Radiopacity Enhancements in Polymeric Implant Biomaterials: A Comprehensive Literature Review.

Polymers as biomaterials possess favorable properties, which include corrosion resistance, light weight, biocompatibility, ease of processing, low cost, and an ability to be easily tailored to meet specific applications. However, their inherent low X-ray attenuation, resulting from the low atomic numbers of their constituent elements, i.e., hydrogen (1), carbon (6), nitrogen (7), and oxygen (8), makes them difficult to visualize radiographically. Imparting radiopacity to radiolucent polymeric implants is necessary to enable noninvasive evaluation of implantable medical devices using conventional imaging methods. Numerous studies have undertaken this by blending various polymers with contrast agents consisting of heavy elements. The selection of an appropriate contrast agent is important, primarily to ensure that it does not cause detrimental effects to the relevant mechanical and physical properties of the polymer depending upon the intended application. Furthermore, its biocompatibility with adjacent tissues and its excretion from the body require thorough evaluation. We aimed to summarize the current knowledge on contrast agents incorporated into synthetic polymers in the context of implantable medical devices. While a single review was found that discussed radiopacity in polymeric biomaterials, the publication is outdated and does not address contemporary polymers employed in implant applications. Our review provides an up-to-date overview of contrast agents incorporated into synthetic medical polymers, encompassing both temporary and permanent implants. We expect that our results will significantly inform and guide the strategic selection of contrast agents, considering the specific requirements of implantable polymeric medical devices.

Implications of ageing effects on thermal and mechanical properties of PMMA-based bone cement for THA revision surgery.

Loosening and infection are the main reasons for revision surgery in total hip arthroplasty (THA). Removing partially detached cemented implant components during revision surgery remains challenging and poses the risk of periprosthetic bone damage. A promising approach for a gentler removal of partially detached prostheses involves softening the PMMA-based bone cement by heating it above its glass transition temperature (TG), thus loosening the implant-cement bond. It is assumed that the TG of PMMA-based bone cement decreases in-vivo due to the gradual absorption of body fluid. Reliable data on TG are essential to develop a heat-based method for removing cemented implant components during revision surgery. The effect of water absorption was investigated in-vitro by ageing PMMA-based bone cement samples for different periods up to 56 days in both Ringer's solution (37 °C) and air (37 °C and 30% humidity). Subsequently, the TG and Vicat softening temperatures of the samples were determined by differential scanning calorimetry and Vicat tests, respectively, according to prescribed methods. Over the entire ageing period, i.e. comparing one day of ageing in air and 56 days in Ringer's solution, the Vicat softening temperature dropped by 16 °C, while the TG dropped by 10 °C for Palacos® R PMMA-based bone cement. Water absorption over time correlated significantly with the Vicat softening temperature until saturation of the PMMA-based bone cement was reached. Based on the TG and Vicat softening temperature measurements, it can be assumed that in body-aged bone cement, an optimal softening can be achieved within a temperature range of 85 °C-93 °C to loosen the bond between the PMMA-based bone cement mantle and the prosthesis stem. These findings may pave the way for a gentler removal of the implant in revision THA.